1 – 10 of 30Akhil Khajuria, Anurag Misra and S. Shiva
An experimental investigation for developing structure-property correlations of hot-rolled E410 steels with different carbon contents, i.e. 0.04wt.%C and 0.17wt.%C metal active…
Abstract
Purpose
An experimental investigation for developing structure-property correlations of hot-rolled E410 steels with different carbon contents, i.e. 0.04wt.%C and 0.17wt.%C metal active gas (MAG) and cold metal transfer (CMT)-MAG weldments was undertaken.
Design/methodology/approach
Mechanical properties and microstructure of MAG and CMT-MAG weldments of two E410 steels with varying content of carbon were compared using standardized mechanical testing procedures, and conventional microscopy.
Findings
0.04wt.%C steel had strained ferritic and cementite sub-structures in blocky shape and large dislocation density, while 0.17wt.%C steel consisted of pearlite and polygonal ductile ferrite. This effected yield strength (YS), and microhardness being larger in 0.04wt.%C steel, %elongation being larger in 0.17wt.%C steel. Weldments of both E410 steels obtained with CMT-MAG performed better than MAG in terms of YS, ultimate tensile strength (UTS), %elongation, and toughness. It was due to low heat input of CMT-MAG that resulted in refinement of weld metal, and subzones of heat affected zone (HAZ).
Originality/value
A substantial improvement in YS (∼9%), %elongation (∼38%), and room temperature impact toughness (∼29%) of 0.04wt.%C E410 steel is achieved with CMT-MAG over MAG welding. Almost ∼10, ∼12.5, and ∼16% increment in YS, %elongation, and toughness of 0.17wt.%C E410 steel is observed with CMT-MAG. Relatively low heat input of CMT-MAG leads to development of fine Widmanstätten and acicular ferrite in weld metal and microstructural refinement in HAZ subzones with nearly similar characteristics of base metal.
Details
Keywords
Chetan Tembhurkar, Sachin Ambade, Ravinder Kataria, Jagesvar Verma and Abhijeet Moon
This paper aims to examine dissimilar joints for various applications in chemical, petrochemical, oil, gas, shipbuilding, defense, rail and nuclear industry.
Abstract
Purpose
This paper aims to examine dissimilar joints for various applications in chemical, petrochemical, oil, gas, shipbuilding, defense, rail and nuclear industry.
Design/methodology/approach
This study examined the effects of cold metal transfer welding on stainless steel welds for 316L austenitic and 430 ferritic dissimilar welds with ER316L, ER309L and without (autogenous) fillers. The microstructural observation was done with an optical microscope. The mechanical test was done to reveal the strength, hardness and toughness of the joint. The electrochemical polarization tests were done to reveal intergranular and pitting corrosion in the dissimilar joints.
Findings
This microstructural study shows the presence of austenitic and ferritic phases with vermicular ferrite for ER309L filler weld, and for ER316L filler weld specimen shows predominately martensitic phase in the weld region, whereas the autogenous weld shows lathy ferrite mixed with martensitic phase. Mechanical test results indicated that filler welded specimen (ER316L and ER309L) has relatively higher strength and hardness than the autogenous weld, whereas ER316L filler weld exhibited the highest impact toughness than ER309L filler weld and lowest in autogenous weld. The electrochemical corrosion results displayed the highest degree of sensitization (DOS) in without filler welded specimen (45.62%) and lower in case of filler welded specimen ER309L (4.95%) and least in case of ER316L filler welded specimen (3.51%). The high DOS in non-filler welded specimen is correlated with the chromium carbide formation. The non-filler welded specimen shows the highest pitting corrosion attack as compared to the ER316L filler weld specimen and relatively better in ER309L filler welded specimen. The highest pitting corrosion resistance is related with the high chromium content in ER309L composition.
Originality/value
This experimental study is original and conducted with 316L and 430 stainless steel with ER316L, ER309 and without fillers, which will help the oil, shipbuilding and chemical industries.
Details
Keywords
In eddy current nondestructive testing, ferrite-cored probes are usually used to detect and locate defects such as cracks and corrosion in conductive materials. However, the…
Abstract
Purpose
In eddy current nondestructive testing, ferrite-cored probes are usually used to detect and locate defects such as cracks and corrosion in conductive materials. However, the generic analytical model for evaluating corrosion in layered conductor using ferrite-cored probe has not yet been developed. The purpose of this paper is to propose and verify the analytical model of an E-cored probe for evaluating corrosion in layered conductive materials.
Design/methodology/approach
A cylindrical coordinate system is adopted and the solution domain is truncated in the radial direction. The magnetic vector potential of each region excited by a filamentary coil is derived first, and then the expansion coefficients of the solution are obtained by matching the boundary and interface conditions between the regions and the subregions. Finally the closed-form expression of the impedance of the multi-turn coil is derived by using the truncated region eigenfunction expansion (TREE) method, and the impedance calculation is carried out in Mathematica. In the frequency range of 100 Hz to 10 kHz, the impedance changes of the E-cored coil and air-cored coil due to the layered conductor containing corrosion are calculated, respectively, and the influences of corrosion on the coil impedance change are investigated.
Findings
An analytical model for the detection and evaluating of corrosion in layered conductive materials using E-cored probe is proposed. The model can quickly and accurately calculate the impedance change of E-cored coil due to corrosion in layered conductor. The correctness of the analytical model is verified by finite element method and experiments.
Originality/value
An accurate theoretical model of E-cored probe for evaluating corrosion of multilayer conductor is presented. The analytical model can be used to detect the inhomogeneity of layered conductor, design ferrite-cored probe or directly evaluate the corrosion defects of layered conductors.
Details
Keywords
Anand Sharma, Sourabh Shukla, Manish Thombre, Ankur Bansod and Sachin Untawale
The purpose of this study is to examine the effects of sensitization on the metallurgical characteristics of weld joints made up of austenitic stainless steel (AISI 316L) and…
Abstract
Purpose
The purpose of this study is to examine the effects of sensitization on the metallurgical characteristics of weld joints made up of austenitic stainless steel (AISI 316L) and ferritic stainless steel (AISI 430), using the gas tungsten arc welding (GTAW) process with ER316L filler wires.
Design/methodology/approach
A non-consumable tungsten electrode with a diameter of 1.6 mm was used during the GTAW procedure. The filler wire, ER316L, was selected based on the recommendation provided in literature. To explore the interconnections among the structure and properties of these weldments, the techniques including scanning electron microscopy and optical analysis have been used. In addition, the sensitization behaviour of the weldments was investigated using the double loop electrochemical potentio-kinetic reactivation (DLEPR) test.
Findings
Microstructural analyses revealed the occurrences of coarsened grains with equiaxed columnar grains and migrating grain boundaries in the weld zone. The results of the DLEPR test demonstrated that heat affected zone (HAZ) of AISI 430 was more susceptible to sensitization than HAZ of AISI 316L. Microstructure analysis also revealed the precipitation of large amounts of chromium carbide at the grain boundaries region of AISI 430 welded steel, causing more sensitization and, as a result, more failure or breaking at the side of AISI 430 weld in the dissimilar weldment of AISI 316L–AISI 430.
Originality/value
The present work has been carried out to determine the appropriate welding conditions for joining AISI 316L and AISI 430, as well as the metallurgical properties of the dissimilar weldment formed between AISI 316L and AISI 430. Owing to the difficulties in measuring the performance of these types of dissimilar joints given their unique mechanical and microstructural characteristics, research on the subject is limited.
Details
Keywords
Suvranshu Pattanayak, Susanta Kumar Sahoo, Ananda Kumar Sahoo, Raviteja Vinjamuri and Pushpendra Kumar Dwivedi
This study aims to demonstrate a modified wire arc additive manufacturing (AM) named non-transferring arc and wire AM (NTA-WAM). Here, the build plate has no electrical arc…
Abstract
Purpose
This study aims to demonstrate a modified wire arc additive manufacturing (AM) named non-transferring arc and wire AM (NTA-WAM). Here, the build plate has no electrical arc attachment, and the system’s arc is ignited between tungsten electrode and filler wire.
Design/methodology/approach
The effect of various deposition conditions (welding voltage, travel speed and wire feed speed [WFS]) on bead characteristics is studied through response surface methodology (RSM). Under optimum deposition condition, a single-bead and thin-layered part is fabricated and subjected to microstructural, tensile testing and X-ray diffraction study. Moreover, bulk texture analysis has been carried out to illustrate the effect of thermal cycles and tensile-induced deformations on fibre texture evolutions.
Findings
RSM illustrates WFS as a crucial deposition parameter that suitably monitors bead width, height, penetration depth, dilution, contact angle and microhardness. The ferritic (acicular and polygonal) and lath bainitic microstructure is transformed into ferrite and pearlitic micrographs with increasing deposition layers. It is attributed to a reduced cooling rate with increased depositions. Mechanical testing exhibits high tensile strength and ductility, which is primarily due to compressive residual stress and lattice strain development. In deposits, ϒ-fibre evolution is more resilient due to the continuous recrystallisation process after each successive deposition. Tensile-induced deformation mostly favours ζ and ε-fibre development due to high strain accumulations.
Originality/value
This modified electrode arrangement in NTA-WAM suitably reduces spatter and bead height deviation. Low penetration depth and dilution denote a reduction in heat input that enhances the cooling rate.
Details
Keywords
Jiabao Pan, Rui Li and Ao Wang
The adverse effects of temperature on the lubricating properties of nano magnetorheological grease are reduced by applying of a magnetic field.
Abstract
Purpose
The adverse effects of temperature on the lubricating properties of nano magnetorheological grease are reduced by applying of a magnetic field.
Design/methodology/approach
Nano magnetorheological grease was prepared via a thermal water bath with stirring. The lubricating properties of the grease were investigated at different temperatures. Then the lubricity of the prepared nano magnetorheological grease was investigated under the effect of thermomagnetic coupling.
Findings
As the temperature rises, the coefficient of friction of grease lubrication gradually increases, surface wear gradually increases and lubrication performance gradually decreases. Compared with grease, magnetorheological grease has a decreased coefficient of friction and enhanced lubrication effect under the action of a magnetic field at different temperatures.
Originality/value
A lubrication method using a magnetic field to reduce the effect of temperature is established, thereby providing new ideas for lubrication design under a wide range of temperature conditions.
Details
Keywords
Kailash Choudhary, Narpat Ram Sangwa and Kuldip Singh Sangwan
This study aims to quantify and compare the environmental impacts of Marble-stone and Kota-stone flooring options widely used for buildings in India. The study discusses the…
Abstract
Purpose
This study aims to quantify and compare the environmental impacts of Marble-stone and Kota-stone flooring options widely used for buildings in India. The study discusses the possibility of carbon sequestration through Bamboo cultivation in India.
Design/methodology/approach
The study has followed a standard life cycle assessment (LCA) framework based on ISO 14040 guidelines. Three distinct phases have been compared on midpoint and endpoint assessment categories – raw material, polishing and disposal. Primary data has been collected from the construction site in India, and secondary data has been collected from the Ecoinvent 3.0 database. Previous studies have been referred to discuss and calculate the area of bamboo cultivation required to sequestrate the generated carbon from the flooring.
Findings
The study has found that endpoint category damage to resources, and midpoint categories of climate change, metal depletion and agricultural land use are highly impacted in building floorings. The study has also found that the Marble-stone floor generates higher environmental impacts than the Kota-stone floor in most of the midpoint and endpoint impact categories. This difference is significant in the raw material phase due to the different compositions of stones. The study also found that Bamboo has excellent potential to act as a carbon sink and mitigate the generated carbon.
Research limitations/implications
This study excludes human labour, cutting and distribution of floor tiles made of Marble-stone and Kota-stone. The researcher can use the study to evaluate, compare and benchmark the various building flooring options from the environmental perspective. The study aids to the body of knowledge available on the various building flooring options by presenting the LCA or the environmental impacts generated by two flooring options. It is expected that the architects and builders can use these results to develop carbon-neutral buildings. This study provides a methodology for governments, constructors, builders and individuals to evaluate, compare and benchmark the various construction materials from the environmental perspective by computing the environmental impacts throughout the life cycle of the materials.
Originality/value
This study compares two widely used building flooring options using the LCA methodology and evaluates the potential of bamboo cultivation near the buildings for carbon sinks. The study is unique because it shows the environmental impacts of two flooring options and the carbon sequestration method to mitigate/absorb the generated environmental impacts in or around the building itself through bamboo cultivation. This study may set the foundation for carbon-neutral buildings.
Details
Keywords
Dongyang Li, Guanghu Yao, Yuyuan Guan, Yaolei Han, Linya Zhao, Lining Xu and Lijie Qiao
In this paper, the authors aim to study the effect of hydrogen on the pitting corrosion behavior of Incoloy 825, a commonly used material for heat exchanger tubes in hydrogenated…
Abstract
Purpose
In this paper, the authors aim to study the effect of hydrogen on the pitting corrosion behavior of Incoloy 825, a commonly used material for heat exchanger tubes in hydrogenated heat exchangers.
Design/methodology/approach
The pitting initiation and propagation behaviors were investigated by electrochemical and chemical immersion experiments and observed and analyzed by scanning electron microscope and energy dispersive spectrometer methods.
Findings
The results show that hydrogen significantly affects the electrochemical behavior of Incoloy 825; the self-corrosion potential decreased from −197 mV before hydrogen charging to −263 mV, −270 mV and −657 mV after hydrogen charging, and the corrosion current density increased from 0.049 µA/cm2 before hydrogen charging to 2.490 µA/cm2, 2.560 µA/cm2 and 2.780 µA/cm2 after hydrogen charging. The pitting susceptibility of the material increases.
Originality/value
Hydrogen is enriched on the precipitate, and the pitting corrosion also initiates at that location. The synergistic effect of hydrogen and precipitate destroys the passive film on the metal surface and promotes pitting initiation.
Details
Keywords
Zhe Liu, Yichen Yang and Xiuchen Wang
Stainless-steel electromagnetic shielding (EMS) fabrics are widely applied as protective materials against electromagnetic interference (EMI). However, these fabrics primarily…
Abstract
Purpose
Stainless-steel electromagnetic shielding (EMS) fabrics are widely applied as protective materials against electromagnetic interference (EMI). However, these fabrics primarily shield electromagnetic waves through reflection, which can lead to the formation of resonance effects that severely compromise their protective capabilities and potentially cause secondary electromagnetic pollution in the external environment.
Design/methodology/approach
In this paper, carbon nanotube fibers are added via spacing method to replace some stainless-steel fibers to impart absorbing properties to stainless-steel EMS fabric. The shielding effectiveness (SE) of the EMS fabrics across various polarization directions is analyzed. Additionally, a spacing arrangement for the carbon nanotube fibers is designed. The EMS fabric with carbon nanotube fibers is manufactured using a semi-automatic sample loom, and its SE is tested using a small window method test box in both vertical and horizontal polarization directions.
Findings
According to the experimental data and electromagnetic theory analysis, it is determined that when the spacing between the carbon nanotube fibers is less than a specific distance, the SE of the stainless-steel EMS fabric significantly improves. The fabric exhibits stable absorbing properties within the tested frequency range, effectively addressing the issue of secondary damage that arises from relying solely on reflective shielding. Conversely, as the spacing between the carbon nanotube fibers exceeds this distance, the SE diminishes. Notably, the SE in the vertical polarization direction is substantially higher than that in the horizontal polarization direction at the same frequency.
Originality/value
This study provides a new path for the development of high-performance EMS fabrics with good wave-absorption characteristics and SE.
Details
Keywords
Ahmed Jan, Muhammad F. Afzaal, Muhammad Mushtaq, Umer Farooq and Muzammil Hussain
This study investigates the flow and heat transfer in a magnetohydrodynamic (MHD) ternary hybrid nanofluid (HNF), considering the effects of viscous dissipation and radiation.
Abstract
Purpose
This study investigates the flow and heat transfer in a magnetohydrodynamic (MHD) ternary hybrid nanofluid (HNF), considering the effects of viscous dissipation and radiation.
Design/methodology/approach
The transport equations are transformed into nondimensional partial differential equations. The local nonsimilarity (LNS) technique is implemented to truncate nonsimilar dimensionless system. The LNS truncated equation can be treated as ordinary differential equations. The numerical results of the equation are accomplished through the implementation of the bvp4c solver, which leverages the fourth-order three-stage Lobatto IIIa formula as a finite difference scheme.
Findings
The findings of a comparative investigation carried out under diverse physical limitations demonstrate that ternary HNFs exhibit remarkably elevated thermal efficiency in contrast to conventional nanofluids.
Originality/value
The LNS approach (Mahesh et al., 2023; Khan et al., 20223; Farooq et al., 2023) that we have proposed is not currently being used to clarify the dynamical issue of HNF via porous media. The LNS method, in conjunction with the bvp4c up to its second truncation level, yields numerical solutions to nonlinear-coupled PDEs. Relevant results of the topic at hand, obtained by adjusting the appropriate parameters, are explained and shown visually via tables and diagrams.
Details