The purpose of this paper is to study the effect of nano alumina (Al₂O₃) on the properties of fresh concrete, hardened concrete and microstructure of concrete incorporated with high range water reducer (HRWR). This initiative was taken to improve characteristic properties of concrete using nano alumina because nano alumina can be easily be manufactured from a scrap of industrial aluminum products, so its incorporation in concrete will not only reduce industrial aluminum waste but will also change the morphology of concrete at the microstructural level.

To accomplish the objectives of the research, four different concrete mixes with the constant water–cement ratio (W/C) and superplasticizer (SP) content 0.4 and 0.6% by weight of cement, respectively, were prepared, whereas nano alumina content was altered by 0.3% and 0.4% by weight of cement. Fresh property of concrete was analyzed by using slump cone test, whereas hardened properties of concrete were analyzed through compression test and flexural strength test. The interaction of nano alumina with concrete composite was evaluated using an X-ray diffraction test.

It was observed that 0.6% superplasticizer by weight of cement increased workability by 22% but with the addition of 0.3%, nano alumina by weight of cement workability decreased by 31%. Compressive strength increased by 4.88% with the addition of 0.6% superplasticizer but with the addition of 0.3% nano alumina by weight of cement compressive strength increased by 18.60%. Also, flexural strength increased by 1.21% with the addition of 0.6% superplasticizer by weight of cement but with the addition of 0.3% nano alumina by weight of cement flexural strength increased by 8.76%. With the addition of superplasticizer, alite and belite phases remained un-hydrated but with the addition of nano alumina alite phase was hydrated while belite phase was un-hydrated. The size of belite crystals in mixes having nano alumina was less than that of mix having 0.6% superplasticizer. Also with the addition of nano alumina, a calcium aluminum silicate phase was formed which was responsible for the increment of strength in mixes having nano alumina.

Incorporation nano alumina (Al₂O₃) in concrete will not only reduce industrial aluminum waste but will also reduce CO₂ emission. Nano alumina (Al₂O₃) also changes morphology of concrete at micro structural level.

The purpose of this paper is to obtain a constitutive model of cement-based material in the rheological stage, which owns the different water-cement ratio (w/c) and temperature and have a significant impact on the workability of concrete materials.

It is introduced a modified Arrhenius equation into the Herschel–Bulkley model, which is widely applied in rheological analysis and constructed an ordinary differential equation (ODE) of w/c from the Navier–Stokes equation. By solving the ODE, an approximate constitutive relation of cement-based materials included w/c and temperature is derived. Compared with the experimental results, the present model is validated.

The shear stress and shear rate curves with different w/c and temperature are simulated by the present method, and the present model can be applied to analyze the changes of apparent viscosity in cement-based material slurry as the w/c and temperature varying.

This work gives a mathematical model, which can effectively approximate the shear stress–shear rate relation with different w/c and temperature in the rheological stage of cement-based material.

Microwave curing (MC) can facilitate rapid concrete repair in cold climates without using conventional accelerated curing technologies which are environmentally unsustainable. Accelerated curing of concrete under MC can contribute to the decarbonisation of the environment and provide economies in construction in several ways such as reducing construction time, energy efficiency, lower cement content, lower carbonation risk and reducing emissions from equipment.

The paper investigates moisture loss and pore properties of six cement-based proprietary concrete repair materials subjected to MC. The impact of MC on these properties is critically important for its successful implementation in practice and current literature lacks this information. Specimens were microwave cured for 40–45 min to surface temperatures between 39.9 and 44.1 °C. The fast-setting repair material was microwave cured for 15 min to 40.7 °C. MC causes a higher water loss which shows the importance of preventing drying during MC and the following 24 h.

Portland cement-based normal density repair mortars, including materials incorporating pfa and polymer latex, benefit from the thermal effect of MC on hydration, resulting in up to 24% reduction in porosity relative to normal curing. Low density and flowing repair materials suffer an increase in porosity up to 16% due to MC. The moisture loss at the end of MC and after 24h is related to the mix water content and porosity, respectively.

