In order to complement a large-scale long-term investigation of prestressing strand types for post-tensionsing of bridges, passive and active electrochemical tests were carried out on bare and grouted specimens exposed to salt water conditions as a function of time. The materials tested included seven-wire strands made of hot dip galvanized or zinc coated steel, stainless steel, stainless clad steel, copper clad steel, flow-filled epoxy coated steel and conventional steel as control. Based on corrosion potentials, polarization resistance tests, potentiodynamic tests, weight loss, and visual observations, epoxy coated strands, stainless and stainless clad strands were identified as possible alternatives to conventional steel that might help to minimize corrosion.

The main purpose of this study was to evaluate the tensile strengths of JIS G3549 super high-strength steel strand wire ropes (1,570 MPa-class high-carbon steels) and wire rope open swaged socket connections at fire and post fire.

Steady-state tests from ambient temperature (20 °C) to 800 °C, transient-state tests under the allowable design tensile force and tensile tests in an ambient temperature environment after heating (heating temperatures of 200–800 °C) were conducted.

The tensile strengths of the wire rope and end-connection specimens at both fire and post fire were obtained. The steel wire rope specimens possessed larger reduction factors than general hot-rolled mild steels (JIS SS400) and high-strength steel bolts (JIS F10T). The end-connection specimens with sufficient socket lengths exhibited ductile fracture of the wire rope part at both fire and post fire; however, those with short socket lengths experienced a pull-out fracture at the socket.

The fundamental and important tensile test results of the super high-strength steel strand wire ropes (1,570 MPa-class high-carbon steels) and wire rope open swaged socket connections were accumulated at fire and post fire, and the fracture modes were clarified. The obtained test results contribute to fire resistance performance-based design of cable steel structures at fire and fire-damage investigations to consider their reusability post fire.

The atmosphere of a tannery is one of the most highly corrosive of industrial atmospheres. Humidity is high, often containing corrosive vapours from the various liquors used in tanning processes, and the tanner has to choose his metal materials carefully. An additional hazard is the danger of harmful corrosion products dropping on to the skins and hides. This article describes the metals used for different tanning processes and also methods of protecting structural steelwork of the tannery.

Details of Electrical and Electronic Apparatus and Applications in the Maintenance and Operation of Aircraft, Missiles and Space Vehicles. The Bristol works of British Aircraft Corporation's Guided Weapons Division has provided some of the equipment for U.K.2, the second Anglo‐American scientific satellite which was put into orbit on March 27.

The times have come down to us as the “Good Old Days”, of Edwardian elegance and grace, peace and plenty, which conceal the poverty, squalor and disease. There seemed less resentment from those who suffered the rigours of the times than from those of today who only know of them by repute. Life was indeed cruel to the submerged tenth of society and the homeless waifs and strays were all too real and true.

With the popularization of electronic products, the electromagnetic radiation pollution has been the fourth largest pollution after water, air and noise pollution. Therefore, electromagnetic shielding property of textiles is attracting more attention. In this paper, the properties of electromagnetic shielding yarns and fabrics were studied.

Ten kinds of yarn, stainless steel short fiber and polyester blend yarn with three different blending ratios T/S 90/10, T/S 80/20 and T/S 70/30, stainless steel short fiber, polyester and cotton blend yarn with blending ratio C/T/S 35/35/30, core-spun yarn with one 30 um stainless steel filament C/T28tex/S(30 um), core-spun yarn with two 15 um stainless steel filaments (C/T28tex/S(15 um)/S(15 um)), twin-core-spun yarn with one 30 um stainless steel filament and one 50D spandex filament C/T28tex/S(30 um)/SP(50D), sirofil wrapped yarn with one 30 um stainless steel filament feeding from left S(30 um)+C/T28tex, sirofil wrapped yarn with one 30 um stainless steel filament feeding from right C/T28tex+S(30 um), sirofil wrapped yarn with two 15 um stainless steel filaments feeding from two sides S(15 um)+C/T28tex+ S(15 um), were spun. The qualities of spun yarns were measured. Then, for analyzing the electromagnetic shielding properties of fabrics made of different spun yarns, 20 kinds of fabrics were woven.

The tested results show that comparing to the T/S 80/20 blend yarn, the resistivity of composite yarns with the same ratio of the stainless steel filament is smaller. The possible reason is that comparing to the stainless steel short fiber, the conductivity of stainless steel filament is better because of the continuous distribution of stainless steel in the filament. Comparing with the core-spun yarn, the conductivity of the sirofil wrapped yarn is a little better. Comparing to the fabric woven by the blend yarn, the electromagnetic shielding of the fabric woven by the composite yarn is better, and comparing to the fabric woven by the core-spun yarn, the electromagnetic shielding of the fabric woven by the sirofil yarn is a little better. The possible reason is that the conduction network can be produced by the stainless steel filament wrapped on the staple fiber yarn surface in the fabric, and the electromagnetic wave can be transmitted in the network.

