This study investigates the impact of the fire decay phase on structural damage using the sectional analysis method. The primary objective of this work is to forecast the non-dimensional capacity parameters for the axial and flexural load-carrying capacity of reinforced concrete (RC) sections for heating and the subsequent post-heating phase (decay phase) of the fire.

The sectional analysis method is used to determine the moment and axial capacities. The findings of sectional analysis and heat transfer for the heating stage are initially validated, and the analysis subsequently proceeds to determine the load capacity during the fire’s heating and decay phases by appropriately incorporating non-dimensional sectional and material parameters. The numerical analysis includes four fire curves with different cooling rates and steel percentages.

The study’s findings indicate that the rate at which the cooling process occurs after undergoing heating substantially impacts the axial and flexural capacity. The maximum degradation in axial and flexural capacity occurred in the range of 15–20% for cooling rates of 3 °C/min and 5 °C/min as compared to the capacity obtained at 120 min of heating for all steel percentages. As the fire cooling rate reduced to 1 °C/min, the highest deterioration in axial and flexural capacity reached 48–50% and 42–46%, respectively, in the post-heating stage.

The established non-dimensional parameters for axial and flexural capacity are limited to the analysed section in the study owing to the thermal profile, however, this can be modified depending on the section geometry and fire scenario.

The study primarily focusses on the degradation of axial and flexural capacity at various time intervals during the entire fire exposure, including heating and cooling. The findings obtained showed that following the completion of the fire’s heating phase, the structural capacity continued to decrease over the subsequent post-heating period. It is recommended that structural members' fire resistance designs encompass both the heating and cooling phases of a fire. Since the capacity degradation varies with fire duration, the conventional method is inadequate to design the load capacity for appropriate fire safety. Therefore, it is essential to adopt a performance-based approach while designing structural elements' capacity for the desired fire resistance rating. The proposed technique of using non-dimensional parameters will effectively support predicting the load capacity for required fire resistance.

The fire-resistant requirements for reinforced concrete structures are generally established based on standard fire exposure conditions, which account for the fire growth phase. However, it is important to note that concrete structures can experience internal damage over time during the decay phase of fires, which can be quantitatively determined using the proposed non-dimensional parameter approach.

The purpose of this paper is to investigate the effect of the replacement of natural coarse aggregate (NCA) with different percentages of recycled coarse aggregate (RCA) on properties of low calcium fly ash (FA)-based geopolymer concrete (GPC) cured at oven temperature. Further, this paper aims to study the effect of partial replacement of FA by ground granulated blast slag (GGBS) in GPC made with both NCA and RCA cured under ambient temperature curing.

M25 grade of ordinary Portland cement (OPC) concrete was designed according to IS: 10262-2019 with 100% NCA as control concrete. Since no standard guidelines are available in the literature for GPC, the same mix proportion was adopted for the GPC by replacing the OPC with 100% FA and W/C ratio by alkalinity/binder ratio. All FA-based GPC mixes were prepared with 12 M of sodium hydroxide (NaOH) and an alkalinity ratio, i.e. sodium hydroxide to sodium silicate (NaOH:Na₂SiO₃) of 1:1.5, subjected to 90^°C temperature for 48 h of curing. The NCA were replaced with 50% and 100% RCA in both OPC and GPC mixes. Further, FA was partially replaced with 15% GGBS in GPC made with the above percentages of NCA and RCA, and they were given ambient temperature curing with the same molarity of NaOH and alkalinity ratio.

The workability, compressive strength, split tensile strength, flexural strength, water absorption, density, volume of voids and rebound hammer value of all the mixes were studied. Further, the relationship between compressive strength and other mechanical properties of GPC mixes were established and compared with the well-established relationships available for conventional concrete. From the experimental results, it is found that the compressive strength of GPC under ambient curing condition at 28 days with 100% NCA, 50% RCA and 100% RCA were, respectively, 14.8%, 12.85% and 17.76% higher than those of OPC concrete. Further, it is found that 85% FA and 15% GGBS-based GPC with RCA under ambient curing shown superior performance than OPC concrete and FA-based GPC cured under oven curing.

