The purpose of this paper is to study the potential of alumina (Al₂O₃) in nanometer size in automotive brake friction materials.

Four brake linings containing alumina differing in particle size (355 µm and 80 nm) and various amount (5 and 10 Wt.%) were designed and produced. The hardness, density and porosity of the samples were measured. All samples were tested on a full-scale brake dynamometer with gray cast iron disc to determine the tribological properties. Detailed examinations on the worn surface were analyzed using a scanning electron microscopy.

It was concluded that all performance parameters were beneficially affected because of nano alumina.

This paper emphasizes the importance of nano-composites in the automotive industry and helps industrial firms and academicians working on wear of materials.

Among the components used for a car brake lining, the chemical and structural properties of the abrasives, jointly with the morphology and size of the particles influence the friction parameters and stability of the composite. This paper aims to investigate the effect of nano SiO2 particles in brake pads on friction and wear properties.

In this paper, the effects of SiO₂ (Silica) particles of varying size on the friction-wear properties of polymeric friction composites are investigated. Four friction composites were prepared containing (5, 10 Wt.%) micro silica (MS) particles and (5, 10 Wt.%) nano silica (NS) particles. The samples were produced by a conventional procedure for a dry formulation following dry-mixing, pre-forming and hot pressing. Friction and wear characteristics of the specimens against to a disk made of cast iron were studied. Friction coefficient, specific wear rate and hardness of specimens were obtained. Detailed examinations on the worn surface were analyzed using a scanning electron microscope.

The results of test showed that the inclusion of nano silicon carbide (SiC) powder improved the wear performance significantly. Friction coefficient (μ) of NS samples was higher than the MS samples. Micro-SiC showed poor performance and μ. High wear performance was exhibited in materials containing 5 Wt.% NS and 10 Wt.% NS.

This paper emphasizes the importance of nano-composites in the automotive industry and helps to industrial firms and academicians working on wear of materials.