This study aims to focus on how reactive diluents with mono- and di-functionalities affect the properties of resin formulation developed from bioderived precursors. A hydroxyethyl methacrylate (HEMA) terminated urethane acrylate oligomer was synthesized and characterized to study its application in stereolithography 3D printing with different ratios of isobornyl acrylate and hexanediol diacrylate.

Polyester polyol was synthesized from suberic acid and butanediol. Additionally, isophorone diisocyanate, polyester polyol and HEMA were used to create urethane acrylate oligomer. Fourier transform infrared spectroscopy and ¹H NMR were used to characterize the polyester polyol and oligomer. Various formulations were created by combining oligomer with reactive diluents in concentrations ranging from 0% to 30% by weight and curing with ultraviolet (UV) radiation. The cured coatings and 3D printed specimens were then evaluated for their properties.

The findings revealed an improvement in thermal stability, contact angle value, tensile strength and surface properties of the product which indicated its suitability for use as a 3D printing material.

This study discusses how oligomers that have been cured by UV radiation with mono- and difunctional reactive diluents give excellent coating characteristics and demonstrate suitability and stability for 3D printing applications.

This study aims to perform the surface treatment of synthetic α-Fe₂O₃ red iron oxide pigment with hydrolysate 3-aminopropyl silane (A) and colloidal silica (CS) and investigate the effects of surface-treated pigment on the styrene acrylic (SA) emulsion and polyurethane (PU) dispersion.

For this purpose, firstly red iron oxide particles were modified with A and CS separately in an aqueous medium. After isolation of the modified iron oxide were characterized by Fourier transform infrared spectroscopy (FTIR), X-ray photoelectron spectroscopy (XPS) and scanning electron microscopy with energy dispersive spectroscopy (SEM-EDS). Moreover, the degree of the dispersion stability of the modified pigment in coatings with SA emulsion and PU dispersion was investigated by using an oscillation rheometer. Loss (G''), storage (G') modulus, loss factor [tan(δ)] and yield stress (τ⁰) values were determined by performing amplitude and frequency sweep tests.

The τ⁰ in SA coatings decreases with the amount of used A and increases with the amount of used CS. The τ⁰ decreases as the amount of used A and CS in PU coatings increases. The use of CS on red iron oxide pigments causes storage modulus to increase in SA coatings at low angular frequencies, while it causes a decrease in PU coatings.

To the best of the authors’ knowledge, for the first time, the suspended state of the iron oxide hybrid pigment formed with CS in the coating was investigated rheologically in this study.

The purpose of this paper is to synthesize a polyacrylate-based dispersant with a determined target molecular weight for oily systems and to determine the optimal dispersant level and monomer ratio of the dispersant.

The dispersant was synthesized by conventional radical polymerization using methacrylic acid, butyl acrylate and dimethylamino ethyl methacrylate as the monomer. It was characterized by Fourier transform infrared spectroscopy, nuclear magnetic hydrogen spectroscopy, gel permeation chromatography and thermogravimetric analysis. The dispersant was used to disperse TiO₂, and the performance of the dispersant was evaluated by measuring the viscosity, particle size and dispersive force of the slurry.

The dispersant exhibited high thermal stability and was successfully anchored to the surface of the TiO₂ pigment. When used to disperse a TiO₂ slurry, it effectively made the TiO₂ slurry more fluid, indicating its strong viscosity-reducing properties. The viscosity, particle sizes and dispersion capabilities of the TiO₂ slurry were found to vary depending on the contents and monomer ratios of the dispersant.

P(MAA-BA-DM) dispersant increases the wettability of TiO₂ only in oily solvents but not in aqueous solvents.

P(MAA-BA-DM) dispersant makes it easier to disperse TiO₂ pigments in oily solvents, increasing the amount of pigment in the solvent and making the preparation of highly pigmented pastes easier.

A dispersant containing suitable carboxyl and tertiary amine groups was initially synthesized to disperse TiO₂ in an oily system. The findings are anticipated to be used in the formulation of pigment concentrates, industrial coatings and other solvent-based coatings.

Intumescent coatings are nowadays a dominant passive system used to protect structural materials in case of fire. Due to their reactive swelling behaviour, intumescent coatings are particularly complex materials to be modelled and predicted, which can be extremely useful especially for performance-based fire safety designs. In addition, many parameters influence their performance, and this challenges the definition and quantification of their material properties. Several approaches and models of various complexities are proposed in the literature, and they are reviewed and analysed in a critical literature review.

Analytical, finite-difference and finite-element methods for modelling intumescent coatings are compared, followed by the definition and quantification of the main physical, thermal, and optical properties of intumescent coatings: swelled thickness, thermal conductivity and resistance, density, specific heat capacity, and emissivity/absorptivity.

