In the recent years, the industries show interest in natural and synthetic fibre-reinforced hybrid composites due to weight reduction and environmental reasons. The purpose of this experimental study is to investigate the properties of the hybrid composites fabricated by using carbon, untreated and alkaline-treated hemp fibres.

The composites were tested for strengths under tensile, flexural, impact and shear loadings, and the water absorption characteristics were also observed. The finite element analysis (FEA) was carried out to analyse the elastic behaviour of the composites and predict the strength by using ANSYS 15.0.

From the experimental results, it is observed that the hybrid composites can withstand the maximum tensile strength of 61.4 MPa, flexural strength of 122.4 MPa, impact strength of 4.2 J/mm² and shear strength of 25.5 MPa. From the FEA results, it is found that the maximum stress during tensile, flexural and impact loading is 47.5, 2.1 and 1.03 MPa, respectively.

The results of the untreated and alkaline-treated hemp-carbon fibre composites were compared and found that the alkaline-treated composites perform better in terms of mechanical properties. Then, the ANSYS-predicted values were compared with the experimental results, and it was found that there is a high correlation occurs between the untreated and alkali-treated hemp-carbon fibre composites. The internal structure of the broken surfaces of the composite samples was analysed using a scanning electron microscopy (SEM) analysis.

The purpose of this study is to evaluate and compare the mechanical performance of FFF parts when subjected to post processing thermal treatment. Therefore, a study of the annealing treatment influence on the mechanical properties was performed. For this, two different types of Nylon (PA12) were used, FX256 and CF15, being the second a short fibre reinforcement version of the first one.

In this study, tensile and flexural properties of specimens produced via FFF were determined after being annealed at temperatures of 135°C, 150°C or 165°C during 3, 6, 12 or 18 h and compared with the non-treated conditions. Differential scanning calorimetry (DSC) was performed to determine the degree of crystallinity. To evaluate the annealing parameters’ influence on the mechanical properties, a full factorial design of experiments was developed, followed by an analysis of variance, as well as post hoc comparisons, to determine the most significative intervening factors and their effect on the results.

The results indicate that CF15 increased its tensile modulus, strength, flexural modulus and flexural strength around 11%, while FX256 presented similar values for tensile properties, doubling for flexural results. Flexural strain presented an improvement, indicating an increased interlayer behaviour. Concerning to the DSC analysis, an increase in the degree of crystallinity for all the annealed parts.

Overall, the annealing treatment process cause a significant improvement in the mechanical performance of the material, with the exception of 165°C annealed specimens, in which a decrease of the mechanical properties was observed, resultant of material degradation.

The purpose of this paper is the selection of production parameters in selective laser sintering – SLS for the production of quality products (e.g. good mechanical properties). The manufacturing procedure affects the properties, which is especially significant in additive procedures, as the products are not cheap and the procedure and material need to be optimally selected.

The paper presents an analysis of the fabrication parameters in selective laser sintering (SLS) that affect the flexural properties of the finished product.

The influence of a new parameter has been found, the overlay ratio, and using the mathematical and scheme method, the selection of parameters for obtaining the optimal flexural properties has been proposed.

The paper presents a new mathematical model for the calculation of the processing parameters in SLS of polymer products and gives a diagram for the determination of which parameters are the best to use for practical purposes.

Existing deterministic models that predict the capacity of corroded reinforced concrete (RC) beams have limited applicability because they were based on accelerated tests that induce general corrosion. This research gap was addressed by performing a combined numerical and statistical analysis on RC beams, subjected to natural corrosion, to achieve a much better forecast.

Data of 42 naturally corroded beams were collected from the literature and analyzed numerically. Four constitutive models and their combinations were considered: the elastic-semi-plastic and elastic-perfectly-plastic models for steel, and two tensile models for concrete with and without the post-cracking stresses. Meanwhile, Popovics’ model was used to describe the behavior of concrete under compression. Corrosion coefficients were developed as functions of corrosion degree and beam parameters through linear regression analysis to fit the theoretical moment capacities with test data. The performance of the coefficients derived from different combinations of constitutive laws was then compared and validated.

