The durability of concrete containing recycled aggregates, sourced from concrete specimens that have been tested in laboratory testing facilities, remains understudied. This paper aims to present the results of experiments investigating the effect of incorporating such type of concrete waste on the strength and durability-related properties of concrete.

A total of 77 concrete cylinders sized Ø100 × 200 mm with varying amount of recycled concrete aggregate (RCA) (0%–100% by volume, at 25% increments) and maximum aggregate size (12.5, 19.0 and 25.0 mm) were fabricated and tested for slump, compressive strength, sorptivity and electrical resistivity. Disk-shaped specimens, 50-mm thick, were cut from the original cylinders for sorptivity and resistivity tests. Analysis of variance and post hoc test were conducted to detect statistical variability among the data.

Compared to regular concrete, a reduction of slump (by 18.6%), strength (15.1%), secondary sorptivity (31.5%) and resistivity (17.0%) were observed from concrete containing 100% RCA. Statistical analyses indicate that these differences are significant. In general, an aggregate size of 19 mm was found to produce the optimum value of slump, compressive strength and sorptivity in regular and RCA-added concrete.

The results of this study suggest that comparable properties of normal concrete were still achieved by replacing 25% of coarse aggregate volume with 19-mm RCA, which was processed from laboratory-tested concrete samples. Therefore, such material can be considered as a potential and sustainable alternative to crushed gravel for use in light or nonstructural concrete construction.

This study aims on a broad review of Concrete's Rheological Properties. The Concrete is a commonly used engineering material because of its exquisite mechanical interpretation, but the addition of constituent amounts has significant effects on the concrete’s fresh properties. The workability of the concrete mixture is a short-term property, but it is anticipated to affect the concrete’s long-term property.

In this review, the concrete and workability definition; concrete’s rheology models like Bingham model, thixotropy model, H-B model and modified Bingham model; obtained rheological parameters of concrete; the effect of constituent’s rheological properties, which includes cement and aggregates; and the concrete’s rheological properties such as consistency, mobility, compatibility, workability and stability were studied in detail.

Also, this review study has detailed the constituents and concrete’s rheological properties effects. Moreover, it exhibits the relationship between yield stress and plastic viscosity in concrete’s rheological behavior. Hence, several methods have been reviewed, and performance has been noted. In that, the abrasion resistance concrete has attained the maximum compressive strength of 73.6 Mpa; the thixotropy approach has gained the lowest plastic viscosity at 22 Pa.s; and the model coaxial cylinder has recorded the lowest stress rate at 8 Pa.

This paper especially describes the possible strategies to constrain improper prediction of concrete’s rheological properties that make the workability and rheological behavior prediction simpler and more accurate. From this, future guidelines can afford for prediction of concrete rheological behavior by implementing novel enhancing numerical techniques and exploring the finest process to evaluate the workability.

Concrete, the second most used material in the world, surpassed only by water, relies on a vast amount of cement. The process of cement production emits substantial amounts of carbon dioxide (CO₂). Consequently, it is crucial to search for cement alternatives. Geopolymer concrete (GC) uses industrial by-product material instead of traditional cement, which not only reduces CO₂ emissions but also enhances concrete durability. On the other hand, the disposal of concrete waste in the landfills represents a significant environmental challenge, emphasising the urgent need for sustainable solutions. This study aimed to investigate waste concrete's best form and rate as the alternative aggregates in self-compacting and ambient-cured GC to preserve natural resources, reduce construction and demolition waste and decrease pertinent CO₂ emissions. The binding material employed in this research encompasses fly ash, slag, micro fly ash and anhydrous sodium metasilicate as an alkali activator. It also introduces the best treatment method to improve the recycled concrete aggregate (RCA) quality.

A total of25%, 50% and 100% of coarse aggregates are replaced with RCAs to cast self-compacting geopolymer concrete (SCGC) and assess the impact of RCA on the fresh, hardened and water absorption properties of the ambient-cured GC. Geopolymer slurry was used for coating RCAs and the authors examined the effect of one-day and seven-day cured coated RCA. The mechanical properties (compressive strength, splitting tensile strength and modulus of elasticity), rheological properties (slump flow, T500 and J-ring) and total water absorption of RCA-based SCGC were studied. The microstructural and chemical compositions of the concrete mixes were studied by the methods of energy dispersive X-Ray and scanning electron microscopy.

