The purpose of this study is to reveal the effect of nano-Al₂O₃ particle addition on the nucleation/growth kinetics, microhardness, wear resistance and corrosion resistance of Co–P–xAl₂O₃ nanocomposite plating.

The kinetics and properties of Co–P–xAl₂O₃ nanocomposite plating prepared by electroplating were investigated by electrochemical measurements, scanning electron microscopy, X-ray diffraction, X-ray photoelectron spectroscopy, Vickers microhardness measurement, SRV5 friction and wear tester and atomic force microscopy.

A 12 g/L nano-Al₂O₃ addition in the plating solution can transform the nucleation/growth kinetics of the plating from the 3D progressive model to the 3D instantaneous model. The microhardness of the plating increased with the increase of nano-Al₂O₃ content in plating. The wear resistance of the plating did not adhere strictly to Archard’s law. An even and denser corrosion product film was generated due to the finer grains, with a high corrosion resistance.

The effect of different nano-Al₂O₃ addition on the nucleation/growth kinetics and properties of Co–P–xAl₂O₃ nanocomposite plating was investigated, and an anticorrosion mechanism of Co–P–xAl₂O₃ nanocomposite plating was proposed.

The demand for titanium alloys has received massive attention in the aerospace and automotive industry owing to their magnificent electrochemically compatibility and corrosion resistance, high strength at elevated temperatures and high strength-to-weight ratio. Although titanium alloy has impressive mechanical properties, they are challenging to machine or metal form due to its poor heat conductivity, high chemical reactivity, low modulus of elasticity, high friction coefficient and difficult lubricant that limits its application field and increases wear. However, surface treatment coating with the strong metallurgical bond between the titanium alloy matrixes is novel technique to resolve these challenges. This research will illustrate the influence of laser scanning power on the microstructure and tribological behavior of Nickel (NI)-composite claddings fabricated on TC4 titanium alloy to realize the strong metallurgical bond between the titanium alloy and NI-composite coating.

In this research, TiC/TC4 alloy nanocomposites were fabricated based on different laser power and temperatures. TC4 has been selected as a base material instead of TiC for the strong metallurgical bond between the titanium alloy matrixes. Then Ni-composite coating was used as the surface treatment coating on TC4 by laser cladding (LC) technique. The Ni-based alloy coating material powder is good self-fluxing, has high-temperature resistance and is analytically pure with 200 mesh, which can easily overcome the various challenges of titanium alloy. The chemical properties of Ni composite coating include 31.2% Chromium, 8%Titenium and 3.6% Carbon. The prepared surface treatment coating characterization and microstructure behavior are analyzed using optical micrograph, X-ray diffraction, scanning electron microscopes, energy dispersive spectroscopy and electron probe micro analyzer methods.

It is evident that at the beginning of the experiment, if the laser power increased, the quality of the coating increased. An optimal quality of the coating is found when the laser scanning power about 12.55 kJ/cm². Further increased laser power diminished the quality of the coating because the material plasticity had deteriorated. The TiC ceramic particle reinforced phase is dispersed into a two-phase solid solution of β-Ti and γ-Ni. The micro-hardness of the used coating is greater than the base alloy.

This research has practical value in the modern aerospace and automobile industry to increase the application of titanium alloy.

This study aims to assess the efficacy of nano-alumina (nano-Al₂O₃) in improving the performance of epoxy adhesives used to assemble archaeological glass. The conservators face a significant problem in assembling this type of artifact. Therefore, the assembling process is considered one of the important stages that must be taken care of to preserve these artifacts from damage and loss.

To evaluate the stability of adhesives, the samples were subjected to artificial aging under varying environmental conditions. Some investigative techniques and mechanical testing were used in this study to evaluate the selected materials. It includes a transmission electron microscope, X-ray diffraction, visual assessment, digital microscope, scanning electron microscopy (SEM), color change and tensile strength test.

The visual evaluation and the digital microscope results showed that the epoxy/nano-Al₂O₃ greatly resisted artificial aging. Although slight yellowing was present, it did not significantly affect the general appearance of the samples. On the other hand, the pure epoxy sample showed cracks of different sizes on its surface due to aging, as evidenced by SEM examination. Furthermore, epoxy/nano-Al₂O₃ has a better tensile strength (11.27 MPa) and slight color change (ΔE = 2.06).

The main objective of the experimental study was to identify appropriate adhesive materials that possess key properties such as non-yellowing and improved tensile strength by conducting various tests and evaluations. Ultimately, the goal was to identify materials that could serve as effective adhesives for assembling the archaeological glass.

The purpose of this study is to prepare ZnFe₂O₄ nanospheres, sheet MoS₂ and three ZnFe₂O₄@MoS₂ core-shell composites with various shell thicknesses, and add them to the base oil for friction and wear tests to simulate the wear conditions of hybrid bearings.

