This study aims to investigate the electrochemical corrosion performance of high velocity oxygen fuel (HVOF) sprayed WC–12Co coating in 3.5 Wt.% NaCl solution, which provided a guiding significance on the corrosion resistance of H13 hot work mould steel.

A WC–12Co coating was fabricated on H13 hot work mould steel using a HVOF, and the electrochemical corrosion behaviors of WC–12Co coating and substrate in 3.5 Wt.% NaCl solution was measured using open circuit potential (OCP), potentiodynamic polarization curve (PPC) and electrochemical impedance spectroscopy (EIS) tests.

The OCP and PPC of WC–12Co coating positively shift than those of substrate, its corrosion tendency and corrosion rate decrease to enhance its corrosion resistance. The curvature radius of capacitance curve on the WC–12Co coating is larger than that on the substrate, and the impedance and polarization resistance of WC–12Co coating increase faster than those of substrate, which reduces the corrosion process.

The electrochemical corrosion behaviors of WC–12Co coating and substrate in 3.5 Wt.% NaCl solution is first measured using OCP, PPC and EIS tests, which improve the electrochemical corrosion resistance of H13 hot work mould steel.

This paper aims to investigate the effect of coating microstructure, mechanical and oxidation property on the tribological behaviour of low-pressure plasma spraying (LPPS) tungsten carbide/cobalt (WC-Co) coatings.

WC-12Co and WC-17Co coatings were deposited via the LPPS spraying method. Tribological tests on the coatings were performed using a high-temperature ball-on-disc tribometer at temperatures from room temperature (RT, approximately 25 °C) up to 800 °C in ambient air.

WC-12Co coating contained brittle phases, pores and microcracks, which led to the low hardness, and finally promoted the splat delamination and the carbide debonding during wear. WC-17Co coating had higher cobalt content which benefited the coating to contain more WC particles, less brittle phases, pores and nearly no microcracks, and resulted in the high hardness and better wear resistance. Higher cobalt content also decelerated the oxidation rate of the coating and promoted the formation of cobalt oxides and CoWO4, which were able to maintain the load-bearing capacity and improve the tribological behaviour of the coating below 650°C. Above 650°C, the increase of oxidation degree and the decrease of mechanical property deteriorated the wear resistance of coatings.

The LPPS WC-Co coating with higher cobalt content had better tribological properties at different temperatures. The LPPS WC-Co coatings should not be used as wear-resistant coatings above 650 °C.

This paper aims to compare the wear behavior, surface roughness, friction coefficient and volume loss of high-velocity oxy-fuel (HVOF) sprayed WC–Co and WC–Cr₃C₂–Ni coatings on AISI 1095 steel with spraying times of 10 and 15 s.

In this study, the pin-on-disc testing technique was used to evaluate the wear characteristics at a speed of 0.24 m/s, load of 40 N and test time of 60 min under dry conditions at room temperature. The wear characteristics were examined and analyzed by scanning electron microscopy and energy dispersive X-ray spectroscopy. The surface roughness of a coated surface was measured, and microhardness measurements were performed on the cross-sectioned and polished surfaces of the coating.

Spraying time and powder material affected the hardness of HVOF coatings due to differences in the porosity of the coated layers. The average hardness of the WC–Cr₃C₂–Ni coating with a spaying time of 15 s was approximately 14% higher than that of the WC–Cr₃C₂–Ni coating with a spraying time of 10 s. Under an applied load of 40 N, the WC–Co coating with a spraying time of 15 s had the lowest variation in the friction coefficient compared with the other coatings. The WC–Co coating with a spraying time of 10 s had the lowest average and variation in volume loss compared to the other coatings. The WC–Cr₃C₂–Ni coating with a spraying time of 10 s exhibited the highest average volume loss. The wear features changed slightly with the spraying time owing to variations in the hardness and friction coefficient.

This study investigated tribological performance of WC–Co; WC-Cr₃C₂-Ni coatings with spraying times of 10 and 15 s using pin-on-disc tribometer by rotating the relatively soft pin (C45 steel) against hard coated substrate (disc).

This paper aims to perform the solid particle erosion studies in simulated coal-fired boiler conditions with a view to compare the erosion behavior of two different types of detonation gun (D-Gun) sprayed cermet coating powders, that is, WC-12%Co and Cr₃C₂-25%NiCr on ASTM A36 steel and bare (uncoated) ASTM A36 steel.

