1 – 10 of over 1000Mauricio Pérez Giraldo, Mauricio Vasquez, Alejandro Toro, Robison Buitrago-Sierra and Juan Felipe Santa
This paper aims to develop a stable gel-type lubricant emulating commercial conditions. This encompassed rheological and tribological assessments, alongside field trials on the…
Abstract
Purpose
This paper aims to develop a stable gel-type lubricant emulating commercial conditions. This encompassed rheological and tribological assessments, alongside field trials on the Medellín tram system.
Design/methodology/approach
The gel-type lubricant with graphite and aluminum powder is synthesized. Rheological tests, viscosity measurements and linear viscoelastic regime assessments are conducted. Subsequently, tribological analyses encompassing four-ball and twin disc methods are executed. Finally, real-world testing is performed on the Medellín tram system.
Findings
An achieved lubricant met the stipulated criteria, yielding innovative insights into the interaction of graphite and aluminum powder additives under varying tests.
Originality/value
Novel findings are unveiled regarding the interaction of graphite and aluminum powder additives in tribological, rheological and real-world trials. In addition, the wear behavior of polymers is observed, along with the potential utilization of such additives in tramway systems.
Details
Keywords
Sara Pope and Robert L. Jackson
The purpose of this paper is to use a wear test to determine the effect of sand on the wear rates of materials typically used in aerospace applications. Once a repeatable wear…
Abstract
Purpose
The purpose of this paper is to use a wear test to determine the effect of sand on the wear rates of materials typically used in aerospace applications. Once a repeatable wear test has been established, it can be used to test any combination of materials or coatings. The effectiveness of several different test methods will also be evaluated, including the sample height, surface roughness and mass difference. In addition, the current work will observe the differences between applying sand before the samples are brought into contact or after. The wear rates obtained from these tests could also be used to predict the wear of other components in similar abrasive particulate environments.
Design/methodology/approach
A modified block-on-flat wear test of anodized aluminum on hard coat anodized aluminum was used to study this. The experiments were performed with and without sand to study the effects of the sand. Two methods of adding sand were also evaluated. Weighing and profilometry were used to study the differences between the tests.
Findings
Wear rates have been calculated based on both the change in the masses of the samples and the change in the height between the upper and lower samples over the course of each test. The wear rates from the change in the masses are repeatable with and without sand, but the results for the change in height show no repeatability without sand. In addition, only in the presence of sand do the trends for the two methods agree. The wear rate was found to be non-linear as a function of load and therefore not in agreement with Archard’s Wear Law. The wear rate also increased significantly when sand was present in the contact for the duration of the test. The sand appears to change the wear mechanism from an adhesive to an abrasive mechanism. Black wear particles formed both when there was sand and when there was not sand. The source of these particles has been investigated but not determined.
Originality/value
This work has not been previously published and is the original work of the authors.
Details
Keywords
Yuchun Huang, Haishu Ma, Yubo Meng and Yazhou Mao
This paper aims to study the synergistic lubrication effects of Sn–Ag–Cu and MXene–Ti3C2 to improve the tribological properties of M50 bearing steel with microporous channels.
Abstract
Purpose
This paper aims to study the synergistic lubrication effects of Sn–Ag–Cu and MXene–Ti3C2 to improve the tribological properties of M50 bearing steel with microporous channels.
Design/methodology/approach
M50 matrix self-lubricating composites (MMSC) were designed and prepared by filling Sn–Ag–Cu and MXene–Ti3C2 in the microporous channels of M50 bearing steel. The tribology performance testing of as-prepared samples was executed with a multifunction tribometer. The optimum hole size and lubricant content, as well as self-lubricating mechanism of MMSC, were studied.
