The purpose of this paper is to investigate the influence of silver nanoparticle additions on the wetting properties of Sn‐Ag‐Cu (SAC) solder paste. In this investigation, the basic solder paste contained 85 wt.% of commercial Sn 96.5 Ag 3 Cu 0.5 powder (with the particle sizes in the range of 20‐38 μm) and 15 wt.% of self‐prepared middle activated rosin flux. To this paste was added 0.5, 1, 2 and 4 wt.% of self‐prepared silver nano‐powders of different grain sizes (from 9 to 138 nm). After the pastes had stabilized, their wetting properties were tested. The main goal of these investigations was to improve the wetting properties of SAC solder paste and to find correlations between the results of the wetting of solder paste with nanoparticles on the copper substrate with the microstructure of the solder joints.

The following methods were applied for the wetting solder paste investigation: spreading on the copper substrate, contact angle measurement on the copper and wetting on a FR‐4 laminate double sided with an 18‐μm thick copper foil. The investigations were performed at temperatures of 220, 230, 240 and 250°C. Cross‐sectioning was performed on the solder paste after reflow on the copper substrate. For the microstructural analysis of the “nano” modified solder joints obtained at 250°C, standard metallographic procedures were applied. Changes in the microstructure, the thickness of the inter‐metallic compounds (IMCs) and their chemical compositions were observed by means of scanning electron microscope (SEM) and energy dispersive spectroscopy (EDS).

As expected, a higher silver nanoparticle addition to the SAC solder paste resulted in better wetting properties on copper. The results indicated the possibility of an improvement of the reflow soldering process by using SAC solder paste with silver nanoparticles and by lowering its soldering temperature. An improvement was also observed in the wettability with a decrease in the silver nanoparticle grain size. Also, the wettability proceeded at a lower temperature (20°C lower) than that for the SAC paste, without the nano‐additives. For the 4 per cent silver nanoparticle addition, Ag₃Sn star‐like IMCs were also found, which grew with the lowering of the silver nanoparticle grain size.

Further studies are necessary for confirmation of the practical application, especially of the mechanical properties, as well as the reliability properties of the solder joints, for the chosen solder paste with silver nanoparticles.

Taking into account the wetting data, the best results of the “nano” SAC solder pastes were obtained for the highest addition of the silver nanoparticles. It was found that the spreading on copper was higher and the contact angles were lower for the SAC solder paste with 4 per cent (by wt.) of 138‐nm grain size silver nanoparticles. A comparison of SAC solder pastes with a 4 per cent silver nanoparticle addition but of a different grain size (138‐9 nm), suggested a further improvement in wetting properties with lowering of the silver nanoparticle grain size. The results suggested the possibility of an improvement in the reflow soldering process by using SAC solder paste with silver nanoparticles and by lowering its soldering temperature.

Spreading, wetting and contact angle measurement methods were used for the wetting determination of the SAC solder paste with the silver nanoparticles on copper under the same temperature conditions. Also, the microstructure of the solder joints obtained at 250°C was determined with the use of SEM and EDS methods. The results obtained made it possible to draw conclusions regarding the correlation between the output of the wetting results and the amount and the grain size of the added silver nanoparticles, and also the microstructure and thickness of the IMCs of the “nano” solder joints.

The purpose of this paper is to focus on the fabrication of SnAgCu (SAC) nanocomposites solder and study the effect of Cu nanopowders (nano-Cu) addition on the microstructure evolution of resultant nanocomposite solder after reflow and thermal aging.

Mechanical mixing is used in this work to incorporate nanoparticles into the solder and produce more homogeneous mixture. Standard metallographic procedures are applied for microstructural analysis of solder joints.

It is found that nano-Cu doped into Sn0.7Ag0.5Cu-BiNi solder has no appreciable influence on melting temperature of the composite solder. The addition of Cu nanoparticles refines the microstructure of bulk solder and suppresses the growth of interfacial intermetallic compound (IMC) layers. However, interfacial IMC grain size increases slightly after 1.0 per cent nano-Cu added.

The paper demonstrates a method of nano-composite solder paste preparation by means of mechanical mixing and a comparison study of the microstructure evolution of composite solder with the basic SAC solder.