Erosion studies were performed using an air jet erosion test rig at impingement angles of 45°, 60° and 90°. During the erosion studies weight loss, erosion rates in terms of volume loss (mm³/g) and measurement of erosion profiles were determined using optical profilometer.

Both cermet coatings had successfully protected the ASTM A36 steel from erosion at impingement angles of 45°, 60° and 90°. In the case of bare ASTM A36 steel, the erosion rates were maximal at an impingement angle of 45° and minimal at an impingement angle of 90°, thus depicting the peculiar erosion behavior of ductile materials. WC-12%Co coated specimens exhibited erosion behavior that is closer to the behavior of ductile materials. Cr₃C₂-25%NiCr coated specimens exhibited the maximum erosion rate at an impingement angle of 90° and minimum at an impingement angle of 45°, hence depicting the typical behavior of brittle materials.

It is expected that these results will contribute to the improvement of erosion resistance of induced draft fans, by the application of D-Gun sprayed WC-12%Co and Cr₃C₂-25%NiCr cermet coatings.

This paper evaluates the solid particle erosion behavior of bare and cermet-coated ASTM A36 steel which will be helpful in choosing the suitable cermet coating for induced draft fan applications.

The purpose of this study is to prepare WC-10Co-4Cr coatings using two processes of plasma spraying and high-velocity oxygen fuel (HVOF) spraying. The decarburization behaviors of the different processes are analyzed individually. The microstructural characteristics of the as-sprayed coatings are presented and the wear mechanisms of the different WC–10Co–4Cr coatings are discussed in detail.

The WC–10Co–4Cr coatings were formed on the surface of Q235 steel by plasma and HVOF spraying.

Plasma spraying causes more decarburizing decomposition of the WC phase than HVOF spraying. In the plasma spraying process, η(Cr25Co25W8C2) phase appears and the C content decreases from the top surface of the coating to the substrate.

In this study, two WC–10Co–4Cr coatings on Q235 steel prepared by plasma and HVOF spraying were compared with respect to the sliding wear behavior.

The wear mechanisms of the plasma- and HVOF-sprayed coatings were abrasive and oxidation, respectively.

The purpose of this study is to investigate the effect of laser scanning speed (LSS) on the corrosive-tribological performance of Ni-60%WC coating in Wusu mine water, which was beneficial to improve the friction–wear performance of cylinder liner on water injection pump.

Ni-60%WC coatings were fabricated on 45 steel by laser cladding, and the microstructure and tribological performance was analyzed using a super depth of field microscope and ball-on-plate friction tester, and the wear mechanism was also discussed.

At room temperature (RT, 25 ± 2 °C), the average coefficients of friction of substrate and Ni-60%WC coatings fabricated at the LSS of 6, 10, 12 and 14 mm/s are 0.48 ± 0.08, 0.23 ± 0.01, 0.21 ± 0.05, 0.22 ± 0.02 and 0.25 ± 0.04, respectively, and the corresponding wear rates are 8.755 × 10⁴, 4.525 × 10³, 1.539 × 10³, 1.957 × 10³ and 2.743 × 10³ µm³·s^–1·N^–1, respectively, showing that the coating fabricated at the LSS of 10 mm/s has best friction reduction and wear resistance. The wear mechanism of Ni-60%WC coating is abrasive wear, fatigue wear and oxidative wear, which is resulted from the WC particles with the high-hardness.

Ni-60%WC coatings were first applied for cylinder liner, and the effect of laser scanning speed on its tribological performance was investigated.

The balanced vane pump is a common transmission component in hydraulic systems. Since the physicochemical properties of water and seawater are different from that of mineral oil, some problems can occur, for instance, poor lubrication, more leakage, and more corrosion. The paper aims to demonstrate the technical feasibility for the water hydraulic vane pump.

The material combinations were selected based on related research in literature. The volumetric efficiency and suction performance were measured in the current experiment. The relations between gap clearances and leakage flow, the contact and the friction forces between a vane tip and a cam contour were simulated based on mathematic models.

The soft‐hard material combinations in the prototype pump show preferable friction characteristics during tests. The axial clearances are the main channels of leakage flow. Pin type vane pump can reduce the contact force of the vane tip.

This paper outlines some key problems of the water hydraulic vane pump, such as the friction pair material,the structure, and the contact force of the vane tip by means of testing the basic performance of pump and mathematic model.