Through the characterization and analysis of the morphology of wear scars and the elemental composition of friction films, the tribological behavior and wear mechanism of sample materials as lubricant additives were investigated and the effects of shell thickness and sample concentration on the tribological properties of core–shell composite lubricant additives were discussed.

The findings demonstrate that each of the five sample materials can, to varying degrees, enhance the lubricating qualities of the base oil and that the core–shell nanocomposite sample lubricant additive has superior lubricating properties to those of ZnFe₂O₄ and MoS₂ alone, among them ZnFe₂O₄@MoS₂-2 core–shell composites with moderate shell thickness performed most ideally. In addition, the optimal concentration of the ZnFe₂O₄@MoS₂ lubricant additive was 0.5 Wt.%, and a concentration that was too high led to particle deposition and affected the friction effect.

In this work, ZnFe₂O₄@MoS₂ core–shell composites were synthesized for the first time using ZnFe₂O₄ as the carrier and the lubrication mechanism of core–shell composites and single materials were compared and studied, which illustrated the advantages of core–shell composite lubricant additives. At the same time, the influence of different shell thicknesses on the lubricant additives of core–shell composites was studied.

The peer review history for this article is available at: https://publons.com/publon/10.1108/ILT-12-2022-0367/

This study aims to focus on how reactive diluents with mono- and di-functionalities affect the properties of resin formulation developed from bioderived precursors. A hydroxyethyl methacrylate (HEMA) terminated urethane acrylate oligomer was synthesized and characterized to study its application in stereolithography 3D printing with different ratios of isobornyl acrylate and hexanediol diacrylate.

Polyester polyol was synthesized from suberic acid and butanediol. Additionally, isophorone diisocyanate, polyester polyol and HEMA were used to create urethane acrylate oligomer. Fourier transform infrared spectroscopy and ¹H NMR were used to characterize the polyester polyol and oligomer. Various formulations were created by combining oligomer with reactive diluents in concentrations ranging from 0% to 30% by weight and curing with ultraviolet (UV) radiation. The cured coatings and 3D printed specimens were then evaluated for their properties.

The findings revealed an improvement in thermal stability, contact angle value, tensile strength and surface properties of the product which indicated its suitability for use as a 3D printing material.

This study discusses how oligomers that have been cured by UV radiation with mono- and difunctional reactive diluents give excellent coating characteristics and demonstrate suitability and stability for 3D printing applications.

The purpose of this paper is to evaluate the effect of titanium oxide (TiO₂) and yttrium oxide (Y₂O₃) nanoparticles-reinforced pure aluminium (Al) on the mechanical properties of hybrid aluminium matrix nanocomposites (HAMNCs).

The HAMNCs were fabricated via a vacuum die-assisted stir casting route by a two-step feeding method. The varying weight percentages of TiO₂ and Y₂O₃ nanoparticles were added as 2.5, 5, 7.5 and 10 Wt.%.

Scanning electron microscope images showed the homogenous dispersion of nanoparticles in Al matrix. The tensile strength by 28.97%, yield strength by 50.60%, compression strength by 104.6% and micro-hardness by 50.90% were improved in HAMNC1 when compared to the base matrix. The highest values impact strength of 36.3 J was observed for HAMNC1. The elongation % was decreased by increasing the weight percentage of the nanoparticles. HAMNC1 improved the wear resistance by 23.68%, while increasing the coefficient of friction by 14.18%. Field emission scanning electron microscope analysis of the fractured surfaces of tensile samples revealed microcracks and the debonding of nanoparticles.

The combined effect of TiO₂ and Y₂O₃ nanoparticles with pure Al on mechanical properties has been studied. The composites were fabricated with two-step feeding vacuum-assisted stir casting.

Titanium(IV) oxide nanoparticles (TiO₂ NP) were deposited to cotton denim fabrics using a self-crosslinking acrylate – a polymer dispersion to extend the lifetime of the products. This study aims to determine the optimum conditions to increase abrasion resistance, to provide self-cleaning properties of denim fabrics and to examine the effects of these applications on other physical properties.

The denim samples were first treated with nonionic surfactant to increase their wettability. Three different amounts of the polymer dispersion and two different pH levels were selected for the experimental design. The finishing process was applied to the fabrics with pad-dry-cure method.

The presence of the coatings and the adhesion of TiO₂ NPs to the surfaces were confirmed by scanning electron microscope and Fourier transform infrared spectroscopy analysis. It was ascertained that the most appropriate self-crosslinking acrylate amount and ambient pH level is 10 mL and “2”, respectively, for providing increased abrasion resistance (2,78%) and enhanced self-cleaning properties (363,4%) in the denim samples. The coating reduced the air permeability and softness of the denim samples. Differential scanning calorimetry and thermogravimetry analysis results showed that the treatments increased the crystallization temperatures and melting enthalpy values of the denim samples. Based on the thermal test results, it is clear that mass loss of the denim samples at 370°C decreased as the amount of self-crosslinking acrylate increased (at pH 3).

