1 – 5 of 5Audu Ibrahim Ali, Mohd Kameil Abdul Hamid, Mohd Azman Bin Abas, Mohd Farid Muhamad Said, Anthony Chukwunonso Opia, Izhari Izmi Bin Mazali and Zul Hilmi Bin Che Daud
Due to the environmental issues caused by petroleum lubricants used in lubrication, the concept of creating various bio-lubricants requires research globally. Thus, this study…
Abstract
Purpose
Due to the environmental issues caused by petroleum lubricants used in lubrication, the concept of creating various bio-lubricants requires research globally. Thus, this study aims to develop, characterize and test the base ficus carica oil (fig oil) for its ethylene vinyl acetate copolymer (EVA) and sodium dodecylbenzene sulfonate (SDBS) content.
Design/methodology/approach
The sample characterization was done using the Fourier transmission infrared spectrum, whereas the morphologies of the EVA, SDBS particles and lubricated surfaces were carried out under scanning electron microscope equipment. To ensure the homogeneity of the solution (base oil and additives), the formulations were subjected to the sonication process. The anti-friction and anti-wear properties of EVA and SDBS particles as lubricant additives were investigated using a ball on a flat high-frequency reciprocating rig tribo-tester.
Findings
According to the findings, the base oil’s anti-friction and anti-wear capabilities can be greatly enhanced by the additions. revealed that the best results were obtained when 1.2% EVA + 2% SDBS was applied for the examination of wear (597.8 µm) and friction coefficient (0.106). Commercial references were used, nevertheless, and the results were excellent. This is because the particles in the contact area during lubrication have strong solubility and quickly penetrate the contact zone. The lubricating mechanisms were explained by a tribological model of the EVA + SDBS and SDBS particles.
Research limitations/implications
The coefficient of friction and wear reduction caused by the use of the additives will certainly enhance system performance and protect the machine components from excessive wear that could cause damage or failure.
Originality/value
The originality and uniqueness of this work are officially affirmed by the authors. The authors’ autonomous and original contribution to the development of sustainable lubrication is represented in this work. To the best of the authors’ knowledge, no other study has been published or made publicly available that duplicates the precise scope and goals of our research, and this conclusion is based on a thorough literature assessment.
Details
Keywords
Ziyan Lu, Feng Qiu, Hui Song and Xianguo Hu
This paper aims to solve the problems molybdenum disulfide (MoS2) nanosheets suffer from inadequate dispersion stability and form a weak lubricating film on the friction surface…
Abstract
Purpose
This paper aims to solve the problems molybdenum disulfide (MoS2) nanosheets suffer from inadequate dispersion stability and form a weak lubricating film on the friction surface, which severely limits their application as lubricant additives.
Design/methodology/approach
MoS2/C60 nanocomposites were prepared by synthesizing molybdenum disulfide (MoS2) nanosheets on the surface of hydrochloric acid-activated fullerenes (C60) by in situ hydrothermal method. The composition, structure and morphology of MoS2/C60 nanocomposites were characterized. Through the high-frequency reciprocating tribology test, its potential as a lubricant additive was evaluated.
Findings
MoS2/C60 nanocomposites that were prepared showed good dispersion in dioctyl sebacate (DOS). When 0.5 Wt.% MoS2/C60 was added, the friction reduction performance and wear resistance improved by 54.5% and 62.7%, respectively.
Originality/value
MoS2/C60 composite nanoparticles were prepared by in-situ formation of MoS2 nanosheets on the surface of C60 activated by HCl through hydrothermal method and were used as potential lubricating oil additives.
Peer review
The peer review history for this article is available at: https://publons.com/publon/10.1108/ILT-10-2023-0321/
Details
Keywords
This paper aims to extracted sericin from the cocoons of Bombyx mori silkworms, and sericin powder was applied onto drawn textured polyethylene terephthalate (PET) yarns as a spin…
Abstract
Purpose
This paper aims to extracted sericin from the cocoons of Bombyx mori silkworms, and sericin powder was applied onto drawn textured polyethylene terephthalate (PET) yarns as a spin finish. The reactivity on the surface of PET yarns was analyzed through Fourier transform infrared spectrophotometry–attenuated total reflectance (FTIR-ATR) and dyeing with methylene blue as a reactive dye. Also, investigations were conducted on the effects of sericin, citrc acid (CA) (as a crosslinking agent), and sodium hypophosphite (as a catalyst) concentrations on some properties of false-twist textured PET yarns.