Findings
The tribological properties of MMSC are strongly dependent on the synergistic lubrication effect of MXene–Ti3C2 and Sn–Ag–Cu. When the hole size of microchannel is 1 mm and the content of MXene–Ti3C2 in mixed lubricant is 4 wt.%, MMSC shows the lowest friction coefficient and wear rate. The Sn–Ag–Cu and MXene–Ti3C2 are extruded from the microporous channels and spread to the friction interface, and a relatively complete lubricating film is formed at the friction interface. Meanwhile, the synergistic lubrication of Sn–Ag–Cu and MXene–Ti3C2 can improve the stability of the lubricating film, thus the excellent tribological property of MMSC is obtained.
Originality/value
The results help in deep understanding of the synergistic lubrication effects of Sn–Ag–Cu and MXene–Ti3C2 on the tribological properties of M50 bearing steel. This work also provides a useful reference for the tribological design of mechanical components by combining surface texture with solid lubrication.
Peer review
The peer review history for this article is available at: https://publons.com/publon/10.1108/ILT-12-2023-0381/
Details
Keywords
Xiaolong Lu, Xudong Sui, Xiao Zhang, Zhen Yan and Junying Hao
This study aims to investigate the effect of V doping on the microstructure, chemical stability, mechanical and vacuum tribological behavior of sputtered MoS2 coatings.
Abstract
Purpose
This study aims to investigate the effect of V doping on the microstructure, chemical stability, mechanical and vacuum tribological behavior of sputtered MoS2 coatings.
Design/methodology/approach
The MoS2-V coatings are fabricated via tuning V target current by magnetron sputtering technique. The structural characteristic and elemental content of the coatings are measured by field emission scanning electron microscopy, X-ray diffractometer, electron probe X-ray micro-analyzer, Raman, X-ray photoelectron spectroscopy, high resolution transmission electron microscope and energy dispersive spectrometer. The hardness of the deposited coatings are tested by a nanoindentation technique. The vacuum tribological properties of MoS2-V coatings are studied by a ball-on-disc tribometer.
Findings
Introducing V into the MoS2 coatings results in a more compact microstructure. The hardness of the coatings increases with the doping of V. The MoS2-V coating deposited at a current of 0.2 A obtains the lowest friction coefficient (0.043) under vacuum. As the amount of V doping increases, the wear rate of the coating decreases first and then increases, among which the coating deposited at a current of 0.5 A has the lowest wear rate of 2.2 × 10–6 mm3/N·m.
Originality/value
This work elucidates the role of V doping on the lubrication mechanism of MoS2 coatings in a vacuum environment, and the MoS2-V coating is expected to be applied as a solid lubricant in space environment.
Details
Keywords
Ferhat Ceritbinmez, Yusuf Kanca, Ahmet Tuna and Erdoğan Kanca
FeNi36 (Invar-36) alloy is widely used in the fabrication of molding tools in aerospace industries but there remains a need to improve its wear and friction performance due to its…
Abstract
Purpose
FeNi36 (Invar-36) alloy is widely used in the fabrication of molding tools in aerospace industries but there remains a need to improve its wear and friction performance due to its relatively low hardness. The formation of a heat affected zone (HAZ) on the surface of Invar-36 cut by wire electric discharge machining (WEDM) is promising to enhance its tribological properties. This study aims to investigate the tribological performance of WEDM-treated Invar-36 via a ball-on-disk tribometer in dry-sliding conditions.
Design/methodology/approach
The untreated and WEDM-treated Invar-36 surfaces were reciprocated against an alumina ball at a sliding velocity of 40 mm/s, a stroke length of 10 mm and a sliding duration of 125 min under loads of 5, 10 and 20 N. The worn surfaces were characterized using a 2D profilometry and a scanning electron microscope equipped with energy-dispersive spectroscopy.
Findings
The results showed that the WEDM-treated surface had a superior friction coefficient and wear resistance in comparison to the untreated surface, due to the grown HAZ. There was found to be a 9.3%–11.4% decrease in the friction coefficient and a 47%–57% reduction in the wear volume after the WEDM treatment. Both the untreated and WEDM-treated Invar-36 surfaces found abrasion and plastic deformation as the dominant wear mechanisms.