The purpose of this work is to investigate the influence of carbon nanotube additions to solder paste on the solder joints mechanical strength and their microstructure. In our investigation, the basic solder paste contains 85 wt.% of the commercial Sn96.5Ag3Cu0.5 powder (with the particle sizes in the range of 20‐38 μm) and 15 wt.% of the self‐prepared middle activated rosin flux. To this paste we added the 0.01, 0.05 and 0.1 wt.% of the self‐modified CNT by functionalized them by mineral acid and than esterificated by methanol (FCNT_Met) or polyethylene glycol 400 (FCNT_PG). After the pastes had stabilized, the reflow soldering process of “zero ohm” chip resistors on PCBs with Ni/Au and SAC (HASL) finishes was carried out and then shear strength of the solder joints was measured. The correlations between the mechanical strength of solder joins without and with the carbon nanotubes and their microstructure were analysed.

For shear strength measurement of solder joints, the printed circuit boards with Ni/Au and SAC (HASL) finishes was applied. The SAC solder paste with different carbon nanotubes and the basic SAC solder paste as reference were used for this experiment. The automatic SMT line was applied for the paste screen printing; “zero ohms” chip resistors: 0201, 0402, 0603 and 0805 were placing on PWBs and then reflowing according to appropriate time – temperature profile. The shear strength of the solder joints was measured. For the solder joints microstructure analysis, the standard metallographic procedures were applied. Changes in the microstructure, the thickness of the intermetallic compounds and their chemical compositions were observed by means of the SEM equipped with EDS.

As the authors expected, the SAC solder paste with the carbon nanotubes addition improve the solder joints shear strength of the chip resistors mounted on PCBs with Ni/Au and SAC (HASL) finishes. The carbon nanotubes addition positive effects on IMCs thickness because of blocking their excessive growth.

It is suggested that further studies are necessary for the confirmation of the practical application, especially of the reliability properties of the solder joints obtained using solder paste with chosen carbon nanotubes.

Taking into account the shear strength data, the best results of the “nano” SAC solder pastes were obtained for the lowest addition of the carbon nanotubes modified by esterification process, especially by the methanol compared to the polyethylene glycol 400.

The obtained results made it possible to draw conclusions regarding the correlation between the output of the mechanical results and the amount of the added carbon nanotubes, and also the microstructure and thickness of the IMCs of the “nano” solder joints. It can be useful from practical point of view.

This paper aims to investigate the characteristics of ultra-fine lead-free solder joints reinforced with TiO₂ nanoparticles in an electronic assembly.

This study focused on the microstructure and quality of solder joints. Various percentages of TiO₂ nanoparticles were mixed with a lead-free Sn-3.5Ag-0.7Cu solder paste. This new form of nano-reinforced lead-free solder paste was used to assemble a miniature package consisting of an ultra-fine capacitor on a printed circuit board by means of a reflow soldering process. The microstructure and the fillet height were investigated using a focused ion beam, a high-resolution transmission electron microscope system equipped with an energy dispersive X-ray spectrometer (EDS), and a field emission scanning electron microscope coupled with an EDS and X-ray diffraction machine.

The experimental results revealed that the intermetallic compound with the lowest thickness was produced by the nano-reinforced solder with a TiO₂ content of 0.05 Wt.%. Increasing the TiO₂ content to 0.15 Wt.% led to an improvement in the fillet height. The characteristics of the solder joint fulfilled the reliability requirements of the IPC standards.

This study provides engineers with a profound understanding of the characteristics of ultra-fine nano-reinforced solder joint packages in the microelectronics industry.

The findings are expected to provide proper guidelines and references with regard to the manufacture of miniaturized electronic packages. This study also explored the effects of TiO₂ on the microstructure and the fillet height of ultra-fine capacitors.

This study aims to investigate the NiO nano-reinforced solder joint characteristics of ultra-fine electronic package.

Lead-free Sn-Ag-Cu (SAC) solder paste was mixed with various percentages of NiO nanoparticles to prepare the new form of nano-reinforced solder paste. The solder paste was applied to assemble the ultra-fine capacitor using the reflow soldering process. A focussed ion beam, high resolution transmission electron microscopy system equipped with energy dispersive X-ray spectroscopy (EDS) was used in this study. In addition, X-ray inspection system, field emission scanning electron microscopy coupled with EDS, X-ray photoelectron spectroscopy (XPS) and nanoindenter were used to analyse the solder void, microstructure, hardness and fillet height of the solder joint.