This paper aims to cover all the aspects of development, investigation and analysis phases to evaluate the slurry erosion performance of test coatings. The powders having composition of Ni-20Al₂O₃ and Ni-15Al2O₃-5TiO₂ were deposited on CA6NM grade turbine steel by using high velocity flame spray (HVFS) technique. The characterization of the coatings was done with the help of SEM/EDS and XRD techniques. Various properties such as micro-hardness and bonding strength of the coatings were also evaluated. Thereafter, these coatings were subjected to an indigenously developed high speed slurry erosion tester at different levels of rotational speed, erodent particle size and slurry concentration. The effect of these parameters on the erosion behavior of coatings was also evaluated. The slurry erosion tests and SEM of the eroded surfaces revealed remarkable improvement in slurry erosion resistance of Ni-15Al₂O₃-5TiO₂ coating in comparison with Ni-20Al₂O₃ coating.

Two different compositions of HVFS coating were developed onto CA6NM steel. Subsequently, these coatings were evaluated by means of mechanical and microstructural characterization. Further, slurry erosion testing was done to analyze the erosive wear behavior of developed coatings.

The coatings were successfully developed by HVFS process. Cross-sectional microscopic analysis of sprayed coatings revealed a continuous and defect-free contact between substrate and coating. Ni-15Al₂O₃-5TiO₂ coating showed higher value of bond strength in comparison with Ni-20Al₂O₃ coating. Under all the testing conditions, Ni-15Al₂O₃-5TiO₂ coatings showed higher resistance to slurry erosion in comparison with Ni-20Al₂O₃ coatings. Rotational speed, average particle size of erodent and slurry concentration were found to have proportional effect on specific mass loss of coatings. The mixed behavior (brittle as well as ductile) of the material removal mechanism was observed for the coatings.

From the literature review, it was found that researchers have documented the various studies on Ni-Al₂O₃, Ni-TiO₂ and Al₂O₃-TiO₂ coatings. No one has ascertained the synergetic effect of Alumina and Titania on the slurry erosion performance of Nickel-based coating. In view of this, the authors have developed Ni-Al₂O₃ and Ni-Al₂O₃-TiO₂ coatings, and an attempt has been made to compare their mechanical, microstructural and slurry erosion characteristics.

This paper presents the application of grey modeling for thermal spray processing parameter analysis in less data environment.

Based on processing knowledge, key processing parameters of thermal spray process are analyzed and preselected. Then, linear and non-linear grey modeling models are integrated to mine the relationships between different processing parameters.

Model A reveals the linear correlation between the HVOF process parameters and the characterization of particle in-flight with average relative errors of 9.230 percent and 5.483 percent for velocity and temperature.

The prediction accuracies of coatings properties vary, which means that there exists more complex non-linear relationship between the identified input parameters and coating results, or more unexpected factors (e.g. factors from material side) should be further investigated.

According to the modeling case in this paper, method has potential to deal with other diverse modeling problems in different industrial applications where challenge to collecting large quantity of data sets exists.

It is the first time to apply grey modeling for thermal spray processing where complicated relationships among processing parameters exist. The modeling results show reasonable results to experiment and existing processing knowledge.

The purpose of this paper is to investigate the effects of parallel texturing coating on antifriction mechanism of lubricating wear-resistant coating.

A KF301/WS2 lubricating wear-resisting coating was prepared on matrix material GCr15 by applying supersonic plasma spraying technology. On the basis of this sample, the KF301/WS2 modified coating with parallel pit-type texture was prepared by laser re-melting technology and a surface texturing technique. Their friction and wear behaviors were evaluated under ambient temperature, and the antifriction mechanism of two kinds of coatings were discussed.

Results showed that parallel texture has a certain impact on the tribological properties of the coating. When friction and wear reach stable state, the value of the friction coefficient of conventional coating was 0.115, while that of parallel texturing coating was 0.09, the latter decreased by 21 per cent. When the friction and wear time was up to 4 hours, the wear loss of the conventional coating was 0.29 mg, while that of the parallel texturing coating was 0.13 mg, the latter decreased by 55 per cent.

The tribological properties of parallel texturing coating were higher than conventional coating. That is because the change of three-body layer reduces the friction coefficient and the abrasive particles were collected by parallel texture, reducing the effects of debris.