In this paper, the properties of electromagnetic shielding yarns and fabrics were studied. Ten kinds of yarn, including three stainless steel short fiber and polyester blend yarns, one stainless steel short fiber, polyester and cotton blend yarn, two core-spun yarns, one twin-core-spun yarn, three sirofil wrapped yarn, were spun. Then, for analyzing the electromagnetic shielding properties of fabrics made of different spun yarns, 20 kinds of fabrics were woven. The effects of fabric warp and weft densities, fabric structures, yarn kinds, yarn distributions in the fabric on electromagnetic shielding were analyzed.

The extrusion-based additive manufacturing method followed by debinding and sintering steps can produce metal parts efficiently at a relatively low cost and material wastage. In this study, 316L stainless-steel metal filled filaments were used to print metal parts using the extrusion-based fused filament fabrication (FFF) approach. The purpose of this study is to assess the effects of common FFF printing parameters on the geometric and mechanical performance of FFF manufactured 316L stainless-steel components.

The microstructural characteristics of the metal filled filament, three-dimensional (3D) printed green parts and final sintered parts were analysed. In addition, the dimensional accuracy of the green parts was evaluated, as well as the hardness, tensile properties, relative density, part shrinkage and the porosity of the sintered samples. Moreover, surface quality in terms of surface roughness after sintering was assessed. Predictive models based on artificial neural networks (ANNs) were used for characterizing dimensional accuracy, shrinkage, surface roughness and density. Additionally, the response surface method based on ANNs was applied to represent the behaviour of these parameters and to identify the optimum 3D printing conditions.

The effects of the FFF process parameters such as build orientation and nozzle diameter were significant. The pore distribution was strongly linked to the build orientation and printing strategy. Furthermore, porosity decreased with increased nozzle diameter, which increased mechanical performance. In contrast, lower nozzle diameters achieved lower roughness values and average deviations. Thus, it should be noted that the modification of process parameters to achieve greater geometrical accuracy weakened mechanical performance.

Near-dense 316L austenitic stainless-steel components using FFF technology were successfully manufactured. This study provides print guidelines and further information regarding the impact of FFF process parameters on the mechanical, microstructural and geometric performance of 3D printed 316L components.

Fused filament fabrication (FFF) technique using metal filled filaments in combination with debinding and sintering steps can be a cost-effective alternative for laser-based powder bed fusion processes. The mechanical behaviour of FFF-metal materials is highly dependent on the processing parameters, filament quality and adjusted post-processing steps. In addition, the microstructural material properties and geometric characteristics are inherent to the manufacturing process. The purpose of this study is to characterize the mechanical and geometric performance of three-dimensional (3-D) printed FFF 316 L metal components manufactured by a low-cost desktop 3-D printer. The debinding and sintering processes are carried out using the BASF catalytic debinding process in combination with the BASF 316LX Ultrafuse filament. Special attention is paid on the effects of build orientation and printing strategy of the FFF-based technology on the tensile and geometric performance of the 3-D printed 316 L metal specimens.

This study uses a toolset of experimental analysis techniques [metallography and scanning electron microcope (SEM)] to characterize the effect of microstructure and defects on the material properties under tensile testing. Shrinkage and the resulting porosity of the 3-D printed 316 L stainless steel sintered samples are also analysed. The deformation behaviour is investigated for three different build orientations. The tensile test curves are further correlated with the damage surface using SEM images and metallographic sections to present grain deformation during the loading progress. Mechanical properties are directly compared to other works in the field and similar additive manufacturing (AM) and Metal Injection Moulding (MIM) manufacturing alternatives from the literature.

It has been shown that the effect of build orientation was of particular significance on the mechanical and geometric performance of FFF-metal 3-D printed samples. In particular, Flat and On-edge samples showed an average increase in tensile performance of 21.7% for the tensile strength, 65.1% for the tensile stiffness and 118.3% for maximum elongation at fracture compared to the Upright samples. Furthermore, it has been able to manufacture near-dense 316 L austenitic stainless steel components using FFF. These properties are comparable to those obtained by other metal conventional processes such as MIM process.

316L austenitic stainless steel components using FFF technology with a porosity lower than 2% were successfully manufactured. The presented study provides more information regarding the dependence of the mechanical, microstructural and geometric properties of FFF 316 L components on the build orientation and printing strategy.

IN ANY survey of stainless steel applications it is soon apparent that in the vast majority of cases it is the corrosion resistance of the material which is the deciding factor in its selection. Appearance, non‐toxicity, retention of strength at high and low temperatures, and ease of fabrication are all important in varying degrees, but the widespread applications of stainless steel— a material which celebrated its first half‐century only a few years ago—follow principally from its inherent ‘stainless’ properties which confer a remarkable degree of resistance to attack in a wide variety of environments.

THE Spacelab Scientific (CPSE) Airlock is equipped with an experiment table to transfer experiments from the Module into space environment. In the table drive system multi‐stranded steel cable is used, running over small‐diameter pulleys. For cleanliness requirements the original cable lubricant was replaced by a fluorinated fluid. Cable cleaning and relubrication methods have been established. The coating thickness can be chosen. Tests were run with and without lubrication. The cables were tested at ESTL on a test rig, based upon the experiment table design, in a thermal vacuum test. The performance has been improved by: • a more flexible cable • increase of lubricant thickness • decrease of contact stresses Testing in air has been included as it appeared to be an aggressive environment, where a failure occurred.