The extrusion-based additive manufacturing method followed by debinding and sintering steps can produce metal parts efficiently at a relatively low cost and material wastage. In this study, 316L stainless-steel metal filled filaments were used to print metal parts using the extrusion-based fused filament fabrication (FFF) approach. The purpose of this study is to assess the effects of common FFF printing parameters on the geometric and mechanical performance of FFF manufactured 316L stainless-steel components.

The microstructural characteristics of the metal filled filament, three-dimensional (3D) printed green parts and final sintered parts were analysed. In addition, the dimensional accuracy of the green parts was evaluated, as well as the hardness, tensile properties, relative density, part shrinkage and the porosity of the sintered samples. Moreover, surface quality in terms of surface roughness after sintering was assessed. Predictive models based on artificial neural networks (ANNs) were used for characterizing dimensional accuracy, shrinkage, surface roughness and density. Additionally, the response surface method based on ANNs was applied to represent the behaviour of these parameters and to identify the optimum 3D printing conditions.

The effects of the FFF process parameters such as build orientation and nozzle diameter were significant. The pore distribution was strongly linked to the build orientation and printing strategy. Furthermore, porosity decreased with increased nozzle diameter, which increased mechanical performance. In contrast, lower nozzle diameters achieved lower roughness values and average deviations. Thus, it should be noted that the modification of process parameters to achieve greater geometrical accuracy weakened mechanical performance.

Near-dense 316L austenitic stainless-steel components using FFF technology were successfully manufactured. This study provides print guidelines and further information regarding the impact of FFF process parameters on the mechanical, microstructural and geometric performance of 3D printed 316L components.

This paper aims to summarize the up-to-date research performed on combinations of various biofibers and resin systems used in different three-dimensional (3D) printing technologies, including powder-based, material extrusion, solid-sheet and liquid-based systems. Detailed information about each process, including materials used and process design, are described, with the resultant products’ mechanical properties compared with those of 3D-printed parts produced from pure resin or different material combinations. In most processes introduced in this paper, biofibers are beneficial in improving the mechanical properties of 3D-printed parts and the biodegradability of the parts made using these green materials is also greatly improved. However, research on 3D printing of biofiber-reinforced composites is still far from complete, and there are still many further studies and research areas that could be explored in the future.

The paper starts with an overview of the current scenario of the composite manufacturing industry and then the problems of advanced composite materials are pointed out, followed by an introduction of biocomposites. The main body of the paper covers literature reviews of recently emerged 3D printing technologies that were applied to biofiber-reinforced composite materials. This part is classified into subsections based on the form of the starting materials used in the 3D printing process. A comprehensive conclusion is drawn at the end of the paper summarizing the findings by the authors.

Most of the biofiber-reinforced 3D-printed products exhibited improved mechanical properties than products printed using pure resin, indicating that biofibers are good replacements for synthetic ones. However, synthetic fibers are far from being completely replaced by biofibers due to several of their disadvantages including higher moisture absorbance, lower thermal stability and mechanical properties. Many studies are being performed to solve these problems, yet there are still some 3D printing technologies in which research concerning biofiber-reinforced composite parts is quite limited. This paper unveils potential research directions that would further develop 3D printing in a sustainable manner.

This paper is a summary of attempts to use biofibers as reinforcements together with different resin systems as the starting material for 3D printing processes, and most of the currently available 3D printing techniques are included herein. All of these attempts are solutions to some principal problems with current 3D printing processes such as the limit in the variety of materials and the poor mechanical performance of 3D printed parts. Various types of biofibers are involved in these studies. This paper unveils potential research directions that would further widen the use of biofibers in 3D printing in a sustainable manner.

This paper aims to evaluate the mechanical behaviour of polycarbonate/acrylonitrile butadiene styrene (PC/ABS) filaments for fusion filament fabrication (FFF). PC/ABS have emerged as a promising material for FFF due to their excellent mechanical properties. However, the optimal processing conditions and the effect of the blending ratio on the mechanical properties of the resulting workpieces are still unclear.

A statistical factorial matrix was designed, including infill pattern, printing speed, nozzle size, layer height and printing temperature as factors (with three levels). A total of 810 workpieces were printed using PC/ABS blends filament with the FFF. The workpieces’ finishing and mass were evaluated. Tensile tests were performed. Analysis of variance was performed to determine the main effects of the processing conditions on the mechanical properties.