The experimental results revealed that the highest fillet height was obtained with the content of 0.01 Wt.% of nano-reinforced NiO, which fulfilled the reliability requirements of the international IPC standard. However, the presence of the NiO in the lead-free solder paste only slightly influenced the changes of the intermetallic layer with the increment of weighted percentage. Moreover, the simulation method was applied to observe the distribution of NiO nanoparticles in the solder joint.

The findings are expected to provide a profound understanding of nano-reinforced solder joint’s characteristics of the ultra-fine package.

The purpose of this paper is to study the manufacturing of SAC 305 solder paste with multiwall carbon nanotubes (MWCNT) before and after structure modification and also to investigate the added carbon nanotubes' influence on the technological properties and the microstructure of “nano” solder pastes. This work is a continuation of similar previous studies of SAC solder pastes with silver nanopowder additions.

The authors applied functionalization and esterification methods for the structural modification of the carbon nanotubes. The “nano” solder paste preparation was performed with the use of a two‐stage method of carbon nanotube dispersion in “own‐manufactured” SAC 305 solder paste. To determine the technological properties of the “nano” solder paste, slump, solder ball, wetting and spreading tests were applied according to the existing standards. Standard metallographic procedures were applied for microstructural analysis.

As expected on the basis of the previous studies of SAC solder pastes with silver nanopowders, positive results were obtained for the own‐manufactured SAC 305 solder paste with carbon nanotubes by applying the dispersion method. Also applied were functionalization and esterification methods, whose results showed microstructural changes in the carbon nanotubes. The “nano” SAC solder pastes showed a positive influence on the slump properties, compared to the basic SAC solder paste. The authors proved a negative influence of the carbon nanotubes' addition (dependent on their concentration) on the spreading and wetting of the SAC solder paste on a copper substrate, which provoked the non‐wetting and dewetting phenomena. A slight improvement was observed for the “nano” SAC solder pastes with modified carbon nanotubes. The carbon nanotubes' presence in the solder paste showed a positive effect on the growth reduction of the IMCs' thickness, which depended on the type.

The authors intend to verify the reinforcement effect of the alloys with carbon nanotubes suggested in the literature (the aim of Part II). For this purpose, an assembly process with RC electronic elements on PCBs with Ni/Au and SAC (HASL) finishes will be performed, with the use of the SAC 305 solder paste with modified carbon nanotubes, for the purpose of reflow soldering. Next, measurements of the mechanical strength of the solder joints and their microstructures will be conducted.

It is suggested that further studies of the mechanical properties and the reliability of solder joints are necessary for the practical implementation of the “nano” SAC solder pastes, but taking into account the wetting data, the investigation should be performed only for “nano” pastes with the lowest additions of modified carbon nanotubes.

The paper demonstrates a method of “nano” solder paste preparation by means of a two‐stage dispersion of carbon nanotubes in the own‐manufactured SAC 305 solder paste and a comparison study of the properties of “nano” pastes with the basic SAC solder paste.

The purpose of this paper is to investigate the creep properties of Sn‐0.7Cu composite solder joints reinforced with optimal nano‐sized Ag particles in order to improve the creep performance of lead‐free solder joints by a composite approach.

The composite approach has been considered as an effective method to improve the creep performance of solder joints. Nano‐sized Ag reinforcing particles were incorporated into Sn‐0.7Cu solder by mechanically mixing. A systematic creep study was carried out on nano‐composite solder joints reinforced with optimal nano‐sized Ag particles and compared with Sn‐0.7Cu solder joints at different temperatures and stress levels. A steady‐state creep constitutive equation for nano‐composite solder joints containing the best volume reinforcement was established in this study. Microstructural features of solder joints were analyzed to help determine their deformation mechanisms during creep.

The creep activation energies and stress exponents of Ag particle‐enhanced Sn‐0.7Cu lead‐free based composite solder joints were higher than those of matrix solder joints under the same stress and temperature. Thus, the creep properties of nano‐composite solder joints are better than those of Sn‐0.7Cu solder joints.

The findings indicated that nano‐sized Ag reinforcing particles could effectively improve the creep properties of solder joints. A new steady‐state creep constitutive equation of nano‐composite solder joints was established. Deformation mechanisms of Sn‐0.7Cu solder and nano‐composite solder joints during creep were determined.

