The purpose of this paper is to study the Mode I fracture behavior of polycarbonate (PC) parts produced using fused deposition modeling (FDM). The focus of this study is on samples printed along the out-of-plane direction with different raster angles.

Tensile and Mode I fracture tests were conducted. Semi-circular bend specimens were used for the fracture tests, which were printed in four different raster patterns of (0/90), (15/−75) (30/−60) and (45/−45). Moreover, the finite element method (FEM) was used to determine the applicability of linear elastic fracture mechanics (LEFM) for the printed PC parts. The fracture toughness results, as well as the fracture path and the fracture surfaces, were studied to describe the fracture behavior of the samples.

Finite element results confirm that the use of LEFM is allowed for the tested PC samples. The fracture toughness results show that changing the direction of the printed rasters can have an effect of up to 50% on the fracture toughness of the printed parts, with the (+45/−45) and (0/90) orientations having the highest and lowest resistance to crack propagation, respectively. Moreover, except for the (0/90) orientation, the other samples have higher crack resistance compared to the bulk material. The fracture toughness of the tested PC depends more on the toughness of the printed sample, rather than its tensile strength.

The toughness and the energy absorption capability of the printed samples (with different raster patterns) were identified as the main properties affecting the fracture toughness of the AM PC parts. Because the fracture resistance of almost all the samples was higher than that of the base material, it is evident that by choosing the right raster patterns for 3D-printed parts, very high resistance to crack growth may be obtained. Also, using FEM and comparing the size of the plastic zones, it was concluded that, although the tensile curves show nonlinearity, LEFM is still applicable for the printed parts.

The purpose of this paper is to investigate the effect of layer orientation on the tensile, flexural and fracture behavior of additively manufactured (AM) polycarbonate (PC) produced using fused deposition modeling (FDM).

An experimental approach is undertaken and a total number of 48 tests are conducted. Two types of tensile specimens are used and their mechanical behavior and fracture surfaces are studied. Also, circular parts with different layer orientations are printed and two semi-circular bending (SCB) samples are extracted from each part. Finally, the results of samples with different build directions are compared to one another to better understand the mechanical behavior of additively manufactured PC.

The results demonstrate anisotropy in the tensile, flexural and fracture behavior of the additively manufactured PC parts with the latter being less anisotropic compared to the first two. It is also demonstrated that the anisotropy of the elastic modulus is small and can be neglected. Tensile strength ranges from 40 MPa to 53 MPa. At the end, mode I fracture toughness prediction curves are provided for different directions of the FDM samples. Fracture toughness ranges from 1.93 to 2.37 MPa.mm^1/2.

The SCB specimen, a very suitable geometry for characterizing anisotropic materials, was used to characterize FDM parts for the first time. Also, the fracture properties of the AM PC have not been studied by the researchers in the past. Therefore, fracture toughness prediction curves are presented for this anisotropic material. These curves can be very suitable for designing parts that are going to be produced by 3D printing. Moreover, the effect of the area to perimeter ratio on the tensile properties of the printed parts is investigated.

Fused filament fabrication of continuous-fiber-reinforced polymers is a promising technique to achieve customized high-performance composites. However, the off-axis tensile strength (TS) and Mode I fracture toughness of fused filament fabricated (FFFed) continuous-glass-fiber-reinforced (CGFR) nylon are unknown. The purpose of this paper is to investigate the mechanical and fracture behavior of FFFed CGFR nylon with various fiber content and off-axis fiber alignment.

Tensile tests were performed on FFFed CGFR-nylon with 9.5, 18.9 and 28.4 fiber vol. %. TS was tested with fiber orientations between 0^∘ and 90^∘ at 15^∘ intervals. Double cantilever beam tests were performed to reveal the Mode I fracture toughness of FFFed composites.

TS increased with increasing fiber vol. % from 122 MPa at 9.5 vol. % to 291 MPa at 28 vol. %. FFFed nylon with a triangular infill resulted in 37 vol. % porosity and a TS of 12 MPa. Composite samples had 11–12 vol. % porosity. TS decreased by 78% from 291 MPa to 64 MPa for a change in fiber angle θ from 0^∘ (parallel to the tensile stress) to 15^∘. TS was between 27 and 17 MPa for 300 < θ < 900. Mode I fracture toughness of all the composites were lower than ∼332 J/m2.

Practical applications of FFFed continuous-fiber-reinforced (CFR) nylon should be limited to designs where tensile stresses align within 15^∘ of the fiber orientation. Interlayer fracture toughness of FFFed CFR composites should be confirmed for product designs that operate under Mode I loading.

To the best of the authors’ knowledge, this is the first study showing the effects of fiber orientation on the mechanical behavior and effects of the fiber content on the Mode I fracture toughness of FFFed CGFR nylon.

The determination of mode-I fracture toughness of brittle structural materials by means of the notched Brazilian disc configuration is studied. Advantage is taken of a recently introduced analytical solution and, also, of data provided by an experimental protocol with notched marble specimens under diametral compression using the loading device suggested by International Society for Rock Mechanics (ISRM) and also the three-dimensional digital image correlation (3D-DIC) technique.

The analytical solution highlighted the role of geometrical factors, like, for example, the width of the notch, which are usually disregarded. The data of the experimental protocol were comparatively considered with those concerning the response of the specific material under uniaxial tensile load.

This combined study provided interesting data concerning some open issues, as it is the exact crack initiation point and the level of the critical load causing crack initiation. It was definitely indicated that the crack initiation point is not a priori known (even for notched specimens) and, also, that the maximum recorded load does not correspond by default to the critical load responsible for the onset of catastrophic macroscopic fracture.

It was suggested that the load considered critical one for the determination of mode-I fracture toughness K_IC is erroneous. At a load equal to about 70% of the maximum one, a process zone is formed (zone of non-reversible phenomena) around the notch's crown, designating termination of the validity of any linear elastic solution used to determine the normalized stress intensity factors (SIFs). Moreover, at a load level equal to about 95% of the macroscopically observed fracture load, crack propagation has already begun. Therefore, the experimental procedure must be monitored with additional equipment, providing an overview of the displacement field developed during loading.

The purpose of this study was to investigate the effects of CaCO₃ nanoparticles on the mechanical properties, and mixed-mode fracture behavior of acrylonitrile butadiene styrene 3D printed samples with different internal architectures.

The nanocomposite filaments have been fabricated by a melt-blending technique. The standard tensile, compact tension and special fracture test samples, named Arcan specimens, have been printed at constant extrusion parameters and at four different internal patterns. A special fixture was used to carry out the mixed-mode fracture tests of Arcan samples. Finite element analyses using the J-integral method were performed to calculate the fracture toughness of such samples. The fractographic observations were used to evaluate the mechanism of fracture at different concentrations of nanoparticles.

The addition of CaCO₃ nanoparticles has resulted in a significant increase in the fracture loading of the samples, although this increase was not consistent for all the filling patterns, being more significant for samples with linear and triangular structures. According to the fractographic observations, the creation of uniformly distributed microvoids due to the blunting effect of nanoparticles and 3D stress state at the crack tip in the samples with linear and triangular structures justify the enhancement in the fracture loading by the addition of CaCO₃ nanoparticles in the matrix.

There is a significant gap in the knowledge of the effects of different nanoparticles in the polymer samples produced by the fused filament fabrication process. One of such nanoparticles is an inorganic CaCO₃ nanoparticle that has been frequently used as nanofillers to improve the thermomechanical properties of thermoplastic polymers. Here, experimental and numerical studies have been conducted to investigate the effects of such nanoadditives on the mechanical and fracture behavior of 3D printed samples.

Acrylonitrile butadiene styrene (ABS), as a light and high strength thermoplastic polymer, has found extensive applications in different industries. Fused filament fabrication, known as three-dimensional (3D) printing technique is considered a rapid prototyping technique that is frequently applied for production of samples of ABS material. Therefore, the purpose of this study is to investigate the mechanical and fracture behavior of such materials and the techniques to improve such properties.

Experimental and numerical analyses have been conducted to investigate the effects of internal architecture and chopped carbon fiber (CF) fillers on the mechanical properties and mixed mode fracture behavior of the ABS samples made by 3D printing technique. Four different filling types at 70% filling ratios have been used to produce tensile and special fracture test samples with pure and CF filled ABS filaments (CF-ABS) using 3D process. A special fixture has been developed to apply mixed mode loading on fracture samples, and finite element analyses have been conducted to determine the geometric function of such samples at different loading angles.

It has been determined that the printing pattern has a significant effect on the mechanical properties of the sample. The addition of 15% CF to pure ABS resulted in a significant increase in tensile strength of 46.02% for line filling type and 15.04% for hexagon filling type. It has been determined that as the loading angle increases from 0° to 90°, the KIC value decreases. The addition of 15% CF increased the K_IC values for hexagonal and line filling type by 64.14% and 12.5%, respectively.

The damage that will occur in ABS samples produced in 3D printers depends on the type, amount, filling speed, filling type, filling ratio, filling direction and mechanical properties of the additives. All these features are clearly dependent on the production method. Even if the same additive is used, the production method difference shows different microstructural parameters, especially different mechanical properties.

