Additive manufacturing (AM) of thermoplastic polymers for powder bed fusion processes typically requires each layer to be fused before the next can be deposited. The purpose of this paper is to present a volumetric AM method in the form of deeply penetrating radio frequency (RF) radiation to improve the speed of the process and the mechanical properties of the polymer parts.

The focus of this study was to demonstrate the volumetric fusion of composite mixtures containing polyamide (nylon) 12 and graphite powders using RF radiation as the sole energy source to establish the feasibility of a volumetric AM process for thermoplastic polymers. Impedance spectroscopy was used to measure the dielectric properties of the mixtures as a function of increasing graphite content and identify the percolation limit. The mixtures were then tested in a parallel plate electrode chamber connected to an RF generator to measure the heating effectiveness of different graphite concentrations. During the experiments, the surface temperature of the doped mixtures was monitored.

Nylon 12 mixtures containing between 10% and 60% graphite by weight were created, and the loss tangent reached a maximum of 35%. Selective RF heating was shown through the formation of fused composite parts within the powder beds.

The feasibility of a novel volumetric AM process for thermoplastic polymers was demonstrated in this study, in which RF radiation was used to achieve fusion in graphite-doped nylon powders.

dding dopants to a powder bed could be a cost-effective method for spatially varying the material properties in laser powder bed fusion (LPBF) or for evaluating new materials and processing relationships. However, these additions may impact the selection of processing parameters. Furthermore, these impacts may be different when depositing nanoparticles into the powder bed than when the same composition is incorporated into the powder particles as by ball milling of powders or mixing similarly sized powders. This study aims to measure the changes in the single bead characteristics with laser power, laser scan speed, laser spot size and quantity of zirconia nanoparticle dopant added to SS 316 L powder.

A zirconia slurry was inkjet-printed into a single layer of 316 SS powder and dried. Single bead experiments were conducted on the composite powder. The line type (continuous vs balling) and the melt pool geometry were compared at various levels of zirconia doping.

The balling regime expands dramatically with the zirconia dopant to both higher and lower energy density values indicating the presence of multiple physical mechanisms that influence the resulting melt track morphology. However, the energy density required for continuous tracks was not impacted as significantly by zirconia addition. These results suggest that the addition of dopants may alter the process parameter ranges suitable for the fabrication of high-quality parts.

This work provides new insight into the potential impact of material doping on the ranges of energy density values that form continuous lines in single bead tests. It also illustrates a potential method for spatially varying material composition for process development or even part optimization in powder bed fusion without producing a mixed powder that cannot be recycled.

During thermal laser processes, heat transfer and fluid flow in the melt pool are primary driven by complex physical phenomena that take place at liquid/vapor interface. Hence, the choice and setting of front description methods must be done carefully. Therefore, the purpose of this paper is to investigate to what extent front description methods may bias physical representativeness of numerical models of laser powder bed fusion (LPBF) process at melt pool scale.

Two multiphysical LPBF models are confronted: a Level-Set (LS) front capturing model based on a C++ code and a front tracking model, developed with COMSOL Multiphysics® and based on Arbitrary Lagrangian–Eulerian (ALE) method. To do so, two minimal test cases of increasing complexity are defined. They are simplified to the largest degree, but they integrate multiphysics phenomena that are still relevant to LPBF process.

LS and ALE methods provide very similar descriptions of thermo-hydrodynamic phenomena that occur during LPBF, providing LS interface thickness is correctly calibrated and laser heat source is implemented with a modified continuum surface force formulation. With these calibrations, thermal predictions are identical. However, the velocity field in the LS model is systematically underestimated compared to the ALE approach, but the consequences on the predicted melt pool dimensions are minor.

This study fulfils the need for comprehensive methodology bases for modeling and calibrating multiphysical models of LPBF at melt pool scale. This paper also provides with reference data that may be used by any researcher willing to verify their own numerical method.

Support structures used in laser powder bed fusion are often difficult to clean from unsintered powder at the end of the process. This issue can be significantly reduced through a proper design of these auxiliary structures. This paper aims to investigate preliminary the airflow within differently oriented support structures and to provide design guidelines to enhance their cleanability, especially the depowdering of them.

This study investigates the cleanability of support structures in powder bed fusion technology. Digital models of cleaning operations were designed through computer-aided engineering systems. Simulations of the airflow running into the powder entrapped within the thin walls of auxiliary supports were implemented by computational fluid dynamics. This approach was applied to a set of randomly generated geometrical configurations to determine the air turbulence intensity depending on their design.

The results, which are based on the assumption that a relationship exists between turbulence and powder removal effectiveness, demonstrated that the maximum cleanability is obtainable through specific relative rotations between consecutive support structures. Furthermore, it was possible to highlight the considerable influence of the auxiliary structures next to the fluid inlet. These relevant findings establish optimal design rules for the cleanability of parts manufactured by powder bed fusion processes.

