1 – 10 of over 3000S.N. Basavana Gowda, Subhash Yaragal, C. Rajasekaran and Sharan Kumar Goudar
In recent years, fire accidents in engineering structures have often been reported worldwide, leading to a severe risk to life and property safety. The present study is carried…
Abstract
Purpose
In recent years, fire accidents in engineering structures have often been reported worldwide, leading to a severe risk to life and property safety. The present study is carried out to evaluate the performance of Ground Granulated Blast Furnace Slag (GGBS) and fly ash–blended laterized mortars at elevated temperatures.
Design/methodology/approach
This test program includes the replacement of natural river sand with lateritic fine aggregates (lateritic FA) in terms of 0, 50 and 100%. Also, the ordinary Portland cement (OPC) was replaced with fly ash and GGBS in terms of 10, 20, 30% and 20, 40 and 60%, respectively, for producing blended mortars.
Findings
This paper presents results related to the determination of residual compressive strengths of lateritic fine aggregates-based cement mortars with part replacement of cement by fly ash and GGBS exposed to elevated temperatures. The effect of elevated temperatures on the physical and mechanical properties was evaluated with the help of microstructure studies and the quantification of hydration products.
Originality/value
A sustainable cement mortar was produced by replacing natural river sand with lateritic fine aggregates. The thermal strength deterioration features were assessed by exposing the control specimens and lateritic fine aggregates-based cement mortars to elevated temperatures. Changes in the mechanical properties were evaluated through a quantitative microstructure study using scanning electron microscopy (SEM) images. The phase change of hydration products after exposure to elevated temperatures was qualitatively analyzed by greyscale thresholding of SEM images using Image J software.
Details
Keywords
Sachin Vijaya Kumar and N. Suresh
The Reinforced Concrete(RC) elements are known to perform well during exposure to elevated temperatures. Hence, RC elements are widely used to resist the extreme heat developing…
Abstract
Purpose
The Reinforced Concrete(RC) elements are known to perform well during exposure to elevated temperatures. Hence, RC elements are widely used to resist the extreme heat developing from accidental fires and other industrial processes. In both of the scenarios, the RC element is exposed to elevated temperatures. However, the primary differences between the fire and processed temperatures are the rate of temperature increase, mode of exposure and exposure durations. In order to determine the effect of two heating modalities, RC beams were exposed to processed temperatures with slow heating rates and fire with fast heating rates.
Design/methodology/approach
In the present study, RC beam specimens were exposed to 200 °C, to 800 °C temperature at 200 °C intervals for 2 h' duration by adopting two heating modes; Fire and processed temperatures. An electrical furnace with low-temperature increment and a fire furnace with standard time-temperature increment is adapted to expose the RC elements to elevated temperatures.
Findings
It is observed from test results that, the reduction in load-carrying capacity, first crack load, and thermal crack widths of RC beams exposed to 200 °C, and 600 °C temperature at fire is significantly high from the RC beams exposed to the processed temperature having the same maximum temperature. As the exposure temperature increases to 800 °C, the performance of RC beams at all heating modes becomes approximately equal.
Originality/value
In this work, residual performance, and failure modes of RC beams exposed to elevated temperatures were achieved through two different heating modes are presented.
Details
Keywords
R.V. Balendran, T.M. Rana, T. Maqsood and W.C. Tang
The inclusion of pozzolans like pulverised fuel ash (PFA), silica fume (SF) and metakaolin (MK) enhances the properties of concrete both in fresh and hardened states. In the case…
Abstract
The inclusion of pozzolans like pulverised fuel ash (PFA), silica fume (SF) and metakaolin (MK) enhances the properties of concrete both in fresh and hardened states. In the case of high performance concrete (HPC), their role in enhancing the workability, strength and durability is extremely significant. However HPC has been observed to be more vulnerable than normal strength concrete when exposed to elevated temperatures. This paper presents an overview and discusses the strength and durability performance of high‐performance pozzolanic concretes incorporating PFA, SF, and MK subjected to elevated temperatures. Various researchers have demonstrated that addition of silica fume causes HPC to perform poorly when subjected to elevated temperatures. Higher loss of strength and spalling risks are also associated with it. Addition of PFA and MK has been found to improve the fire performance of HPC both in terms of residual strength and durability.