It is evident from the test observations that 100% replacement of natural aggregate with coated RCA using geopolymer slurry containing fly ash, slag, micro fly ash and anhydrous sodium metasilicate cured for one day before mixing enhances the concrete's quality and complies with the flowability requirements. Assessment is based on the fresh and hardened properties of the SCGC with various RCA contents and coating periods. The fresh properties of the mix with a seven-day curing time for coated RCA did not meet the requirements for self-compacting concrete, while this mix demonstrated better compressive strength (31.61 MPa) and modulus of elasticity (15.39 GPa) compared to 29.36 MPa and 9.8 GPa, respectively, for the mix with one-day cured coated RCA. However, incorporating one-day-cured coated RCA in SCGC demonstrated better splitting tensile strength (2.32 MPa) and water absorption (15.16%).

A potential limitation of this study on SCGC with coated RCAs is the focus on the short-term behaviour of this concrete. This limited time frame may not meet the long-term requirements for ensuring the sustained durability of the structures throughout their service life.

This paper highlights the treatment technique of coating RCA with geopolymer slurry for casting SCGC.

The purpose of this paper is to make a contribution to understanding the influence of factors such as the water/cement (W/C) ratio and the granular class on the mechanical and physical properties of high-strength concretes (HSCs). In the formulations of HSC, aggregates by their high mass and volume proportion play an important role. When selecting aggregates, it is necessary to know their intrinsic properties. These properties influence the performance of concrete, in particular the quality of the granulate cimentary adhesion.

This experimental study focused on the effect of W/C ratio (0.25, 0.30, 0.35), the effect of replacing a part of cement by silica fume (SF) (8%), the effect of fraction of aggregate on properties of fresh and hardened concrete, the effect of different environment conversation like drinking water and sea water on compressive strength and the study of absorption of water and softening using the mix design method of the University of Sherbrooke combined with the Dreux-Gorisse method which gives good results.

At the end of our work, the examination of the results obtained made it possible to establish the correlations between the formulations studied and the physicomechanical characteristics of the concrete compositions (HSC25, HSC16, HSC8). The results of this study show that the use of three granular classifications (DMAX8, DMAX16 and DMAX25) and three report W/C (0.25, 0.30 and 0.35) in two different conservation environment (drinking water and sea water) give HSCs, HSC25 with an W/C = 0.25 ratio has reached the largest mechanical strength of 90 MPa for different environments of conservation. For selecting aggregates, it is necessary to know their intrinsic properties, these properties influence the strength of concrete. In general, there is a slight decrease in the compressive resistance of the specimens stored in seawater, it can be said that the conservation life has not had effect on the resistance (28 days). The effect of aggressive environment can appear in the long term.

Mixed design and concrete fabrication with a 28-day compressive strength of up to 68 MPa or more of 90 MPa can now be possible used in Jiel (Algeria), and it should no longer be considered to be used only in an experimental domain. Addition of SF in concrete showed good development of strength between 7 and 28 days, depending on the design of the mix.

Concrete containing 8% SF with W/B of 0.25 has higher compressive strength than the other concretes, and concretes with SF are more resistant than concretes without SF, so it is possible to have concrete with a compressive strength of 82 MPa for W/C 0.25 without SF. Like as a result, we can avoid the use of SF to affect the strength of concrete at compressive strength of 68 MPa, and a slump of 21 cm, because the SF is the most expensive ingredient used in the composition of concrete and is therefore very important economically. One of the main factors of production of HSC above 90 MPa is use of aggregate DMAX25, which is stronger with W/B of 0.25 and 0.30.

This mixtures leads to a very dense microstructure and low porosity and produces increased permeability of HSC and is able to resist the penetration of aggressive agents. This combination has a positive effect on the economy of concrete.

The combination of the Dreux-Gorisse method with the Sherbrook method is very beneficial for determining the percentage of aggregates used, and the use of coarse aggregates of Jijel to obtain HSC with 90 MPa and 16 cm of workability.

The purpose of this paper is to investigate the effect of the replacement of natural coarse aggregate (NCA) with different percentages of recycled coarse aggregate (RCA) on properties of low calcium fly ash (FA)-based geopolymer concrete (GPC) cured at oven temperature. Further, this paper aims to study the effect of partial replacement of FA by ground granulated blast slag (GGBS) in GPC made with both NCA and RCA cured under ambient temperature curing.

