This study aims to enhance merging of additive manufacturing (AM) techniques with powder injection molding (PIM). In this way, the prototypes could be 3D-printed and mass production implemented using PIM. Thus, the surface properties and mechanical performance of parts produced using powder/polymer binder feedstocks [material extrusion (MEX) and PIM] were investigated and compared with powder manufacturing based on direct metal laser sintering (DMLS).

PIM parts were manufactured from 17-4PH stainless steel PIM-quality powder and powder intended for powder bed fusion compounded with a recently developed environmentally benign binder. Rheological data obtained at the relevant temperatures were used to set up the process parameters of injection molding. The tensile and yield strengths as well as the strain at break were determined for PIM sintered parts and compared to those produced using MEX and DMLS. Surface properties were evaluated through a 3D scanner and analyzed with advanced statistical tools.

Advanced statistical analyses of the surface properties showed the proximity between the surfaces created via PIM and MEX. The tensile and yield strengths, as well as the strain at break, suggested that DMLS provides sintered samples with the highest strength and ductility; however, PIM parts made from environmentally benign feedstock may successfully compete with this manufacturing route.

This study addresses the issues connected to the merging of two environmentally efficient processing routes. The literature survey included has shown that there is so far no study comparing AM and PIM techniques systematically on the fixed part shape and dimensions using advanced statistical tools to derive the proximity of the investigated processing routes.

This paper aims to explore the history of Anglican churches in Malaysia and discusses their typical features and their respective maintenance practices.

A narrative review of 84 literacy sources published between 1967 and 2020 on the development and features of Anglican churches in Malaysia, along with recommendations on maintenance practices from the asset and facilities management perspective. The exploration of churches’ features follows three main disciplines in building maintenance according to the Jabatan Kerja Raya Guideline for as-built buildings in Malaysia.

The findings of the study have then been tabulated to form a maintenance framework to recommend suitable maintenance practices on specific building components based on different materials. The paper argues that as places of worship, the assets of religious facilities are intangible compared to any other types of building that serve a tangible function (i.e. shelter, commercial or industrial operation). Throughout the exploration of their maintenance practices suggested by vast sources of literature, it is proven that the maintenance of churches is not as straightforward as merely remedying the defects, but it requires the maintenance to radically minimise any disturbance to their aesthetics, thus making maintenance a more challenging task at churches.

This paper proposes a maintenance framework for Anglican churches in Malaysia by categorising building disciplines and their corresponding building components, which supports future research to improve the maintenance practices of religious facilities.

In this study, AlCoCrFeNi–Cu (Cu-based) and AlCoCrFeNi–Ti (Ti-based) high entropy alloys (HEAs) were fabricated using a direct blown powder technique via laser additive manufacturing on an A301 steel baseplate for aerospace applications. The purpose of this research is to investigate the electrical resistivity and oxidation behavior of the as-built copper (Cu)- and titanium (Ti)-based alloys and to understand the alloying effect, the HEAs core effects and the influence of laser parameters on the physical properties of the alloys.

The as-received AlCoCrFeNiCu and AlCoCrFeNiTi powders were used to fabricate HEA clads on an A301 steel baseplate preheated at 400°C using a 3 kW Rofin Sinar dY044 continuous-wave laser-deposition system fitted with a KUKA robotic arm. The deposits were sectioned using an electric cutting machine and prepared by standard metallographic methods to investigate the electrical and oxidation properties of the alloys.

The results showed that the laser power had the most influence on the physical properties of the alloys. The Ti-based alloy had better resistivity than the Cu-based alloy, whereas the Cu-based alloy had better oxidation residence than the Ti-based alloy which attributed to the compositional alloying effect (Cu, aluminum and nickel) and the orderliness of the lattice, which is significantly associated with the electron transportation; consequently, the more distorted the lattice, the easier the transportation of electrons and the better the properties of the HEAs.

It is evident from the studies that the composition of HEAs and the laser processing parameters are two significant factors that influence the physical properties of laser deposited HEAs for aerospace applications.

This paper aims to examine how collaborative supplier development (SD) activities, supplier capabilities and buyer–supplier relationship interrelate in technology-based, luxury product business contexts characterized by small volumes, difficult targets and resource constraints relative to those targets.

Using inductive case research method, the authors investigate multiple embedded cases involving six dyadic buyer–supplier relationships of two luxury product manufacturers in the motorcycle and automotive industries. Each dyad represents an important sub-system for which the buying firm committed significant SD efforts to help the supplier successfully achieve difficult targets.

