The purpose of this study is to investigate the thermomechanical condition on the shape memory property of Polybutylene adipate-co-terephthalate (PBAT). PBAT is a widely researched and rapidly developed biodegradable copolyester. In a tensile test, we found that the fractured PBAT samples had a heat-driven shape memory effect which piqued our interest, and it will lay a foundation for the application of PBAT in new fields (such as heat shrinkable film).

The shape memory effect of PBAT and the effect of the thermomechanical condition on its shape memory property were confirmed and systematically investigated by a thermal mechanical analyzer and tensile machine.

The results showed that the PBAT film had broad shape memory transform temperature and exhibited excellent thermomechanical stability and shape memory properties. The shape memory fixity ratio (Rf) of the PBAT films was increased with the prestrain temperature and prestrain, where the highest Rf exceeded 90%. The shape memory recovery ratio (Rr) of the PBAT films was increased with the shape memory recovery temperature and decreased with the prestrain value, and the highest Rr was almost 100%. Moreover, the PBAT films had high shape memory recovery stress which increased with the prestrain value and decreased with the prestrain temperature, and the highest shape memory recovery stress can reach 7.73 MPa.

The results showed that PBAT had a broad shape memory transform temperature, exhibited excellent thermomechanical stability and shape memory performance, especially for the sample programmed at high temperature and had a larger prestrian, which will provide a reference for the design, processing and application of PBAT-based heat shrinkable film and smart materials.

This study confirmed and systematically investigated the shape memory effect of PBAT and the effect of the thermomechanical condition on the shape memory property of PBAT.

Aluminum alloy is considered an ideal material in aerospace, automobile and other fields because of its lightweight, high specific strength and easy processing. However, low hardness and strength of the surface of aluminum alloys are the main factors that limit their applications. The purpose of this study is to obtain a composite coating with high hardness and lubricating properties by applying GO–PVA over MAO coating.

A pulsed bipolar power supply was used as power supply to prepare the micro-arc oxidation (MAO) coating on 6061 aluminum sample. Then a graphene oxide-polyvinyl alcohol (GO–PVA) composite coating was prepared on MAO coating for subsequent experiments. Samples were characterized by Fourier infrared spectroscopy, X-ray diffraction, Raman spectroscopy and thermogravimetric analysis. The friction test is carried out by the relative movement of the copper ball and the aluminum disk on the friction tester.

Results showed that the friction coefficient of MAO samples was reduced by 80% after treated with GO–PVA composite film.

This research has made a certain contribution to the surface hardness and tribological issues involved in the lightweight design of aluminum alloys.

The peer review history for this article is available at: https://publons.com/publon/10.1108/ILT-12-2023-0427/

The color painting of ancient buildings has high historical and artistic value but is prone to aging due to long-term outdoor exposure. The purpose of this study is to develop a new type of sealing coating to mitigate the impact of ultraviolet (UV) light on color painting.

The new coating was subjected to a 500-h UV-aging test. Compared with the existing acrylic resin Primal AC33, the UV aging behavior of the new coating, such as color difference and gloss, was studied with aging time. The Fourier infrared spectra of the coatings were analyzed after the UV-aging test.

Compared with AC33, the antiaging performance of SF8 was substantially improved. SF8 has a lower color difference value and better light retention and hydrophobicity. The Fourier transform infrared spectroscopy results showed that the C-F bond and Si-O bonds in the resin of the optimized sealing coating protected the main chain C-C structure from degradation during the aging process; thus, the resin maintained good stability. The hindered amine light stabilizer TN292 added to the coating inhibited the antiaging process by trapping active free radicals.

To address the problem of UV aging of oil-decorated colored paintings, a new type of sealing coating with excellent antiaging properties was developed, laying the foundation for its demonstration application on the surface of ancient buildings.

This paper aims to study the synergistic lubrication effects of Sn–Ag–Cu and MXene–Ti₃C₂ to improve the tribological properties of M50 bearing steel with microporous channels.

M50 matrix self-lubricating composites (MMSC) were designed and prepared by filling Sn–Ag–Cu and MXene–Ti₃C₂ in the microporous channels of M50 bearing steel. The tribology performance testing of as-prepared samples was executed with a multifunction tribometer. The optimum hole size and lubricant content, as well as self-lubricating mechanism of MMSC, were studied.

The tribological properties of MMSC are strongly dependent on the synergistic lubrication effect of MXene–Ti₃C₂ and Sn–Ag–Cu. When the hole size of microchannel is 1 mm and the content of MXene–Ti₃C₂ in mixed lubricant is 4 wt.%, MMSC shows the lowest friction coefficient and wear rate. The Sn–Ag–Cu and MXene–Ti₃C₂ are extruded from the microporous channels and spread to the friction interface, and a relatively complete lubricating film is formed at the friction interface. Meanwhile, the synergistic lubrication of Sn–Ag–Cu and MXene–Ti₃C₂ can improve the stability of the lubricating film, thus the excellent tribological property of MMSC is obtained.

The results help in deep understanding of the synergistic lubrication effects of Sn–Ag–Cu and MXene–Ti₃C₂ on the tribological properties of M50 bearing steel. This work also provides a useful reference for the tribological design of mechanical components by combining surface texture with solid lubrication.

The peer review history for this article is available at: https://publons.com/publon/10.1108/ILT-12-2023-0381/

Polymer-based thermal interface materials (TIMs) are having pump out problem and could be resolved for reliable application. Solid-based interface materials have been suggested and reported. The purpose of this paper is suggesting thin film-based TIM to sustain the light-emiting diode (LED) performance and electronic device miniaturization.

Consequently, ZnO thin film at various thicknesses was prepared by chemical vapour deposition (CVD) method and tested their thermal behaviour using thermal transient analysis as solid TIM for high-power LED.

Low value in total thermal resistance (R_th-tot) was observed for ZnO thin film boundary condition than bare Al boundary condition. The measured interface (ZnO thin film) resistance {(R_th-bhs) thermal resistance of the interface layer (thin film) placed between metal core printed circuit board (MCPCB) board and Al substrates} was nearly equal to Ag paste boundary condition and showed low values for ZnO film prepared at 30 min process time measured at 700 mA. The T_J value of LED mounted on ZnO thin film (prepared at 30 min.) coated Al substrates was measured to be 74.8°C. High value in junction temperature difference (ΔT_J) of about 4.7°C was noticed with 30 min processed ZnO thin film when compared with Al boundary condition. Low correlated colour temperature and high luminous flux values of tested LED were also observed with ZnO thin film boundary condition (processed at 30 min) compared with both Al substrate and Ag paste boundary condition.

Overall, 30 min CVD processed ZnO thin film would be an alternative for commercial TIM to achieve efficient thermal management. This will increase the life span of the LED as the proposed material decreases the T_J values.

The purpose of this paper is to study the electronic transport performance of Ag-ZnO film under dark and UV light conditions.

Ag-doped ZnO thin films were prepared on fluorine thin oxide (FTO) substrates by sol-gel method. The crystal structure of ZnO and Ag-ZnO powders was tested by X-ray diffraction with Cu Kα radiation. The absorption spectra of ZnO and Ag-ZnO films were recorded by a UV–visible spectrophotometer. The micro electrical transport performance of Ag-ZnO thin films in dark and light state was investigated by photoassisted conductive atomic force microscope (PC-AFM).

The results show that the dark reverse current of Ag-ZnO films does not increase, but the reverse current increases significantly under illumination, indicating that the response of Ag-ZnO films to light is greatly improved, owing to the formation of Ohmic contact.

To the best of the author’s knowledge, the micro electrical transport performance of Ag-ZnO thin films in dark and light state was firstly investigated by PC-AFM.

In this paper, the authors aim to study the effect of hydrogen on the pitting corrosion behavior of Incoloy 825, a commonly used material for heat exchanger tubes in hydrogenated heat exchangers.

The pitting initiation and propagation behaviors were investigated by electrochemical and chemical immersion experiments and observed and analyzed by scanning electron microscope and energy dispersive spectrometer methods.

The results show that hydrogen significantly affects the electrochemical behavior of Incoloy 825; the self-corrosion potential decreased from −197 mV before hydrogen charging to −263 mV, −270 mV and −657 mV after hydrogen charging, and the corrosion current density increased from 0.049 µA/cm² before hydrogen charging to 2.490 µA/cm², 2.560 µA/cm² and 2.780 µA/cm² after hydrogen charging. The pitting susceptibility of the material increases.

Hydrogen is enriched on the precipitate, and the pitting corrosion also initiates at that location. The synergistic effect of hydrogen and precipitate destroys the passive film on the metal surface and promotes pitting initiation.

This paper aims to study the influence of cylindrical texture parameters on the lubrication performance of static and dynamic pressure thrust bearings (hereinafter referred to as thrust bearings) and to optimize their lubrication performance using multiobjective optimization.

The influence of texture parameters on the lubrication performance of thrust bearings was studied based on the modified Reynolds equation. The objective functions are predicted through the BP neural network, and the texture parameters were optimized using the improved multiobjective ant lion algorithm (MOALA).

Compared with smooth surface, the introduction of texture can improve the lubrication properties. Under the optimization of the improved algorithm, when the texture diameter, depth, spacing and number are approximately 0.2 mm, 0.5 mm, 5 mm and 34, respectively, the loading capacity is increased by around 27.7% and the temperature is reduced by around 1.55°C.

This paper studies the effect of texture parameters on the lubrication properties of thrust bearings based on the modified Reynolds equation and performs multiobjective optimization through an improved MOALA.

This study aims to synthesize Prussian blue {Fe^III₄[Fe^II(CN)₆]₃} pigment by reacting ferric chloride with different ferrocyanides through the same procedure. The influence of the ferrocyanide used on resulting pigment properties is studied.

Prussian blue is commonly synthesized by direct or indirect methods, through iron salt and ferrocyanide/ferricyanide reactions. In this study, the direct, single-step process was pursued by dropwise addition of the ferrocyanide into ferric chloride (both as aqueous solutions). Two batches – (K-PB) and (Na-PB) – were prepared by using potassium ferrocyanide and sodium ferrocyanide, respectively. The development of pigment was confirmed by an identification test and characterized by spectroscopic techniques. Pigment properties were determined, and light fastness was observed for acrylic emulsion films incorporating dispersed pigment.

The two pigments differed mainly in elemental detection owing to the dissimilar ferrocyanide being used; IR spectroscopy where only (Na-PB) showed peaks indicating water molecules; and bleeding tendency where (K-PB) was water soluble whereas (Na-PB) was not. The pigment exhibited remarkable blue colour and good bleeding resistance in several solvents and showed no fading in 24 h of light exposure though oil absorption values were high.

This article is a comparative study of Prussian blue pigment properties obtained using different ferrocyanides. The dissimilarity in the extent of water solubility will influence potential applications as a colourant in paints and inks. K-PB would be advantageous in aqueous formulations to confer a blue colour without any dispersing aid but unfavourable in systems where other coats are water-based due to their bleeding tendency.

This paper aims to solve the problems molybdenum disulfide (MoS₂) nanosheets suffer from inadequate dispersion stability and form a weak lubricating film on the friction surface, which severely limits their application as lubricant additives.

MoS₂/C₆₀ nanocomposites were prepared by synthesizing molybdenum disulfide (MoS₂) nanosheets on the surface of hydrochloric acid-activated fullerenes (C₆₀) by in situ hydrothermal method. The composition, structure and morphology of MoS₂/C₆₀ nanocomposites were characterized. Through the high-frequency reciprocating tribology test, its potential as a lubricant additive was evaluated.

MoS₂/C₆₀ nanocomposites that were prepared showed good dispersion in dioctyl sebacate (DOS). When 0.5 Wt.% MoS₂/C₆₀ was added, the friction reduction performance and wear resistance improved by 54.5% and 62.7%, respectively.

MoS₂/C₆₀ composite nanoparticles were prepared by in-situ formation of MoS₂ nanosheets on the surface of C₆₀ activated by HCl through hydrothermal method and were used as potential lubricating oil additives.