The results showed that the PC/ABS (70/30) exhibited higher tensile. Tensile rupture corresponded to 30% of the tensile strength. The infill pattern showed the highest contribution to the responses. The concentric pattern showed higher tensile strength. Tensile strength and mass ratio demonstrated the influence of mass on tensile strength. The influence of printing parameters on deformation depended on the blend proportions. Higher printing speed and lower layer height provided better quality workpieces.

This study has implications for the design and manufacturing of three-dimensional printed parts using PC/ABS filaments. An extensive experimental matrix was applied, aiming at a complete understanding of mechanical behavior, considering the main printing parameters and combinations not explored by literature.

Masked stereolithography (MSLA) or resin three-dimensional (3D) printing is one of the most extensively used high-resolution additive manufacturing technologies. Even though, the quality of 3D printing is determined by several factors, including the equipment, materials and slicer. Besides, the layer height, print orientation and exposure time are important processing parameters in determining the quality of the 3D printed green state specimen. The purpose of the paper is to optimize the printing parameters of the Masked Stereolithography apparatus for its dimensional correctness of 3D printed parts using the Taguchi method.

The acrylate-based photopolymer resin is used to produce the parts using liquid crystal display (LCD)-type resin 3D printer. This study is mainly focused on optimizing the processing parameters by using Taguchi analysis, L-9 orthogonal array in Minitab software. Analysis of variance (ANOVA) was performed to determine the most influencing factors, and a regression equation was built to predict the best potential outcomes for the given set of parameters and levels. The signal-to-noise ratios were calculated by using the smaller the better characteristic as the deviations from the nominal value should be minimum. The optimal levels for each factor were determined with the help of mean plots.

Based on the findings of ANOVA, it was observed that exposure time plays an important role in most of the output measures. The model’s goodness was tested using a confirmation test and the findings were found to be within the confidence limit. Also, a similar specimen was printed using the fused filament fabrication (FFF) technique; it was compared with the quality and features of MSLA 3D printing technology.

The study presents the statistical analysis of experimental results of MSLA and made a comparison with FFF in terms of dimensional accuracy and print quality.

Many previous studies reported the results based on earlier 3D printing technology such as stereolithography but LCD-based MSLA is not yet reported for its dimensional accuracy and part quality. The presented paper proposes the use of statistical models to optimize the printing parameters to get dimensional accuracy and the good quality of the 3D printed green part.

Fused filament fabrication (FFF) is one of the most popular additive manufacturing (AM) technologies due to its ability to build thermoplastic parts with complex geometries at low cost. The FFF technique has been mainly used for rapid prototyping owing to the poor mechanical and geometrical properties of pure thermoplastic parts. However, both the development of new fibre-reinforced filaments with improved mechanical properties, and more accurate composite 3D printers have broadened the scope of FFF applications to functional components. FFF is a complex process with a large number of parameters influencing product quality and mechanical properties, and the effects of the combined parameters are usually difficult to evaluate. An array of parameter combinations has been analysed for improving the mechanical performance of thermoplastic parts such as layer thickness, build orientation, raster angle, raster width, air gap, infill density and pattern, fibre volume fraction, fibre layer location, fibre orientation and feed rate. This study aims to assess the effects of nozzle diameter on the mechanical performance and the geometric properties of 3D printed short carbon fibre-reinforced composites processed by the FFF technique.

Tensile and three-point bending tests were performed to characterise the mechanical response of the 3D printed composite samples. The dimensional accuracy, the flatness error and surface roughness of the printed specimens were also evaluated. Moreover, manufacturing costs, which are related to printing time, were evaluated. Finally, scanning electron microscopy images of the printed samples were analysed to estimate the porosity as a function of the nozzle diameter and to justify the effect of nozzle diameter on dimensional accuracy and surface roughness.

The effect of nozzle diameter on the mechanical and geometric quality of 3D printed composite samples was significant. In addition, large nozzle diameters tended to increase mechanical performance and enhance surface roughness, with a reduction in manufacturing costs. In contrast, 3D printed composite samples with small nozzle diameter exhibited higher geometric accuracy. However, the effect of nozzle diameter on the flatness error and surface roughness was of slight significance. Finally, some print guidelines are included.

The effect of nozzle diameter, which is directly related to product quality and manufacturing costs, has not been extensively studied. The presented study provides more information regarding the dependence of the mechanical, microstructural and geometric properties of short carbon fibre-reinforced nylon composite components on nozzle diameter.

