The purpose of this paper is to highlight the sustainability benefits of using demolition and industrial wastes as a replacement for aggregates and cement in traditional concrete mixes.

Crushed concrete from demolition sites served as a replacement for fine and coarse aggregate in some of the mixes at various ratios. In addition, ground granulated blast furnace slag, metakaolin, silica fume, and fly ash each served as a cement replacement for cement content in the mixes tested in this research at various rates. Compression strength tests, permeability, and thermal expansion tests were performed on various mixes to compare their performance to that of traditional mixes with natural aggregate, and with no cement replacement.

The compressive strength results indicated the suitability of using such demolition wastes as replacements in producing green concrete (GC) without hindering its mechanical characteristics significantly. In addition, the results indicated an enhancement in the mechanical characteristics of GC when replacing cement with pozzolanic industrial wastes and byproducts.

The research assesses the utilization of sustainable GC using recycled waste aggregate and byproducts.

The purpose of this study is to investigate the behaviour of M40 grade of self-compacting concrete (SCC) with high volume of ground granulated blast furnace slag (GGBS) (50%) and recycled concrete aggregate (RCA) content up to 100% to assess the mechanical properties of SCC. As per guidelines of IS: 383 – 2016, the RCA can be replaced up to 20% of natural coarse aggregate up to M25 grade of concrete. This study assesses the mechanical properties of SCC beyond 20% of RCA content. Based on the experimental investigations, the compressive strength of mixes decreases as the content of RCA increases. It is found that concrete mixes with 20% RCA and shows the maximum compressive strength at 56 days.

The fresh properties as per EFNARC and IS: 10262–2019 guidelines, ultrasonic pulse velocity testing, mechanical properties and microstructure analysis have been conducted to evaluate the performance of SCC with RCA for practical applications.

From the experimental investigations, it is found that up to 50% of recycled coarse aggregate can be used for structural applications.

The environmental pollution and dumping of waste on green land can be reduced by effective utilization of recycled coarse aggregate and GGBS in the production of SCC.

The purpose of this paper is to investigate the effect of the replacement of natural coarse aggregate (NCA) with different percentages of recycled coarse aggregate (RCA) on properties of low calcium fly ash (FA)-based geopolymer concrete (GPC) cured at oven temperature. Further, this paper aims to study the effect of partial replacement of FA by ground granulated blast slag (GGBS) in GPC made with both NCA and RCA cured under ambient temperature curing.

M25 grade of ordinary Portland cement (OPC) concrete was designed according to IS: 10262-2019 with 100% NCA as control concrete. Since no standard guidelines are available in the literature for GPC, the same mix proportion was adopted for the GPC by replacing the OPC with 100% FA and W/C ratio by alkalinity/binder ratio. All FA-based GPC mixes were prepared with 12 M of sodium hydroxide (NaOH) and an alkalinity ratio, i.e. sodium hydroxide to sodium silicate (NaOH:Na₂SiO₃) of 1:1.5, subjected to 90^°C temperature for 48 h of curing. The NCA were replaced with 50% and 100% RCA in both OPC and GPC mixes. Further, FA was partially replaced with 15% GGBS in GPC made with the above percentages of NCA and RCA, and they were given ambient temperature curing with the same molarity of NaOH and alkalinity ratio.

The workability, compressive strength, split tensile strength, flexural strength, water absorption, density, volume of voids and rebound hammer value of all the mixes were studied. Further, the relationship between compressive strength and other mechanical properties of GPC mixes were established and compared with the well-established relationships available for conventional concrete. From the experimental results, it is found that the compressive strength of GPC under ambient curing condition at 28 days with 100% NCA, 50% RCA and 100% RCA were, respectively, 14.8%, 12.85% and 17.76% higher than those of OPC concrete. Further, it is found that 85% FA and 15% GGBS-based GPC with RCA under ambient curing shown superior performance than OPC concrete and FA-based GPC cured under oven curing.