The main aim of this study is to investigate the mixed-mode I/II failure and the cracking manner of three-dimensional (3D)-printed components made by the fused deposition modeling technique in an experimental and theoretical manner.

Acrylonitrile butadiene styrene (ABS) material and a modified printing method (that increases the adhesion and integrity between the layers and strands) are used for manufacturing the semicircular bending (SCB) test samples. In addition to precracking, the effect of additional stress concentration on the stress field is studied by introducing three small holes to the SCB fracture samples. The critical mixed-mode I/II failure loads obtained from the experiments are predicted using different stress/strain-based fracture theories, including maximum tangential stress (MTS), maximum tangential strain (MTSN), generalized form of MTS and MTSN and combination of them with equivalent material concept (EMC). The effects of plastic deformation, as well as the structural stress concentration, are considered for a more realistic prediction of mixed-mode fracture load.

The stress-based criteria are more suitable than the strain-based theories. Among the investigated fracture models, the EMC–generalized maximum tangential stress theory provided the best agreement with the experimental results obtained from 3D-printed SCB tests.

The influences of stress risers and applicability of different failure theories in cracked layered 3D-printed parts are studied on the fracture behavior of tested specimens under mixed-mode I/II.

The main aim of this study is to determine the fracture toughness and accordingly to predict the fracture initiation, crack propagation and mode of crack extension accurately in polypropylene subsea pipes subjected to internal pressure.

Tensile test was performed following the ISO 527–1 standard. An elastic-plastic constitutive model was developed based on the tensile test results, and it is implemented in the FEA model to describe the constitutive behaviour of the polypropylene material. Three-point bend tests with linear-elastic fracture mechanics (LEFM) approach were conducted following ISO-13586 standard, from which the average fracture toughness of the polypropylene pipe material in crack-opening mode was found as KIc = 3.3 MPa√m. A numerical model of the experiments is developed based on the extended finite element method (XFEM), which showed markedly good agreement with the experimental results.

The validated XFEM modelling approach is utilised to illustrate its capabilities in predicting fracture initiation and crack propagation in a polypropylene subsea pipe subjected to an internal pressure containing a semi-elliptical surface crack, which agrees well with existing analytical solutions. The XFEM model is capable of predicting the crack initiation and propagation in the polypropylene pipe up to the event of leakage.

The methodology proposed herein can be utilised to assess the structural integrity and resistance to fracture of subsea plastic pipes subjected to operational loads (e.g. internal pressure).

The purpose of this paper is to assess the quality of adhesively bonded joints using an alternative artificial neural networks (ANN) approach.

Following the necessary surface pre-treatment and bonding process, the coupons were investigated for possible defects using C-scan ultrasonic inspection. Afterwards, the damage severity factor (DSF) theory was applied in order to quantify the existing damage state. A series of G _IC mechanical tests was then conducted so as to assess the fracture toughness behavior of the bonded samples. Finally, the data derived both from the NDT tests (DSF) and the mechanical tests (fracture toughness energy) were combined and used to train the ANN which was developed within the present work.

Using the developed neural network (NN) the bonding quality, in terms not only of defects but also of fracture toughness behavior, can be accessed through NDT testing, minimizing the need for mechanical tests only in the initial material characterization phase.

The innovation of the paper stands on the feasibility of an alternative approach for assessing the quality of adhesively bonded joints using and ANNs, thus minimizing the necessary testing effort.

Engineered stone is a material which can be described as an artificial stone. The exemplary application area is sink production. There are very few research projects about this type of material. In fact, most of them are research conducted by the manufacturing company, which are limited to the basic properties of the material. However, knowledge about fracture mechanic of this material may be crucial in terms of usage. The paper aims to discuss this issue.

Analysis of the inside structure was made using an optical microscope as well as SEM. In the paper, methods which can be used to obtain data about fracture behaviour of material are presented. Using eXtended Finite Element Method and experimental data from three-point bending of notched specimens stress intensity factors (SIFs) for I and II load modes were obtained. Finally, a comparison between the fracture initiation angle in the function of the ration of SIFs for I/II load modes and maximum tangential stress hypothesis prediction was presented.

Analysis of the inside structure proves that this type of material has an uneven distribution of particle size. This can follow to void and micronotches formation and, later, to the failure of the material. A method of obtaining stress intensity factors for the discussed type of material and specimens can be successfully applied to other similar material, as proposed in this work. Standard crack angle propagation criteria are not sufficient for this type of material.

There are very few research papers about this type of material. The subject of fracture mechanic is not properly discovered, despite the fact that IT is important in terms of the application area of these materials.