Design/methodology/approach
A false-twist texturing machine (Scragg-Shirley minibulk, England) was used with the draw ratio of 1.05, heating temperature of 120°C, texturing speed of 100 m min−1 and applied twist of 3,000 TPM. The aqueous extraction of sericin was carried out by the boiling of the raw silk in distilled water with L:R: 40:1 for 120 min. The aqueous solution was filtered with a filter paper to remove the impurities and insoluble fibroin. Finally, the sericin solution was freeze-dried to obtain the sericin powder. The sericin solution was applied on the drawn textured PET yarns using the “pad-dry-cure” method.
Findings
Sericin fixation onto the PET yarns was confirmed by FTIR-ATR. The results showed that there were no significant changes in the tensile strength, linear density, crimp contraction and crimp modulus, elongation at break and shrinkage. In contrast, a substantial increase was observed in moisture regain, vertical wicking, dye uptake and ultraviolet protection. There was also a reduction just in the electrical resistivity, in the presence of sericin.
Originality/value
Although sericin has been known to have numerous beneficial properties, its application in textile industry as a spin finish has not been reported yet.
Details
Keywords
Jian Sun, Zhanshuai Fan, Yi Yang, Chengzhi Li, Nan Tu, Jian Chen and Hailin Lu
Aluminum alloy is considered an ideal material in aerospace, automobile and other fields because of its lightweight, high specific strength and easy processing. However, low…
Abstract
Purpose
Aluminum alloy is considered an ideal material in aerospace, automobile and other fields because of its lightweight, high specific strength and easy processing. However, low hardness and strength of the surface of aluminum alloys are the main factors that limit their applications. The purpose of this study is to obtain a composite coating with high hardness and lubricating properties by applying GO–PVA over MAO coating.
Design/methodology/approach
A pulsed bipolar power supply was used as power supply to prepare the micro-arc oxidation (MAO) coating on 6061 aluminum sample. Then a graphene oxide-polyvinyl alcohol (GO–PVA) composite coating was prepared on MAO coating for subsequent experiments. Samples were characterized by Fourier infrared spectroscopy, X-ray diffraction, Raman spectroscopy and thermogravimetric analysis. The friction test is carried out by the relative movement of the copper ball and the aluminum disk on the friction tester.
Findings
Results showed that the friction coefficient of MAO samples was reduced by 80% after treated with GO–PVA composite film.
Originality/value
This research has made a certain contribution to the surface hardness and tribological issues involved in the lightweight design of aluminum alloys.
Peer review
The peer review history for this article is available at: https://publons.com/publon/10.1108/ILT-12-2023-0427/
Details
Keywords
The purpose of this study is to prepare a state-of-the-art review on advanced ceramic materials including their fabrication techniques, characteristics, applications and…
Abstract
Purpose
The purpose of this study is to prepare a state-of-the-art review on advanced ceramic materials including their fabrication techniques, characteristics, applications and wettability.
Design/methodology/approach
This review paper presents the various types of advanced ceramic materials according to their compounding elements, fabrication techniques of advanced ceramic powders as well as their consolidation, their characteristics, applications and wetting properties. Hydrophobic/hydrophilic properties of advanced ceramic materials are described in the paper with their state-of-the-art application areas. Optical properties of fine ceramics with their intrinsic characteristics are also presented within. Special focus is given to the brief description of application-based manipulation of wetting properties of advanced ceramics in the paper.
Findings
The study of wetting/hydrophobicity/hydrophilicity of ceramic materials is important by which it can be further modified to achieve the required applications. It also makes some sense that the material should be tested for its wetting properties when it is going to be used in some important applications like biomedical and dental. Also, these advanced ceramics are now often used in the fabrication of filters and membranes to purify liquid/water so the study of wetting characteristics of these materials becomes essential. The optical properties of advanced ceramics are equally making them suitable for many state-of-the-art applications. Dental, medical, imaging and electronics are the few sectors that use advanced ceramics for their optical properties.
Originality/value
This review paper includes various advanced ceramic materials according to their compounding elements, different fabrication techniques of powders and their consolidation, their characteristics, various application area and hydrophobic/hydrophilic properties.
Details