M25 grade of ordinary Portland cement (OPC) concrete was designed according to IS: 10262-2019 with 100% NCA as control concrete. Since no standard guidelines are available in the literature for GPC, the same mix proportion was adopted for the GPC by replacing the OPC with 100% FA and W/C ratio by alkalinity/binder ratio. All FA-based GPC mixes were prepared with 12 M of sodium hydroxide (NaOH) and an alkalinity ratio, i.e. sodium hydroxide to sodium silicate (NaOH:Na₂SiO₃) of 1:1.5, subjected to 90^°C temperature for 48 h of curing. The NCA were replaced with 50% and 100% RCA in both OPC and GPC mixes. Further, FA was partially replaced with 15% GGBS in GPC made with the above percentages of NCA and RCA, and they were given ambient temperature curing with the same molarity of NaOH and alkalinity ratio.

The workability, compressive strength, split tensile strength, flexural strength, water absorption, density, volume of voids and rebound hammer value of all the mixes were studied. Further, the relationship between compressive strength and other mechanical properties of GPC mixes were established and compared with the well-established relationships available for conventional concrete. From the experimental results, it is found that the compressive strength of GPC under ambient curing condition at 28 days with 100% NCA, 50% RCA and 100% RCA were, respectively, 14.8%, 12.85% and 17.76% higher than those of OPC concrete. Further, it is found that 85% FA and 15% GGBS-based GPC with RCA under ambient curing shown superior performance than OPC concrete and FA-based GPC cured under oven curing.

The scope of the present paper is limited to replace the FA by 15% GGBS. Further, only 50% and 100% RCA are used in place of natural aggregate. However, in future study, the replacement of FA by different amounts of GGBS (20%, 25%, 30% and 35%) may be tried to decide the optimum utilisation of GGBS so that the applications of GPC can be widely used in cast in situ applications, i.e. under ambient curing condition. Further, in the present study, the natural aggregate is replaced with only 50% and 100% RCA in GPC. However, further investigations may be carried out by considering different percentages between 50 and 100 with the optimum compositions of FA and GGBS to enhance the use of RCA in GPC applications. The present study is further limited to only the mechanical properties and a few other properties of GPC. For wider use of GPC under ambient curing conditions, the structural performance of GPC needs to be understood. Therefore, the structural performance of GPC subjected to different loadings under ambient curing with RCA to be investigated in future study.

The replacement percentage of natural aggregate by RCA may be further enhanced to 50% in GPC under ambient curing condition without compromising on the mechanical properties of concrete. This may be a good alternative for OPC and natural aggregate to reduce pollution and leads sustainability in the construction.

This paper aims to characterize and develop a new ecological lightweight concrete reinforced by addition of palm plant fibers (from vegetal waste) to be used in the thermal and acoustical insulation of local constructions. The date palm plant fibers are characterized by their low sensitivity to chemical reactions, low cost and large availability in local regions. Therefore, the newly obtained lightweight concrete may suggest a great interest, as it seems to be able to achieve good solutions for local construction problems, technically, economically and ecologically.

The experimental program focused on developing the composition of palm-fiber-reinforced concrete, by studying the effect of the length of the fibers (10, 20, 30 and 40 mm) and their mass percentage (0.5%, 1%, 1.5% and 2%), on the mechanical and acoustical properties of the composite. The main measured parameters were the compressive strength and flexural strength, sound absorption coefficient, noise reduction coefficient (NRC), etc. These tests were also borne out by the measure of density and water absorption, as well as microstructure analyses. To fully appreciate the behavior of the material, visualizations under optical microscope and scanning electron microscope analyses were carried out.

The addition of plant fibers to concrete made it possible to formulate a new lightweight concrete having interesting properties. The addition of date palm fibers significantly decreased the density of the concrete and consequently reduced its mechanical strength, particularly in compression. Acceptable compressive strength values were possible, according to the fibers content, while better values have been obtained in flexion. On the other hand, good acoustical performances were obtained: a considerable increase in the sound absorption coefficient and the NRC was recorded, according to the content and length of fibers. Even the rheological behavior has been improved with the addition of fibers, but with short fibers only.

Over the recent decades, many studies have attempted to search for more sustainable and environmentally friendly building materials. Therefore, this work aims to study the possibility of using waste from date palm trees as fibers in concrete instead of the conventionally used fibers. Although many researches have already been conducted on the effect of palm plant fibers on the mechanical/physical properties of concrete, no information is available neither on the formulation of this type of concrete nor on its acoustical properties. Indeed, due to the scarcity of raw materials and the excessive consumption of energy, the trend of plant fibers as resources, which are natural and renewable, is very attractive. It is therefore a major recycling project of waste and recovery of local materials.