This study helped us to find out optimum amount of self-crosslinking acrylate and proper pH level for enhanced self-cleaning and abrasion strength on denim fabrics. With this finishing process, an environmentally friendly and long-life denim fabric was designed.

This paper aims to investigate the thermal stability and hydrophobicity of difference alkyl chain of silanes with silicon (Si) micro- and nanoparticles.

Sol-gel methods have been used to design superhydrophobic glass substrates through surface modification by using low-surface-energy Isooctyl trimethoxysilane (ITMS) and Ethyl trimethoxysilane (ETMS) solution. Hierarchical double-rough scale solid surface was built by Si micro- and nanoparticles to enhance the surface roughness. The prepared sol was applied onto glass substrate using dip-coating method and was dried at control temperature of 400°C inside the tube furnace.

The glass substrate achieved the water contact angle as high as 154 ± 2° and 150.4 ± 2° for Si/ITMS and Si/ETMS films, respectively. The Si/ITMS and Si/ETMS also were equipped with low sliding angle as low as 3° and 5°, respectively. The Si micro- and nanoparticles in the coating system have created nanopillars between them, which will suspend the water droplets. Both superhydrophobic coatings have showed good stability against high temperature up to 200°C as there are no changes in WCA shown by both coatings. Si/ITMS film sustains its superhydrophobicity after impacting with further temperature up to 400°C and turns hydrophobic state at 450°C.

Findings will be useful to develop superhydrophobic coatings with high thermal stability.

Sol method provides a suitable medium for the combination of organic-inorganic network to achieve high hydrophobicity with optimum surface roughness.

Application of different alkyl chain groups of silane resin blending with micro- and nanoparticles of Si pigments develops superhydrophobic coatings with high thermal stability.

This paper aims to investigation of processes for Pb²⁺ elimination from water/wastewater as a significant public health issue in many parts of world. The removal of Pb²⁺ ions by various nanocomposites has been explained from water/wastewaters. ZnO-based nanocomposites, as eco-friendly nanoparticles with unique physicochemical properties, have received increased attention to remove Pb²⁺ ions from water/wastewaters.

In this review, different ZnO-based nanocomposites were reviewed for their application in the removal of Pb²⁺ ions from the aqueous solution, typically for wastewater treatment using methodology, such as adsorption. This review focused on the ZnO-based nanocomposites for removing Pb²⁺ ions from water and wastewaters systems.

The ZnO-based nanocomposite was prepared by different methods, such as electrospinning, hydrothermal/alkali hydrothermal, direct precipitation and polymerization. Depending on the preparation method, various types of ZnO-based nanocomposites like ZnO-metal (Cu/ZnO, ZnO/ZnS, ZnO/Fe), ZnO-nonmetal (PVA/ZnO, Talc/ZnO) and ZnO-metal/nonmetal (ZnO/Na-Y zeolite) were obtained with different morphologies. The effects of operational parameters and adsorption mechanisms were discussed in the review.

The findings may be greatly useful in the application of the ZnO-based nanocomposite in the fields of organic and inorganic pollutants adsorption.

The present study is novel, because it investigated the morphological and structural properties of the synthesized ZnO-based nanocomposite using different methods and studied the capability of green-synthesized ZnO-based nanocomposite to remove Pb²⁺ ions as water contaminants.

The current review can be used for the development of environmental pollution control measures.

This paper reviews the rapidly developing field of nanocomposite technology.

This paper aims to investigate the prepared modified alkyd and poly(ester-amide) (PEA) resins as antimicrobial and insecticide binders for surface coating applications.

Salicylic diethanolamine and 4-(N, N-dimethylamino) benzylidene glutamic acid were prepared and used as new sources of polyol and dibasic acid for PEA and alkyd resins, then confirmed by: acid value, FT-IR and 1H-NMR. The coating performance of the resins was determined using measurements of physico-mechanical properties. The biological and insecticide activities of the prepared resins were investigated.

The tests carried out revealed that the modified PEA and alkyd enhanced both phyisco-mechanical and chemical properties in addition to the biological and insecticide activities. The results of this paper illustrate that the introduction of salicylic diethanolamine and 4-(N, N-dimethylamino) benzylidene glutamic acid within the resin structure improved the film performance and enhanced the antimicrobial activity performance of PEA and alkyd resins.

The modified alkyd and PEA organic resins can be used as biocidal binders when incorporated into paint formulations for multiple surface applications, especially those that are exposed to several organisms.

Modified alkyd and PEA resins based on newly synthesized modifiers have a significant potential to be promising in the production and development of antimicrobial and insecticide paints, allowing them to function to restrict the spread of insects and microbial infection.