Concrete-filled double skin steel tubes (CFDST) columns are taken more attention due to their ability to withstand high structural loads in structures such as high-rise buildings, bridges' piers, offshore and marine structures. This paper is intended to improve the CFDST column's capacity without the need to increase the column's size to maintain its lightweight by filling it with self-compacted concrete (SCC) containing nanoclay (NC).

First, experimental investigation is conducted to select the optimal NC percentage that improves the mechanical properties. Different mixing method, mixture ingredients, cement content, and NC percentage are considered. Then, slender and short CFDST columns are tested for axial capacity to investigate the effect of adding the optimum NC percentage on column's capacity and failure mode.

The test results show that adding 3% NC by cement weight using dry mixing method to SCC is the optimum ratio. It is concluded that adding 3% NC by cement weight increased the CFDST column's capacity, especially the specimens with higher slenderness ratio. Moreover, it is concluded that more specimens should be tested under various geometric and reinforcement details.

Recently, CFDST tube columns solve many structural and architectural problems that engineers have encountered in traditional systems. Therefore, more studies are required to design high-performance columns capable of carrying complex loads with high efficiency since the traditional design could not achieve the required performance. Since concrete contributes to a large portion in the axial capacity of the CFDST columns, it is proposed to improve the CFDST column's capacity without the need to increase the column's size to maintain its lightweight by filling it with (SCC containing NC. Previous research has affirmed the effectiveness of employing nanoclay in the concrete's workability, durability, microstructures, and mechanical properties.

This paper aims to achieve an anti-corrosive coating via uniform dispersion of nanoclay particles (montmorillonite) and polypyrrole (PPy) as a conductive polymer as well as their effects on the anti-corrosion features in the presence of the eco-friendly ionic liquids (ILs).

In this research, PPy with different forms of nanoclay were used. Moreover, ILs additive is used to enhance the better dispersion process of clay and PPy nanoparticles in the resin.

As a result, the IL additive in the formulation of nano-composite coatings greatly improves the dispersion process of clay and PPy nanoparticles in the resin. Due to its high compatibility with polyurethane resin and clay and PPy nanoparticles, this additive contains a high dispersing power to disperse the investigated nanoparticles in the resin matrix.

High polarity of ILs as well as abilities to dissolve both mineral and organic materials, they can provide the better chemical processes compared to common solvents.

IL abilities have not been discovered to a large extent such as catalysts and detectors.

ILs have been emerging as promising green solvents to replace conventional solvents in recent years. They possess unique properties such as nonvolatility, low toxicity, ease of handling, nonflammability and high ionic conductivity. Thus, they have received much attention as green media for various chemistry processes.

The simultaneous existence of clay, PPy and IL additive in the nano-composite coating formulation is responsible for the high corrosion resistance of the coating.

The purpose of this paper is to give compiled information on previously applied cotton fabric surface modifications. The paper covered most of the modifications done on cotton fabric to improve its properties or to add some functional properties. The paper presented mostly studied research works that brought a significant surface improvement on cotton fabric.

Different previous works on surface modifications of cotton fabrics such as pilling, wrinkle and microbial resistance, hydrophobicity, cationization, flame retardancy and UV-protection characteristics were studied and their methods of modification including the main findings are well reported in this paper.

Several modification treatments on surface modification of cotton fabrics indicated an improvement in the desired properties in which the modification is needed. For instance, the pilling tendency, wrinkling, microbial degradation and UV degradation drawbacks of cotton fabric can be overcome through different modification techniques.

To the best of the author’s knowledge, there are no compressive documents that covered all the portions presented in this review. The author tried to cover the surface modifications done to improve the main properties of cotton fabric.

The purpose of this paper is to investigate the performance of bio-based lubricants (BBL), namely, palm mid-olein (PMO) enriched with an antioxidant agent, tertiary-butylhydroquinone (TBHQ) and a viscosity improver, ethylene-vinyl acetate (EVA), in journal bearing (JB) applications.

Samples of the BBL were prepared by blending it with TBHQ and EVA at various blending ratios. The oxidative stability (OS) and viscosity of the BBL samples were examined using differential scanning calorimetry and a viscometer, respectively. Meanwhile, their performance in JB applications was evaluated through the use of a JB test rig with a 0.5 length-to-diameter ratio at various operating conditions.