Details
Keywords
Mariyana Aida Ab Kadir, Mohammad Iqbal Khiyon, Abdul Rahman Mohd. Sam, Ahmad Beng Hong Kueh, Nor Hasanah Abdul Shukor Lim, Muhammad Najmi Mohamad Ali Mastor, Nurizaty Zuhan and Roslli Noor Mohamed
The purpose of this paper is to examine the mechanical properties, material composition of spent garnet as a sand replacement in high-strength concrete at room and elevated…
Abstract
Purpose
The purpose of this paper is to examine the mechanical properties, material composition of spent garnet as a sand replacement in high-strength concrete at room and elevated temperatures. Bonding of the concrete containing spent garnet and reinforcing rebar is investigated. Moreover, the optimum thickness of concrete cover subjected to elevated temperatures is investigated.
Design/methodology/approach
First, the plain spent garnet was physically, chemically and thermally studied. Then, a series of concrete specimens with 0, 20, 40, 60, 80 and 100 per cent of spent garnet were prepared to determine the optimum percentage of spent garnet. Finally, the physical and mechanical behaviours of concrete specimens and effects of cover thickness on steel rebar when subjected to elevated temperature of 200°C, 400°C, 600°C and 800°C for 1 h were studied. It was observed that spent garnet was thermally stable compared to river sand.
Findings
Mechanical properties were found to be optimal for concrete with 40% spent garnet replacement. Physically, spent garnet concrete changed colour to brown at 400°C, and to whitish grey at 600°C. The residual compressive strength of spent garnet concrete was also found slightly higher than that for control specimens. At various high temperatures, the reduction in ultimate tensile stress for steel bar inside concrete cover of 30 mm was the lowest compared to that of 20 mm.
Research limitations/implications
Spalling effect it not considered in this study.
Practical implications
The optimum concrete cover is important issues in reinforced concrete design. This can be used as a guideline by structural designers when using a different type of concrete material in the construction.
Social implications
Utilization of the waste spent garnet reduces usage of natural aggregates in concrete production and enhances its performance at elevated temperatures. Natural aggregates are normally taken from sand and rock. The new innovation in concrete perhaps can produce light concrete, reduce the cost of concrete production and at the same time also mitigates environmental problems affect from waste material such as minimizing disposal area.
Originality/value
Utilization of spent garnet in ordinary Portland cement (OPC) concrete at high temperature is a new innovation. It shows that the concrete cover of the concrete element reduced as compared to the OPC concrete. Reduce in weight concrete however the strength of concrete is similar to conventional concrete. This study at elevated temperature has never been performed by any previous researcher.
Details
Keywords
Subhash Yaragal, Chethan Kumar B. and Manoj Uddavolu Abhinav
To reduce environmental impact caused by excessive use of ordinary Portland cement (OPC) and to mitigate scarcity of base materials such as natural coarse aggregate (NCA)…
Abstract
Purpose
To reduce environmental impact caused by excessive use of ordinary Portland cement (OPC) and to mitigate scarcity of base materials such as natural coarse aggregate (NCA), industrial by-products can be carefully used as alternatives to OPC and NCA, in production of concrete. This paper aims to describe the performance of using ground granulated blast furnace slag (GGBS), fly ash (FA) as a complete replacement to OPC and ferrochrome slag (FCS) as replacement to NCA in production of novel FCS based alkali activated slag/fly ash concretes (AASFC) and evaluate their performance at elevated temperatures.
Design/methodology/approach
Two control factors with three levels each i.e. FA (0, 25 and 50 per cent by weight) and FCS (0, 50 and 100 per cent by volume) as a GGBS and NCA replacement, respectively, were adopted in AASFC mixtures. Further, AASFC mixture specimens were subjected to different levels of elevated temperature, i.e. 200°C, 400°C, 600°C and 800°C. Compressive strength and residual compressive strength were considered as responses. Three different optimization techniques i.e. gray relational analysis, technique for order preference by similarity to ideal solution and Desirability function approach were used to optimize AASFC mixtures subjected to elevated temperatures.
Findings
As FA replacement increases in FCS based AASFC mixtures, workability increases and compressive strength decreases. The introduction of FCS as replacement to NCA in AASFC mixture did not show any significant change in compressive strength under ambient condition. AASFC produced with 75 per cent GGBS, 25 per cent FA and 100 per cent FCS was found to have excellent elevated temperature enduring properties among all other AASFC mixtures studied.
Originality/value
Although several studies are available on using GGBS, FA and FCS in production of OPC-based concretes, present study reports the performance of novel FCS based AASFC mixtures subjected to elevated temperatures. Further, GGBS, FA and FCS used in the present investigation significantly reduces CO2 emission and environmental degradation associated with OPC production and NCA extraction, respectively.
