The purpose of this study is to reduce the cracks, pores and unfused defects in arc welding, improve the crystalline structure of the weld, refine its grains and improve the mechanical properties.

Taking E690 marine steel as the research object, the experiment adopts a new process method of laser forging coupled arc welding. Welding for comparative experiments. Experiments show that the “V”-shaped groove arc welding process has a larger fusion area, but has pores, the arc current is 168 A, the arc voltage is 28 V and the welding speed is 600 mm/min.

It can be seen from tensile tests that the coupling welding process has the highest tensile strength and yield strength, 872 MPa and 692 MPa, respectively, and the fracture elongation is 29.29%. The single-beam laser forging coupled arc welding process has a distance of laser and wire of 6–8 mm, a laser wavelength of 1,064 nm and the highest weld fusion ratio. The microhardness test shows that the average hardness of single-beam laser forging in the weld zone is 487.54 HV, which is 10.30% higher than that of arc welding. The average hardness in the fusion zone is 788.08 HV, which is 14.52% higher than that of the arc welding process.

The originality of the experiment: proposed a new process method of coupling arc repair for offshore steel forging; adopted a new process method of simultaneous coupling of single-beam short-pulse laser, double-beam short-pulse laser and arc welding; and obtained effect of pulsed laser and arc composite repair on porosity and fusion of E690 marine steel welds.

The purpose of this study is to examine the effects of sensitization on the metallurgical characteristics of weld joints made up of austenitic stainless steel (AISI 316L) and ferritic stainless steel (AISI 430), using the gas tungsten arc welding (GTAW) process with ER316L filler wires.

A non-consumable tungsten electrode with a diameter of 1.6 mm was used during the GTAW procedure. The filler wire, ER316L, was selected based on the recommendation provided in literature. To explore the interconnections among the structure and properties of these weldments, the techniques including scanning electron microscopy and optical analysis have been used. In addition, the sensitization behaviour of the weldments was investigated using the double loop electrochemical potentio-kinetic reactivation (DLEPR) test.

Microstructural analyses revealed the occurrences of coarsened grains with equiaxed columnar grains and migrating grain boundaries in the weld zone. The results of the DLEPR test demonstrated that heat affected zone (HAZ) of AISI 430 was more susceptible to sensitization than HAZ of AISI 316L. Microstructure analysis also revealed the precipitation of large amounts of chromium carbide at the grain boundaries region of AISI 430 welded steel, causing more sensitization and, as a result, more failure or breaking at the side of AISI 430 weld in the dissimilar weldment of AISI 316L–AISI 430.

The present work has been carried out to determine the appropriate welding conditions for joining AISI 316L and AISI 430, as well as the metallurgical properties of the dissimilar weldment formed between AISI 316L and AISI 430. Owing to the difficulties in measuring the performance of these types of dissimilar joints given their unique mechanical and microstructural characteristics, research on the subject is limited.

This article aims to investigate and model the effects of welding-generated thermal cycle on the resulting residual stress distribution and its role in the initiation and propagation of fatigue failure in thick shaft sections.

Experimental and numerical techniques were applied in the present study to explore the relationship(s) between welding residual-stress distribution and fatigue failure characteristics in a hydropower generator shaft. Experimental techniques included stereomicroscopy, optical and scanning electron microscopy (SEM), chemical analysis and mechanical testing. Finite element modelling (FEM) was used to model the shaft welding cycle in terms of thermal (temperature) history and the associated development of residual stresses within the weld joint.

Experimental analyses have confirmed the suitability of the used material for the intended application and confirmed the failure mode to be low cycle fatigue. The observed failure characteristics, however, did not match with the applied loading in terms of design stress levels, directionality and expected crack imitation site(s). FEM results have revealed the presence of a sharp stress peak in excess of 630 MPa (about 74% of material's yield strength) around weld start point and a non-uniform residual stress distribution in both the circumferential and through-thickness directions. The present results have shown very close matching between FEM results and observed failure characteristics.

The present article considers an actual industrial case of a hydropower generator shaft failure. Present results are valuable in providing insight information regarding such failures as well as some preventive design and fabrication measures for the hydropower and other power generation and transmission sector.

The presence of the aforementioned stress peak around welding start/end location and the non-uniform distribution of residual-stress field are in contrast to almost all published results based on some uniformity assumptions. The present FEM results were, however, the only stress distribution scenario capable of explaining the failure considered in the present research.