It was found that the combination of PMO + TBHQ + EVA demonstrated a superior oil film pressure and load-carrying capacity, resulting in a reduced friction coefficient and a smaller attitude angle compared to the use of only PMO or VG68. However, it was observed that the addition of TBHQ and EVA to the PMO did not have a significant impact on the minimum oil film thickness.

The results would be quite useful for researchers generally and designers of bearings in particular.

This study used PMO as the base stock, and its compatibility with TBHQ and EVA was investigated in terms of its OS and viscosity. The performance of this treated BBL was evaluated in a hydrodynamic JB.

The peer review history for this article is available at: https://publons.com/publon/10.1108/ILT-11-2023-0363/

The purpose of this study is the development of sustainable and low-formaldehyde emission wood adhesive formulations.

Three-step urea formaldehyde (UF) resin has been in situ modified with calcium lignosulfonate (LS) and/or 1,4 butanediol diglycidyl ether (GE). The structural, chemical, thermal and morphological characterizations were carried out on resin samples. These resins have been applied for particleboard pressing, and UF, UF-LS and UF-GE were evaluated as P2 classes according to EN 312.

The results show that the improved LS- or diglycidyl ether-modified UF wood adhesives were successful in their adhesive capacity, and the formaldehyde content of the final product was obtained as low as 8 mg/100 g. This paper highlights that the presented adhesive formulations could be a potential eco-friendly and cost-effective alternative to formaldehyde-based wood adhesives for interior particleboard production.

Combination of LS and GE resulted in weaker mechanical properties and fulfilled P1 class particleboards due to temperature and duration conditions. Therefore, in situ usage of LS or GE in UF resins is highly recommended for particleboard pressing. Formaldehyde content of particleboards was determined with the perforator method according to EN 12460-5 and all of the particleboards exhibited E1 class. LS was more efficient in decreasing formaldehyde content than GE.

This study provides the application of particleboards with low formaldehyde emission.

The developed LS- and diglycidyl ether-modified UF resins made it possible to obtain boards with significantly low formaldehyde content compared with commercial resins.

The developed formaldehyde-based resin formulation made it possible to produce laboratory-scale board prototypes using LS or GE without sacrificing of press factors and panel quality.

The study aims to assess the efficiency of nanocomposite to improve the properties of gap-filling materials for pottery artifacts.

Five different pastes were used in the laboratory studies. The pastes consist mainly of pottery powder (grog), dental plaster, microballoons and an adhesive of Primal AC33, nano-silica and nano kaolinite in various concentrations. The prepared samples were subjected to accelerated heat and light aging. Besides, some investigations were used to evaluate the efficacy of the additive nanomaterials, such as TEM, digital and scanning electron microscopy microscopes. Contact angle, color change, shrinkage degree, physical properties and compressive strength tests were also conducted.

The results indicated that using Nano-silica considerably improves the mechanical strength and decreases the shrinkage of gap-filling materials. According to the results, a mixture of grog, microballoons and Primal AC33/Nano-silica Nanocomposites is the optimal gap-filling paste for archaeological pottery. Moreover, this paste showed a higher contact angle (120°), lower color change (ΔE = 2.62), lower shrinkage (3.3%), lower water absorption (3.36%), lower porosity (5.05%) and higher compressive strength (5124 N/mm²).

This paper attains to develop an economic polymer-nanocomposite that can be used with gap-filling materials for pottery artifacts.

This study aims to explore the synergistic effect of oxide nanoparticles (ZnO, Fe₂O₃, SiO₂) and cerium nitrate inhibitor on anti-corrosion performance of epoxy coating. First, cerium nitrate inhibitors are absorbed on the surface of various oxide nanoparticles. Thereafter, epoxy nanocomposite coatings have been fabricated on carbon steel substrate using these oxide@Ce nanoparticles as both nano-fillers and nano-inhibitors.

To evaluate the impact of oxides@Ce nanoparticles on mechanical properties of epoxy coating, the abrasion resistance and impact resistance of epoxy coatings have been examined. To study the impact of oxides@Ce nanoparticles on anti-corrosion performance of epoxy coating for steel, the electrochemical impedance spectroscopy has been carried out in 3% NaCl solution.

ZnO@Ce3+ and SiO2@Ce3+ nanoparticles provide more enhancement in the epoxy pore network than modification of the epoxy/steel interface. Whereas, Fe2O3@Ce3+ nanoparticles have more to do with modification of the epoxy/steel interface than to change the epoxy pore network.

