Erosion and abrasion are the prominent wear mechanisms reducing the lifetime of machine components. Both wear mechanisms are playing a role meanwhile, generating a synergy, leading to a material removal on the target. The purpose of study is to create a mathematical expression for erosive abrasive wear.

Many factors such as environmental cases and material character have an influence in erosive abrasive wear. In the work, changes in abrasive size and material hardness have been analyzed. As an abrasive particle, quartz sand has been used. All tests have been done in 20 wt.% slurry. Heat treatment has been applied to different steel specimens (steel grades C15, St 37 and Ck45) to change hardness value, which ranged from 185 to 880 Vickers hardness number.

After the four-hour test, it is determined that by an increase in abrasive size and decrease in material hardness, wear rate increases. Worn surfaces of the targets have been examined to figure out the wear mechanisms at different conditions under scanning electron microscopy. The results indicate that by an increase in material hardness, the number and diameter of micro-craters on the worn surfaces decrease. The diameters of micro-craters have been about 3–8 µm in hard materials and about 120–140 µm in soft materials.

It is determined that by an increase in abrasive size and decrease in material hardness, wear rate increases. The results indicate that by an increase in material hardness, the number and diameter of micro-craters on the worn surfaces decrease.

The study enables to indicate the dominant factor in worn steel used in mechanical components.

After analyzing the test results, a novel mathematical expression, considering both abrasive size and material hardness, has been developed.

In the process of conveying the solid–liquid two-phase medium of the centrifugal slurry pump, the wear of the flow-passing parts is an important problem affecting its life and safe operation. Therefore, a numerical investigation on the wear characteristics of the centrifugal slurry pump under different particle conditions was conducted.

A solid-liquid two-phase model based on CFD-DEM coupling is established and used to analyze the flow field and the wear characteristics of the flow-passing parts with different particle densities, volume fractions and sizes.

Particle conditions will affect the pump flow field. To analyze the pump wear characteristics, the wear distribution, wear value and cumulative force laws of flow-passing parts under different particle conditions are obtained. In each flow-passing part, with the increase of particle density, volume fraction and size, the wear area is concentrated and the wear depth increases. Under different particle conditions, the wear is mainly on the volute chamber and the blade pressure surface, and the tangential cumulative force of flow-passing parts is much larger than the normal cumulative force.

An accurate model and a coupled simulation method for predicting the wear of the slurry pump are obtained, and the wear characteristic law can provide a reference for the design of the slurry pump to reduce friction.

This paper aims to investigate the high temperature corrosion behaviour of ZrO₂-reinforced Cr₂O₃ matrix-based composite coatings on ASTM-SA213-T-22 steel at 900°C in molten salt environment. The different coatings were deposited by high velocity oxy fuel (HVOF) method.

Hot corrosion studies were conducted in simulated boiler environment in silicon carbide tube furnace at 900°C for 50 cycles on bare and HVOF-coated boiler steel specimens. Each cycle consisted 50 h of heating in the simulated boiler environment followed by 20 min of cooling in air. The weight change measurements were performed after each cycle to establish the kinetics of corrosion using thermogravimetric technique. X-ray diffraction and scanning electron microscopy techniques were used to analyse the corroded specimens.

The addition of 20 Wt.% ZrO₂ in Cr₂O₃ helped reduce corrosion rate by 89.25% as compared to that of uncoated specimen. The phase analysis revealed the presence of Cr₂O₃ and ZrO₂ phases in composite coating matrix, which may have prevented the base metal from interacting with the corrosive elements present in the highly aggressive environment and thus had increased the resistance to hot corrosion.

It should be mentioned here that high temperature corrosion behaviour of thermally sprayed ZrO₂–Cr₂O₃ composite coatings has never been studied, and to the best of the authors’ knowledge, it is not available in the literature. Hence, present investigation can provide valuable information for application of ZrO₂-reinforced coatings in high temperature fuel combustion environments.

The purpose of this study was to introduce three-dimensional printing (3DP) of functionally graded sandwich foams (FGSFs). This work was continued by predicting the mechanical buckling and free vibration behavior of 3DP FGSFs using experimental and numerical analyses.

Initially, hollow glass microballoon-reinforced high-density polyethylene-based polymer composite foams were developed, and these materials were extruded into their respective filaments. These filaments are used as feedstock materials in fused filament fabrication based 3DP for the development of FGSFs. Scanning electron microscopy analysis was performed on the freeze-dried samples to observe filler sustainability. Furthermore, the density, critical buckling load (P_cr), natural frequency (f_n) and damping factor of FGSFs were evaluated. The critical buckling load (P_cr) of the FGSFs was estimated using the double-tangent method and modified Budiansky criteria.