The purpose of this paper is to develop a new composite solder to improve the reliability of composite solder joints. Nano-particles modified multi-walled carbon nanotubes (Ni-MWCNTs) can indeed improve the microstructure of composite solder joints and improve the reliability of solder joints. Although many people have conducted in-depth research on the composite solder of Ni-MWCNTs. However, no one has studied the performance of Ni-MWCNTs composite solder under different aging conditions. In this article, Ni-MWCNTs was added to Sn-Ag-Cu (SAC) solder, and the physical properties of composite solder, the microstructure and mechanical properties were evaluated.

In this study, the effect of different aging conditions on the intermetallic compound (IMC) layer growth and shear strength of Ni-modified MWCNTs reinforced SAC composite solder was studied. Compared with SAC307 solder alloy, the influence of Ni-MWCNTs with different contents (0, 0.1 and 0.2 Wt.%) on composite solder was examined. To study the aging characteristics of composite solder joints, the solder joints were aged at 80°C, 120°C and 150°C.

The experimental results show that the content of Ni-MWCNTs affects the morphology and growth of the IMC layer at the interface. The microhardness of the solder increases and the wetting angle decreases. After aging at moderate (120°C) and high temperature (150°C), the morphology of the Cu6Sn5 IMC layer changed from scallop to lamellar and the grain size became coarser. The following two different phase compositions were observed in the solder joints with Ni-MWCNTs reinforcement: Cu3Sn and (Cu, Ni)6Sn5. The fracture surface of the solder joints all appeared ductile dents, and the size of the pits increased significantly with the increase of the aging temperature. Through growth kinetic analysis, Ni-modified MWCNTs in composite solder joints can effectively inhibit the diffusion of atoms in solder joints. In short, when the addition amount of Ni-MWCNTs is 0.1 Wt.%, the solder joints exhibit the best wettability and the highest shear strength.

In this study, the effects of aging conditions on the growth and shear strength of the IMC layer of Ni modified MWCNTs reinforced SAC307 composite solder were studied. The effects of Ni MWCNTs with different contents (0, 0.1 and 0.2 Wt.%) on the composite solder were examined.

Recently nanoparticles reinforced lead free solders are vastly developed in electronics packaging industry. Studies and investigations have been conducted to learn and investigate the types, properties, method, availability and importance of nanoparticles in this field.

Mechanical properties, melting temperature and microstructural conditions are taken into major considerations in any of the preparation on nanoparticles and being reviewed in this paper. Segregation of the types of nanoparticles being added together with their properties is summarized in this paper. High temperature reliability is crucial in providing a good viable solder and hence addition of nanoparticles have been seen to give a positive outcome in this particular property.

This paper reviews on the beneficial of the various nanoparticles addition in the solder. Briefed explanations and the factors are revealed in this review.

This paper reviews on the beneficial of the various nanoparticles addition in the solder.

The research on lead-free solder alloys has increased in past decades due to awareness of the environmental impact of lead contents in soldering alloys. This has led to the introduction and development of different grades of lead-free solder alloys in the global market. Tin-silver-copper is a lead-free alloy which has been acknowledged by different consortia as a good alternative to conventional tin-lead alloy. The purpose of this paper is to provide comprehensive knowledge about the tin-silver-copper series.

The approach of this study reviews the microstructure and some other properties of tin-silver-copper series after the addition of indium, titanium, iron, zinc, zirconium, bismuth, nickel, antimony, gallium, aluminium, cerium, lanthanum, yttrium, erbium, praseodymium, neodymium, ytterbium, nanoparticles of nickel, cobalt, silicon carbide, aluminium oxide, zinc oxide, titanium dioxide, cerium oxide, zirconium oxide and titanium diboride, as well as carbon nanotubes, nickel-coated carbon nanotubes, single-walled carbon nanotubes and graphene-nano-sheets.

The current paper presents a comprehensive review of the tin-silver-copper solder series with possible solutions for improving their microstructure, melting point, mechanical properties and wettability through the addition of different elements/nanoparticles and other materials.

This paper summarises the useful findings of the tin-silver-copper series comprehensively. This information will assist in future work for the design and development of novel lead-free solder alloys.