The high specific strength makes magnesium alloys have a wide range of applications in aerospace, military, automotive, marine and construction industries. However, its poor corrosion resistance and weldability have limited its development and application. Friction stir welding (FSW) can effectively avoid the defects of fusion welding. However, the microstructure, mechanical properties and corrosion behavior of FSW joints in magnesium alloys vary among different regions. The purpose of this paper is to review the corrosion of magnesium alloy FSW joints, and to summarize the protection technology of welded joints.

The corrosion of magnesium alloy FSW joints includes electrochemical corrosion and stress corrosion. This paper summarizes corrosion protection techniques for magnesium alloys FSW joints, focusing on composition, microstructure changes and surface treatment methods.

Currently, this research is mainly focused on enhancing the corrosion resistance of magnesium alloy FSW joints by changing compositions, structural modifications and surface coating technologies. Refinement of the grains can be achieved by adjusting welding process parameters, which in turn minimizes the effects of the second phase on the alloy’s corrosion resistance.

This paper presents a comprehensive review on the corrosion and protection of magnesium alloys FSW joints, covering the latest research advancements and practical applications. It aims to equip researchers with a better insight into the field and inspire new studies on this topic.

This paper aims to examine dissimilar joints for various applications in chemical, petrochemical, oil, gas, shipbuilding, defense, rail and nuclear industry.

This study examined the effects of cold metal transfer welding on stainless steel welds for 316L austenitic and 430 ferritic dissimilar welds with ER316L, ER309L and without (autogenous) fillers. The microstructural observation was done with an optical microscope. The mechanical test was done to reveal the strength, hardness and toughness of the joint. The electrochemical polarization tests were done to reveal intergranular and pitting corrosion in the dissimilar joints.

This microstructural study shows the presence of austenitic and ferritic phases with vermicular ferrite for ER309L filler weld, and for ER316L filler weld specimen shows predominately martensitic phase in the weld region, whereas the autogenous weld shows lathy ferrite mixed with martensitic phase. Mechanical test results indicated that filler welded specimen (ER316L and ER309L) has relatively higher strength and hardness than the autogenous weld, whereas ER316L filler weld exhibited the highest impact toughness than ER309L filler weld and lowest in autogenous weld. The electrochemical corrosion results displayed the highest degree of sensitization (DOS) in without filler welded specimen (45.62%) and lower in case of filler welded specimen ER309L (4.95%) and least in case of ER316L filler welded specimen (3.51%). The high DOS in non-filler welded specimen is correlated with the chromium carbide formation. The non-filler welded specimen shows the highest pitting corrosion attack as compared to the ER316L filler weld specimen and relatively better in ER309L filler welded specimen. The highest pitting corrosion resistance is related with the high chromium content in ER309L composition.

This experimental study is original and conducted with 316L and 430 stainless steel with ER316L, ER309 and without fillers, which will help the oil, shipbuilding and chemical industries.

The main purpose of the present work is to study the multi response optimization of dissimilar friction stir welding (FSW) process parameters using Taguchi-based grey relational analysis and desirability function approach (DFA).

The welded sheets were fabricated as per Taguchi orthogonal array design. The effects of tool rotational speed, transverse speed and tool tilt angle process parameters on ultimate tensile strength and hardness were analyzed using grey relational analysis, and DFA and optimum parameters combination was determined.

The tensile strength and hardness values were evaluated from the welded joints. The optimum values of process parameters were estimated through grey relational analysis and DFA methods. Similar kind of optimum levels of process parameters were obtained through two optimization approaches as tool rotational speed of 1150 rpm, transverse speed of 24 mm/min and tool tilt angle of 2° are the best process parameters combination for maximizing both the tensile strength and hardness. Through these studies, it was confirmed that grey relational analysis and DFA methods can be used to find the multi response optimum values of FSW process parameters.

In the present study, the FSW is performed with L9 orthogonal array design with three process parameters such as tool rotational speed, transverse speed and tilt angle and three levels.

Aluminium alloys are widely using in automotive and aerospace industries due to holding a high strength to weight property.

Very limited work had been carried out on multi objective optimization techniques such as grey relational analysis and DFA on friction stir welded joints made with dissimilar aluminium alloys sheets.

Aluminium alloys can be used as lightweight and high-strength materials in combination with the technology of laser beam welding, an efficient joining method, in the manufacturing of automotive parts. The purposes of this paper are to conduct laser welding experiments with Al2024 in the lap joint configuration, model the laser welding process parameters of Al2024 alloys and use propounded models to optimize the process parameters.