The density of FGSFs decreased with increasing filler percentage. The mechanical buckling load increased with the filler percentage. The natural frequency corresponding to the first mode of the FGSFs exhibited a decreasing trend with an increasing load in the pre-buckling regime and an increase in post-buckled zone, whereas the damping factor exhibited the opposite trend.

The current research work is valuable for the area of 3D printing by developing the functionally graded foam based sandwich beams. Furthermore, it intended to present the buckling behavior of 3D printed FGSFs, variation of frequency and damping factor corresponding to first three modes with increase in load.

The purpose of this paper was to prepare a ternary hierarchical rough particle to accelerate the anti-corrosive design for coastal concrete infrastructures.

A kind of micro-nano hydrophobic ternary microparticles was fabricated from SiO₂/halloysite nanotubes (HNTs) and recycled concrete powders (RCPs), which was then mixed with sodium silicate and silane to form an inorganic slurry. The slurry was further sprayed on the concrete surface to construct a superhydrophobic coating (SHC). Transmission electron microscopy and energy-dispersive X-ray spectroscopy mappings demonstrate that the nano-sized SiO₂ has been grafted on the sub-micron HNTs and then further adhered to the surface of micro-sized RCP, forming a kind of superhydrophobic particles (SiO₂/HNTs@RCP) featured of abundant micro-nano hierarchical structures.

The SHC surface presents excellent superhydrophobicity with the water contact angle >156°. Electrochemical tests indicate that the corrosion rate of mild steel rebar in coated concrete reduces three-order magnitudes relative to the uncoated one in 3.5% NaCl solution. Water uptake and chloride ion (Cl^-) diffusion tests show that the SHC exhibits high H₂O and Cl^- ions barrier properties thanks to the pore-sealing and water-repellence properties of SiO₂/HNTs@RCP particles. Furthermore, the SHC possesses considerable mechanical durability and outstanding self-cleaning ability.

SHC inhibits water uptake, Cl^- diffusion and rebar corrosion of concrete, which will promote the sustainable application of concrete waste in anti-corrosive concrete projects.

The purpose of this paper is to use a wear test to determine the effect of sand on the wear rates of materials typically used in aerospace applications. Once a repeatable wear test has been established, it can be used to test any combination of materials or coatings. The effectiveness of several different test methods will also be evaluated, including the sample height, surface roughness and mass difference. In addition, the current work will observe the differences between applying sand before the samples are brought into contact or after. The wear rates obtained from these tests could also be used to predict the wear of other components in similar abrasive particulate environments.

A modified block-on-flat wear test of anodized aluminum on hard coat anodized aluminum was used to study this. The experiments were performed with and without sand to study the effects of the sand. Two methods of adding sand were also evaluated. Weighing and profilometry were used to study the differences between the tests.

Wear rates have been calculated based on both the change in the masses of the samples and the change in the height between the upper and lower samples over the course of each test. The wear rates from the change in the masses are repeatable with and without sand, but the results for the change in height show no repeatability without sand. In addition, only in the presence of sand do the trends for the two methods agree. The wear rate was found to be non-linear as a function of load and therefore not in agreement with Archard’s Wear Law. The wear rate also increased significantly when sand was present in the contact for the duration of the test. The sand appears to change the wear mechanism from an adhesive to an abrasive mechanism. Black wear particles formed both when there was sand and when there was not sand. The source of these particles has been investigated but not determined.

This work has not been previously published and is the original work of the authors.

Foundry produces cast metal components and parts for various industries and drives manufacturing excellence all over the world. Assuring quality of these components and parts is vital for the end product quality. The complexity in foundry operations increases with the complexity in designs, patterns and geometry and the quality parameters of the casting processes need to be monitored, evaluated and controlled to achieve expected quality levels.

The literature addresses quality improvement in foundry industry primarily focusing on surface roughness, mechanical properties, dimensional accuracy and defects in the cast parts and components which are often affected by numerous process variables. Primary data are collected from the experts working in sand and investment casting processes. The authors perform machine learning analysis of the data to model the quality parameters with appropriate process variables. Further, cluster analysis using k-means clustering method is performed to develop clusters of correlated process variables for sand and investment casting processes.

The authors identified primary process variables determining each quality parameter using machine learning approach. Quality parameters such as surface roughness, defects, mechanical properties and dimensional accuracy are represented by the identified sand-casting process variables accurately up to 83%, 83%, 100% and 83% and are represented by the identified investment-casting process variables accurately up to 100%, 67%, 67% and 100% respectively. Moreover, the prioritization of process variables in influencing the quality parameters is established which further helps the practitioners to monitor and control them within acceptable levels. Further the clusters of process variables help in analyzing their combined effect on quality parameters of casting products.

