This study aims to embed anatase, rutile and brookite TiO₂ nanoparticles (NPs) with different crystal phases into cotton fabrics by epoxy silane and to examine the effect of these applications on the photocatalytic and mechanical properties of the fabric.

Different aqueous dispersions which contain anatase, rutile and brookite were prepared at three different concentrations (5%, 10% and 15%). These NPs were embedded in cotton fabrics by using GPTS [(3-glycidyloxypropyl) trimethoxysilane]. Characterization tests were performed by scanning electron microscopy (SEM), Raman and Fourier-transform infrared spectroscopy (FT/IR). Samples were stained with methylene blue (MB) and then exposed to solar light for different periods. Color changes of the samples were examined with a spectrophotometer. Air permeability, abrasion and tear strength tests were applied to all samples.

According to SEM images, the NPs were successfully attached to the cotton fabrics, and epoxy silane coating surrounded the fiber surfaces. The presence of the coating was also confirmed by Raman spectroscopy and FT/IR. The treatments reduced the stainability of the samples. The most effective applications for ensuring photocatalytic activity in cotton fabrics were suspensions as 10% brookite, 10% anatase and 5% anatase, in descending order. The applied coating slightly reduced the samples’ air permeability, and wear and tear strength.

The importance of this study is to determine the optimal crystal phase and its concentration by using epoxy silane to ensure self-cleaning properties on cotton fabrics. The sample treated with 10% brookite is the most approached its original white color by 99.65% as a result of degradation of MB (after 120 min). On the other hand, using the pure rutile with epoxy silane was not suitable for removing MB from the fabric.

This study aims to propose that the corrosion resistance of the neat epoxy coating can be further enhanced by incorporating reinforcing agents.

Chitosan, silica and their hybrid compound were used to study the subject of corrosion resistance of epoxy coating systems. This work used 3.5 Wt.% NaCl solution as the electrolyte, and electrochemical impedance spectroscopy (EIS) was used to investigate the electrochemical behaviour of the studied coating systems. Standard and accelerated states were used without and with scratch on the coating layer.

It was found that the impedance value of composite coating incorporated with the hybrid compound was significantly higher at 10¹⁰ Ω after 14 days of exposure in both testing states. The breakpoint frequency (f_b) determination also proves with large capacitive region at low-to-high frequency of impedance plots corresponding to the high corrosion resistance.

The hybrid compound consisting of chitosan as organic biopolymer and silica as inorganic material, respectively, served as a promising reinforcing agent for composite coating as a promising corrosion inhibitor. Different states of EIS measurement were used which are standard (without scratch) and accelerated (with scratch) states associated with the f_b values.

This study aims to fabricate the acrylic-based polymeric composite coating with a hydrophobic surface associated with natural oil polyol (NOP) and polydimethylsiloxane with the incorporation of 3 Wt.% SiO₂ nanoparticle (SiO₂np) against the corrosive NaCl media.

The structural properties of the formulated polymeric composite coatings were investigated by using Fourier transform infrared spectroscopy, ultraviolet-visible spectroscopy, water contact angle (WCA) and cross-hatch (X-Hatch) tests. The WCA measurement was used to study the surface wettability of the formulated polymeric composite coatings. The corrosion protection performance of the nanocomposite coated on the mild steel substrate was studied by immersing the samples in 3.5 Wt.% NaCl solution for 30 days using electrochemical impedance spectroscopy.

The enhanced polymeric composite coating system performed with an excellent increase in the WCA up to 111.1° which is good hydrophobic nature and very high coating resistance in the range of 10¹⁰ Ω attributed to the superiority of SiO₂np.

The incorporation of SiO₂np into the polymeric coating could enhance the surface roughness and hydrophobic properties that could increase corrosion protection. This approach is a novel attempt of using NOP along with the addition of SiO₂np.

The silicone modifications of two-component epoxy resin coatings are commonly built on epoxy resins rather than on epoxy curing agents. The silicone-modified epoxy curing agent system is rarely reported yet. This study aims to prepare the polysiloxane (PS)-modified waterborne epoxy coatings based on aqueous curing agents technology.

Waterborne epoxy curing agents with different contents of terminal epoxy PS were synthesized by reacting with triethylenetetramine, followed by incorporating of epoxy resin (NPEL-128) and polyethylene glycol diglycidyl ether. The waterborne epoxy coatings were prepared with the above curing agents, and their performance was investigated through thermogravimetric analysis, scanning electron microscopy, mechanical characterization, gloss measurement, chemical resistance test and ultraviolet (UV) aging experiment.

The results showed that the epoxy coating prepared by silicon-modified curing agent has higher gloss, better chemical resistance and UV resistance than the coating from unmodified curing agent with terminal epoxy PS and commercially available waterborne epoxy curing agent (Aradur 3986), as well as the competitive mechanical properties and heat resistance. Reduced water absorption on fibrous paper was also obtained with the help of silicon-modified curing agent.