This study presents a preliminary investigation into the cleanability of support structures in laser powder bed fusion, which has not been addressed by previous literature. The results allow for a better understanding of the fluid dynamics during cleaning operations. New guidelines to enhance the cleanability of support structures are provided based on the results of simulations.

The purpose of this study is, to compare laser-based additive manufacturing and subtractive methods. Laser-based manufacturing is a widely used, noncontact, advanced manufacturing technique, which can be applied to a very wide range of materials, with particular emphasis on metals. In this paper, the governing principles of both laser-based subtractive of metals (LB-SM) and laser-based powder bed fusion (LB-PBF) of metallic materials are discussed and evaluated in terms of performance and capabilities. Using the principles of both laser-based methods, some new potential hybrid additive manufacturing options are discussed.

Production characteristics, such as surface quality, dimensional accuracy, material range, mechanical properties and applications, are reviewed and discussed. The process parameters for both LB-PBF and LB-SM were identified, and different factors that caused defects in both processes are explored. Advantages, disadvantages and limitations are explained and analyzed to shed light on the process selection for both additive and subtractive processes.

The performance of subtractive and additive processes is highly related to the material properties, such as diffusivity, reflectivity, thermal conductivity as well as laser parameters. LB-PBF has more influential factors affecting the quality of produced parts and is a more complex process. Both LB-SM and LB-PBF are flexible manufacturing methods that can be applied to a wide range of materials; however, they both suffer from low energy efficiency and production rate. These may be useful when producing highly innovative parts detailed, hollow products, such as medical implants.

This paper reviews the literature for both LB-PBF and LB-SM; nevertheless, the main contributions of this paper are twofold. To the best of the authors’ knowledge, this paper is one of the first to discuss the effect of the production process (both additive and subtractive) on the quality of the produced components. Also, some options for the hybrid capability of both LB-PBF and LB-SM are suggested to produce complex components with the desired macro- and microscale features.

The consolidation process and morphology evolution in ceramics-based additive manufacturing (AM) are still not well-understood. As a way to better understand the ceramic selective laser sintering (SLS), a dynamic three-dimensional computational model was developed to forecast thermal behavior of hydroxyapatite (HA) bioceramic.

AM has revolutionized automotive, biomedical and aerospace industries, among many others. AM provides design and geometric freedom, rapid product customization and manufacturing flexibility through its layer-by-layer technique. However, a very limited number of materials are printable because of rapid melting and solidification hysteresis. Melting-solidification dynamics in powder bed fusion are usually correlated with welding, often ignoring the intrinsic properties of the laser irradiation; unsurprisingly, the printable materials are mostly the well-known weldable materials.

The consolidation mechanism of HA was identified during its processing in a ceramic SLS device, then the effect of the laser energy density was studied to see how it affects the processing window. Premature sintering and sintering regimes were revealed and elaborated in detail. The full consolidation beyond sintering was also revealed along with its interaction to baseplate.

These findings provide important insight into the consolidation mechanism of HA ceramics, which will be the cornerstone for extending the range of materials in laser powder bed fusion of ceramics.

Since the biomedical implants with an improved compressive strength, near bone elastic modulus, controlled porosity, and sufficient surface roughness, can assist in long term implantation. Therefore, the fine process tuning plays its crucial role to develop optimal settings to achieve these desired properties. This paper aims to find applications for fine process tuning in laser powder bed fusion of biomedical Ti alloys for load-bearing implants.

In this work, the parametric porosity simulations were initially performed to simulate the process-induced porosity for selective laser-melted Ti₆Al₄V as per full factorial design. Continually, the experiments were performed to validate the simulation results and perform multiresponse optimization to fine-tune the processing parameters. Three levels of each control variable, namely, laser power – Pl (180, 190, 200) W, scanning speed – Vs (1500, 1600, 1700) mm/s and scan orientation – ϴ{1(0,0), 2(0,67°), 3(0,90°)} were used to investigate the processing performance. The measured properties from this study include compressive yield strength, elastic modulus, process-induced porosity and surface roughness. Finally, confirmatory experiments and comparisons with the already published works were also performed to validate the research results.

The results of porosity parametric simulation and experiments in selective laser melting of Ti₆Al₄V were found close to each other with overall porosity (less than 10%). The fine process tuning was resulted in optimal settings [Pl (200 W), Vs (1500 mm/s), ϴ (0,90°)], [Pl (200 W), Vs (1500 mm/s), ϴ (0,67°)], [Pl (200 W), Vs (1500 mm/s), ϴ (0,0)] and [Pl (200 W), Vs (1500 mm/s), ϴ (0,0)] with higher compressive strength (672.78 MPa), near cortical bone elastic modulus (12.932 GPa), process-induced porosity (0.751%) and minimum surface roughness (2.72 µm). The morphology of the selective laser melted (SLMed) surface indicated that the lack of fusion pores was prominent because of low laser energy density among the laser and powder bed. Confirmatory experimentation revealed that an overall percent improvement of around 15% was found between predicted and the experimental values.

