Search results

The purpose of this study is to examine how well reinforced concrete structures can be shielded against concrete carbonation using anti-carbonation coatings based on synthetic polymer.

Applying free radical polymerization, an acrylate terpolymer emulsion that a surfactant had stabilized was created. A thermogravimetric analysis, minimum film-forming temperature, Fourier transform infrared spectroscopy and particle size distribution are used to characterize the prepared eco-friendly water base acrylate terpolymer emulsion. Using three different percentages of the acrylate terpolymer emulsion produced, 35%, 45% and 55%, the anti-carbonation coating was formed. Tensile strength, tensile strain, elongation, crack-bridging ability, carbon dioxide permeability, chloride ion diffusion, average pull-off adhesion strength, water vapor transmission, gloss, wet scrub resistance, QUV/weathering and storage stability are the characteristics of the anti-carbonation coating.

The formulated acrylate terpolymer emulsion enhances anti-carbonation coating performance in CO₂ permeability, Cl-diffusion, crack bridging, pull-off adhesion strength and water vapor transmission. The formed coating based on the formulated acrylate terpolymer emulsion performed better than its commercial counterpart.

To protect the steel embedded in concrete from corrosion and increase the life span of concrete, the surface of cement is treated with an anti-carbonation coating based on synthetic acrylate terpolymer emulsion.

In addition to saving lives from building collapse, it maintains the infrastructure for the long run.

The anti-carbonation coating, which is based on the synthetic acrylate terpolymer emulsion, is environmentally benign and stops the entry of carbon dioxide and chlorides, which are the main causes of steel corrosion in concrete.

The purpose of this paper is to develop a high-performance composite emulsion cement waterproof coating. The coating has excellent durability and is effective in protecting cement mortar substrates from harmful ions.

The polymer cement waterproof coatings with different emulsion compounding ratios were tested for mechanical properties and water resistance after alkali immersion, water immersion, thermal aging and UV aging, and the coatings were analyzed by infrared spectroscopy after aging to evaluate its durability. Meanwhile, the coating that presents favorable durability was applied to cement mortar test blocks. The protective effect of the coating on the test blocks was tested by immersion method, and X-ray diffraction analysis was performed on the eroded test blocks.

The coating with neoprene latex/acrylate latex weight ratio of 90/10 presents favorable durability and has superior overall performance. Besides, when it is applied to cement mortar blocks, the coatings effectively reduced the erosive effect of harmful ions on cement mortar blocks, resulting in much lower mass change ratios and less internal structural damage of the blocks significantly.

The obtained coating will be of great application potential for use in building waterproofing construction. Moreover, the coating can practically prevent chloride ions and sulfate ions from penetrating cement-based materials.

This study aims to synthesize Prussian blue {Fe^III₄[Fe^II(CN)₆]₃} pigment by reacting ferric chloride with different ferrocyanides through the same procedure. The influence of the ferrocyanide used on resulting pigment properties is studied.

Prussian blue is commonly synthesized by direct or indirect methods, through iron salt and ferrocyanide/ferricyanide reactions. In this study, the direct, single-step process was pursued by dropwise addition of the ferrocyanide into ferric chloride (both as aqueous solutions). Two batches – (K-PB) and (Na-PB) – were prepared by using potassium ferrocyanide and sodium ferrocyanide, respectively. The development of pigment was confirmed by an identification test and characterized by spectroscopic techniques. Pigment properties were determined, and light fastness was observed for acrylic emulsion films incorporating dispersed pigment.

The two pigments differed mainly in elemental detection owing to the dissimilar ferrocyanide being used; IR spectroscopy where only (Na-PB) showed peaks indicating water molecules; and bleeding tendency where (K-PB) was water soluble whereas (Na-PB) was not. The pigment exhibited remarkable blue colour and good bleeding resistance in several solvents and showed no fading in 24 h of light exposure though oil absorption values were high.

This article is a comparative study of Prussian blue pigment properties obtained using different ferrocyanides. The dissimilarity in the extent of water solubility will influence potential applications as a colourant in paints and inks. K-PB would be advantageous in aqueous formulations to confer a blue colour without any dispersing aid but unfavourable in systems where other coats are water-based due to their bleeding tendency.

The color painting of ancient buildings has high historical and artistic value but is prone to aging due to long-term outdoor exposure. The purpose of this study is to develop a new type of sealing coating to mitigate the impact of ultraviolet (UV) light on color painting.

The new coating was subjected to a 500-h UV-aging test. Compared with the existing acrylic resin Primal AC33, the UV aging behavior of the new coating, such as color difference and gloss, was studied with aging time. The Fourier infrared spectra of the coatings were analyzed after the UV-aging test.