Details
Keywords
Shanglong Fang, Wei Xiao, Kewen Chen and Xuding Song
Resin-based friction materials are the most widely used key materials in industry for braking and transmission. However, the friction coefficient of resin-based friction materials…
Abstract
Purpose
Resin-based friction materials are the most widely used key materials in industry for braking and transmission. However, the friction coefficient of resin-based friction materials significantly decreases at temperatures above 300°C, which reduces their friction performance.
Design/methodology/approach
This study combines elevated-temperature mechanical experiments with friction and wear experiments to explain the thermal degradation resistance performance and temperature recovery performance of resin-based friction materials. It also investigates the influence of friction material strength and worn morphology on the friction coefficient of materials at elevated temperature.
Findings
The experimental results show that the increase in friction coefficient of friction materials below 300°C is mainly due to the increase in worn morphology characterization parameters, and the thermal degradation phenomenon above 300°C is mainly due to the decrease of shear strength of friction film. Basalt fiber can significantly improve the thermal degradation resistance of friction materials. The friction coefficient of basalt fiber-reinforced specimens after thermal degradation reaches 0.421–0.443, which is 19–25% higher than the original. The thermal decay rate is 9.03–11.0%, which is 7.9–9.87% lower than the original. Moreover, the friction coefficient has good cooling recovery performance.
Originality/value
Revealed the thermal degradation mechanism of resin-based friction materials, verified that basalt fibers can improve the thermal degradation resistance of friction materials and provided reference for the development of new friction materials.
Details
Keywords
Nurizaty Zuhan, Mariyana Aida Ab Kadir, Muhammad Najmi Mohamad Ali Mastor, Shek Poi Ngian and Abdul Rahman Mohd. Sam
Concrete-filled steel hollow (CFHS) column is an innovation to improve the performance of concrete or steel column. It is believed to have high compressive strength, good…
Abstract
Purpose
Concrete-filled steel hollow (CFHS) column is an innovation to improve the performance of concrete or steel column. It is believed to have high compressive strength, good plasticity and is excellent for seismic and fire performance as compared to hollow steel column without a filler.
Design/methodology/approach
Experimental and numerical investigation has been carried out to study the performance of CFHS having different concrete in-fill and shape of steel tube.
Findings
In this paper, an extensive review of experiment performed on CFHS columns at elevated temperature is presented in different types of concrete as filling material. There are three different types of concrete filling used by the researchers, such as normal concrete (NC), reinforced concrete and pozzolanic-fly ash concrete (FC). A number of studies have conducted experimental investigation on the performance of NC casted using recycled aggregate at elevated temperature. The research gap and the recommendations are also proposed. This review will provide basic information on an innovation on steel column by application of in-filled materials.
Research limitations/implications
Design guideline is not considered in this paper.
Practical implications
Fire resistance is an important issue in the structural fire design. This can be a guideline to define the performance of the CFHS with different type of concrete filler at various exposures.
Social implications
Utilization of waste fly ash reduces usage of conventional cement (ordinary Portland cement) in concrete production and enhances its performance at elevated temperature. The new innovation in CFHS columns with FC can reduce the cost of concrete production and at the same time mitigate the environmental issue caused by waste material by minimizing the disposal area.
Originality/value
Review on the different types of concrete filler in the CFHS column. The research gap and the recommendations are also proposed.
Details
Keywords
Abbas Rezaeian, Mona Mansoori and Amin Khajehdezfuly
Top-seat angle connection is known as one of the usual uncomplicated beam-to-column joints used in steel structures. This article investigates the fire performance of welded…
Abstract
Purpose
Top-seat angle connection is known as one of the usual uncomplicated beam-to-column joints used in steel structures. This article investigates the fire performance of welded top-seat angle connections.
Design/methodology/approach
A finite element (FE) model, including nonlinear contact interactions, high-temperature properties of steel, and material and geometric nonlinearities was created for accomplishing the fire performance analysis. The FE model was verified by comparing its simulation results with test data. Using the verified model, 24 steel-framed top-seat angle connection assemblies are modeled. Parametric studies were performed employing the verified FE model to study the influence of critical factors on the performance of steel beams and their welded angle joints.
