This study aims to investigate the effect of post-treatment on anti-corrosion performance of Al coating on the surface of Ti-6Al-4V (TC4) fastener.

The Al coatings with different layer structures were prepared on TC4 by middle-frequency and direct-current combined magnetron sputtering. The cross-sectional morphology and surface roughness of coatings were characterized by scanning electron microscope and atomic force microscope. The corrosion resistance was evaluated by electrochemical method. The monolayer coating was post-treated by Alodine chemical conversion, Ar⁺ bombardment and a combination of two methods above.

The results show that the interfaces in bilayer and trilayer coatings reduce the defects. Ar⁺ bombardment reduces the corrosion current density, and Alodine chemical conversion leads to a higher pitting corrosion potential. The combined post-treatment has the highest polarization resistance.

The corrosion resistance of the Al coating is enhanced as the layer quantity increases. The combination of two post-treatments, Ar⁺ bombardment and Alodine chemical conversion, could achieve an overall improvement in corrosion resistance of Al coating.

Gallic acid is a substance that is widely found in nature. Initially, it was only used as a corrosion inhibitor to retard the rate of corrosion of metals. In recent years, with intensive research by scholars, the modification of coatings containing gallic acid has become a hot topic in the field of metal protection. This study aims to summarize the various preparation methods of gallic acid and its research progress in corrosion inhibitors and coatings, as well as related studies using quantum chemical methods to assess the predicted corrosion inhibition effects and to systematically describe the prospects and current status of gallic acid applications in the field of metal corrosion inhibition and protection.

First, the various methods of preparation of gallic acid in industry are understood. Second, the corrosion inhibition principles and research progress of gallic acid as a metal corrosion inhibitor are presented. Then, the corrosion inhibition principles and research progress of gallic acid involved in the synthesis and modification of various rust conversion coatings, nano-coatings and organic resin coatings are described. After that, studies related to the evaluation and prediction of gallic acid corrosion inhibition on metals by quantum chemical methods are presented. Finally, new research ideas on gallic acid in the field of corrosion inhibition and protection of metals are summarized.

Gallic acid can be used as a corrosion inhibitor or coating in metal protection.

There is a lack of research on the synergistic improvement of gallic acid and other substances.

The specific application of gallic acid in the field of metal protection was summarized, and the future research focus was put forward.

To the best of the authors’ knowledge, this paper systematically expounds on the research progress of gallic acid in the field of metal protection for the first time and provides new ideas and directions for future research.

This study aims to develop a sol-gel-based coating to provide a long-lasting corrosion protection on AZ31 Mg alloy. Silane-based sol-gel coatings have been successfully applied to Mg alloys for corrosion protection. However, the micro or nano defects formed during condensation and solidification will cause the coating failure during a long-lasting immersion in a saline solution. More durable corrosion-protective sol-gel coatings are needed.

A sol-gel-based coating was modified on AZ31 Mg alloy by levodopa (DOPA). The long-lasting corrosion protection mechanism was studied by multiple electrochemical testing methods and surface characterization techniques.

Long-term testing by electrochemical impedance spectroscopy in aqueous 0.1 M NaCl indicated that the modified DOPA@sol-gel coating exhibited significant corrosion protection performance (>14 days). In comparison, the DOPA-free sol-gel coating failed only after three days of testing. The improved corrosion protection is attributed to the self-polymerized DOPA filling to the micro or nano defects in the glassy cross-linked networks of the sol-gel coating, which greatly improves the compactness of the coating.

The method of this study is simple and easy to process, the raw materials are green and the protective effect is excellent, which is of significance for the study of magnesium alloy corrosion protection.

The anticorrosion coatings used in marine and atmospheric environment are subjected to many environmental factors. And the aging failure has been puzzling researchers. The purpose of this study is to find the correlation between the initial aging of epoxy coatings and the typical marine atmospheric environmental factors.

The epoxy coatings were subjected to a one-year exposure in three typical marine atmospheres. Meanwhile, principal component analysis, linear regression and Spearman and gray correlation analysis were applied to quantify the environmental characteristics and establish correlations with the coating aging.