The study highlights the scarce consideration of key influencing factors on the material properties, and the tendency to simplify the problem into effective thermo-physical properties, such as effective thermal conductivity. As a conclusion, the literature review underlines the lack of homogenisation of modelling approaches and material properties, as well as the need for a universal modelling method that can generally simulate the performance of intumescent coatings, combine the large amount of published experimental data, and reliably produce fire-safe performance-based designs.

Due to their limited applicability, high complexity and little comparability, the presented literature review does not focus on analysing and comparing different multi-component models, constituted of many model-specific input parameters. On the contrary, the presented literature review compares various approaches, models and thermo-physical properties which primarily focusses on solving the heat transfer problem through swelling intumescent systems.

The presented literature review analyses and discusses the various modelling approaches to describe and predict the behaviour of swelling intumescent coatings as fire protection for structural materials. Due to the vast variety of available commercial products and potential testing conditions, these data are rarely compared and combined to achieve an overall understanding on the response of intumescent coatings as fire protection measure. The study highlights the lack of information and homogenisation of various modelling approaches, and it underlines the research needs about several aspects related to the intumescent coating behaviour modelling, also providing some useful suggestions for future studies.

The purpose of this study is to prepare thermal transfer ribbons with good alcohol resistance.

A variety of alcohol-resistant thermal transfer inks were prepared using different polyester resins. The printing temperature, printing effect, adhesion and alcohol resistance of the inks on the label were studied to determine the feasibility of using the ink for manufacturing thermal transfer ribbons. The ink formulations were prepared by a simple and stable grinding technology, and then use mature coating technology to make the ink into a thermal transfer ribbon.

The results show that the thermal transfer ink has good scratch resistance, good alcohol resistance and low printing temperature when the three resins coexist. Notably, the performance of the ribbon produced by 500 mesh anilox roller was better than that of other meshes. Specifically, the ink on the matte silver polyethylene terephthalate (PET) label surface was wiped with a cotton cloth soaked in isopropyl alcohol under 500 g of pressure. After 50 wiping cycles, the ink remained intact.

The proposed method not only ensures good alcohol resistance but also has lower printing temperature and wider label applicability. Therefore, it can effectively reduce the loss of printhead and reduce production costs, because of the low printing temperature.

This paper aims to study the physical and chemical characteristics of inkjet titanium dioxide inks for cotton fabric digital printing.

Different dispersing agents through the reaction of glycerol monooleate and toluene diisocyanate were prepared and then performed by using three different polyols (succinic anhydride-modified polyethylene glycol PEG 600, EO/PO Polyether Monoamine and p-chloro aniline Polyether Monoamine), to obtain three different dispersing agents for water-based titanium dioxide inkjet inks. The prepared dispersants were characterized using FTIR to monitor the reaction progress. Then the prepared dispersants were formulated in titanium dioxide inkjet inks formulation and characterized by particle size, dynamic surface tension, transmission electron microscopy, viscosity and zeta potential against commercial dispersants. Also, the study was extended to evaluate the printed polyester by using the prepared inks according to washing and crock fastness.

The obtained results showed that p-chloro aniline Polyether Monoamine (J) and succinic anhydride modified polyethylene glycol PEG 600 (H) dispersants provided optimum performance as compared to commercial standards especially, particle size distribution data while EO/PO Polyether Monoamine based on dispersant was against and then failed with the wettability and dispersion stability tests.

These ink formulations could be used for printing on cotton fabric by DTG technique of printing and can be used for other types of fabrics.

The newly prepared ink formulation for digital textile printing based on synthesized polyurethane prepolymers has the potential to be promising in this type of printing inks, to prevent clogging of nozzles on the printhead and to improve the print quality on the textile fiber.

The paper aims to design the optimum formulation of the nano-titanium dioxide (TiO2) hydrophilic coating system using the synthetic polypropylene glycol (PPG), which can create the reflection and absorption property.

TiO2 nanoparticles are used as fillers, and PPG has been blended at the proper ratio of 1PPG: 0.2TiO2. The prepared resin has been applied onto the glass substrate at different numbers of glass immersions during the dip-coating fabrication process. One-time glass immersion is labeled as T1 coating, two-time glass immersion is labeled as T2 coating and three-time glass immersion is labeled as T3 coating. All the prepared coating systems were left dry at ambient temperature.

T3 coating showed the lowest reading of WCA value at 40.50°, due to higher surface energy at 61.73 mN/m. The T3 coating also shows the greatest absorbance property among the prepared coating systems among the prepared coating. In terms of reflectance property, the T2 coating system has great reflectance in UV region and near-infrared region, which is 16.47% and 2.77 and 2.73%, respectively. The T2 coating also has great optical transmission about 75.00% at the visible region.