Since no significant works are available on the collaborative optimization and fine process tuning in laser powder bed fusion of biomedical Ti alloys for different load bearing implants. Therefore, this work involves the comprehensive investigation and multi-objective optimization to determine optimal parametric settings for better mechanical and physical properties. Another novel aspect is the parametric porosity simulation using Ansys Additive to assist in process parameters and their levels selection. As a result, selective laser melted Ti alloys at optimal settings may help in examining the possibility for manufacturing metallic implants for load-bearing applications.

The purpose of this paper is to investigate the effect of remelting each layer on the homogeneity of nickel-titanium (NiTi) parts fabricated from elemental nickel and titanium powders using laser powder bed fusion (LPBF). In addition, the influence of manufacturing parameters and different melting strategies, including multiple cycles of remelting, on printability and macro defects, such as pore and crack formation, have been investigated.

An LPBF process was used to manufacture NiTi alloy from elementally blended powders and was evaluated with the use of a remelting scanning strategy to improve the homogeneity of fabricated specimens. Furthermore, both single melt and up to two remeltings were used.

The results indicate that remelting can be beneficial for density improvement as well as chemical and phase composition homogenization. Backscattered electron mode in scanning electron microscope showed a reduction in the presence of unmixed Ni and Ti elemental powders in response to increasing the number of remelts. The microhardness values of NiTi parts for the different numbers of melts studied were similar and ranged from 487 to 495 HV. Nevertheless, it was observed that measurement error decreases as the number of remelts increases, suggesting an increase in chemical and phase composition homogeneity. However, X-ray diffraction analysis revealed the presence of multiple phases regardless of the number of melt runs.

For the first time, to the best of the authors’ knowledge, elementally blended NiTi powders were fabricated via LPBF using remelting scanning strategies.

Selective laser melting and electron beam melting processes are well-known for the additive manufacturing of metal parts. Metal powder bed fusion (MPBF) is a common term for them. The MPBF process can empower the manufacturing of intricate shapes by reducing the use of special tools, shortening the supply chain and allowing small batches. However, the MPBF process suffers from many quality issues. In literature, several works are recorded for qualification of the MPBF part. The purpose of this study is to recollect those works done for quality control and report their helpful findings for further research and development.

A systematic literature review was conducted to highlight the major quality issues in the MPBF process and its root causes. Further, the works reported in the literature for mitigation of these issues are classified and discussed in five categories: experimental investigation, finite element method-based numerical models, physics-based analytical models, in-situ control using artificial intelligence (AI) and machine learning (ML) methods and statistical approaches. A comparison is also prepared among these strategies based on their suitability and limitations. Additionally, improvements in MPBF printers are pointed out to enhance the part quality.

Analytical models require less computational time to simulate the MPBF process and need a smaller number of experiments to confirm the results. They can be used as an efficient process parameter planning tool to print metal parts for noncritical applications. The AI-ML based quality control is also suitable for MPBF processes as it can control many processing parameters that may affect the quality of the MPBF part. Moreover, capabilities of MPBF printers like thinner layer thickness, smaller beam diameter, multiple lasers and high build temperature range can help in quality control.

This study converts the piecemeal data on MPBF part qualification methods into interesting information and presents it in tabular form under each strategy. This tabular information provides the basis for further quality improvement efforts in the MPBF process.

This study references researchers and practitioners on recent quality control efforts and their significant findings for a better quality of MPBF part.

This study aims to provide a comprehensive overview of the current state of the art in powder bed fusion (PBF) techniques for additive manufacturing of multiple materials. It reviews the emerging technologies in PBF multimaterial printing and summarizes the latest simulation approaches for modeling them. The topic of “multimaterial PBF techniques” is still very new, undeveloped, and of interest to academia and industry on many levels.

This is a review paper. The study approach was to carefully search for and investigate notable works and peer-reviewed publications concerning multimaterial three-dimensional printing using PBF techniques. The current methodologies, as well as their advantages and disadvantages, are cross-compared through a systematic review.

The results show that the development of multimaterial PBF techniques is still in its infancy as many fundamental “research” questions have yet to be addressed before production. Experimentation has many limitations and is costly; therefore, modeling and simulation can be very helpful and is, of course, possible; however, it is heavily dependent on the material data and computational power, so it needs further development in future studies.

This work investigates the multimaterial PBF techniques and discusses the novel printing methods with practical examples. Our literature survey revealed that the number of accounts on the predictive modeling of stresses and optimizing laser scan strategies in multimaterial PBF is low with a (very) limited range of applications. To facilitate future developments in this direction, the key information of the simulation efforts and the state-of-the-art computational models of multimaterial PBF are provided.