The purpose of this paper is to investigate growth kinetics of interfacial Cu-Sn intermetallic compound (IMC) at the solid Cu/liquid Sn interface.

The Sn/Cu solid–liquid interfacial IMCs are fabricated under various soldering temperatures (240°C-270°C) and soldering times (5-240 s) by dipping method. The thickness and morphology of IMC are observed and analyzed by the optical microscope and scanning electron microscope.

Holding at 260°C, Cu/Sn solid–liquid interface Cu₆Sn₅ growth index experience a change from 0.08 to 0.30 within 10-190 s. The growth index is 0.08 in 10-40 s; the growth index is 0.30 in 40-190 s. Cu₆Sn₅ grain coarsening index is constant within 10-190 s. It is 0.13. The result of the index of Cu₆Sn₅ grain coarsening is different from predecessors 27 results Cu₆Sn₅ grain coarsening index for 1/3. This is because Cu₆Sn₅ grain grows at the expense of its near small grain to reduce the surface Gibbs free energy, and its morphology changes from regular shape to irregular shape. It sets up the mathematical expression about the initial formation time and temperature of Cu₃Sn in 240°C-270°C.

It obtains a mathematical model to express the changes of solid–liquid interface frontier concentration which has an effect on the interfacial Cu₆Sn₅ layer growth index and the Cu₆Sn₅ grain coarsening index. Different indexes can be obtained by establishing relevance equations, which can be used to predict the growth of the interface IMC layer. This mathematical model is established to design the solder pads and the sizes of the solder joints.

The purpose of this paper is to develop a new composite solder to improve the reliability of composite solder joints. Nano-particles modified multi-walled carbon nanotubes (Ni-MWCNTs) can indeed improve the microstructure of composite solder joints and improve the reliability of solder joints. Although many people have conducted in-depth research on the composite solder of Ni-MWCNTs. However, no one has studied the performance of Ni-MWCNTs composite solder under different aging conditions. In this article, Ni-MWCNTs was added to Sn-Ag-Cu (SAC) solder, and the physical properties of composite solder, the microstructure and mechanical properties were evaluated.

In this study, the effect of different aging conditions on the intermetallic compound (IMC) layer growth and shear strength of Ni-modified MWCNTs reinforced SAC composite solder was studied. Compared with SAC307 solder alloy, the influence of Ni-MWCNTs with different contents (0, 0.1 and 0.2 Wt.%) on composite solder was examined. To study the aging characteristics of composite solder joints, the solder joints were aged at 80°C, 120°C and 150°C.

The experimental results show that the content of Ni-MWCNTs affects the morphology and growth of the IMC layer at the interface. The microhardness of the solder increases and the wetting angle decreases. After aging at moderate (120°C) and high temperature (150°C), the morphology of the Cu6Sn5 IMC layer changed from scallop to lamellar and the grain size became coarser. The following two different phase compositions were observed in the solder joints with Ni-MWCNTs reinforcement: Cu3Sn and (Cu, Ni)6Sn5. The fracture surface of the solder joints all appeared ductile dents, and the size of the pits increased significantly with the increase of the aging temperature. Through growth kinetic analysis, Ni-modified MWCNTs in composite solder joints can effectively inhibit the diffusion of atoms in solder joints. In short, when the addition amount of Ni-MWCNTs is 0.1 Wt.%, the solder joints exhibit the best wettability and the highest shear strength.

In this study, the effects of aging conditions on the growth and shear strength of the IMC layer of Ni modified MWCNTs reinforced SAC307 composite solder were studied. The effects of Ni MWCNTs with different contents (0, 0.1 and 0.2 Wt.%) on the composite solder were examined.

The purpose of this paper is to investigate the effect of fullerene (FNS) reinforcements on the microstructure and mechanical properties of 96.5Sn3Ag0.5Cu (SAC305) lead-free solder joints under isothermal ageing and electrical-migration (EM) stressing.

In this paper, SAC305 solder alloy doped with 0.1 Wt.% FNS was prepared via the powder metallurgy method. A sandwich-like sample and a U-shaped sample were designed and prepared to conduct an isothermal ageing test and an EM test. The isothermal ageing test was implemented under vacuum atmosphere at 150°C, whereas the EM experiment was carried out with a current density of 1.5 × 10⁴ A/cm². The microstructural and mechanical evolutions of both plain and composite solder joints after thermal ageing and EM stressing were comparatively studied.

A growth of Ag₃Sn intermetallic compounds (IMCs) in solder matrix and Cu-Sn interfacial IMCs in composite solder joints was notably suppressed under isothermal ageing condition, whereas the hardness and shear strength of composite solder joints significantly outperformed those of non-reinforced solder joints throughout the ageing period. The EM experimental results showed that for the SAC305 solder, the interfacial IMCs formulated a protrusion at the anode after 360 h of EM stressing, whereas the surface of the composite solder joint was relatively smooth. During the stressing period, the interfacial IMC on the anode side of the plain SAC305 solder showed a continuous increasing trend, whereas the IMC at the cathode presented a decreasing trend for its thickness as the stressing time increased; after 360 h of stressing, some cracks and voids had formed on the cathode side. For the SAC305/FNS composite solder, a continuous increase in the thickness of the interfacial IMC was found on both the anode and cathode sides; the growth rate of the interfacial IMC at the anode was higher than that at the cathode. The nanoindentation results showed that the hardness of the SAC305 solder joint presented a gradient distribution after EM stressing, whereas the hardness data showed a relatively homogeneous distribution in the SAC305/FNS solder joint.

The experimental results showed that the FNS reinforcement could effectively mitigate the failure risk in solder joints under isothermal ageing and high-current stressing. Specifically, the FNS particles in solder joints can work as a barrier to suppress the diffusion and migration of Sn and Cu atoms. In addition, the nanoidentation results also indicated that the addition of the FNS reinforcement was very helpful in maintaining the mechanical stability of the solder joint. These findings have provided a theoretical and experimental basis for the practical application of this novel composite solder with high-current densities.