The purpose of this paper is to improve the comfort and shaping function of seamless shapewear on the material and structure and develop new seamless shapewear products. The shaping figure effect will be verified as well.

The performance of the knitted fabrics made of Polytrimethylene terephthalate (PTT) filament was analyzed by orthogonal experiment and fuzzy mathematical methods analysis, in order to get the optimal conditions for the best performance. The new products were designed and made based on the results of the material research with the consideration of the aesthetic requirements. The shaping effect of seamless shapewears on local and global figure was tested by the methods of the combination of subjective and objective evaluation.

The sample which renders the optimal performance for shapewear is the one with PTT filament as face yarn, nylon core-spun yarn as ground yarn and 3+1 simulate rib knit structure. The material of face yarn, mixed proportion and structure can influence the shape retention, appearance and comfort of PTT fabric in various degrees. Three shapewears which were developed according to the results of material research have different shaping effect. And women with different figures put different satisfaction degrees on each shapewear’s shaping effect.

This paper provides scientific basis and reference for enterprise to design good tight seamless shapewear as well as for consumer to buy suitable products.

In the view of the problems of present shapewears, this paper completed the development of the shapewears and verified the shaping effect of them on women with different figures. The shapewears can be put into production directly.

The purpose of this paper is to understand the recovery mechanism of poly(trimethylene terephthalate) (PTT) shape memory fabrics.

Tests were designed to study the effects of force, temperature and their combinations on the fabrics' crease recoveries. In the test a cantilever device and an ironing force which simulated people ironing their clothes were used, respectively.

Temperature was found to have little effect on the recovery of both the warp and filling of the fabrics. Crease recoveries did not improve significantly when the temperature was increased to above the polymer's glass transition. However, forces, applied in primarily compressive and tensile modes to simulate ironing and hand stroking actions, were found to be very effective in the fabrics' crease recoveries. Recoveries were 81‐87 per cent even when the applied force was very small, at 5 N/cm². When forces were applied at elevated temperatures, just below and above the polymer's glass transition, there were no significant improvements in crease recoveries. Therefore, force was the main factor in PTT shape memory fabrics' recovery mechanism for the fabrics to return to their initial shapes.

The results suggest that PTT shape memory fabric has excellent shape recoverability and easy care property and it has large application potentiality.

Examines the fifthteenth published year of the ITCRR. Runs the whole gamut of textile innovation, research and testing, some of which investigates hitherto untouched aspects. Subjects discussed include cotton fabric processing, asbestos substitutes, textile adjuncts to cardiovascular surgery, wet textile processes, hand evaluation, nanotechnology, thermoplastic composites, robotic ironing, protective clothing (agricultural and industrial), ecological aspects of fibre properties – to name but a few! There would appear to be no limit to the future potential for textile applications.

As one kind of filament/staple fiber composite yarn, core spun yarn has been widely used, especially on Jeans. However, there is only one filament in the commonly used core spun yarn, such as spandex, and the performance of the one filament often is influenced during dyeing and finishing. Therefore, in the paper, twin-core spun yarns with two different filaments feeding simultaneously were spun on ring spinning frame modified by one kind of filament feeding numerical control device. The paper aims to discuss these issues.

Four kinds of twin-core spun yarns, cotton/spandex/PBT, cotton/spandex/CM800, cotton/spandex/T400, cotton/spandex/SPH with linear density 36.4tex/40D/50D were spun. For improving the covering effect of the two filaments, the filament feeding position, filament pre-drafting multiple, distance between two staple roving, designed twist factor of the core spun yarn were optimized.

It is shown that comparing with the core spun yarn, the breaking strength and elongation of the twin-core spun yarns are improved since the addition of another elastic filament, while the evenness is a little worse.

By using the twin-core spun yarns, corresponding knitted and woven fabrics are produced. Meanwhile, for simulating the dyeing and finishing process, the knitted fabrics were treated during the 150°C high temperature. It is shown that comparing with the fabrics produced by cotton/spandex yarn, addition of another elastic filament can improve the fabric strength and resistant and has positive effect on worsen prevention for high temperature treated fabric elastic recovery, and on change prevention during the dyeing and finishing process for fabric handle properties, and improves the fabric stability.