These findings will be valuable for resin researchers in addressing the modification issues about waterborne epoxy resin and curing agent.

The aim of this study is to determine the fracture behavior of wool felt and fabric based epoxy composites and their responses to electromagnetic waves.

Notched and unnotched tensile tests of composites made of wool only and hybridized with a glass fiber layer were carried out, and fracture behavior and toughness at macro scale were determined. They were exposed to electromagnetic waves between 8 and 18 GHz frequencies using two horn antennas.

The keratin and lignin layer on the surface of the wool felt caused lower values to be obtained compared to the mechanical values given by pure epoxy. However, the use of wool felt in the symmetry layer of the laminated composite material provided higher mechanical values than the composite with glass fiber in the symmetry layer due to the mechanical interlocking it created. The use of wool in fabric form resulted in an increase in the modulus of elasticity, but no change in fracture toughness was observed. As a result of the electromagnetic analysis, it was also seen in the electromagnetic analysis that the transmittance of the materials was high, and the reflectance was low throughout the applied frequency range. Hence, it was concluded that all of the manufactured materials could be used as radome material over a wide band.

Sheep wool is an easy-to-supply and low-cost material. In this paper, it is presented that sheep wool can be evaluated as a biocomposite material and used for radome applications.

The combined evaluation of felt and fabric forms of a natural and inexpensive reinforcing element such as sheep wool and the combined evaluation of fracture mechanics and electromagnetic absorption properties will contribute to the evaluation of biocomposites in aviation.

This study explores how titanium oxide (TiO₂) filler influences the specific wear rate (SWR) in flax fiber-reinforced epoxy composites (FFRCs) through a Taguchi approach. It aims to boost abrasive wear resistance by incorporating TiO₂ filler, promoting sustainable and eco-friendly materials.

This study fabricates epoxy/flax composites with TiO₂ particles (0–8 wt%) using hand layup. Composites were tested for wear following American Society for Testing and Materials (ASTM) G99-05. Statistical analysis used Taguchi design of experiments (DOE), with ANOVA identifying key factors affecting SWR in abrasive sliding conditions.

The study illuminates how integrating TiO2 filler particles into epoxy/flax composites enhances abrasive wear properties. Statistical analysis of SWR highlights abrasive grit size (grit) as the most influential factor, followed by normal load, wt% of TiO₂ and sliding distance. Grit size has the highest effect at 43.78%, and wt% TiO₂ filler contributes 15.61% to SWR according to ANOVA. Notably, the Taguchi predictive model closely aligns with experimental results, validating its reliability.

This paper integrates TiO₂ filler and flax fibers to form a novel hybrid composite with enhanced tribological properties in epoxy composites. The use of Taguchi DOE and ANOVA offers valuable insights for optimizing control variables, particularly in natural fiber-reinforced composites (NFRCs).

This paper aims to report the effect of titanium oxide (TiO₂) particles on the specific wear rate (SWR) of alkaline treated bamboo and flax fiber-reinforced composites (FRCs) under dry sliding condition by using a robust statistical method.

In this research, the epoxy/bamboo and epoxy/flax composites filled with 0–8 Wt.% TiO₂ particles have been fabricated using simple hand layup techniques, and wear testing of the composite was done in accordance with the ASTM G99-05 standard. The Taguchi design of experiments (DOE) was used to conduct a statistical analysis of experimental wear results. An analysis of variance (ANOVA) was conducted to identify significant control factors affecting SWR under dry sliding conditions. Taguchi prediction model is also developed to verify the correlation between the test parameters and performance output.

The research study reveals that TiO₂ filler particles in the epoxy/bamboo and epoxy/flax composite will improve the tribological properties of the developed composites. Statistical analysis of SWR concludes that normal load is the most influencing factor, followed by sliding distance, Wt.% TiO2 filler and sliding velocity. ANOVA concludes that normal load has the maximum effect of 31.92% and 35.77% and Wt.% of TiO2 filler has the effect of 17.33% and 16.98%, respectively, on the SWR of bamboo and flax FRCs. A fairly good agreement between the Taguchi predictive model and experimental results is obtained.

This research paper attempts to include both TiO₂ filler and bamboo/flax fibers to develop a novel hybrid composite material. TiO₂ micro and nanoparticles are promising filler materials, it helps to enhance the mechanical and tribological properties of the epoxy composites. Taguchi DOE and ANOVA used for statistical analysis serve as guidelines for academicians and practitioners on how to best optimize the control variable with particular reference to natural FRCs.

The purpose of this study is to investigate the impact of titanium oxide (TiO₂) filler on the abrasive wear properties of bamboo fiber reinforced epoxy composites (BFRCs) using a Taguchi approach. The study aims to enhance the abrasive wear resistance of these composites by introducing TiO₂ filler as a potential reinforcement, thus contributing to the development of sustainable and environmentally friendly materials.