The results showed that the highest accuracy (R² = 0.90) was achieved when the tensile response of concrete was modeled without the residual stresses after cracking and the steel was analyzed as an elastic-perfectly-plastic material. The proposed procedure and regression model also showed reasonable agreement with experimental data, even performing better than the current models derived from accelerated tests and traditional procedures.

This study presents a simple but reliable approach for quantifying the capacity of RC beams under more realistic conditions than previously reported. This method is simple and requires only a few variables to be employed. Civil engineers can use it to obtain a quick and rough estimate of the structural condition of corroding RC beams.

A bibliographical review of the finite element methods (FEMs) applied for the linear and nonlinear, static and dynamic analyses of basic structural elements from the theoretical as well as practical points of view is given. The bibliography at the end of the paper contains 1,726 references to papers, conference proceedings and theses/dissertations dealing with the analysis of beams, columns, rods, bars, cables, discs, blades, shafts, membranes, plates and shells that were published in 1996‐1999.

This paper gives a review of the finite element techniques (FE) applied in the analysis and design of machine elements; bolts and screws, belts and chains, springs and dampers, brakes, gears, bearings, gaskets and seals are handled. The range of applications of finite elements on these subjects is extremely wide and cannot be presented in a single paper; therefore the aim of this paper is to give FE researchers/users only an encyclopaedic view of the different possibilities that exist today in the various fields mentioned above. An Appendix included at the end of the paper presents a bibliography on finite element applications in the analysis/design of machine elements for 1977‐1997.

This study investigates the impact of the fire decay phase on structural damage using the sectional analysis method. The primary objective of this work is to forecast the non-dimensional capacity parameters for the axial and flexural load-carrying capacity of reinforced concrete (RC) sections for heating and the subsequent post-heating phase (decay phase) of the fire.

The sectional analysis method is used to determine the moment and axial capacities. The findings of sectional analysis and heat transfer for the heating stage are initially validated, and the analysis subsequently proceeds to determine the load capacity during the fire’s heating and decay phases by appropriately incorporating non-dimensional sectional and material parameters. The numerical analysis includes four fire curves with different cooling rates and steel percentages.

The study’s findings indicate that the rate at which the cooling process occurs after undergoing heating substantially impacts the axial and flexural capacity. The maximum degradation in axial and flexural capacity occurred in the range of 15–20% for cooling rates of 3 °C/min and 5 °C/min as compared to the capacity obtained at 120 min of heating for all steel percentages. As the fire cooling rate reduced to 1 °C/min, the highest deterioration in axial and flexural capacity reached 48–50% and 42–46%, respectively, in the post-heating stage.

The established non-dimensional parameters for axial and flexural capacity are limited to the analysed section in the study owing to the thermal profile, however, this can be modified depending on the section geometry and fire scenario.

The study primarily focusses on the degradation of axial and flexural capacity at various time intervals during the entire fire exposure, including heating and cooling. The findings obtained showed that following the completion of the fire’s heating phase, the structural capacity continued to decrease over the subsequent post-heating period. It is recommended that structural members' fire resistance designs encompass both the heating and cooling phases of a fire. Since the capacity degradation varies with fire duration, the conventional method is inadequate to design the load capacity for appropriate fire safety. Therefore, it is essential to adopt a performance-based approach while designing structural elements' capacity for the desired fire resistance rating. The proposed technique of using non-dimensional parameters will effectively support predicting the load capacity for required fire resistance.

The fire-resistant requirements for reinforced concrete structures are generally established based on standard fire exposure conditions, which account for the fire growth phase. However, it is important to note that concrete structures can experience internal damage over time during the decay phase of fires, which can be quantitatively determined using the proposed non-dimensional parameter approach.

Understanding the effect of process parameters on interfaces and interfacial bonding between two materials during multi-material additive manufacturing (MMAM) is crucial to the fabrication of high-quality and strong multi-material structures. The purpose of this paper is to conduct an experimental and statistical study to investigate the effect of process parameters of soft and hard materials on the flexural behavior of multi-material structures fabricated via material extrusion-based MMAM.

