1 – 4 of 4Gustavo Tressia, Luis H.D. Alves, Amilton Sinatora, Helio Goldenstein and Mohammad Masoumi
The purpose of this study is to develop a lower bainite structure consists of a dispersion of fine carbide inside plates of bainitic ferrite from chemical composition unmodified…
Abstract
Purpose
The purpose of this study is to develop a lower bainite structure consists of a dispersion of fine carbide inside plates of bainitic ferrite from chemical composition unmodified conventional pearlitic steel under bainitic transformation and to investigate its effect on tensile properties and wear resistance.
Design/methodology/approach
A commercial hypereutectoid pearlitic rail steel was subjected to three different bainitic transformation treatments followed by tempering to develop a desirable microstructure with a DIL805 BÄHR dilatometer. A comprehensive microstructural study was performed by scanning electron microscopy and energy dispersive x-ray spectroscopy. Finally, the mechanical properties and wear resistance were evaluated by tensile, microhardness, and pin-on-disc tests.
Findings
The results showed that the best combination of mechanical properties and sliding wear resistance was obtained in the sample subjected to bainitic transformation at 300°C for 600 s followed by tempering at 400°C for 300 s. This sample, which contained a bainitic ferrite structure, exhibited approximately 20% higher hardness and approximately 53% less mass loss than the as-received pearlitic sample due to the mechanically induced transformation in the contact surface.
Originality/value
Although pearlitic steel is widely used in the construction of railways, recent studies have revealed that bainitic transformation at the same rail steels exhibited higher wear resistance and fatigue strengths than conventional pearlitic rail at the same hardness values. Such a bainitic microstructure can improve the mechanical properties and wear resistance, which is a great interest in the railway industry.
Peer review
The peer review history for this article is available at: https://publons.com/publon/10.1108/ILT-07-2019-0282/
Details
Keywords
Akhil Khajuria, Anurag Misra and S. Shiva
An experimental investigation for developing structure-property correlations of hot-rolled E410 steels with different carbon contents, i.e. 0.04wt.%C and 0.17wt.%C metal active…
Abstract
Purpose
An experimental investigation for developing structure-property correlations of hot-rolled E410 steels with different carbon contents, i.e. 0.04wt.%C and 0.17wt.%C metal active gas (MAG) and cold metal transfer (CMT)-MAG weldments was undertaken.
Design/methodology/approach
Mechanical properties and microstructure of MAG and CMT-MAG weldments of two E410 steels with varying content of carbon were compared using standardized mechanical testing procedures, and conventional microscopy.
Findings
0.04wt.%C steel had strained ferritic and cementite sub-structures in blocky shape and large dislocation density, while 0.17wt.%C steel consisted of pearlite and polygonal ductile ferrite. This effected yield strength (YS), and microhardness being larger in 0.04wt.%C steel, %elongation being larger in 0.17wt.%C steel. Weldments of both E410 steels obtained with CMT-MAG performed better than MAG in terms of YS, ultimate tensile strength (UTS), %elongation, and toughness. It was due to low heat input of CMT-MAG that resulted in refinement of weld metal, and subzones of heat affected zone (HAZ).
Originality/value
A substantial improvement in YS (∼9%), %elongation (∼38%), and room temperature impact toughness (∼29%) of 0.04wt.%C E410 steel is achieved with CMT-MAG over MAG welding. Almost ∼10, ∼12.5, and ∼16% increment in YS, %elongation, and toughness of 0.17wt.%C E410 steel is observed with CMT-MAG. Relatively low heat input of CMT-MAG leads to development of fine Widmanstätten and acicular ferrite in weld metal and microstructural refinement in HAZ subzones with nearly similar characteristics of base metal.
Details
Keywords
Mayur Pratap Singh, Dinesh Kumar Shukla, Rajneesh Kumar and Kanwer Singh Arora
The key purpose of conducting this review is to identify the issues that affect the structural integrity of pipeline structures. Heat affected zone (HAZ) has been identified as…
Abstract
Purpose
The key purpose of conducting this review is to identify the issues that affect the structural integrity of pipeline structures. Heat affected zone (HAZ) has been identified as the weak zone in pipeline welds which is prone to have immature failures
Design/methodology/approach
In the present work, literature review is conducted on key issues related to the structural integrity of pipeline steel welds. Mechanical and microstructural transformations that take place during welding have been systematically reviewed in the present review paper.
Findings
Key findings of the present review underline the role of brittle microstructure phases, and hard secondary particles present in the matrix are responsible for intergranular and intragranular cracks.
Research limitations/implications
The research limitations of the present review are new material characterization techniques that are not available in developing countries.
Practical implications
The practical limitations are new test methodologies and associated cost.
Social implications
The fracture of pipelines significantly affects the surrounding ecology. The continuous spillage of oil pollutes the land and water of the surroundings.
Originality/value
The present review contains recent and past studies conducted on welded pipeline steel structures. The systematic analysis of studies conducted so far highlights various bottlenecks of the welding methods.
Details
Keywords
I. Chattoraj, A.K. Bhattamishra, A. Joarder and D.K. Bhattacharya
The corrosion of boiler drums is intimately linked to the deterioration of the protective oxide film separating the steel substrate from the boiler fluid, which often contains…
Abstract
The corrosion of boiler drums is intimately linked to the deterioration of the protective oxide film separating the steel substrate from the boiler fluid, which often contains constituents conducive to corrosion. Various forms of corrosion occur in the boiler drums and such occurrences can be due to: