The purpose of this paper is to based upon the joining and characterization (mechanical and metallurgical) of ferritic stainless steel (SS)-430 using a microwave hybrid heating (MHH) phenomenon.

The preliminary experiments were conducted using nickel-based powder as interface material using a domestic microwave oven at a frequency of 2.45 GHz and 900 W power for 720 s. The processed joint was metallurgically characterized by means of X-ray diffraction, Energy-dispersive X-ray spectroscopy and Field emission scanning electron microscopy. Mechanical characterization was done by means of tensile and Vickers’ microhardness testing to check the hardness and strength of the joint.

The metallurgical study revealed that the microstructure and formation of numerous phases of Fe₂Si₃ accompanied by chromium and nickel carbides. The average hardness of 359 Hv at the center of the joint and 637 Hv around the boundaries of the joint was observed. The tensile strength of the joint was observed to 471 MPa with an elongation of 9.02%. The worn surface of the joint signifies the presence of plastic deformation and it was limited due to the presence of harder phases such as Ni₃Si and Ni₃C.

The concept of microwave joining of metals is a very challenging task as the temperature can not be controlled in the inert atmosphere of the microwave. It has been also observed that at certain elevated temperatures, the material starts absorbing the microwaves; which is unknown. So, a more intensive study is required to overcome these kinds of limitations.

MHH technique can be used to process different materials such as ceramics, composites and polymers. SS-430 joined by microwave heating is highly corrosion resistive and has wide applications in refrigerators cabinet panels, dishwasher linings, chimney liners, lashing wires, etc.

As of the author’s best knowledge, no work has been reported on the joining of SS-430 which has huge potential in the industries. Also, no work has been reported on the characterization of microwave joined SS-430.

This paper aims to concentrate on research that has been conducted in the previous decade on metamaterial (MTM)-based sensors for material characterization, which includes solid dielectrics, micro fluids and biomolecules.

There has been a vast advancement in sensors based on MTM since the past few decades. MTM elements provide a sensitive response to materials while having a tiny footprint, making them an appealing alternative for realizing diverse sensing devices.

Related research papers on MTM sensors published in reputable journals were reviewed in this report, with a specific emphasis on the structure, size and nature of the materials characterized. Because electromagnetic wave interaction excites MTM structures, sensing applications around the electromagnetic spectrum are possible.

The paper contains valuable information on MTM sensor technology for material characterization, and this study also highlights the challenges and approaches that will guide future development.

Stability of a nonlinear, tuned amplifier has been investigated based on the describing function method. On stability, this paper means global asymptotic stability. The tuned amplifier comprises a saturated amplifying device with feedback and two resonators, at the input and the output. Describing function method here means introduction of the two-port describing functions.

Describing function method is applied, extended for two ports. Results from complex analysis and matrix algebra are heavily used. The two resonators have identical resonant frequency and bandwidth. Instability is represented by non-vanishing output perturbation for zero-input perturbation. Applying a simple transistor model with saturation and feedback, stability is analyzed in the form of output voltage as a function of input voltage.

Two-port scattering and admittance describing functions have been introduced. At a certain input voltage amplitude, instability appears in the form of unwanted sidebands, then at a higher input voltage, instability disappears, in good agreement with experiments. The hand calculated stability limits are in good agreement with the computer analysis.

The paper is based on an early publication of the author (Baranyi and Ladvánszky, 1984). Here, the full material is presented, explained step by step, extended and revised. All neglections that were earlier made in the author’s paper have been avoided here. This paper has significant tutorial value as well.

The dielectric properties of materials (complex permittivity) can be deduced from the admittance measured at the discontinuity plane of a coaxial open‐ended probe. This implies the implementation of an inversion procedure. The purpose of this paper is to develop a new non‐iterative inversion methodology in the field of microwave characterization allowing reducing the computation cost comparatively to iterative procedures.

The inversion methodology combines the support vector machine (SVM) technique and the finite element method (FEM). The SVM are used as inverse models. They show good approximation and generalization capabilities. FEM allows the generation of the data sets required by the SVM parameter adjustment. A data set is constituted of input (complex admittance and frequency) and output (complex permittivity) pairs.

The results show the applicability of SVM to solve microwave inverse problems instead of using traditional iterative inversion methods which can be very time‐consuming. The experimental results demonstrate the accuracy which can be provided by the SVM technique.

The paper allows extending the capability of microwave characterization cells developed at Laboratoire de Génie Électrique de Paris.

A new inversion method is developed and applied to microwave characterization. This new concept introduces SVM in the context of microwave characterization. SVM results and iterative inversion procedure results are compared in order to evaluate the effectiveness of the developed technique.

The principle of microwave characterization of dielectric materials using open-ended coaxial line probe is to link the dielectric properties of the sample under test to the measurements of the probe admittance (Y(f) = G(f)+ jB(f )). The purpose of this paper is to develop an alternative inversion tool able to predict the evolution of the complex permittivity (ε = ε′ – jε″) on a broad band frequency (f from 1 MHz to 1.8 GHz).

The inverse problem is solved using adaptive network based fuzzy inference system (ANFIS) which needs the creation of a database for its learning. Unfortunately, train ANFIS using f, G and B as inputs has given unsatisfying results. Therefore, an inputs selection procedure is used to select the three optimal inputs from new inputs, created mathematically from original ones, using the Jang method.

Inversion results of measurements give, after training, in real time the complex permittivity of solid and liquid samples with a very good accuracy which prove the applicability of ANFIS to solve inverse problems in microwave characterization.

The originality of this paper consists on the use of ANFIS with input selection procedure based on the Jang method to solve the inverse problem where the three optimal inputs are selected from 26 new inputs created mathematically from original ones (f, G and B).

The transparency of wood to microwave radiation is subject to changes in the wood's properties caused by softening of the wood material during fungal attack or the addition of moisture. A prototype microwave system that measures microwave attenuation and phase delay between two antennae was developed to detect fungal decay in wood at equilibrium moisture content. A total of twelve wooden stakes of 200 x 65 x 65 mm Pinus radiata (softwood) and twelve stakes of Eucalyptus regnans (hardwood) of the same dimensions were exposed to soil containing decay fungi for 12, 16, 20 and 24 weeks in an Accelerated Field Simulator (AFS), which is a climate conditioned room that simulates humid tropical conditions. A control set of three stakes of each wood type was also included in the experiment. Samples were washed and dried in an oven before testing with the prototype system. Orienting the antennae such that the microwave field was perpendicular to the wood grain could not distinguish between sound and decayed wood; however orienting the antennae so that the microwave fields were parallel to the wood grain and having the antennae pressed against the wood sample easily distinguished between sound wood and decayed wood. The phase delay data could not distinguish between sound or decayed wood.

This paper aims to focus on research work related to metamaterial-based sensors for material characterization that have been developed for past ten years. A decade of research on metamaterial for sensing application has led to the advancement of compact and improved sensors.

In this study, relevant research papers on metamaterial sensors for material characterization published in reputed journals during the period 2007-2018 were reviewed, particularly focusing on shape, size and nature of materials characterized. Each sensor with its design and performance parameters have been summarized and discussed here.

As metamaterial structures are excited by electromagnetic wave interaction, sensing application throughout electromagnetic spectrum is possible. Recent advancement in fabrication techniques and improvement in metamaterial structures have led to the development of compact, label free and reversible sensors with high sensitivity.

The paper provides useful information on the development of metamaterial sensors for material characterization.

The purpose of this study is to introduce a new type of sensor which uses microwave metamaterials and direct-coupled split-ring resonators (DC-SRRs) to measure the dielectric properties of solid materials in real time. The sensor uses a transmission line with a bridge-type structure to measure the differential frequency, which can be used to calculate the dielectric constant of the material being tested. The study aims to establish an empirical relationship between the dielectric properties of the material and the frequency measurements obtained from the sensor.

In the proposed design, the opposite arm of the bridge transmission line is loaded by DC-SRRs, and the distance between DC-SRRs is optimized to minimize the mutual coupling between them. The DC-SRRs are loaded with the material under test (MUT) to perform differential permittivity sensing. When identical MUT is placed on both resonators, a single transmission zero (notch) is obtained, but non-identical MUTs exhibit two split notches. For the design of differential sensors and comparators based on symmetry disruption, frequency splitting is highly useful.

The proposed structure is demonstrated using electromagnetic simulation, and a prototype of the proposed sensor is fabricated and experimentally validated to prove the differential sensing principle. Here, the sensor is analyzed for sensitivity by using different MUTs with relative permittivity ranges from 1.006 to 10 and with a fixed dimension of 9 mm × 10 mm ×1.2 mm. It shows a very good average frequency deviation per unit change in permittivity of the MUTs, which is around 743 MHz, and it also exhibits a very high average relative sensitivity and quality factor of around 11.5% and 323, respectively.

The proposed sensor can be used for differential characterization of permittivity and also as a comparator to test the purity of solid dielectric samples. This sensor most importantly strengthens robustness to environmental conditions that cause cross-sensitivity or miscalibration. The accuracy of the measurement is enhanced as compared to conventional single- and double-notch metamaterial-based sensors.

The purpose of this paper was to determine the complex permittivity of bismuth strontium manganites (Bi_1−xSr_xMnO₃) in the 8‐12 GHz range by using perturbation of Ag thick film microstrip ring resonator (MSRR) due to superstrate of both bulk and thick film.

The BSM ceramics were synthesized by simple low cost solid state reaction method and their fritless thick films were fabricated by screen printing technique on alumina substrate. A comparison has been made between the X band response of Ag thick film microstrip ring resonator due to perturbation of bulk and thick film Bi_1−xSr_xMnO₃ ceramic.

The bulk and thick film superstrate decreases the resonance frequency of MSRR. In this technique even minor change in the properties of superstrate material changes the MSRR response. Variation of strontium content also influences microwave conductivity and penetration depth of bulk and thick films.

The microwave complex permittivity decreases with increase in Sr content in bismuth manganite and it is higher for bulk as compared to its thick films. The superstrate on Ag thick film microstrip ring resonator is an efficient tool capable of detecting the composition dependent changes in microwave properties of ceramic bulk and thick films.

The purpose of this study to investigate the organized porous network zinc (OPNZ) scaffolds. Their mechanical characteristics, surface roughness and fracture mechanism were assessed in relation to their structural properties. The prospects of fused deposition modeling (FDM) for printing metal scaffolds via rapid tooling have also been studied.

Zn scaffolds with different pore and strut sizes were manufactured via the rapid tooling method. This method is a multistep process that begins with the 3D printing of a polymer template. Later, a paraffin template was obtained from the prepared polymer template. Finally, this paraffin template was used to fabricate the Zn scaffold using microwave sintering. The characterization of prepared Zn samples involved structural characterization, microstructural study, surface roughness testing and compression testing. Moreover, based on the Gibson–Ashby model analysis, the model equations’ constant values were evaluated, which can help in predicting the mechanical properties of Zn scaffolds.

The scanning electron microscopy study confirmed that the fabricated sample pores were open and interconnected. The X-ray diffraction analysis revealed that the Zn scaffold contained hexagonal closed-packed Zn peaks related to the a-Zn phase, validating that scaffolds were free from contamination and impurity. The range for ultimate compressive strength, compressive modulus and plateau stresses for Zn samples were found to be 6.75–39 MPa, 0.14–3.51 GPa and 1.85–12.6 MPa by adjusting their porosity, which are comparable with the cancellous bones. The average roughness value for the Zn scaffolds was found to be 1.86 µm.

This research work can widen the scope for extrusion-based FDM printers for fabricating biocompatible and biodegradable metal Zn scaffolds. This study also revealed the effects of scaffold structural properties like porosity, pore and strut size effect on their mechanical characteristics in view of tissue engineering applications.