The scope of the present paper is limited to replace the FA by 15% GGBS. Further, only 50% and 100% RCA are used in place of natural aggregate. However, in future study, the replacement of FA by different amounts of GGBS (20%, 25%, 30% and 35%) may be tried to decide the optimum utilisation of GGBS so that the applications of GPC can be widely used in cast in situ applications, i.e. under ambient curing condition. Further, in the present study, the natural aggregate is replaced with only 50% and 100% RCA in GPC. However, further investigations may be carried out by considering different percentages between 50 and 100 with the optimum compositions of FA and GGBS to enhance the use of RCA in GPC applications. The present study is further limited to only the mechanical properties and a few other properties of GPC. For wider use of GPC under ambient curing conditions, the structural performance of GPC needs to be understood. Therefore, the structural performance of GPC subjected to different loadings under ambient curing with RCA to be investigated in future study.

The replacement percentage of natural aggregate by RCA may be further enhanced to 50% in GPC under ambient curing condition without compromising on the mechanical properties of concrete. This may be a good alternative for OPC and natural aggregate to reduce pollution and leads sustainability in the construction.

This study aims to practically determine the optimum proportion of aggregates to attain the desired strength of geopolymer concrete (GPC) and then compare the results using established analytical particle packing methods. The investigation further aims to assess the influence of various amounts of recycled aggregate (RA) on properties of low-calcium fly ash-based GPC of grade M25.

Fine and coarse aggregates were blended in various proportions and the proportion yielding maximum packing density was selected as the optimum proportion and they were compared with analytical models, such as Modified Toufar Model (MTM) and J. D. Dewar Model. RAs for this study were produced in laboratory and they were used in various amounts, namely, 0%, 50% and 100%. 12M NaOH solution was mixed with Na₂SiO₃ in the ratio of 1:2. The curing of concrete was done at the temperatures of 60° and 90 °C for 24, 48 and 72h.

The experimentally obtained optimum proportion of coarse to fine aggregate was 60:40 for all amounts of RA. Meanwhile, MTM and Dewar Model resulted in coarse aggregate to fine aggregates as 40:60, 45:55, 55:45 and 55:45, 35:65, 60:40, respectively, for 0% 100% and 50% RAs. The compressive strength of GPC elevated with the increase in curing regime. In addition, the ultrasonic pulse velocity also displayed a similar trend as that of strength.

The GPC with 50% RAs may be considered for use, as it exhibited superior properties compared to GPC with 100% RAs and was comparable to GPC with natural aggregates. Furthermore, compressive strength is correlated with split tensile strength and ultrasonic pulse velocity.

Due to the high demand of concrete, significant volume of natural resources is required, including virgin aggregates. Many studies have shown that the production of concrete has one of the highest CO₂ levels. Although efforts are in place to recycle, enormous effects on landfill and the wider environment remain. Research has suggested the importance of reusing construction and demolition waste such as aggregate for use in recycled concrete. However, robust construction and demolition waste reduction strategies are required. There have been numerous researches on the use of recycled concrete and its management in the construction industry. This paper further consolidates this position.

This paper exhibits the barriers and benefits of using recycled aggregates for construction industry. This is achieved via reviewing the current construction and demolition waste reduction strategies used mainly in three countries: the UK, Australia and Japan. These countries were selected since they seemingly have similar construction industry and environment. Subsequently, evolving barriers and benefits of using recycled aggregates for construction industry are also reviewed and discussed. And to support such focus, robust construction and demolition waste reduction strategies will be advocated.

The findings are summarized as follows. The recycling construction and demolition waste could have a positive net benefit compared to the procurement and production of virgin aggregate materials with the same properties. This is not only financially beneficial but also environmentally viable, as fewer resources would be required to produce the same aggregate material. There are effective ways to achieve a high recycle rate target, as demonstrated by Japan. The implementation of a similar recycling process could be implemented globally to achieve a more effective recycle rate through the help of governments at all levels. By creating awareness about the financial and environmental benefits of using recycled aggregate products, large recycling companies can be also enticed to follow suit.

The findings from this paper can ultimately support the construction industry to further consolidate and advocate the use of recycled aggregates.

To achieve the research aim, this paper reviews some of the main sustainability factors of recycled aggregates (including coarse and fine aggregates) and provides comparison to virgin aggregates.