Originality/value
Previous works have not focused on the tribological performance of the WEDM-treated Invar-36 extensively used for molding tools in aerospace industries. Our findings provide compelling evidence that the WEDM treatment improved the wear and friction performance of Invar-36 alloy because of the grown HAZ.
Details
Keywords
Bo Zhang, Yuqian Zheng, Zhiyuan Cui, Dongdong Song, Faqian Liu and Weihua Li
The impact of rolling on the performance of micro arc oxidation (MAO) coatings on ZM5 alloy has been underreported. The purpose of this study is to explore the correlation between…
Abstract
Purpose
The impact of rolling on the performance of micro arc oxidation (MAO) coatings on ZM5 alloy has been underreported. The purpose of this study is to explore the correlation between rolling and the failure mechanism of MAO coatings in greater depth.
Design/methodology/approach
The influence of rolling on the corrosion and wear properties of MAO coating was investigated by phase structure, bond strength test (initial bond strength and wet adhesion), electrochemical impedance spectroscopy and wear test. The change of the surface electrochemical properties was studied by first principles analysis.
Findings
The results showed that the MAO coating on rolled alloy had better corrosion and wear resistance compared to cast alloy, although the structure and component content of two kinds of MAO coating are nearly identical. The difference in interface bonding between MAO coating and Mg substrate is the primary factor contributing to the disparity in performance between the two types of samples. Finally, the impact of the rolling process on MAO coating properties is explained through first-principle calculation.
Originality/value
A comprehensive explanation of the impact of the rolling process on MAO coating properties will provide substantial support for enhancing the application of Mg alloy anticorrosion.
Graphical abstract
Details
Keywords
Meigui Yin, Lei Zhang and Longxiang Huang
The purpose of this paper is to study the effect of surface salt spray duration on the fretting wear and electrochemical corrosion behaviors of Inconel 690 alloy.
Abstract
Purpose
The purpose of this paper is to study the effect of surface salt spray duration on the fretting wear and electrochemical corrosion behaviors of Inconel 690 alloy.
Design/methodology/approach
A high-temperature steam generator was applied to salt spray test samples, a fretting wear rig was used to realize the damage behavior tests, an electrochemical workstation was applied to analysis the changes of each sample’s corrosion dynamic response before and after fretting wear.
Findings
The thickness of the oxide film that formed on sample surface was increased with the salt spray duration, and somewhat it could act as lubrication during the fretting wear process; however, the corrosive chloride would accelerate the fretting mechanical damage behavior.
Originality/value
In a salt steam spray condition, the fretting tribo-corrosion behaviors of Inconel 690 alloy surface was studied.
Details
Keywords
Xiao Xu and Yimin Zhang
This study aims to form composite solid lubricant coatings on the surface of bearing steel, which can significantly improve the tribological properties of thrust cylindrical…
Abstract
Purpose
This study aims to form composite solid lubricant coatings on the surface of bearing steel, which can significantly improve the tribological properties of thrust cylindrical roller bearings (TCRBs). Phosphating films possess microscopic porosity that typically needs to be sealed with oil, grease or wax. Due to its unique crystal structure, the phosphating film itself also exhibits a certain degree of lubricity. In this study, solid lubricants are used to fill the pores of the phosphating film. By combining the phosphating film with solid lubricants, lubrication and wear reduction can be achieved.
Design/methodology/approach
In this study, the surfaces of the shaft washer (WS) and seat washer (GS) were treated with zinc-phosphating. Subsequently, a solid lubricant solution (polytetrafluoroethylene [PTFE], MoS2 and graphite) was sprayed onto the phosphated samples at concentrations of 1 , 2 and 3 g/L. The porous and adsorptive nature of the phosphating film was used to embed the solid lubricant particles into the film, thus forming a composite lubrication layer containing solid lubricants on the surface of the bearing steel.
