This study aims to embed anatase, rutile and brookite TiO₂ nanoparticles (NPs) with different crystal phases into cotton fabrics by epoxy silane and to examine the effect of these applications on the photocatalytic and mechanical properties of the fabric.

Different aqueous dispersions which contain anatase, rutile and brookite were prepared at three different concentrations (5%, 10% and 15%). These NPs were embedded in cotton fabrics by using GPTS [(3-glycidyloxypropyl) trimethoxysilane]. Characterization tests were performed by scanning electron microscopy (SEM), Raman and Fourier-transform infrared spectroscopy (FT/IR). Samples were stained with methylene blue (MB) and then exposed to solar light for different periods. Color changes of the samples were examined with a spectrophotometer. Air permeability, abrasion and tear strength tests were applied to all samples.

According to SEM images, the NPs were successfully attached to the cotton fabrics, and epoxy silane coating surrounded the fiber surfaces. The presence of the coating was also confirmed by Raman spectroscopy and FT/IR. The treatments reduced the stainability of the samples. The most effective applications for ensuring photocatalytic activity in cotton fabrics were suspensions as 10% brookite, 10% anatase and 5% anatase, in descending order. The applied coating slightly reduced the samples’ air permeability, and wear and tear strength.

The importance of this study is to determine the optimal crystal phase and its concentration by using epoxy silane to ensure self-cleaning properties on cotton fabrics. The sample treated with 10% brookite is the most approached its original white color by 99.65% as a result of degradation of MB (after 120 min). On the other hand, using the pure rutile with epoxy silane was not suitable for removing MB from the fabric.

Titanium(IV) oxide nanoparticles (TiO₂ NP) were deposited to cotton denim fabrics using a self-crosslinking acrylate – a polymer dispersion to extend the lifetime of the products. This study aims to determine the optimum conditions to increase abrasion resistance, to provide self-cleaning properties of denim fabrics and to examine the effects of these applications on other physical properties.

The denim samples were first treated with nonionic surfactant to increase their wettability. Three different amounts of the polymer dispersion and two different pH levels were selected for the experimental design. The finishing process was applied to the fabrics with pad-dry-cure method.

The presence of the coatings and the adhesion of TiO₂ NPs to the surfaces were confirmed by scanning electron microscope and Fourier transform infrared spectroscopy analysis. It was ascertained that the most appropriate self-crosslinking acrylate amount and ambient pH level is 10 mL and “2”, respectively, for providing increased abrasion resistance (2,78%) and enhanced self-cleaning properties (363,4%) in the denim samples. The coating reduced the air permeability and softness of the denim samples. Differential scanning calorimetry and thermogravimetry analysis results showed that the treatments increased the crystallization temperatures and melting enthalpy values of the denim samples. Based on the thermal test results, it is clear that mass loss of the denim samples at 370°C decreased as the amount of self-crosslinking acrylate increased (at pH 3).

This study helped us to find out optimum amount of self-crosslinking acrylate and proper pH level for enhanced self-cleaning and abrasion strength on denim fabrics. With this finishing process, an environmentally friendly and long-life denim fabric was designed.

Titanium dioxide (TiO₂) has high opacity, high brightness and whiteness, owing to its high refractive index value. It is mainly used in the coating industry and continuous efforts have been made to replace some of the TiO₂ in paint with new pigments. This study aims to replace part of TiO₂ pigment with various percentages of BaSO₄, CaCO₃ and kaolin in styrene butyl acrylate-based paint formulations, without changing the properties of paints using only titanium dioxide.

To determine the optimum use rate of new pigment mixing, opacity, gloss, scrub resistance and weather resistance properties have been investigated in the water-based paint formulation. The morphological properties of these samples were examined by scanning electron microscopy analysis.

In the total color change (ΔE) measurements, it was observed that the sample coded 85Ti/15Ba produced extremely similar results to the situation when TiO₂ was used alone. It was seen that the best results were obtained when 85Ti/15Ba was used instead of TiO₂.

Comparison research on the impact of replacing TiO₂ with BaSO₄, CaCO₃ and kaolin on the performance characteristics of water-based styrene butyl acrylate-based paint formulations has not been done in the literature, according to the literature search.

This paper introduced the simple synthesis process of self-cleaning coating with fog-resistance property using hydrophobic polydimethylsiloxane (PDMS) polymer and nano-calcium carbonate (nano-CaCO₃) and titanium dioxide (TiO₂).

The synthesis method of PDMS/nano-CaCO₃-TiO₂ is based on sol-gel process. The crosslinking between PDMS and nanoparticles is driven by the covalent bond at temperature of 50°C. The 3-Aminopropyltriethoxysilane is used as binder for nanoparticles attachment in polymer matrix. Two fabrication methods are used, which are dip- and spray-coating methods.