The research on the application of MC for rapid repair of concrete is original. The research was funded by the European commission following a very rigorous and competitive review process which ensured its originality. Original data on the parameters of porosity and moisture loss under MC are provided for different generic cementitious repair materials which have not been studied before. Application of MC to concrete construction especially in cold climates will provide environmental, economic and energy benefits.

The coal-based synthetic natural gas slag (CSNGS) is a solid waste remaining from the incomplete combustion of raw coal to produce gas. With the continuous promotion of efficient and clean utilization of coal in recent years, the stockpiling of CSNGS would increase gradually, and it would have significant social and environmental benefits with reasonable utilization of CSNGS. This study prepared a new geopolymer by mixing CSNGS with PC42.5 cement in a certain mass ratio as the precursor, with sodium hydroxide and sodium silicate solution as the alkali activators.

The formulation of coal-based synthetic natural gas slag geopolymer (CSNGSG) was determined by an orthogonal test, and then the strength mechanism and microstructure of CSNGSG were characterized by multi-scale tests.

The results show that the optimum ratio of CSNGSG was a sodium silicate modulus of 1.3, an alkali dosage of 21% and a water cement ratio of 0.36 and the maximum unconfined compressive strength of CSNGSG at 7 d was 26.88 MPa. The increase of curing temperature could significantly improve the compressive strength of CSNGSG, and the curing humidity had little effect on the compressive strength of CSNGSG. The development of the internal strength of CSNSG at high temperatures consumed SiO₂, Al₂O₃ and CaO and the intensity of corresponding crystalline peaks decreased.

Moreover, the vibration of chemical bonds in different wavenumbers also revealed the reaction mechanism of CSNSG from another perspective. Finally, the relevant test results indicated that CSNGS had practical application value as a raw material for the preparation of geopolymer cementing materials.

The purpose of this paper is to add expanded perlite (EP) immobilized microorganisms that replace part of the standard sand in mortar to improve the self-healing ability of mortar cracks and reduce the water absorption of mortar after healing.

Bacillus pseudofirmus spores were immobilized with EP particles as self-healing agents. The effects of adding self-healing agents on the compressive strength of mortar specimens were observed. The ability of mortar specimens to heal cracks was evaluated using crack microscopic observation and water absorption experiments. The filler at the cracks was microscopically analyzed by scanning electron microscope and X-ray diffraction experiments.

First, the internal curing effect of EP promotes the hydration of cement in mortar, which generates more amount and denser crystal structure of Ca(OH)2 at mortar cracks and improves the self-healing ability of mortar. Second, the self-healing ability of mortar improves with the increase of self-healing agent admixture. Adding a self-healing agent of high admixture makes the planar undulation of calcite crystal accumulation at mortar cracks more significant. Finally, the initial crack widths that can be completely healed by adding EP and self-healing agents to the mortar are 200 µm and 600 µm, respectively.

The innovation points of this study are as follows. (1) The mechanism of the internal curing effect of EP particles on the self-healing ability of mortar cracks was revealed by crack microscopic observation tests and microscopic experiments. (2) The effect of different self-healing agent amounts on the self-healing ability of mortar cracks has been studied. (3) The effects of EP particles and self-healing agents on healing different initial widths were elucidated by crack microscopic observation tests.

Cement can be replaced to reduce the energy consumption and the environmental impact of cement. Also, foamed concrete can be used structurally in residential buildings to reduce weight and improve thermal insulation. To achieve these two goals, this paper aims to investigate the effect of basalt powder as a partial replacement of either cement or sand.

This paper investigates the effect of basalt powder as a partial replacement of either cement or sand on the mechanical properties of foamed concrete used to cast slabs. First, mechanical properties of foamed concrete are tested with and without replacement of basalt. Then, six slabs of different thicknesses and mixes are investigated. The thicknesses considered are 150- and 200-mm slabs. The three mixes used to construct these slabs are foamed concrete with no basalt powder, foamed concrete with replacement of 20% of cement by basalt powder and foamed concrete with replacement of 20% of sand by basalt powder. The flexural behavior of these slabs is investigated.