The analysis reveals how paradoxical tensions might emerge as the firms engage in successful SD activities, which could lead to decreasing relationship commitment ultimately resulting in the termination of the relationship. The authors utilize the “value co-creation and value capture” paradox framework to understand the SD and relationship dynamic and characterize it as developing-leveraging paradox to explain its dualities, i.e. commitment-based SD efforts (increasing value co-creation), and unilateral leveraging of the newly acquired capabilities (increasing value capture) by both the buyer and the supplier. Overemphasis on value capture by one of the exchange partners spurs a detrimental vicious cycle leading to the decline of the relationship.

The study explains the paradoxical dynamics that may emerge in SD activities of innovative, technologically complex, luxury product firms. The findings contribute to the SD literature by highlighting how learnings from SD activities could contribute to the dark sides of buyer–supplier relationship. The technologically complex, luxury product contextual characteristics of the study may limit the generalizability of the study findings.

The study provides novel insights into the emergence and management of paradoxes in buyer–supplier relationships, in terms of virtuous and vicious dynamics of developing-leveraging.

The purpose of this study is to investigate the effect of laser scanning speed (LSS) on the corrosive-tribological performance of Ni-60%WC coating in Wusu mine water, which was beneficial to improve the friction–wear performance of cylinder liner on water injection pump.

Ni-60%WC coatings were fabricated on 45 steel by laser cladding, and the microstructure and tribological performance was analyzed using a super depth of field microscope and ball-on-plate friction tester, and the wear mechanism was also discussed.

At room temperature (RT, 25 ± 2 °C), the average coefficients of friction of substrate and Ni-60%WC coatings fabricated at the LSS of 6, 10, 12 and 14 mm/s are 0.48 ± 0.08, 0.23 ± 0.01, 0.21 ± 0.05, 0.22 ± 0.02 and 0.25 ± 0.04, respectively, and the corresponding wear rates are 8.755 × 10⁴, 4.525 × 10³, 1.539 × 10³, 1.957 × 10³ and 2.743 × 10³ µm³·s^–1·N^–1, respectively, showing that the coating fabricated at the LSS of 10 mm/s has best friction reduction and wear resistance. The wear mechanism of Ni-60%WC coating is abrasive wear, fatigue wear and oxidative wear, which is resulted from the WC particles with the high-hardness.

Ni-60%WC coatings were first applied for cylinder liner, and the effect of laser scanning speed on its tribological performance was investigated.

The purpose of this paper is to study the correlation between different topographies and the reaction of Ulva Linza fouling species.

In this research, topographies with a different method, such as hot embossing and hot pulling, were achieved, and biological analyses were done with macroalgae Ulva Linza cells. The effect of topography via local binding geometry (honeycomb size gradients) and Wenzel roughness on the settling of Ulva microorganisms was tested.

As a result, Ulva spores confirmed different reactions to a similar set of tapered microstructures that was in agreement with the results on distinct honeycombs. The local binding geometry and the Wenzel roughness factor “r” were dominant on settling of Ulva Linza spores.

The reaction of an organism at the interface of vehicles’ substrate is powerfully affected by surface topographies.

The best embedment occurred on structures with bigger sizes than Ulva Linza’s spores. The density of settled spores was proportional to Wenzel roughness and the spores favour to attach to “kink sites” positions.

Unfortunately, unpleasant aggregation of marine biofouling on marine vehicles’ surfaces, generate terrific difficulties in the relevant industry.

There was a sharp relationship between Wenzel roughness and settle of Ulva Linza spores. The local binding geometry and the Wenzel roughness factor “r” were dominant on settling of Ulva Linza spores.

This paper aims to investigate the effect of Ti₃SiC₂ on the high-temperature tribological behaviors of NiCr coating, which was beneficial to improve the friction-wear performance of hot work mold.

NiCr-Ti₃SiC₂ coatings were prepared on H13 steel substrate by laser cladding. The microstructure, phases and hardness of obtained coatings were analyzed using a super-depth of field microscope, X-ray diffraction and microhardness tester, respectively, and the tribological performance of obtained coatings at 500°C was investigated using a high-temperature tester.

The results show the NiCr-Ti₃SiC₂ coatings are comprised of γ-Ni solid, solution, Ti_xNi_y, TiC and Ti₃SiC₂ phases, and the coating hardness is increased with the increase of Ti₃SiC₂ mass fraction, which is contributed to the fine-grain and dispersion strengthening effect by the addition of Ti₃SiC₂. The NiCr-Ti₃SiC₂ coatings present excellent friction reduction and wear resistance by the synergetic action of Ti₃SiC₂ lubricant and hard phase, and the wear mechanism is predominated by abrasive wear and oxidation wear.

Ti₃SiC₂ phase was used to reinforce the tribological performance of H13 steel at high temperature, and the roles of friction reduction and wear resistance were discussed.