The scope of the present paper is limited to replace the FA by 15% GGBS. Further, only 50% and 100% RCA are used in place of natural aggregate. However, in future study, the replacement of FA by different amounts of GGBS (20%, 25%, 30% and 35%) may be tried to decide the optimum utilisation of GGBS so that the applications of GPC can be widely used in cast in situ applications, i.e. under ambient curing condition. Further, in the present study, the natural aggregate is replaced with only 50% and 100% RCA in GPC. However, further investigations may be carried out by considering different percentages between 50 and 100 with the optimum compositions of FA and GGBS to enhance the use of RCA in GPC applications. The present study is further limited to only the mechanical properties and a few other properties of GPC. For wider use of GPC under ambient curing conditions, the structural performance of GPC needs to be understood. Therefore, the structural performance of GPC subjected to different loadings under ambient curing with RCA to be investigated in future study.

The replacement percentage of natural aggregate by RCA may be further enhanced to 50% in GPC under ambient curing condition without compromising on the mechanical properties of concrete. This may be a good alternative for OPC and natural aggregate to reduce pollution and leads sustainability in the construction.

When the reinforced concrete beams are reinforced by bonding steel plates to the bottom, excessive use of steel plates will make the reinforced concrete beams become super-reinforced beams, and there are security risks in the actual use of super-reinforced beams. In order to avoid the occurrence of this situation, the purpose of this paper is to study the calculation method of the maximum number of bonded steel plates to reinforce reinforced concrete beams.

First of all, when establishing the limit failure state of the reinforced member, this paper comprehensively considers the role of the tensile steel bar and steel plate and takes the load effect before reinforcement as the negative contribution of the maximum number of bonded steel plates that can be used for reinforcement. Through the definition of the equivalent tensile strength, equivalent elastic modulus and equivalent yield strain of the tensile steel bar and steel plate, a method to determine the relative limit compression zone height of the reinforced member is obtained. Second, based on the maximum ratio of (reinforcement + steel plate), the relative limit compression zone height and the equivalent tensile strength of the tensile steel bar and steel plate of the reinforced member, the calculation method of the maximum number of bonded steel plates is derived. Then, the static load test of the test beam is carried out and the corresponding numerical model is established, and the reliability of the numerical model is verified by comparison. Finally, the accuracy of the calculation method of the maximum number of bonded steel plates is proved by the numerical model.

The numerical simulation results show that when the steel plate width is 800 mm and the thickness is 1–4 mm, the reinforced concrete beam has a delayed yield platform when it reaches the limit state, and the failure mode conforms to the basic stress characteristics of the balanced-reinforced beam. When the steel plate thickness is 5–8 mm, the sudden failure occurs without obvious warning when the reinforced concrete beam reaches the limit state. The failure mode conforms to the basic mechanical characteristics of the super-reinforced beam failure, and the bending moment of the beam failure depends only on the compressive strength of the concrete. The results of the calculation and analysis show that the maximum number of bonded steel plates for reinforced concrete beams in this experiment is 3,487 mm². When the width of the steel plate is 800 mm, the maximum thickness of the steel plate can be 4.36 mm. That is, when the thickness of the steel plate, the reinforced concrete beam is still the balanced-reinforced beam. When the thickness of the steel plate, the reinforced concrete beam will become a super-reinforced beam after reinforcement. The calculation results are in good agreement with the numerical simulation results, which proves the accuracy of the calculation method.

This paper presents a method for calculating the maximum number of steel plates attached to the bottom of reinforced concrete beams. First, based on the experimental research, the failure mode of reinforced concrete beams with different number of steel plates is simulated by the numerical model, and then the result of the calculation method is compared with the result of the numerical simulation to ensure the accuracy of the calculation method of the maximum number of bonded steel plates. And the study does not require a large number of experimental samples, which has a certain economy. The research result can be used to control the number of steel plates in similar reinforcement designs.

Rebar corrosion in reinforced concrete is the major reason for the durability degradation, especially under harsh environment. This paper presents an experiment conducted to investigate the influence of freeze-thaw cycles on the rebar corrosion in reinforced concrete. The purpose of this paper is to provide fundamental information about rebar corrosion under frost environment and improvement measures.