The development of thermal insulation coating by studying the relationship between convection heat and reflectance at different wavelengths of incident light.

The developed coating shows high potential for glass window application.

The application of the hydrophilic coating on light absorption, reflectance and transmission at different wavelengths.

The surface characteristics of thermally and chemically modified wood, such as surface roughness, surface free energy (SFE) and wettability, are important properties that influence further manufacturing processes such as gluing and coating. The aim of this paper was to determine the influence of the surface roughness of thermally and chemically modified teak wood on their SFE, wettability and bonding quality for water-based acrylic and solvent-based alkyd varnishes. In addition, durability against subterranean termites in the field of these modified teak woods was also investigated to give a valuable information for their further application.

The woods tested in this study were fast-growing teak woods that were prepared in untreated and treated with furfuryl alcohol (FA), glycerol maleic anhydride (GMA) and thermal. SFE values were calculated using the Rabel method. The wettability values were measured based on the contact angle between varnish liquids and wood surfaces using the sessile drop method, and the Shi and Gardner model model was used to evaluate the wettability of the varnishes on the wood surface. The bonding quality of the varnishes was measured using a cross-cut test based on ASTM 3359-17 standard. In addition, durability against subterranean termites in the field of these modified teak woods was also investigated according to ASTM D 1758-06.

The results showed that furfurylated and GMA-thermal 220°C improved the durability of teak wood against termites. The furfurylated teak wood had the roughest surface with an arithmetic average roughness (Ra) value of 15.65 µm before aging and 27.11 µm after aging. The GMA-thermal 220°C treated teak wood was the smoothest surface with Ra value of 6.44 µm before aging and 13.75 µm after aging. Untreated teak wood had the highest SFE value of 46.90 and 57.37 mJ/m² before and after aging, respectively. The K values of untreated and treated teak wood increased owing to the aging treatment. The K values for the water-based acrylic varnish were lower than that of the solvent-based alkyd varnish. The untreated teak wood with the highest SFE produced the highest bonding quality (grades 4–5) for both acrylic and alkyd varnishes. The solvent-based alkyd varnish was more wettable and generated better bonding quality than the water-based acrylic varnish.

The originality of this research work is that it provides evaluation values of the durability and SFE. The SFE value can be used to quantitatively determine the wettability of paint liquids on the surface of wood and its varnish bonding quality.

The purpose of this study is to investigate the effects of a pigment coating on the mechanical properties of fluting paper.

Two different calcium carbonate pigments were used in the preparation of the coated color, precipitated calcium carbonate (PCC) and ground calcium carbonate (GCC). Fluting paper produced by recycling waste paper was used as base paper. The effects of PCC and GCC pigments on mechanical properties were compared. Ring crush test (RCT), corrugating medium test (CMT), corrugating crush test (CCT), tensile and burst strength tests were applied to the coated papers, and the results were compared to the mechanical properties of base paper.

The tensile and burst indices of the coated papers were found to be higher than base papers about 13.9% and 6.05%, respectively. While the coating process positively affected the RCT and CCT values, it did not show a significant impact on the CMT values. GCC, one of the pigments used in coating colors, had a more effective effect on the mechanical properties of fluting papers compared to PCC.

These results suggest that coating of fluting papers has a positive effect on mechanical properties and the use of GCC as a pigment is more effective than PCC.

This study aims to assess the efficacy of nano-alumina (nano-Al₂O₃) in improving the performance of epoxy adhesives used to assemble archaeological glass. The conservators face a significant problem in assembling this type of artifact. Therefore, the assembling process is considered one of the important stages that must be taken care of to preserve these artifacts from damage and loss.

To evaluate the stability of adhesives, the samples were subjected to artificial aging under varying environmental conditions. Some investigative techniques and mechanical testing were used in this study to evaluate the selected materials. It includes a transmission electron microscope, X-ray diffraction, visual assessment, digital microscope, scanning electron microscopy (SEM), color change and tensile strength test.

The visual evaluation and the digital microscope results showed that the epoxy/nano-Al₂O₃ greatly resisted artificial aging. Although slight yellowing was present, it did not significantly affect the general appearance of the samples. On the other hand, the pure epoxy sample showed cracks of different sizes on its surface due to aging, as evidenced by SEM examination. Furthermore, epoxy/nano-Al₂O₃ has a better tensile strength (11.27 MPa) and slight color change (ΔE = 2.06).

The main objective of the experimental study was to identify appropriate adhesive materials that possess key properties such as non-yellowing and improved tensile strength by conducting various tests and evaluations. Ultimately, the goal was to identify materials that could serve as effective adhesives for assembling the archaeological glass.