This study focuses on the fabrication of epoxy/bamboo composites infused with TiO₂ particles within the Wt.% range of 0–8 Wt.% using hand layup techniques. The resulting composites were subjected to wear testing according to ASTM G99-05 standards. Statistical analysis of the wear results was carried out using the Taguchi design of experiments (DOE). Additionally, an analysis of variance (ANOVA) was used to determine the influential control factors impacting the specific wear rate (SWR) and coefficient of friction (COF).

The study illuminates how integrating TiO₂ filler enhances abrasive wear in epoxy/bamboo composites. Statistical analysis of SWR highlights abrasive grit size (grit) as the most influential factor, followed by normal load, Wt.% of TiO₂ and sliding distance. Analysis of the COF identifies normal load as the primary influential factor, followed by grit, Wt.% of TiO₂ and sliding distance. The Taguchi predictive model closely aligns with experimental results, validating its reliability. The morphological study revealed significant differences between the unfilled and TiO₂-filled composites. The inclusion of TiO₂ improved wear resistance, as evidenced by reduced surface damage and wear debris.

This research paper aims to integrate TiO₂ filler and bamboo fibers to create an innovative hybrid composite material. TiO₂ micro and nanoparticles show promise as filler materials, contributing to improved tribological properties of epoxy composites. The utilization of Taguchi’s DOE and ANOVA for statistical analysis provides valuable guidance for academic researchers and practitioners in optimizing control variables, especially in the context of natural fiber reinforced composites.

This study aims to explore the synergistic effect of oxide nanoparticles (ZnO, Fe₂O₃, SiO₂) and cerium nitrate inhibitor on anti-corrosion performance of epoxy coating. First, cerium nitrate inhibitors are absorbed on the surface of various oxide nanoparticles. Thereafter, epoxy nanocomposite coatings have been fabricated on carbon steel substrate using these oxide@Ce nanoparticles as both nano-fillers and nano-inhibitors.

To evaluate the impact of oxides@Ce nanoparticles on mechanical properties of epoxy coating, the abrasion resistance and impact resistance of epoxy coatings have been examined. To study the impact of oxides@Ce nanoparticles on anti-corrosion performance of epoxy coating for steel, the electrochemical impedance spectroscopy has been carried out in 3% NaCl solution.

ZnO@Ce3+ and SiO2@Ce3+ nanoparticles provide more enhancement in the epoxy pore network than modification of the epoxy/steel interface. Whereas, Fe2O3@Ce3+ nanoparticles have more to do with modification of the epoxy/steel interface than to change the epoxy pore network.

Incorporation of both oxide nanoparticles and inorganic inhibitor into the epoxy resin is a promising approach for enhancing the anti-corrosion performance of carbon steel.

The incompatibility of natural fibers with polymer matrices is one of the key obstacles restricting their use in polymer composites. The interfacial connection between the fibers and the matrix was weak resulting in a lack of mechanical properties in the composites. Chemical treatments are often used to change the surface features of plant fibers, yet these treatments have significant drawbacks such as using substantial amounts of liquid and chemicals. Plasma modification has recently become very popular as a viable option as it is easy, dry, ecologically friendly, time-saving and reduces energy consumption. This paper aims to explore plasma treatment for improving the surface adhesion characteristics of sisal fibers (SFs) without compromising the mechanical attributes of the fiber.

A cold glow discharge plasma (CGDP) modification using N₂ gas at varied power densities of 80 W and 120 W for 0.5 h was conducted to improve the surface morphology and interfacial compatibility of SF. The mechanical characteristics of unmodified and CGDP-modified SF-reinforced epoxy composite (SFREC) were examined as per the American Society for Testing and Materials standards.

The cold glow discharge nitrogen plasma treatment of SF at 120 W (30 min) enhanced the SFREC by nearly 122.75% superior interlaminar shear strength, 71.09% greater flexural strength, 84.22% higher tensile strength and 109.74% higher elongation. The combination of improved surface roughness and more effective lignocellulosic exposure has been responsible for the increase in the mechanical characteristics of treated composites. The development of hydrophobicity in the SF had been induced by CGDP N₂ modification and enhanced the size of crystals and crystalline structure by removing some unwanted constituents of the SF and etching the smooth lignin-rich surface layer of the SF particularly revealed via FTIR and XRD.

Chemical and physical treatments have been identified as the most efficient ways of treating the fiber surface. However, the huge amounts of liquids and chemicals needed in chemical methods and their exorbitant performance in terms of energy expenditure have limited their applicability in the past decades. The use of appropriate cohesion in addition to stimulating the biopolymer texture without changing its bulk polymer properties leads to the formation and establishment of plasma surface treatments that offer a unified, repeatable, cost-effective and environmentally benign replacement.

The authors are sure that this technology will be adopted by the polymer industry, aerospace, automotive and related sectors in the future.