All the slabs failed in the commonly intended flexural mode. The results show that the basalt powder acted as a strong filler material in the foamed concrete mix based on mechanical properties and flexural behavior. The proposed foamed concrete slabs can be used structurally in residential buildings.

A natural waste material that can be used to promote energy efficiency and reduce emission is basalt. In this paper, basalt powder is suggested to be used due to its chemical composition that is similar to cement. Also, basalt powder is low in cost as it is waste, while basalt aggregate is prepared, and it is only used as filler in paved roads. Accordingly, basalt is partially used instead of cement to reduce the emission of carbon dioxide that results from the cement manufacturing. Also, it is used as a partial alternative to sand which can be considered as a new stronger source as filling material used in the production of concrete.

This paper aims to express a mathematical model that predicts the effect of mineral additives on the physical–mechanical properties of high-performance sand concrete (HPSC), using SAS's JMP7 statistical analysis software.

A mixture design modeling approach is applied to sand concrete (SC) for optimizing mixtures without being obliged to do a lot of experiments, where the cement is partially replaced with two mineral additives silica fume (SF) and blast furnace slag (BFS) in proportions as high as 20% of the mass. A total of 15 mixtures of sand concrete is prepared in the laboratory using this analytical technique in combinations with binary and ternary systems to estimate the workability and the compressive strength (CS) of sand concrete at 7 and 28 days.

The results obtained showed that the use of derived models based on the experimental design approach greatly assisted in understanding the interactions between the various parameters of the studied mixtures; the mathematical models present excellent correlation coefficients (R² = 0.96 for CS7 days, R² = 0.93 for CS28 days and R² = 0.95 for slump) for all studied responses. Moreover, it was also found that the inclusion of additives (SF and BFS) in binary mixture SC12 and ternary mixtures SC8 leads to a significant improvement in mechanical strength compared to reference sand concrete SC15. These results give the possibility to obtain a formulation of HPSC.

This paper shows the possibility of manufacturing high-performance sand-concrete with good compressive strength; the developed mathematical model by using SAS's JMP7 statistical analysis software allowed us to reach a strength compression value of about 60 MPa, in 28 days, by replacing 10% of the cement weight with silica fume. Furthermore, with partial replacement of the cement weight (15%) with two additions such as silica fume (10%) and blast furnace slag (5%), a 58 MPa of compressive strength can be achieved, without overlooking the fact that this can be a key economic and environmental alternative.

Using coconut shell aggregates (CSA) in concrete benefits agricultural waste management and reduces the demand for mineral resources. Several studies have found that concrete containing CSA can achieve strengths that are comparable to regular concrete. The purpose of the present work is to evaluate the concrete’s durability-related properties to supplement these earlier findings.

Cylindrical specimens were prepared with a constant water–cement ratio of 0.50 and CSA content ranging from 0% to 50% (at 10% increment) by volume of the total coarse aggregates. The specimens were cured for 28 days and then tested for density, surface hardness, electrical resistivity and water sorptivity. The surface hardness was measured to describe the concrete resistance to surface wearing, while the resistivity and sorptivity were evaluated to describe the material’s resistance to fluid penetration.

The results showed that the surface hardness of concrete remained on average at 325 Leeb and did not change significantly with CSA addition. The distribution of surface hardness was also similar across all CSA groups, with the interquartile range averaging 59 Leeb. These results suggest that the cement paste and gravel stiffness had a more pronounced influence on the surface hardness than CSA. On the other hand, concrete became lighter by about 9%, had lower resistivity by 80% and had significantly higher initial sorptivity by up to 110%, when 50% of its natural gravel was replaced with CSA. Future work may be done to improve the durability of CSA when used as coarse aggregate.