Compared with AC33, the antiaging performance of SF8 was substantially improved. SF8 has a lower color difference value and better light retention and hydrophobicity. The Fourier transform infrared spectroscopy results showed that the C-F bond and Si-O bonds in the resin of the optimized sealing coating protected the main chain C-C structure from degradation during the aging process; thus, the resin maintained good stability. The hindered amine light stabilizer TN292 added to the coating inhibited the antiaging process by trapping active free radicals.

To address the problem of UV aging of oil-decorated colored paintings, a new type of sealing coating with excellent antiaging properties was developed, laying the foundation for its demonstration application on the surface of ancient buildings.

Self-crosslinked long fluorocarbon acrylate polymer latex has good hydrophobic and oleophobicity, weather resistance, aging resistance, stability and other excellent properties, which make the polymer be widely used in coatings, dyes, adhesives and other products. The purpose of this study is to prepare self-crosslinked long fluorocarbon acrylate polymer latex via semi-continuous seeded emulsion technology and carry out comparative study on two different cross-linked monomers.

Methyl methacrylate (MMA) and butyl acrylate (BA) were used as the main monomers, dodecafluoroheptyl methacrylate (DFMA) as the fluoromonomer, hydroxypropyl methacrylate (HPMA) and N-methylol acrylamide (NMA) as cross-linked monomers, and 1-allyloxy-3–(4-nonylphenol)-2-propanol polyoxyethylene (10) ether (ANPEO10) and 1-allyloxy-3–(4-nonylphenol)-2-propanol polyoxyethylene (10) ether ammonium sulfate (DNS-86) as compound emulsifiers via the semicontinuous-seeded emulsion polymerization.

The properties of the polymer emulsions, which are prepared with two different cross-linked monomers, are compared and discussed, and it is concluded that HPMA is more suitable for the preparation of self-crosslinked polymer emulsions. The formula of the polymer latex is ANPEO10: DNS-86 = 1:1, and the mass ratio of the monomers used in the polymer is MMA: BA: DFMA: HPMA = 14.40:14.40:0.60:0.60.

Self-crosslinked long fluorocarbon acrylate polymer latex can be used in many fields such as coatings, dyes, adhesives and other products.

The self-crosslinked long fluorocarbon acrylate polymer latex is prepared by mixing the nonionic emulsifier ANPEO10 and the anionic emulsifier DNS-86 when potassium persulfate is used as the thermal decomposition initiator and the semicontinuous-seeded emulsion technology is adopted and the comparative study on two different cross-linked monomer is carried out, which is not reported in the open literatures.

Titanium(IV) oxide nanoparticles (TiO₂ NP) were deposited to cotton denim fabrics using a self-crosslinking acrylate – a polymer dispersion to extend the lifetime of the products. This study aims to determine the optimum conditions to increase abrasion resistance, to provide self-cleaning properties of denim fabrics and to examine the effects of these applications on other physical properties.

The denim samples were first treated with nonionic surfactant to increase their wettability. Three different amounts of the polymer dispersion and two different pH levels were selected for the experimental design. The finishing process was applied to the fabrics with pad-dry-cure method.

The presence of the coatings and the adhesion of TiO₂ NPs to the surfaces were confirmed by scanning electron microscope and Fourier transform infrared spectroscopy analysis. It was ascertained that the most appropriate self-crosslinking acrylate amount and ambient pH level is 10 mL and “2”, respectively, for providing increased abrasion resistance (2,78%) and enhanced self-cleaning properties (363,4%) in the denim samples. The coating reduced the air permeability and softness of the denim samples. Differential scanning calorimetry and thermogravimetry analysis results showed that the treatments increased the crystallization temperatures and melting enthalpy values of the denim samples. Based on the thermal test results, it is clear that mass loss of the denim samples at 370°C decreased as the amount of self-crosslinking acrylate increased (at pH 3).

This study helped us to find out optimum amount of self-crosslinking acrylate and proper pH level for enhanced self-cleaning and abrasion strength on denim fabrics. With this finishing process, an environmentally friendly and long-life denim fabric was designed.

This study aims to evaluate the efficiency of using some polymers at different concentrations in the consolidation of vegetable-tanned leather artifacts.

New vegetable-tanned leather samples were prepared. The consolidants used were polyacrylamide (PAM) and polymethyl methacrylate/hydroxyethyl methacrylate (MMA-HEMA). Accelerated heat aging was applied to the untreated and treated samples. Analytical techniques used were Fourier transform infrared spectroscopy (FTIR), digital microscope, scanning electron microscope (SEM), change of color and mechanical properties.