This study aims to reveal the influences of three-dimensional (3D) printing parameters such as layer heights (0.1 mm, 0.2 mm and 0.4 mm), infill rates (40, 70 and 100%) and geometrical property as tapered angle (0, 0.25 and 0.50) on vibrational behavior of 3D-printed polyethylene terephthalate glycol (PET-G) tapered beams with fused filament fabrication (FFF) method.

In this performance, all test specimens were modeled in AutoCAD 2020 software and then 3D-printed by FFF. The effects of printing parameters on the natural frequencies of 3D-printed PET-G beams with different tapered angles were also analyzed experimentally, and numerically (finite element analysis) via Ansys APDL 16 program. In addition to vibrational properties, tensile strength, elasticity modulus, hardness, and surface roughness of the 3D-printed PET-G parts were examined.

It can be stated that average surface roughness values ranged between 1.63 and 6.91 µm. In addition, the highest and lowest hardness values were found as 68.6 and 58.4 Shore D. Tensile strength and elasticity modulus increased with the increase of infill rate and decrease of the layer height. In conclusion, natural frequency of the 3D-printed PET-G beams went up with higher infill rate values though no critical change was observed for layer height and a change in tapered angle fluctuated the natural frequency values significantly.

The influence of printing parameters on the vibrational properties of 3D-printed PET-G beams with different tapered angles was carried out and the determination of these effects is quite important. On the other hand, with the addition of glass or carbon fiber reinforcements to the PET-G filaments, the material and vibrational properties of the parts can be examined in future works.

As a result of this study, it was shown that natural frequencies of the 3D-printed tapered beams from PET-G material can be predicted via finite element analysis after obtaining material data with the help of mechanical/physical tests. In addition, the outcome of this study can be used as a reference during the design of parts that are subjected to vibration such as turbine blades, drone arms, propellers, orthopedic implants, scaffolds and gears.

It is believed that determination of the effect of the most used 3D printing parameters (layer height and infill rate) and geometrical property of tapered angle on natural frequencies of the 3D-printed parts will be very useful for researchers and engineers; especially when the importance of resonance is known well.

When the literature efforts are scanned in depth, it can be seen that there are many studies about mechanical or wear properties of the 3D-printed parts. However, this is the first study which focuses on the influences of the both 3D printing parameters and tapered angles on the vibrational behaviors of the tapered PET-G beams produced with material extrusion based FFF method. In addition, obtained experimental results were also supported with the performed finite element analysis.

In industry, fused filament fabrication (FFF) offers flexibility and agility by promoting a reduction in costs and in the lead-time (i.e. time-to-market). Nevertheless, FFF parts exhibit some limitations such as lack of accuracy and/or lower mechanical performance. As a result, some alternatives have been developed to overcome some of these restrictions, namely, the formulation of high performance polymers, the creation of fibre-reinforced materials by FFF process and/or the design of new FFF-based technologies for printing composite materials. This work aims to analyze these technologies.

This work aims to study and understand the advances in the behaviour of 3D printed parts with enhanced performance by its reinforcement with several shapes and types of fibres from nanoparticles to continuous fibre roving. Thus, a comprehensive survey of significant research studies carried out regarding FFF of fibre-reinforced thermoplastics is provided, giving emphasis to the most relevant and innovative developments or adaptations undergone at hardware level and/or on the production process of the feedstock.

It is shown that the different types of reinforcement present different challenges for the printing process with different outcomes in the part performance.

This review is focused on joining the most important researches dedicated to the process of FFF-printed parts with different types reinforcing materials. By dividing the reinforcements in categories by shape/geometry and method of processing, it is possible to better quantify performance improvements.

The hygroscopic properties of 3D-printed filaments and moisture absorption itself during the process result in dimensional inaccuracy, particularly for nozzle movement along the x-axis and for micro-scale features. In view of that, this study aims to analyze in depth the dimensional errors and deviations of the fused filament fabrication (FFF)/fused deposition modeling (FDM) 3D-printed micropillars (MPs) from the reference values. A detailed analysis into the variability in printed dimensions below 1 mm in width without any deformations in the printed shape of the designed features, for challenging filaments like polymethyl methacrylate (PMMA) has been done. The study also explores whether the printed shape retains the designed structure.

A reference model for MPs of width 800 µm and height 2,000 µm is selected to generate a g-code model after pre-processing of slicing and meshing parameters for 3D printing of micro-scale structure with defined boundaries. Three SETs, SET-A, SET-B and SET-C, for nozzle diameter of 0.2 mm, 0.25 mm and 0.3 mm, respectively, have been prepared. The SETs containing the MPs were fabricated with the spacing (S) of 2,000 µm, 3,200 µm and 4,000 µm along the print head x-axis. The MPs were measured by taking three consecutive measurements (top, bottom and middle) for the width and one for the height.