The present study is the first to show the lack of correlation between CSA content and surface hardness. It would mean that the surface hardness test may not completely capture the porous nature of CSA-added concrete. The paper concludes that without additional treatment prior to mixing, CSA may be limited only to applications where concrete is not in constant contact with water or deleterious substances.

The purpose of this study is to experimentally determine whether mechanical properties of concrete can be improved by using olive pomace aggregates (OPA) as a substitute for natural sand. Two types of OPA were tested by replacing an equivalent amount of natural sand. The first type was OPA mixed with olive mill wastewater (OMW), and the second type was OPA not mixed with OMW. For each type, two series of concrete were produced using OPA in both dry and saturated states. The percentage of partial substitution of natural sand by OPA varied from 0% to 15%.

The addition of OPA leads to a reduction in the dry density of hardened concrete, causing a 5.69% decrease in density when compared to the reference concrete. After 28 days, ultrasonic pulse velocity tests indicated that the resulting material is of good quality, with a velocity of 4.45 km/s. To understand the mechanism of resistance development, microstructural analysis was conducted to observe the arrangement of OPA and calcium silicate hydrates within the cementitious matrix. The analysis revealed that there is a low level of adhesion between the cement matrix and OPA at interfacial transition zone level, which was subsequently validated by further microstructural analysis.

The laboratory mechanical tests indicated that the OPCD_OPW (5) sample, containing 5% of OPA, in a dry state and mixed with OMW, demonstrated the best mechanical performance compared to the reference concrete. After 28 days of curing, this sample exhibited a compressive strength (R_c) of 25 MPa. Furthermore, it demonstrated a tensile strength of 4.61 MPa and a dynamic modulus of elasticity of 44.39 GPa, with rebound values of 27 MPa. The slump of the specimens ranged from 5 cm to 9 cm, falling within the acceptable range of consistency (Class S2). Based on these findings, the OPCD_OPW (5) formulation is considered optimal for use in concrete production.

This research paper provides a valuable contribution to the management of OPA and OMW (OPA_OMW) generated from the olive processing industry, which is known to have significant negative environmental impacts. The paper presents an intriguing approach to recycling these materials for use in civil engineering applications.

The purpose of this paper is to study and analyze the effects of fly ash (FA) as a mineral admixture on compressive strength (CS), carbonation resistance and corrosion resistance of reinforced concrete (RC). In addition, the utilization of inexpensive and abundantly available FA as a cement replacement in concrete has several benefits including reduced OPC usage and elimination of the FA disposal problem.

Reinforcement corrosion and carbonation significantly affect the strength and durability of the RC structures. Also, the utilization of FA as green corrosion inhibitors, which are nontoxic and environmentally friendly alternatives. This review discusses the effects of FA on the mechanical characteristics of concrete. Also, this review analyzes the impact of FA as a partial replacement of cement in concrete and its effect on the depth of carbonation in concrete elements and the corrosion rate of embedded steel as well as the chemical composition and microstructure (X-ray diffraction analysis and scanning electron microscopy) of FA concrete were also reviewed.

This review provides a clear analysis of the available study, providing a thorough overview of the current state of knowledge on this topic. Regarding concrete CS, the findings indicate that the incorporation of FA often leads to a loss in early-age strength. However, as the curing period increased, the strength of fly ash concrete (FAC) increased with or even surpassed that of conventional concrete. Analysis of the accelerated carbonation test revealed that incorporating FA into the concrete mix led to a shallower carbonation depth and slower diffusion of carbon dioxide (CO₂) into the concrete. Furthermore, the half-cell potential test shows that the inclusion of FA increases the durability of RC by slowing the rate of steel-reinforcement corrosion.

This systematic review analyzes a wide range of existing studies on the topic, providing a comprehensive overview of the research conducted so far. This review intends to critically assess the enhancements in mechanical and durability attributes (such as CS, carbonation and corrosion resistance) of FAC and FA-RC. This systematic review has practical implications for the construction and engineering industries. This can support engineers and designers in making informed decisions regarding the use of FA in concrete mixtures, considering both its benefits and potential drawbacks.