The characteristic FTIR bands showed the effect of accelerated heat aging on the molecular structure of the studied samples, but treated and aged treated samples used were better than aged untreated samples. Microscopic investigations (digital and SEM), and mechanical properties proved that 2% was the best concentration for polymers used. The change in the total color difference of the treated and aged treated samples was limited.

This study presents the important results obtained from PAM and poly(MMA-HEMA) used for the consolidation of vegetable-tanned leather artifacts. The best results of the studied polymers can be applied directly to protect historical vegetable-tanned leathers.

This paper aims to synthesize new screen-printing ink formula based on new derivatives of azo thiadiazol disperse dyes and evaluate their characteristics after being printed on polyester fabric substrates.

New dispersed dyes based on 1, 3, 4-Thiadiazole derivatives (dyes 1 and 2) were prepared and confirmed by different analyses, infrared (IR), mass and nuclear magnetic resonance (NMR) spectroscopy, and then formulated as colored materials in the screen-printing ink formulations. Printing pastes containing the prepared dyestuffs and other ingredients were used for printing polyester using screen-printing or traditional printing. The characteristics of printed polyester fabric substrates were measured by color measurements such as a*, b*, L*, C*, E, Ho, R% and color strength, as well as light, washing, crock and alkali perspiration fastness, and finally, the depth of penetration was evaluated.

The prepared 1, 3, 4-Thiadiazole derivatives (dyes 1 and 2) were obtained from the reaction of 5,5’-(1,4-phenylene)bis(1,3,4-Thiadiazole-2-amine) with resorcinol and m-toluidine as a coupling component. The suitability of the prepared dyestuffs for silk screen-printing on polyester fabrics has been investigated. The prints obtained from a formulation containing dye 1 possess high color strength as well as good overall fastness properties if compared to those obtained using dye 2.

The method of synthesis of the new dyestuffs and screen-printing ink provides a simple and practical solution to prepare some new heterocyclic disperse azo dyes, and they are formulated in the screen-printing inks for printing on a polyester fabric substrate.

The prepared disperse dyes based on 1,3,4-Thiadiazole derivatives (dyes 1 and 2) could be used in textile printing of polyester on an industrial scale.

This paper aims to investigate the effect of shear rate, concentration (4–20 kg/m³) and temperature (20°C–60 °C) on the apparent viscosity of apricot gum solutions.

Apparent viscosity has been measured using a rotational viscometer.

It has been observed that the shear stress and apparent viscosity values increase at high concentrations in the prepared apricot gum solutions. However, it is understood that the higher the temperature in the operation conditions, the lower the apparent viscosity results. Power-law is found the best-fitting model to illustrate the changes in temperature and concentration. According to the consistency coefficient and flow behavior indices, the apricot gum displayed shear-thinning behavior (pseudoplastic). The apricot gum is a polysaccharide with amino and uronic acids, according to Fouirer Transform Infrared Spektrofotometre spectra.

The results suggest that power-law model can be used to estimate the viscosity of apricot gum solutions at different temperatures and concentrations for applications for which flow behavior should be taken into account.

Exudate gums have good rheological properties and, therefore, are widely used in the food industry. Apricot gum is a biodegradable and abundant polysaccharide that enhances viscosity, stabilizes suspension or emulsion and improves the flow properties of foods. Different rheological models are used to investigate rheological properties. However, those models are time-independent to fit the experimental data.

This study aims to extend the pot life without altering the qualities and performance of the coating, which is important to increase when manufacturing polyurethane coatings.

An acrylic polyol from a mixture of different monomers of hydroxypropyl methacrylate, methacrylic acid, 2-ethylhexyl acrylate, methyl methacrylate and n-butyl methacrylate was prepared with different ratios of 2,4-pentanedione as a pot life extender. The reaction takes place in presence of di-tert-butyl peroxide as initiator with samples (T1–T7). The physical properties of prepared acrylic polyol were characterized. Then, coating polyurethane varnish was prepared from the prepared acrylic polyol with an aliphatic polyisocyanate in a 1:1 equivalent ratio of OH:NCO at room temperature, in presence of paint thinner (diluents/solvent) and dibutyltin dilaurate as a catalyst to give samples (T1C–T7C). This coating was evaluated via Fourier-transform infrared spectroscopy, drying time, hardness and gloss, distinctness of image and reflected image quality.

The coating has a prolonged pot life while still maintaining the other qualities, thanks to the greater 2,4-pentanedione content.

It is desired to have a paint which has a satisfactory pot life, short curing time and reduces many drawbacks such as inefficient working and deterioration of the paint before application.