The related elastic modulus and compressive strength of different concrete specimens were measured after different freeze-thaw cycles. The accelerated rebar corrosion test was carried out after different freeze-thaw cycles; additionally, the value of calomel half-cell potential was determined. The actual rebar corrosion appearance was checked to prove the accuracy of the results of calomel half-cell potential.

The results show that frost damage aggravates the rebar corrosion rate and degree under freeze-thaw environment; furthermore, the results become more obvious with the freeze-thaw cycles increasing. Mixing the air-entrained agent into fresh concrete to prepare air-entrained concrete, increasing the cover thickness and processing the surface of concrete with a waterproofing agent can significantly improve the resistance to rebar corrosion. From the actual appearance of rebar corrosion, the results of calomel half-cell potential can well reflect the actual rebar corrosion in reinforced concrete.

The durability of reinforced concrete is mainly determined on chloride penetration that brings about rebar corrosion in chloride environments. Furthermore, the degradation of concrete durability becomes more serious in the harsh environment. As the concrete exposure to the freeze-thaw cycles environment, the freeze-thaw cycles accelerate the concrete damage, and the penetration of chloride into the concrete becomes easier because of the growing pore and crack sizes. In addition, rebar corrosion caused by chloride is one of the major forms of environmental attack on reinforced concrete. The tests conducted in this paper will describe the rebar corrosion in reinforced concrete under freeze-thaw environment.

This paper aims to present a research finding that establishes a regression model between ultrasonic pulse velocity (UPV) tests and actual strength of high performance concrete (HPC).

In this study, a total of 270 cube samples were made from six different mix proportions. The mixes were grouped in two series that consist of nominal maximum aggregate sizes of 10 mm (A₁₀) and 19 mm (A₁₉). Silica fume were used as mineral admixtures at 5 percent, 10 percent and 15 percent of cement in both series. UPV tests were conducted for each of the specimens, followed by destructive strength tests. The tests were carried out for concrete at different ages of between three to 56 days. The destructive test results were used as the true strength of the mixes and the UPV test results were used as strength estimation.

Concrete strength correlations between UPV and destructive tests were analysed for each mix proportions and in each series. These correlations are presented in the form of regression equations that displays standard error of between ±2.4 to ±5.7 MPa regardless of mix for the concrete in series A₁₀. Similarly, in series A₁₉ concrete, standard errors of between ±3.2 to ±6.7 MPa were found. Strength prediction models using UPV for high performance concrete are proposed. The models have overall correlation coefficients above 0.80 for all the mixes.

There are no standard relationships that had been established for high performance concrete strength with UPV test methods. The proposed relationship can be used for concrete strength estimation that is normally required in building or structural assessment, especially with the present trend of constructing modern structures using high performance concrete.

Discusses the properties of concrete and the process of carbonation which can lead to corrosion and its ultimate destruction. Outlines the conditions which lead to carbonation, detailing design faults which facilitate the process, and suggests preventatives which can protect the surface. Examines the results of carbonation, the forming of distressed concrete and mentions tests which can be performed to check the health of the structure. Assesses the impact of additional factors leading to corrosion and offers advice on remedial actions.

About 26,000 Airey Houses were erected during the post war years (1946–55) as part of the house building programme of that period. The Airey House is essentially a prefabricated concrete structure which was erected on site to form a box. This box was erected upon a concrete raft which acted as the foundation and floor of the dwelling. The basic box was formed from several framed ‘goal posts’ to which thin concrete cladding panels were fastened to the upright columns by copper wire. The vertical loading from the first floor and roof is taken on the vertical columns but may also be shared with the concrete cladding panels (see Figure 1).

This paper aims to investigate the 28-day compressive strength of concrete produced with aggregates from different sources.

Coarse aggregates were crushed granite and natural local stones mined from Umunneochi, Lokpa and Uturu, Isuakwato, respectively, in Abia State, Nigeria. Fine aggregate (river sand) and another coarse aggregate (river stone) were dredged from Otammiri River in Owerri, Imo State, Nigeria. The nominal mix ratios were 1:1:2, 1:2:4 and 1:3:6, whereas the respective water–cement ratios were 0.45, 0.5, 0.55 and 0.6.