The prepared coated glass fulfilled the requirement of standard self-cleaning and fog-resistance performance. For the self-cleaning test BS EN 1096-5:2016, the coated glasses exhibited the dust haze value around 20%–25% at tilt angle of 10°. For the antifog test, the coated glasses showed the fog haze value were below 2% and the gloss value were above 85%. The obtained results completely achieved the standard antifog value ASTM F659-06 protocol.

Findings will provide an infrastructure support for the building glass to enhance building’s energy efficiency, cleaning performance and friendly environment.

This study proposed the simple synthesis method using hydrophobic polymer and nano-CaCO₃ and nano-TiO₂, which can achieve optimum self-cleaning property at low tilt angle and fog-resistance performance for building glass.

The research findings have high potential for building company, cleaning building company and government sector. The proposed project capable to reduces the energy consumption about 20% per annum due to labor cost, time-consuming and safety during manual cleaning.

The novel method to develop self-cleaning coating with fog-resistance using simple synthesis process and fabrication method for building glass application.

This paper aims to design the nano-titanium dioxide (TiO₂) coating system which has superhydrophilic property, self-cleaning mechanism and antifog property as well as strong adhesion on glass substrate.

Two hydrophilic materials have been used such as TiO₂ nanoparticles as fillers and hydrophilic copolymer, Pluronic F-127 by using simple sol–gel approach. The prepared solution was applied onto glass through dip- and spray-coating techniques and then left for drying at ambient temperature.

The nano-TiO₂ superhydrophilic coating has achieved the water contact angle of 4.9° ± 0.5°. The superhydrophilic coating showed great self-cleaning effect against concentrated syrup and methylene blue where thin layer of water washes the dirt contaminants away. The nano-TiO₂ coating exhibits great antifog performance that maintains high transparency of around 89% when the coated glass is placed above hot-fog vapor for 10 min. The fog droplets were condensed into water film which allowed the transmission of light through the glass. The strong adhesion of coated glass shows no total failure at scratch profile when impacted with scratch load of 500, 800 and 1,200 mN.

Findings will be useful in the development of self-cleaning superhydrophilic coating that is applicable on building glass and photovoltaic panel.

The developed nano-TiO₂ coating is developed by the combination of hydrophilic organic copolymer–inorganic TiO₂ network to achieve great superhydrophilic property, optimum self-cleaning ability and supreme antifog performance.

The findings will be useful for residents in building glass window where the application will reduce dust accumulation and keep the glass clean for longer period.

The synthesis of nano-TiO₂ superhydrophilic coating which can be sprayed on large glass panel and cured at ambient temperature.

The purpose of this paper is to enhance the compatibility of titanium dioxide in epoxy resins and thus the corrosion resistance of the coatings.

In this work, TiO₂ was modified by the mechanochemistry method where mechanical energy was combined with thermal energy to complete the modification. The stability of modified TiO₂ in epoxy was analyzed by sedimentation experiment. The modified TiO₂-epoxy coating was prepared, and the corrosion resistance of the coating was analyzed by open circuit potential, electrochemical impedance spectroscopy and neutral salt spray test.

High-temperature mechanical modification can improve the compatibility of TiO₂ in epoxy resin. At the same time, the modified TiO₂-epoxy coating showed better corrosion resistance. Compared to the unmodified TiO₂-epoxy coating, the coating improved the dry adhesion force by 61.7% and the adhesion drop by 33.3%. After 2,300 h of immersion in 3.5 Wt.% NaCl solution, the coating resistance of the modified TiO₂ coating was enhanced by nearly two orders of magnitude compared to the unmodified coating.

The authors have grafted epoxy molecules onto TiO₂ surfaces using a high-temperature mechanical force modification method. The compatibility of TiO₂ with epoxy resin is enhanced, resulting in improved adhesion of the coating to the substrate and corrosion resistance of the coating.

This paper aims to determine the optimum parametric settings for yielding superior mechanical properties, namely, ultimate tensile strength (UTS), yield strength (YS) and percentage elongation (EL) of AZ91D/AgNPs/TiO₂ hybrid composite fabricated by friction stir processing.

An empirical model has been developed to govern crucial influencing parameters, namely, rotation speed (RS), tool transverse speed (TS), number of passes (NPS) and reinforcement fraction (RF) or weight percentage. Box Behnken design (BBD) with four input parameters and three levels of each parameter was used to design the experimental work, and analysis of variance (ANOVA) was used to check the acceptability of the developed model. Desirability function analysis (DFA) for a multiresponse optimization approach is integrated with response surface methodology (RSM). The individual desirability index (IDI) was calculated for each response, and a composite desirability index (CDI) was obtained. The optimal parametric settings were determined based on maximum CDI values. A confirmation test is also performed to compare the actual and predicted values of responses.

The relationship between input parameters and output responses (UTS, YS, and EL) was investigated using the Box-Behnken design (BBD). Silver nanoparticles (AgNPs) and nano-sized titanium dioxide (TiO₂) enhanced the ultimate tensile strength and yield strength. It was observed that the inclusion of AgNPs led to an increase in ductility, while the increase in the weight fraction of TiO₂ resulted in a decrease in ductility.