Incorporation of both oxide nanoparticles and inorganic inhibitor into the epoxy resin is a promising approach for enhancing the anti-corrosion performance of carbon steel.

This study aims to deal with both the development and mechanical investigations of unsaturated polyester matrix (UPR) composites containing recycled polyethylene terephthalate (PET) fibers as new fillers.

UPR/PET fibers composites have been developed as mats by incorporating 5, 8, 13 and 18 parts per hundred of rubber (phr) of 6-, 10- and 15-mm length PET fibers from the recycling of postconsumer bottles. The mechanical and physical properties of the composites were investigated as a function of fiber content and length. A significant increase in stress at break and in ultimate stress (sr) were observed for composites reinforced with 5 and 8 phr of 15-mm length PET fibers. The Izod impact strength of UPR/mat PET fiber composites as a function of fiber rate and length showed that the 5 and 8 phr composites for the 15-mm length PET fiber have the optimal mechanical properties 13.55 and 10.50 Kj/m², respectively. The morphological study showed that the strong adhesion resulting from the affinity of the PET fiber for the UPR matrix. The ductile fracture of materials reinforced with 5 and 8 phr is confirmed by the fiber deformation and fracture surface roughness.

This study concluded that the PET fiber enhances the properties of composites, a good correlation was observed between the results of the mechanical tests and the structural analysis revealing that for the lower concentrations, the PET fibers are well dispersed into the resin, but entanglements are evidenced when the fiber content increases.

It can be shown from scanning electron microscopy micrographs that the fabrication technique produced composites with good interfacial adhesion between PET fibers and UPR matrix.

This study aims to observe the coloring efficacy of graphite (G) and nano bentonite clay (BCNPs) on the adsorption of Basic Blue 5 dye from residual dye bath solution.

Some factors that affected the adsorption processes were examined and found to have significant impacts on the adsorption capacity such as the initial concentration of G and/or BCNPs (Co: 40–2,320 mg/L), adsorbent bath pH (4–9), shaking time (30–150 min.) and initial dye concentration (40–200 mg/L). The adsorption mechanism of dye by using G and/or BCNPs was studied using two different models (first-pseudo order and second-pseudo order diffusion models). The equilibrium adsorption data for the dye understudy was analyzed by using four different models (Langmuir, Freundlich, Temkin modle and Dubinin–Radushkevich) models.

It has been found that the adsorption kinetics follow rather a pseudo-first-order kinetic model with a determination coefficient (R²) of 0.99117 for G and 0.98665 for BCNPs. The results indicate that the Freundlich model provides the best correlation for G with capacities q_max = 2.33116535 mg/g and R² = 0.99588, while the Langmuir model provides the best correlation for BCNPs with R² = 0.99074. The adsorbent elaborated from BCNPs was found to be efficient and suitable for removing basic dyes rather than G from aqueous solutions due to its availability, good adsorption capability, as well as low-cost preparation.

There is no research limitation for this work. Basic Blue 5 dye graphite (G) and nano bentonite clay (BCNPs) were used.

This work has practical applications for the textile industry. It is concluded that using graphite and nano bentonite clay can be a possible alternative to adsorb residual dye from dye bath solution and can make the process greener.

Socially, it has a good impact on the ecosystem and global community because the residual dye does not contain any carcinogenic materials.

The work is original and contains value-added products for the textile industry and other confederate fields.

One of the low-cost minerals that can be used as reinforcing filler in polymer industry is pumice powder. Pumice is a highly porous volcanic glass formed during explosive eruptions. This pumice has received significant interest because of its large surface area with various polar groups and can be processed easily.

This study is carried out to investigate the effect of partial replacement of silica (as traditional filler) by naturally occurring pumice powder to improve the thermal and mechanical properties of nitrile butadiene rubber cured with electron beam radiation (doses from 25 to 150 kGy).

The results indicated that the addition of pumice powder increase the tensile strength at lower doses up to 75 kGy (especially at concentration of 5 phr). Besides, an improvement in the thermal stability was attained with the addition of pumice powder.

Pumice powder is volcanic-based alumina and silica which is mainly composed of SiO₂. It has porous structure which is formed by dissolved gases precipitated during the cooling as the lava hurtles through air. Due to its porous structure, it has low density and high thermal insulation. It also has high temperature and chemical resistance, for these reasons it became preferable material to be used as filler in the plastic and rubber industry.