Sandwich beam samples composed of a soft core and hard shells are fabricated via MMAM under different printing conditions. A design of experiments is conducted to investigate the effect of the print speed and nozzle temperature on the flexural behavior of soft-hard sandwich beams. Analysis of variance and logistic regression analysis are used to analyze the significance of each process parameter. The interfacial morphology of the samples after the flexural tests is characterized. Thermal distributions during the MMAM process are captured to understand the effect of process parameters on the flexural behavior based on inter-bonding formation mechanisms.

Experimental results show that the soft-hard sandwich beams exhibited two different failure modes, including shell failure and interfacial failure. A transition of failure modes from interfacial failure to shell failure is observed as the nozzle temperatures increase. The samples that fail because of interfacial cracking exhibit a pure adhesive failure because of weak interfacial fracture properties. The samples that fail because of shell cracking exhibit a mixed adhesive and cohesive failure. The flexural strength and modulus are affected by the nozzle temperature for the hard material and the print speeds for both hard and soft materials significantly.

This paper first investigates the effect of process parameters for soft and hard materials on the flexural behavior of additively manufactured multi-material structures. Especially, the ranges of the selected process parameters are distinct, and the effect of all possible combinations of the process parameters on the flexural behavior is characterized through a full factorial design of experiments. The experimental results and conclusions of this paper provide guidance for future research on improving the interfacial bonding and understanding the failure mechanism of multi-material structures fabricated by MMAM.

Fused deposition modelling (FDM) is increasingly being explored as a commercial fabrication method due to its ability to produce net or near-net shape parts directly from a computer-aided design model. Other benefits of technology compared to conventional manufacturing include lower cost for short runs, reduced product lead times and rapid product design. High-performance polymers such as polyetherimide, have the potential for FDM fabrication and their high-temperature capabilities provide the potential of expanding the applications of FDM parts in automotive and aerospace industries. However, their relatively high glass transition temperature (215 °C) causes challenges during manufacturing due to the requirement of high-temperature build chambers and controlled cooling rates. The purpose of this study is to investigate the mechanical properties of ULTEM 1010, an unfilled polyetherimide grade.

In this research, mechanical properties were evaluated through tensile and flexural tests. Analysis of variance was used to determine the significance of process parameters to the mechanical properties of the specimens, their main effects and interactions. The fractured surfaces were analysed by scanning electron microscopy and optical microscopy and porosity was assessed by X-ray microcomputed tomography.

A range of mean tensile and flexural strengths, 60–94 MPa and 62–151 MPa, respectively, were obtained highlighting the dependence of performance on process parameters and their interactions. The specimens were found to fracture in a brittle manner. The porosity of tensile samples was measured between 0.18% and 1.09% and that of flexural samples between 0.14% and 1.24% depending on the process parameters. The percentage porosity was found to not directly correlate with mechanical performance, rather the location of those pores in the sample.

This analysis quantifies the significance of the effect of each of the examined process parameters has on the mechanical performance of FDM-fabricated specimens. Further, it provides a better understanding of the effect process parameters and their interactions have on the mechanical properties and porosity of FDM-fabricated polyetherimide specimens. Additionally, the fracture surface of the tested specimens is qualitatively assessed.

This paper aims to propose a generalized finite element technique that can accurately approximate the solution of the flexural-shear cantilever model of wall-frame structures proposed by Heidebrecht and Stafford Smith.

This approach adopts scaled monomials as enrichment functions, and they are highly effective in accurately capturing the solution of the problem, as it consists of smooth functions such as polynomials, hyperbolic and trigonometric functions. Several numerical experiments are performed on the static and modal analyses of the flexural-shear cantilever wall-frame structures using the proposed generalized finite element method (GFEM), and their accuracies are compared with those obtained using the standard finite element method.

The proposed GFEM is able to achieve theoretical convergence rates of the static and modal analyses, which are, in principle, identical to those of the standard FEM, for various polynomial orders of its shape functions such as quadratic, cubic and quartic orders. The proposed GFEM with quartic enrichment functions can provide more accurate solutions than the standard FEM, and thus can be effectively used at the initial design stage of high-rise wall-frame structures.

This work is the first paper where the GFEM is applied to the analysis of high-rise wall-frame structures, and the developed technique can be used as a good analysis tool at the initial design stage.