The compressive strength of granite concrete, river stone concrete and local stone concrete ranged 17.79-38.13, 15.37-34.57 and 14.17-31.96 N/mm², respectively. Compressive strength was found to increase with decreasing water–cement ratio and increasing cement content.

Granite concrete should be used in reinforced-concrete construction, especially when a cube compressive strength of 30 N/mm² or higher is required.

Granite concrete exceeded the target compressive strength for all the concrete specimens, whereas river stone concrete and local stone concrete failed to achieve the target strength for some mix proportions and water–cement ratios.

The aim of this paper is to make lightweight high-performance concrete (LWHPC) with high economic performance from existing materials on the Algerian market. Concrete with high values with regard to following properties: mechanical, physical, rheological and durability. Because of the implementation of some basic scientific principles on the technology of LWHPC, this study is part of the valuation of local materials to manufacture LWHPC with several enhanced features such as mechanical, physical chemical, rheological and durability in the first place and with regard to the economic aspect in the second place.

The experimental study focused on the compatibility of cement/superplasticizer, the effect of water/cement ratio (W/C 0.22, 0.25, 0.30), the effect of replacing a part of cement by silica fume (8 per cent), the effect of combined replacement of a part of cement by silica fume (8 per cent) and natural pozzolan (10 per cent, 15 per cent, 25 per cent) and the effect of fraction of aggregate on properties of fresh and hardened concrete using the mix design method of the University of Sherbrooke, which is easy to realize and gives good results.

The results obtained allow to conclude that it is possible to manufacture LWHPC with good mechanical and physical properties in the authors’ town with available materials on the Algerian market. The mix design and manufacture of concrete with a compressive strength at 28 days reaching 56 MPa or more than 72 MPa is now possible in Biskra (Algeria), and it must no longer be used only in the experimental field. The addition of silica fume in concrete showed good strength development between the ages of 7 and 28 days depending on the mix design; concrete containing 8 per cent silica fume with a W/B (water/binder) of 0.25 has a compressive strength higher than other concretes, and concrete with silica fume is stronger than concrete without silica fume, so we can have concrete with a compressive strength of 62 MPa for W/C of 0.25 without silica fume. Then, one can avoid the use of silica fume to a resistance of concrete to the compressive strength of 62 MPa and a slump of 21 cm, as silica fume is the most expensive ingredient in the composition of the concrete and is very important economically. A main factor in producing high-strength concrete above 72 MPa is to use less reactive natural pozzolan (such as silica fume) in combination with silica fume and a W/B low of 0.25 and 0.30. The combination of silica fume and natural pozzolan in mixtures resulted in a very dense microstructure and low porosity and produced an enhanced permeability of concrete of high strength, as with resistance to the penetration of aggressive agents; thus, an economical concrete was obtained using this combination.

The study of the influence of cementitious materials on concrete strength gain was carried out. Other features of LWHPC such as creep, cracking, shrinkage, resistance to sulphate attack, corrosion resistance, fire resistance and durability should be also studied, because there are cases where another feature is most important for the designer or owner than the compressive strength at 28 days. Further studies should include a range of variables to change mixtures significantly and determine defined applications of LWHPC to produce more efficient and economical concretes. It is important to gather information on LWHPC to push forward the formulation of characteristics for pozzolan concrete for the building industry.

The LWHPC can be used to obtain high modules of elasticity and high durability in special structures such as marine structures, superstructures, parking, areas for aircraft/airplane runways, bridges, tunnels and industrial buildings (nuclear power stations).

The novel finding of the paper is the use of crystallized slag aggregates and natural pozzolan aggregates to obtain LWHPC.

This article, by a noted French authority, summarises the work done in French territories over the past 30 years, and presents the conclusions derived from these long and thorough investigations. The author is a chemical and geological engineer and is a Docteur ès Sciences of the University of Nancy. He has long been associated with prestressed concrete work and is currently the President of the Concrete Group of the Commission Europèenne de la Corrosion.