Laser welding of Al2024 alloy has been conducted in the lap joint configuration. Then, the influences of explanatory variables (laser peak power, scanning speed and frequency) on outcome variables (weld width [WW], throat length [TL] and breaking load [BL]) have been investigated with Poisson regression analysis of the data set derived from experimentation. Thereafter, a multi-objective genetic algorithm (MOGA) has been used using MATLAB to find the optimum solutions. The effects of various input process parameters on the responses have also been analysed using response surface plots.

The promulgated statistical models, derived with Poisson regression analysis, are evinced to be well-fit ones using the analysis of deviance approach. Pareto fronts have been used to demonstrate the optimization results, and the maximized load-bearing capacity is computed to be 1,263 N, whereas the compromised WW and TL are 714 µm and 760 µm, respectively.

This work of conducting laser welding of lap joint of Al2024 alloy incorporating the Taguchi method and optimizing the input process parameters with the promulgated statistical models proffers a neoteric perspective that can be useful to the manufacturing industry.

This paper presents a review concerning the analytical and inverse methods of small punch creep test (SPCT) in order to evaluate the mechanical property of component material at elevated temperature.

In this work, the effects of temperature, specimen size and shape on material properties are mainly discussed using the finite element (FE) method. The analytical approaches including membrane stretching, empirical or semi-empirical solutions that are currently used for data interpretation have been presented.

The state-of-the-art research progress on the inverse method, such as non-linear optimization program and neutral network, is critically reviewed. The capabilities of the inverse technique, the uniqueness of the solution and future development are discussed.

The state-of-the-art research progress on the inverse method such as non-linear optimization program and neutral network is critically reviewed. The capabilities of the inverse technique, the uniqueness of the solution and future development are discussed.

This Friction stir welding study aims to weld thick AA8011 aluminium plates, and the interface joints created with a variety of tool pin profiles were examined for their effects on the welding process.

Scanning electron microscopy and optical microscopy and X-ray diffraction were used to examine the macro and micro-structural characteristics, as well as the fracture surfaces, of tensile specimens. The mechanical properties (tensile, hardness tests) of the base metal and the welded specimens under a variety of situations being tested. Additionally, a fracture toughness test was used to analyse the resilience of the base metal and the best weldments to crack formation. Using a response surface methodology with a Box–Behnken design, the optimum values for the three key parameters (rotational speed, welding speed and tool pin profile) positively affecting the weld quality were established.

The results demonstrate that a defect-free junction can be obtained by using a cylindrical tool pin profile, increasing the rotational speed while decreasing the welding speeds. The high temperature and compressive residual stress generated during welding leads to the increase in grain size. The grain size of the welded zone for optimal conditions is significantly smaller and the hardness of the stir zone is higher than the other experimental run parameters.

The work focuses on the careful examination of microstructures behaviour under various tool pin profile responsible for the change in mechanical properties. The mathematical model generated using Taguchi approach and parameters was optimized by using multi-objectives response surface methodology techniques.

Material extrusion (MEX) 3D printers suffer from an intrinsic limitation of small size of the prints due to its restricted bed dimension. On the other hand, friction stir spot welding (FSSW) is gaining wide interest from automobile, airplane, off-road equipment manufacturers and even consumer electronics. This paper aims to explore the possibility of FSSW on Acrylonitrile Butadiene Styrene/Polylactic acid 3D-printed components to overcome the bed size limitation of MEX 3D printers.

Four different tool geometries (tapered cylindrical pin with/without concavity, pinless with/without concavity) were used to produce the joints. Three critical process parameters related to FSSW (tool rotational speed, plunge depth and dwell time) and two related to 3D printing (material combination and infill percentages) were investigated and optimized using the Taguchi L27 design of experiments. The influence of each welding parameter on the shear strength was evaluated by analysis of variance.

Results revealed that the infill percentage, a 3D printing parameter, had the maximum effect on the joint strength. The joints displayed pull nugget, cross nugget and substrate failure morphologies. The outcome resulted in the joint efficiency reaching up to 100.3%, better than that obtained by other competitive processes for 3D-printed thermoplastics. The results, when applied to weld a UAV wing, showed good strength and integrity. Further, grafting the joints with nylon micro-particles was also investigated, resulting in a detrimental effect on the strength.

To the best of the authors’ knowledge, this is the first study to demonstrate that the welding of dissimilar 3D-printed thermoplastics with/without microparticles is possible by FSSW, whilst the process parameters have a considerable consequence on the bond strength.