Scarcity in the construction aggregates necessitated the use of suitable alternative materials such as recycled aggregates. However, the higher porosity of recycled aggregates due to the presence of adhered mortar affects its quality resulting in limited utilization. The purpose of this paper is to investigate the use of Bacillus subtilis to enhance the properties of the recycled coarse aggregate (RCA). The strains of the bacterial species were collected from the Gene bank, Chandigarh, and cultured to 105 cells/ml to treat the RCA.

The concrete mixtures are prepared with 0%, 50% and 100% of treated and untreated RCA by mortar mixing approach. The concrete specimens are tested for compressive strength, split tensile strength, flexural strength and elastic modulus at 7, 14 and 28 days, respectively.

Microbial treatment to RCAs increased the weight of the aggregate and decreased the water absorption of the aggregates. The optimal replacement of RCA was observed to be 50% and the strength of the concrete with 50% of treated RCA was comparable to the normal aggregate concrete. The CaCO3 precipitation by bacterial species fills the pores on the RCA and thus increasing the strength of the concrete.

The originality of the research is to produce concrete with waste recycled aggregate treated by bacteria to overcome the problem of scarcity in construction materials.

The durability of concrete containing recycled aggregates, sourced from concrete specimens that have been tested in laboratory testing facilities, remains understudied. This paper aims to present the results of experiments investigating the effect of incorporating such type of concrete waste on the strength and durability-related properties of concrete.

A total of 77 concrete cylinders sized Ø100 × 200 mm with varying amount of recycled concrete aggregate (RCA) (0%–100% by volume, at 25% increments) and maximum aggregate size (12.5, 19.0 and 25.0 mm) were fabricated and tested for slump, compressive strength, sorptivity and electrical resistivity. Disk-shaped specimens, 50-mm thick, were cut from the original cylinders for sorptivity and resistivity tests. Analysis of variance and post hoc test were conducted to detect statistical variability among the data.

Compared to regular concrete, a reduction of slump (by 18.6%), strength (15.1%), secondary sorptivity (31.5%) and resistivity (17.0%) were observed from concrete containing 100% RCA. Statistical analyses indicate that these differences are significant. In general, an aggregate size of 19 mm was found to produce the optimum value of slump, compressive strength and sorptivity in regular and RCA-added concrete.

The results of this study suggest that comparable properties of normal concrete were still achieved by replacing 25% of coarse aggregate volume with 19-mm RCA, which was processed from laboratory-tested concrete samples. Therefore, such material can be considered as a potential and sustainable alternative to crushed gravel for use in light or nonstructural concrete construction.

Concrete, the second most used material in the world, surpassed only by water, relies on a vast amount of cement. The process of cement production emits substantial amounts of carbon dioxide (CO₂). Consequently, it is crucial to search for cement alternatives. Geopolymer concrete (GC) uses industrial by-product material instead of traditional cement, which not only reduces CO₂ emissions but also enhances concrete durability. On the other hand, the disposal of concrete waste in the landfills represents a significant environmental challenge, emphasising the urgent need for sustainable solutions. This study aimed to investigate waste concrete's best form and rate as the alternative aggregates in self-compacting and ambient-cured GC to preserve natural resources, reduce construction and demolition waste and decrease pertinent CO₂ emissions. The binding material employed in this research encompasses fly ash, slag, micro fly ash and anhydrous sodium metasilicate as an alkali activator. It also introduces the best treatment method to improve the recycled concrete aggregate (RCA) quality.

A total of25%, 50% and 100% of coarse aggregates are replaced with RCAs to cast self-compacting geopolymer concrete (SCGC) and assess the impact of RCA on the fresh, hardened and water absorption properties of the ambient-cured GC. Geopolymer slurry was used for coating RCAs and the authors examined the effect of one-day and seven-day cured coated RCA. The mechanical properties (compressive strength, splitting tensile strength and modulus of elasticity), rheological properties (slump flow, T500 and J-ring) and total water absorption of RCA-based SCGC were studied. The microstructural and chemical compositions of the concrete mixes were studied by the methods of energy dispersive X-Ray and scanning electron microscopy.