The purpose of this paper is to facilitate the production of cotton spandex woven fabric with some user-friendly properties like wearer comfort, super stretch and elasticity. The findings could contribute to ease spandex production and to optimize its property of elasticity. Stretch or a super stretch property is generally desirable, as it can increase the comfort level of those who wear it. In this experiment, the difficulties which were identified while manufacturing cotton spandex woven fabric resolved after identification.

In this experiment, three types of cotton spandex woven fabrics, with different composition and constructions, were used to find out their elastic properties. Temperature ranging from 160°C to 200°C with the machine speed of 20 to 26 MPM (meter per minute) was applied with an adjusted industrial setting with the facilities of a stenter machine to optimize the properties of cotton spandex woven fabric.

The findings establish that the temperature treatment closely compacted the elastic portions with cotton fibers, giving stability to the spandex yarn, which as a result, influenced cotton spandex woven fabric’s elastic properties, namely, stretch, growth and recovery. The consequences of temperature on cotton spandex yarns were assessed using a microscope, and the results were subsequently analyzed.

Because of the poor facilities in testing laboratory, only few tests with microscopic evaluation were conducted to assess the elastic performances of cotton spandex woven fabric.

It is a practice-based research, and the findings could be beneficial to personnel in the textile industry, who are responsible for the manufacturing of cotton spandex woven fabric.

This research could enhance the wearer’s satisfaction, with some comfort elastic properties, which can have a positive influence over spandex clothing industries.

This research establishes that heat setting had a progressive influence on the production of cotton spandex woven fabric and for the optimization of its elastic performances. This research opens a possible way for scholars to further study in this field.

In order to develop high shape retention yarn and investigate the effects of spinning process and core yarn contents on the shape retention of yarn, in this paper, three kinds of yarns, JC/T400 18.5tex (55.6dtex) core-spun yarn, JC/T400 18.5tex (44.4dtex) core-spun yarn and JC18.5tex pure cotton yarn were spun by using the complete condensing Siro-spinning technology. The paper aims to discuss these issues.

In this paper, the core-spun yarns were spun by using the complete condensing spinning and Siro-spinning technology. Two key spinning processes, yarn twist factor and core yarn pre-draft ratio, were optimized by using the orthogonal test method first. Then, via the variable control method, the position of the core yarn, the position of the bell mouth and the center distance between two bell mouths were optimized, respectively, and corresponding optimal spinning process of the three yarns was determined. Finally, the yarns were spun under the optimal process, and the performance of the spun yarns was tested and compared.

Results show that the yarn twist factor affects yarn strength and hairiness, the position of bell mouth affects the evenness and hairiness of the yarn mainly, and the position of the core yarn affects the coverage and hairiness of the yarn. For the Z-twist spinning, the core yarn enters the front roller from the left side of two strands center, which is beneficial to improve the covering effect of core yarn, and reduce the pilling phenomenon of the yarn. The contents of core yarn affect indicators of the yarn shape retention, such as yarn strength, elastic recovery and abrasion resistance.

The shape retention of yarns affects the shape retention of fabrics, and the production of yarn with high shape retention is a key step in achieving shape retention of fabrics. At present, there are little studies on the shape retention of yarns, most researchers shave focused on shape retention of fabrics. Using the complete condensing Siro-spinning method to spin the core-spun yarn can improve the quality of the yarn. Compared with traditional ring-spinning yarns, the addition of the core yarn can improve the shape retention of the yarn.

This paper is based on the simulation of wind tunnel experiment for better understanding and predicting the behavior of PET fabric in the wind tunnel. This software calculates the drag force of fabric, illustrates pressure in the surrounding of airfoil and velocity of wind in the tunnel during different angles of attack (0°, 45° and 90°). The paper aims to discuss these issues.

The sol-gel method was applied for the synthesis of silica nano particles. So, PET fabric was coated with precursor (Tetra ethyl ortho silicate) solution first and the process continued on PET fabric. The morphology of obtained hydrophobic fabric samples and their surface roughness was observed and determined by atomic microscopes (AFM and SEM). Experimental data were used for simulation and modeling, and then results were interpreted.

It was concluded that the surface roughness and its amount can play a significant role in the drag reduction of PET fabric, and surface roughness can change the boundary layer from laminar to turbulent.

At 45 degrees angle of attack, larger boundary layer separation results in a large increase in the drag force. This model is useful for predicting flow behavior in the experimental wind tunnel.