The purpose of this paper is to synthesize a new kind of conductive grease which possesses a prominent conductive capacity and good tribological properties.

A two-step method was used to prepare complex lithium-based grease. Ketjen black (KB), acetylene black (AB) and carbon black (CB) were characterized by transmission electron microscope and used as lubricant additives to prepare conductive greases. Conductive capacity was evaluated by a conductivity meter, a surface volume resistivity meter and a circuit resistance meter. Tribological properties were investigated by a reciprocating friction and wear tester (MFT-R4000). The worn surfaces were analyzed by a scanning electron microscope, Raman spectroscopy, energy-dispersive X-ray spectroscopy and X-ray photoelectron spectroscope.

The conductive grease prepared with KB has a prominent conductive capacity at room temperature, 100°C and 150°C. Further, this conductive grease also possesses better tribological properties than AB and KB greases. When the concentration of KB is 1.8 Wt.%, the coefficient of friction and wear width reduced by 11 and 14 per cent, respectively.

This work is a new application of nanometer KB as a lubricant additive in grease, which provides a direction for preparing conductive grease. The conductivity and tribology experiments have been carried out though the variation of experiment conductions.

The purpose of this paper is to compare the electrical conductivity and tribological properties of magnetron sputtered silver (Ag), copper (Cu) and aluminum (Al) thin films under conductive grease lubrication.

Three types of silver (Ag), copper (Cu) and aluminum (Al) thin films were prepared by magnetron sputtering. Current-carrying friction tests were carried out by a ball-on-plate reciprocating friction and wear tester. Scanning electron microscopy (SEM), X-ray diffraction (XRD) and energy dispersive X-ray spectroscopy (EDX) were used to observe and analyze the worn surface and cross-section morphology of the films.

Silver and Cu films exhibited good conductivity and tribological properties, which were mainly attributed to the synergy of the protective tribofilm generated by conductive grease, current-induced thermal effect and magnetron sputtered films effect. Al film was worn through. Large pitting storing lubricate were only found in Ag film. Cu film showed a similar surface uniformity with Ag film.

This study provides a reference for the design and application of conductive grease and investigates the current-carrying friction behaviors of magnetron sputtered films as electrical contact materials. The comparison of current-carrying friction behaviors of the three films was rarely covered in previous studies.