It is evident from the test observations that 100% replacement of natural aggregate with coated RCA using geopolymer slurry containing fly ash, slag, micro fly ash and anhydrous sodium metasilicate cured for one day before mixing enhances the concrete's quality and complies with the flowability requirements. Assessment is based on the fresh and hardened properties of the SCGC with various RCA contents and coating periods. The fresh properties of the mix with a seven-day curing time for coated RCA did not meet the requirements for self-compacting concrete, while this mix demonstrated better compressive strength (31.61 MPa) and modulus of elasticity (15.39 GPa) compared to 29.36 MPa and 9.8 GPa, respectively, for the mix with one-day cured coated RCA. However, incorporating one-day-cured coated RCA in SCGC demonstrated better splitting tensile strength (2.32 MPa) and water absorption (15.16%).

A potential limitation of this study on SCGC with coated RCAs is the focus on the short-term behaviour of this concrete. This limited time frame may not meet the long-term requirements for ensuring the sustained durability of the structures throughout their service life.

This paper highlights the treatment technique of coating RCA with geopolymer slurry for casting SCGC.

The purpose of this paper is to investigate whether concrete that includes un‐graded recycled aggregates can be manufactured to a comparable strength to concrete manufactured from virgin aggregates.

A paired comparison test was used to evaluate the difference between concrete made with virgin aggregates (plain control) and concrete including recycled waste. Un‐graded construction demolition waste and un‐graded ground glass were used as aggregate replacements. With regard to concrete, compressive strength is widely used as a measure of suitability as being fit for purpose. Therefore compressive strength was mainly used to compare the different concrete batches; however density was measured across the range of samples.

The findings show that a lower average compressive strength is achieved when compared to the plain control sample manufactured with virgin aggregates. Correct particle packing may not be achieved and grading of aggregates is essential prior to mix design. The recycled aggregate was highly variable in terms of the fine particle content, which affected the water demand of the concrete.

This manufacturing practice is considered necessary because of the current trend in using waste products in concrete to replace binders and aggregates; thus reducing the impact on the environment and use of finite natural resources. The research shows the risk of mixing concrete using a simple aggregate replacement without careful aggregate grading and adjustments to the mix design.

The paper examines 100 per cent ungraded aggregate replacement with glass and demolition waste.

The majority of previous studies made on Recycled Concrete Aggregates (RCA) are limited to the utilisation of non-structural grade concrete due to unfavourable physical characteristics of RCA including the higher absorption of water, tending to increased water requirement of concrete. This seriously limits its applicability and as a result it reduces the usage of RCA in structural members. In the present study, the impact of hybrid fibres on cracking behaviour of RCA concrete beams along with the inclusion of reinforcing steel bars under two-point loading system exposed to different sustained elevated temperatures are being investigated.

RCA is substituted for Natural Coarse Aggregates (NCA) at 0, 50 and 100 percentages. The study involves testing of 150 mm cubes and beams of size (700 × 150 × 150) mm, i.e. with steel reinforcing bars along with the addition of 0.35% Steel fibres+ 0.15% polypropylene fibres. The specimens are being exposed to temperatures from 100° to 500°C with 100° interval for 2 h. Studies were made on the post crack analysis, which includes the measurement of crack width, crack length and load at first crack. The crack patterns were analysed in order to understand the effect of fibres and RCA at sustained elevated temperatures.

The result shows that ultimate load carrying capacity of reinforced concrete beams and load at first crack decreases with the raise in temperatures and increased percentage of RCA content in the mix. Further that 100% RCA replacement specimens showed lesser cracks when compared to the other mixes and the inclusion of fibres enhances the flexural capacity of members highlighting the importance of fibres.

RCA can be used for structural purposes and the study can be projected for assessing the performance of real structures with the extent of fire damage when recycled aggregates are used.

Most of recycled materials can be used in the regular concrete which solves two problems namely avoiding the dumping of C&D waste and preventing the usage of natural aggregates. Hence the study provides sustainable option for the production of concrete.

The reduction in capacity of flexural members due to the utilisation of recycled aggregates can be negated by the usage of fibres. Hence improved flexural performance is observed for specimens with fibres at sustained elevated temperatures.