This study identified potential process variables and collected data from experts, researchers and practitioners on the effect of these on the quality aspects of cast products. While most of the previous studies focus on a very limited process variables for enhancing the quality characteristics of cast parts and components, this study represents each quality parameter as the function of influencing process variables which will enable the quality managers in Indian foundries to maintain capability and stability of casting processes. The models hence developed for both sand and investment casting for each quality parameter are validated with real life applications. Such studies are scarcely reported in the literature.

To explore the economical and reasonable semi-rigid permeable base layer ratio, solve the problems caused by rainwater washing over the pavement base layer on the slope, improve its drainage function, improve the water stability and service life of the roadbed pavement and promote the application of semi-rigid permeable base layer materials in the construction of asphalt pavement in cold regions.

In this study, three semi-rigid base course materials were designed, the mechanical strength and drainage properties were tested and the effect and correlation of air voids on their performance indexes were analyzed.

It was found that increasing the cement content increased the strength but reduced the air voids and water permeability coefficient. The permeability performance of the sandless material was superior to the dense; the performance of the two sandless materials was basically the same when the cement content was 7%. Overall, the skeleton void (sand-containing) type gradation between the sandless and dense types is more suitable as permeable semi-rigid base material; its gradation is relatively continuous, with cement content? 4.5%, strength? 1.5 MPa, water permeability coefficient? 0.8 cm/s and voids of 18–20%.

The study of permeable semi-rigid base material with large air voids could help to solve the problems of water damage and freeze-thaw damage of the base layer of asphalt pavements in cold regions and ensure the comfort and durability of asphalt pavements while having good economic and social benefits.

This study aims to comparatively analyze the cut parts obtained as a result of cutting the Ni-based Inconel 625 alloy, which is widely used in the aerospace industry, with the wire electro-discharge machining (WEDM) and abrasive water jet machining (AWJM) methods in terms of macro- and microanalyses.

In this study, calipers, Mitutoyo SJ-210, Nikon SMZ 745 T, scanning electron microscope and energy dispersive X-ray were used to determine kerf, surface roughness and macro- and microanalyses.

Considering the applications in the turbine industry, it has been determined that the WEDM method is suitable to meet the standards for the machinability of Inconel 625 alloy. In contrast, the AWJM method does not meet the standards. Namely, while the kerf angle was formed because the hole entrance diameters of the holes obtained with AWJM were larger than the hole exit diameters, the equalization of the hole entry and exit dimensions, thanks to the perpendicularity and tension sensitivity of the wire electrode used in the holes drilled with WEDM ensured that the kerf angle was not formed.

It is known that the surface roughness of the parts used in the turbine industry is accepted at Ra = 0.8 µm. In this study, the average roughness value obtained from the successful drilling of Inconel 625 alloy with the WEDM method was 0.799 µm, and the kerf angle was obtained as zero. In the cuts made with the AWJM method, thermal effects such as debris, microcracks and melted materials were not observed; an average surface roughness of 2.293 µm and a kerf of 0.976° were obtained.

This study aims to investigate the corrosion behavior of stir-cast hybrid aluminum composite reinforced with CeO₂ and graphene nanoplatelets (GNPs) nanoparticulates used as cylinder liner material in the engines (automotive, aerospace and aircraft industries).

The composites were prepared using the stir-casting technique, and their microstructure and corrosion behavior was evaluated using scanning electron microscopy (SEM) and potentiodynamic polarization test, respectively.

The results showed that the addition of CeO₂ and GNPs improved the corrosion resistance of the composites, and the optimal combination of these two nanoparticles was found to be 3 wt.% CeO₂ and 3 wt.% GNPs. The enhanced corrosion resistance was attributed to the formation of a protective layer on the surface of the composite, as well as the effective dispersion and uniform distribution of nanoparticles in the matrix. The 0.031362 was noted as the lowest corrosion rate (mmpy) and was noticed in 94% Al-6061 alloy + (3 Wt.% CeO₂ + 3 Wt.% GNPs) sample at room temperature and at elevated temperatures; the corrosion rate (mmpy) was observed as 0.0601 and 0.0636 at 45 °C and 75 °C, respectively.

In the vast majority of the published research publications, either cerium oxide or graphene nanoplatelets were utilized as a single reinforcement or in conjunction with other types of reinforcement such as alumina, silicon carbide, carbon nano-tubes, tungsten carbide, etc., but on the combination of the CeO₂ and GNPs as reinforcements have very less literatures with 2 wt.% each only. The prepared hybrid aluminum composite (reinforcing 1 wt.% to 3 wt.% in Al-6061 alloy) was considered for replacing the cylinder liner material in the piston-cylinder arrangement of engines.