The aim is to investigate the feasibility of increasing the transparency of the samples or models which were fabricated by three dimensional printing technology and study the properties of such developed system.

Polymethyl methacrylate powders were mixed with maltodextrin binders and used as raw materials for 3DP machine to fabricate samples. The samples were then divided into two groups either infiltrating with heat‐cured acrylate infiltrant or subjected to binder elimination prior to infiltration. As‐fabricated and two types of infiltrated samples were characterized to compare the influence of post‐processing on properties such as shrinkage, light transmittance and flexural properties including modulus, strength and strain at break.

It was observed that the combination of binder elimination and resin infiltration showed the greatest increase in flexural properties and transmittance percentage approaching the values of polymethyl methacrylate sheet and stereolithography samples. Infiltration without binder elimination increased the transmittance of samples slightly in comparison to as‐fabricated samples. This is related to the level of porosity in the samples and the difference in refractive index of different compositions within the samples namely PMMA, binder and infiltrant.

Additional step of binder elimination prior to infiltration is needed and this may take time to complete.

The technique presented can be used to fabricate a translucent and strong 3DP models.

This study demonstrates the factors that are needed to consider increasing the transparency and even strength of 3DP models.

The potential implications of the three-dimensional printing (3DP) technology are growing enormously in the various health-care sectors, including surgical planning, manufacturing of patient-specific implants and developing anatomical models. Although a wide range of thermoplastic polymers are available as 3DP feedstock, yet obtaining biocompatible and structurally integrated biomedical devices is still challenging owing to various technical issues.

Polyether ether ketone (PEEK) is an organic and biocompatible compound material that is recently being used to fabricate complex design geometries and patient-specific implants through 3DP. However, the thermal and rheological features of PEEK make it difficult to process through the 3DP technologies, for instance, fused filament fabrication. The present review paper presents a state-of-the-art literature review of the 3DP of PEEK for potential biomedical applications. In particular, a special emphasis has been given on the existing technical hurdles and possible technological and processing solutions for improving the printability of PEEK.

The reviewed literature highlighted that there exist numerous scientific and technical means which can be adopted for improving the quality features of the 3D-printed PEEK-based biomedical structures. The discussed technological innovations will help the 3DP system to enhance the layer adhesion strength, structural stability, as well as enable the printing of high-performance thermoplastics.

The content of the present manuscript will motivate young scholars and senior scientists to work in exploring high-performance thermoplastics for 3DP applications.

This paper aims to present the methodology and results of the experimental characterization of three-dimensional (3D) printed acrylonitrile butadiene styrene (ABS) and polycarbonate (PC) parts utilizing digital image correlation (DIC).

Tensile and shear characterizations of ABS and PC 3D-printed parts were performed to determine the extent of anisotropy present in 3D-printed materials. Specimens were printed with varying raster ([+45/−45], [+30/−60], [+15/−75] and [0/90]) and build orientations (flat, on-edge and up-right) to determine the directional properties of the materials. Tensile and Iosipescu shear specimens were printed and loaded in a universal testing machine utilizing two-dimensional (2D) DIC to measure strain. The Poisson’s ratio, Young’s modulus, offset yield strength, tensile strength at yield, elongation at break, tensile stress at break and strain energy density were gathered for each tensile orientation combination. Shear modulus, offset yield strength and shear strength at yield values were collected for each shear combination.

Results indicated that raster and build orientations had negligible effects on the Young’s modulus or Poisson’s ratio in ABS tensile specimens. Shear modulus and shear offset yield strength varied by up to 33 per cent in ABS specimens, signifying that tensile properties are not indicative of shear properties. Raster orientation in the flat build samples reveals anisotropic behavior in PC specimens as the moduli and strengths varied by up to 20 per cent. Similar variations were observed in shear for PC. Changing the build orientation of PC specimens appeared to reveal a similar magnitude of variation in material properties.

This article tests tensile and shear specimens utilizing DIC, which has not been employed previously with 3D-printed specimens. The extensive shear testing conducted in this paper has not been previously attempted, and the results indicate the need for shear testing to understand the 3D-printed material behavior fully.

This paper aims to present a survey concerning the accuracy of thermoplastic polymeric parts fabricated by additive manufacturing (AM). Based on the scientific literature, the aim is to provide an updated map of trends and gaps in this relevant research field. Several technologies and investigation methods are examined, thus giving an overview and analysis of the growing body of research.

Permutations of keywords, which concern materials, technologies and the accuracy of thermoplastic polymeric parts fabricated by AM, are used for a systematic search in peer-review databases. The selected articles are screened and ranked to identify those that are more relevant. A bibliometric analysis is performed based on investigated materials and applied technologies of published papers. Finally, each paper is categorised and discussed by considering the implemented research methods.

The interest in the accuracy of additively manufactured thermoplastics is increasing. The principal sources of inaccuracies are those shrinkages occurring during part solidification. The analysis of the research methods shows a predominance of empirical approaches. Due to the experimental context, those achievements have consequently limited applicability. Analytical and numerical models, which generally require huge computational costs when applied to complex products, are also numerous and are investigated in detail. Several articles deal with artificial intelligence tools and are gaining more and more attention.

The cross-technology survey on the accuracy issue highlights the common critical aspects of thermoplastics transformed by AM. An updated map of the recent research literature is achieved. The analysis shows the advantages and limitations of different research methods in this field, providing an overview of research trends and gaps.