The prominent highlight of this study is the successful FFF/FDM 3D printing of thin features (<1mm) without any deformation. The mathematical analysis of the variance of the optical microscopy measurements concluded that printed dimensions for micropillar widths did not vary significantly, retaining more than 65% of the recording within the first standard deviation (SD) (±1 s). The minimum value of SD is obtained from the samples of SET-B, that is, 31.96 µm and 35.865 µm, for height and width, respectively. The %RE for SET-B samples is 5.09% for S = 2,000µm, 3.86% for S = 3,200µm and 1.09% for S = 4,000µm. The error percentage is so small that it could be easily compensated by redesigning.

The study does not cover other 3D printing techniques of additive manufacturing like stereolithography, digital light processing and material jetting.

The presented study can be potentially implemented for the rapid prototyping of microfluidics mixer, bioseparator and lab-on-chip devices, both for membrane-free bioseparation based on microfiltration, plasma extraction from whole blood, size-selection trapping of unwanted blood cells, and also for membrane-based plasma extraction that requires supporting microstructures. Our developed process may prove to be far more economical than the other existing techniques for such applications.

For the first time, this work presents a comprehensive analysis of the fabrication of micropillars using FDM/FFF 3D printing and PMMA in filament form. The primary focus of the study is to minimize the dimensional inaccuracies in the 3D printed devices containing thin features, especially in the area of biomedical engineering, by delivering benefits from the choice of the parameters. Thus, on the basis of errors and deviations, a thorough comparison of the three SETs of the fabricated micropillars has been done.

The purpose of this study is to confirm that the stiffness of fused filament fabrication (FFF) three-dimensionally (3D) printed fiber-reinforced thermoplastic (FRP) materials can be predicted using classical laminate theory (CLT), and to subsequently use the model to demonstrate its potential to improve the mechanical properties of FFF 3D printed parts intended for load-bearing applications.

The porosity and the fiber orientation in specimens printed with carbon fiber reinforced filament were calculated from micro-computed tomography (µCT) images. The infill portion of the sample was modeled using CLT, while the perimeter contour portion was modeled with a rule of mixtures (ROM) approach.

The µCT scan images showed that a low porosity of 0.7 ± 0.1% was achieved, and the fibers were highly oriented in the filament extrusion direction. CLT and ROM were effective analytical models to predict the elastic modulus and Poisson’s ratio of FFF 3D printed FRP laminates.

In this study, the CLT model was only used to predict the properties of flat plates. Once the in-plane properties are known, however, they can be used in a finite element analysis to predict the behavior of plate and shell structures.

By controlling the raster orientation, the mechanical properties of a FFF part can be optimized for the intended application.

Before this study, CLT had not been validated for FFF 3D printed FRPs. CLT can be used to help designers tailor the raster pattern of each layer for specific stiffness requirements.

The fiber reinforced polymer composites are becoming more critical because of their exceptional mechanical properties and lightweight structures. Fused filament fabrication (FFF) is a three-dimensional (3D) printing technique that can manufacture composite structures. However, the effect of impact performance on the structural integrity of FFF made composites compared to the pre-preg composites is a primary concern for the practical usage of 3D printed parts. Therefore, this paper aims to investigate the effect of different processing parameters on the impact performance of 3D printed composites.

This paper investigates the impact of build orientation, fiber stacking sequence and fiber angle on the impact properties. Two build orientations, three fiber stacking sequences and two different fiber angles have been selected for this study. Charpy impact testing is carried out to investigate the impact energy absorption of the parts. Onyx as a matrix material and two different types of fibers, that is, fiberglass and high strength high temperature (HSHT) fiberglass as reinforcements, are used for the fabrication.

Results indicate that build orientation and fiber angle largely affect the impact performance of composite parts. The composite part built with XYZ orientation, 0º/90º fiber angle and B type fiber stacking sequence resulted into maximum impact energy. However, comparing both types of fiber reinforcement, HSHT fiberglass resulted in higher impact energy than regular fiberglass.

This study evaluates the damage modes during the impact testing of the 3D printed composite parts. The impact energy absorbed by the composite samples during the impact testing is measured to compare the effect of different processing conditions. The investigation of different types of fiberglass reinforced with Onyx material is very limited for the FFF-based process. The results also provide a database to select the different parameters to obtain the required impact properties.