AZ91D/AgNPs/TiO₂ hybrid composite finds enormous applications in biomedical implants, aerospace, sports and aerospace industries, especially where lightweight materials with high strength are critical.

In terms of optimum value through desirability, the experimental trials yield the following results: maximum value of UTS (318.369 MPa), maximum value of YS (200.120 MPa) and EL (7.610) at 1,021 rpm of RS, 70 mm/min of TS, 4 NPS and level 3 of RF.

This work aims to concentrate on the mixed convection of the stagnation point flow of ternary hybrid nanofluids towards vertical Riga plate. Aluminum trioxide (Al₂O₃), silicon dioxide (SiO₂) and titanium dioxide (TiO₂) are regarded as nanoparticles, with water serving as the base fluid. The mathematical model incorporates momentum boundary layer and energy equations. The Grinberg term for the viscous dissipation and the wall parallel Lorentz force coming from the Riga plate are taken into consideration in the context of the energy equation.

Through the use of appropriate nonsimilar transformations, the governing system is transformed into nonlinear nondimensional partial differential equations (PDEs). The numerical method bvp4c (built-in package for MATLAB) is used in this study to simulate governing equations using the local non-similarity (LNS) approach up to the second truncation level.

Numerous graphs and numerical tables expound on the physical properties of the nanofluid temperature and velocity profiles. The local Nusselt correlations and the drag coefficient for pertinent parameters have been computed in tabular form. Additionally, the temperature profile drops while the velocity profile increases when the mixed convection parameter is included to oppose the flow.

The fundamental goal of this work is to comprehend how ternary nanofluids move towards a vertical Riga plate in a mixed convective domain with stagnation point flow.

The main purpose of this study was to prepare the cotton fibers and cellulose powder by a layer of nano-crystalline-titanium dioxide (TiO₂) using the sol-gel sono-synthesis method to clean the wastewater containing reactive dye. Moreover, TiO₂ nano-materials are remarkable due to their photoactive properties and valuable applications in wastewater treatment.

In this research, TiO₂ was synthesized and deposited effectively on cotton fibers and cellulose powder using ultrasound-assisted coating. Further, tetra butyl titanate was used as a precursor to the synthesis of TiO₂ nanoparticles. Reactive dye (red 195) was used in this study. X-ray Diffraction, scanning electron microscopy and Fourier transform infrared spectroscopy were performed to prove the aptitude for the formation of crystal TiO2 on the cotton fibers and cellulose powder along with TiO₂ nanoparticles as well as to analyze the chemical structure. Decoloration of the wastewater was investigated through ultraviolet (UV-Visible) light at 30 min.

The experimental results revealed that the decolorization was completed at 2.0 min with the cellulose nano TiO₂ treatment whereas cotton nano TiO₂ treated solution contained reactive dyestuffs even after the treatment of 2 min. This was the fastest method up to now than all reported methods for sustainable decolorization of wastewater by absorption. Furthermore, this study explored that the cellulose TiO₂ nano-composite was more effective than the cotton TiO₂ nano-composite of decoloration wastewater for the eco-friendly remedy.

Cotton fibers and cellulose powder with nano-TiO₂, and only reactive dye (red 195) were tested.

With reactive dye-containing wastewater, it seems to be easier to get rid of the dye than to retain it, especially from dyeing of yarn, fabric, apparel, and as well as other sectors where dyestuffs are used.

This research would help to reduce pollution in the environment as well as save energy and cost.

Decoloration of wastewater treatment is an essential new track with nano-crystalline TiO2 to fast and efficient cleaning of reactive dyes containing wastewater used as a raw material.

The paper aims to investigate the effect of Degussa P-25 Titanium Dioxide (TiO₂) nanoparticles on hydrophobicity and self-cleaning ability as a single organic coating on glass substrate.

Two methods have been used to enhance the hydrophobicity on glass substrates, namely, surface modification by using low surface energy isooctyltrimethoxysilane (ITMS) solution and construction of rough surface morphology using Degussa P-25 TiO₂ nanoparticles with simple bottom-up approach. The prepared sol was applied onto glass substrate using dip-coating technique and stoved in the vacuum furnace 350°C.

The ITMS coating with nano TiO₂ pigment has modified the glass substrate surface by achieving the water contact angle as high as 169° ± 2° and low sliding angle of 0° with simple and low-cost operation. The solid and air phase interface has created excellent anti-dirt and self-cleaning properties against dilute ketchup solution, mud and silicon powder.

Findings will be useful in the development of self-cleaning and anti-dirt coating for photovoltaic panels.

Sol method provides the suitable medium for the combination of organic–inorganic network to achieve high superhydrophobicity and optimum self-cleaning ability.

Application of blended organic–inorganic sol as self-cleaning and anti-dirt coating film.