Findings
The results obtained from the parametric studies illustrate that decreasing the gap size and the top angle size and increasing the top angles thickness affect fire behavior of top-seat angle joints and decrease the beam deflection by about 16% at temperatures beyond 570 °C. Also, the fire-resistance rating of the beam with seat angle stiffener increases about 15%, compared to those with and without the web stiffener. The failure of the beam happens when the deflections become more than span/30 at temperatures beyond 576 °C. Results also show that load type, load ratio and axial stiffness levels significantly control the fire performance of the beam with top-seat angle connections in semi-rigid steel frames.
Originality/value
Development of design methodologies for these joints and connected beam in fire conditions is delayed by current building codes due to the lack of adequate understanding of fire behavior of steel beams with welded top-seat angle connections.
Details
Keywords
Vadiraj Rao, N. Suresh and G.P. Arun Kumar
The majority of previous studies made on Recycled Concrete Aggregates (RCA) are limited to the utilisation of non-structural grade concrete due to unfavourable physical…
Abstract
Purpose
The majority of previous studies made on Recycled Concrete Aggregates (RCA) are limited to the utilisation of non-structural grade concrete due to unfavourable physical characteristics of RCA including the higher absorption of water, tending to increased water requirement of concrete. This seriously limits its applicability and as a result it reduces the usage of RCA in structural members. In the present study, the impact of hybrid fibres on cracking behaviour of RCA concrete beams along with the inclusion of reinforcing steel bars under two-point loading system exposed to different sustained elevated temperatures are being investigated.
Design/methodology/approach
RCA is substituted for Natural Coarse Aggregates (NCA) at 0, 50 and 100 percentages. The study involves testing of 150 mm cubes and beams of size (700 × 150 × 150) mm, i.e. with steel reinforcing bars along with the addition of 0.35% Steel fibres+ 0.15% polypropylene fibres. The specimens are being exposed to temperatures from 100° to 500°C with 100° interval for 2 h. Studies were made on the post crack analysis, which includes the measurement of crack width, crack length and load at first crack. The crack patterns were analysed in order to understand the effect of fibres and RCA at sustained elevated temperatures.
Findings
The result shows that ultimate load carrying capacity of reinforced concrete beams and load at first crack decreases with the raise in temperatures and increased percentage of RCA content in the mix. Further that 100% RCA replacement specimens showed lesser cracks when compared to the other mixes and the inclusion of fibres enhances the flexural capacity of members highlighting the importance of fibres.
Practical implications
RCA can be used for structural purposes and the study can be projected for assessing the performance of real structures with the extent of fire damage when recycled aggregates are used.
Social implications
Most of recycled materials can be used in the regular concrete which solves two problems namely avoiding the dumping of C&D waste and preventing the usage of natural aggregates. Hence the study provides sustainable option for the production of concrete.
Originality/value
The reduction in capacity of flexural members due to the utilisation of recycled aggregates can be negated by the usage of fibres. Hence improved flexural performance is observed for specimens with fibres at sustained elevated temperatures.
Details
Keywords
Balamurali Kanagaraj, N. Anand, Johnson Alengaram and Diana Andrushia
The present work focuses on evaluating the physical and mechanical characteristics of geopolymer concrete (GPC) by replacing the sodium silicate waste (SSW) in place of…
Abstract
Purpose
The present work focuses on evaluating the physical and mechanical characteristics of geopolymer concrete (GPC) by replacing the sodium silicate waste (SSW) in place of traditional river sand. The aim is to create eco-friendly concrete that mitigates the depletion of conventional river sand and conserves natural resources. Additionally, the study seeks to explore how the moisture content of filler materials affects the performance of GPC.
Design/methodology/approach
SSW obtained from the sodium silicate industry was used as filler material in the production of GPC, which was cured at ambient temperature. Instead of the typical conventional river sand, SSW was substituted at 25 and 50% of its weight. Three distinct moisture conditions were applied to both river sand and SSW. These conditions were classified as oven dry (OD), air dry (AD) and saturated surface dry (SSD).
Findings
As the proportion of SSW increased, there was a decrease in the slump of the GPC. The setting time was significantly affected by the higher percentage of SSW. The presence of angular-shaped SSW particles notably improved the compressive strength of GPC when replacing a portion of the river sand with SSW. When exposed to elevated temperatures, the performance of the GPC with SSW exhibited similar behavior to that of the mix containing conventional river sand, but it demonstrated a lower residual strength following exposure to elevated temperatures.
Originality/value
Exploring the possible utilization of SSW as a substitute for river sand in GPC, and its effects on the performance of the proposed mix. Analyzing, how varying moisture conditions affect the performance of GPC containing SSW. Evaluating the response of the GPC with SSW exposed to elevated temperatures in contrast to conventional river sand.