The peer review history for this article is available at: https://publons.com/publon/10.1108/ILT-01-2023-0004/

This study aims to prevent occupational accidents occurring in the manufacturing industry by means of touch sensors. When the occupational accidents occurring in the manufacturing industry around the world are examined, it is seen that approximately 88% of occupational accidents occur from “dangerous movement” and 10% from “dangerous situation.” Although some studies related to safety culture studies, safety studies in design and collective or personal protective measures have been started, they have not been brought to an adequate level. It is observed that studies on dangerous movements continue even in many developed countries. In this study, first of all, a literature study was conducted. Occupational accidents experienced in the manufacturing sector in Turkey have been examined. In line with these investigations, a prototype circuit protection system has been developed that can prevent accidents caused by dangerous movement. With the circuit, its applicability and effectiveness were measured by conducting experiments on different manufacturing machines. The prototype circuit applied in this paper was made based on the logic of protective measures made on sawstop machines used in different sectors. In the experimental study conducted, it was observed that in 30 experiments conducted with a prototype on ten separate manufacturing machines, it stopped the machines 26 times at minimum and 29 times at maximum. On average, when looking at the system efficiency values, it was seen that the system was 81.6% effective, and it was observed that positive results could be obtained when converted into a real product.

In this study, their contribution to the prevention of work accidents caused by presses and rotary accents from machines used in the manufacturing industry by means of touch sensors used in Industry 4.0 was examined.

With Industry 4.0, different automation systems began to be switched in many areas and sectors. Studies have started on different sensors used also in Industry 4.0 in occupational health and safety studies, but it is seen that they have not been applied at an adequate level. It should be designed in such a way as to prevent errors or stop these errors in the studies performed. Today, sensors are produced at much lower costs than before. In addition, the constantly developing technology provides great convenience for these applications.

This study was applied for press and cylinder machines from manufacturing machines. This study has been tried for machines producing a maximum pressure of 300 tons.

A prototype was designed. Trials were done on some machines by prototype. There could be improve and find different solutions for safety problems in the industry with this perspective.

This study aims to comprehensively investigate the mixed-mode fracture behavior and mechanical properties of selective laser sintering (SLS) polyamide 12 (PA12) components, considering different build orientations and layer thicknesses. The primary objectives include the following. Conducting mixed-mode fracture and mechanical analyses on SLS PA12 parts. Investigating the influence of build orientation and layer thickness on the mechanical properties of SLS-printed components. Examining the fracture mechanisms of SLS-produced Arcan fracture and tensile specimens through experimental methods and finite element analyses.

The research used a combination of experimental techniques and numerical analyses. Tensile and Arcan fracture specimens were fabricated using the SLS process with varying build orientations (X, X–Y, Z) and layer thicknesses (0.1 mm, 0.2 mm). Mechanical properties, including tensile strength, modulus of elasticity and critical stress intensity factor, were quantified through experimental testing. Mixed-mode fracture tests were conducted using a specialized fixture, and finite element analyses using the J-integral method were performed to calculate fracture toughness. Scanning electron microscopy (SEM) was used for detailed morphological analysis of fractured surfaces.

The investigation revealed that the highest tensile properties were achieved in samples fabricated horizontally in the X orientation with a layer thickness of 0.1 mm. Additionally, parts manufactured with a layer thickness of 0.2 mm exhibited favorable mixed-mode fracture behavior. The results emphasize the significance of build orientation and layer thickness in influencing mechanical properties and fracture behavior. SEM analysis provided valuable insights into the failure mechanisms of SLS-produced PA12 components.

This study contributes to the field of additive manufacturing by providing a comprehensive analysis of the mixed-mode fracture behavior and mechanical properties of SLS-produced PA12 components. The investigation offers novel insights into the influence of build orientation and layer thickness on the performance of such components. The combination of experimental testing, numerical analyses and SEM morphological observations enhances the understanding of fracture behavior in additive manufacturing processes. The findings contribute to optimizing the design and manufacturing of high-quality PA12 components using SLS technology.

Epoxy zinc-rich coatings are widely used in harsh environments because of the long-lasting cathodic protection of steel surfaces. The purpose of this paper is to use flake zinc powder instead of the commonly used spherical zinc powder to reduce the zinc powder content.

In this paper, the authors have prepared an anticorrosive zinc-rich coating using a flake zinc powder instead of the conventional spherical zinc powder. The optimal dispersion of scaly zinc powder in zinc-rich coatings has been explored by looking at the surface and cross-sectional morphology and studying the cathodic protection time of the coating.

The final epoxy zinc-rich coating with 35 Wt.% flake zinc powder content was prepared using sand-milling dispersions. It has a similar cathodic protection time and salt spray resistance as the 60 Wt.% spherical zinc-rich coating, with a higher low-frequency impedance modulus value.

This study uses flake zinc powder instead of the traditional spherical zinc powder. This reduces the amount of zinc powder in the coating and improves the corrosion resistance of the coating.