Findings
The addition of solid lubricant materials has shown significant potential in reducing wear losses compared with phosphated samples without such additives. Increasing the amount of solid lubricant added can facilitate the formation of a transfer film, which further enhances the protective properties. However, it is important to note that excessive amounts of solid lubricant material can contribute to seizure, leading to increased wear losses of the cage and a higher average coefficient of friction (ACOF).By spraying a PTFE solution with a concentration of 2 g/L, the lowest ACOF and cage wear loss were achieved, resulting in reductions of 60.5% for the ACOF and 89.4% for the cage wear loss. Similarly, when spraying a graphite solution with a concentration of 3 g/L, the lowest wear losses for GS and WS were observed, with reductions of 51.7% for GS wear loss and 38.9% for WS wear loss.
Originality/value
The combination of the phosphating film and solid lubricants aims to achieve lubrication and wear reduction, providing a new approach to wear-resistant technology for TCRBs.
Peer review
The peer review history for this article is available at: https://publons.com/publon/10.1108/ILT-07-2023-0231/
Details
Keywords
Rajat Yadav, Anas Islam and Vijay Kumar Dwivedi
The purpose of this paper is to study Al-based green composite. To make composite samples of aluminium alloy (AA3105) with different weight percentages of rice husk ash (RHA) and…
Abstract
Purpose
The purpose of this paper is to study Al-based green composite. To make composite samples of aluminium alloy (AA3105) with different weight percentages of rice husk ash (RHA) and eggshell (ES) particles as reinforcement, stir casting method was used.
Design/methodology/approach
Several other aspects, including the weight percent of reinforcing agent particles, the applied stress and the sliding speed, were taken into consideration. During the course of the wear test, the sliding distance that was recorded varied from a minimum of 1,000 m all the way up to a maximum of 3,135 m (10, 15, 20, 25 and 30 min). The typical range for normal loads is 8–24 N, and their speed is 1.58 m/s.
Findings
With the AA/ES/RHA composite, the wear rates decreases when the grain size of the reinforcing particles enhanced. Scanning electron microscopy images of worn surfaces show that at low speeds, delaminating and ploughing are the main causes of wear. At high speeds, ploughing is major cause of wear. Composites with better wear-resistant properties can be used in wide range of tribological applications, especially in the automotive industry. It was found that hardness increases at the same time as the weight of the reinforcement increases. Tensile and hardness were maximized at 10% reinforcement mix in Al3105.
Originality/value
In this work, ES and RHA has been used to develop green metal matrix composite to support green revolution as promoted/suggested by United Nations thus reducing the environmental pollution.
Details
Keywords
Guangwei Liang, Zhiming Gao, Cheng-Man Deng and Wenbin Hu
The purpose of this study is to reveal the effect of nano-Al2O3 particle addition on the nucleation/growth kinetics, microhardness, wear resistance and corrosion resistance of…
Abstract
Purpose
The purpose of this study is to reveal the effect of nano-Al2O3 particle addition on the nucleation/growth kinetics, microhardness, wear resistance and corrosion resistance of Co–P–xAl2O3 nanocomposite plating.
Design/methodology/approach
The kinetics and properties of Co–P–xAl2O3 nanocomposite plating prepared by electroplating were investigated by electrochemical measurements, scanning electron microscopy, X-ray diffraction, X-ray photoelectron spectroscopy, Vickers microhardness measurement, SRV5 friction and wear tester and atomic force microscopy.
Findings
A 12 g/L nano-Al2O3 addition in the plating solution can transform the nucleation/growth kinetics of the plating from the 3D progressive model to the 3D instantaneous model. The microhardness of the plating increased with the increase of nano-Al2O3 content in plating. The wear resistance of the plating did not adhere strictly to Archard’s law. An even and denser corrosion product film was generated due to the finer grains, with a high corrosion resistance.
Originality/value
The effect of different nano-Al2O3 addition on the nucleation/growth kinetics and properties of Co–P–xAl2O3 nanocomposite plating was investigated, and an anticorrosion mechanism of Co–P–xAl2O3 nanocomposite plating was proposed.
Details