The results indicate that the coating will undergo macroscopic fading and chalking upon exposure to the marine atmosphere, while microscopic examination reveals holes, cracks and partial peeling. The adhesion performance and electrochemical properties of the coating deteriorated with prolonged exposure, coating aging mainly occurs with the generation of O-H bonds and the breakage of molecular chains such as C-N and C-O-C. The coating was most deeply aged after exposure to the Xisha, followed by Zhoushan and finally Qingdao. Environmental factors affect the photooxidative aging and hydrolytic degradation processes of coatings and thus coating aging. To further demonstrate the correlation between environmental factors and coating aging, principal component analysis was used. The correlation model between environmental factors and coating aging was subsequently obtained. The correlation model between the rate of coating adhesion loss (E) and the comprehensive evaluation parameter of environmental factors (Z) is expressed as E = 0.142 + 0.028Z. Meanwhile, the Spearman correlation analysis and gray correlation method were used to investigate the impact of each environmental factor on coating aging. Solar irradiation, relative humidity and wetting time have the highest correlation with coating aging, which are all above 0.8 and have the greatest influence on coating aging; wind speed and temperature have the smallest correlation with coating aging, which are about 0.6 and have the least influence on coating aging.

This paper establishes a correlation between typical marine environmental factors and coating aging performance, which is crucial for predicting the service life of other coatings in diverse environments.

This paper aims to comprehensively review the preparation methods of superhydrophobic surfaces (SHPS) for corrosion protection of Mg alloy in recent years.

The preparation methods, wettability and corrosion resistance of SHPS on Mg alloy in the past three years are systematically described in this paper.

Two types of SHPS, including single-layer and multilayer coatings for corrosion protection of Mg alloy are summarized. Preparing multilayered coatings with multifunction is the current trend in developing SHPS on Mg alloy.

This paper reviewed the preparation methods and corrosion resistance of SHPS on Mg alloys. It provides a valuable reference for researchers to develop highly durable SHPS with excellent corrosion resistance for Mg alloys.

This study aims to review the current one-step electrodeposition of superhydrophobic coatings on metal surfaces.

One-step electrodeposition is a versatile and simple technology to prepare superhydrophobic coatings on metal surfaces.

Preparing superhydrophobic coatings by one-step electrodeposition is an efficient method to protect metal surfaces.

Even though there are several technologies, one-step electrodeposition still plays a significant role in producing superhydrophobic coatings.

This paper aims to focus on the research progress of intelligent self-healing anti-corrosion coatings in the aviation field in the past few years. The paper provides certain literature review supports and development direction suggestions for future research on intelligent self-healing coatings in aviation.

This mini-review uses a systematic literature review process to provide a comprehensive and up-to-date review of intelligent self-healing anti-corrosion coatings that have been researched and applied in the field of aviation in recent years. In total, 64 articles published in journals in this field in the last few years were analysed in this paper.

The authors conclude that the incorporation of multiple external stimulus-response mechanisms makes the coatings smarter in addition to their original self-healing corrosion protection function. In the future, further research is still needed in the research and development of new coating materials, the synergistic release of multiple self-healing mechanisms, coating preparation technology and corrosion monitoring technology.

To the best of the authors’ knowledge, this is one of the few systematic literature reviews on intelligent self-healing anti-corrosion coatings in aviation. The authors provide a comprehensive overview of the topical issues of such coatings and present their views and opinions by discussing the opportunities and challenges that self-healing coatings will face in future development.

This paper aims to investigate the corrosion resistance of two types of coatings – one is ceria sol coating and the other is ceria sol coating modified by ZnO nanoparticles on 7075 aluminum alloy in 3.5% NaCl solution.

Aluminum alloys were dipped into ceria sol and ceria sol modified by ZnO nanoparticles separately and removed after 10 min from the solutions and dried at 110°C for 30 min and heated at 500 °C for 30 min to form the coatings. The coatings have been characterized by using field emission scanning electron microscopy (FE-SEM), electrochemical impedance spectroscopy (EIS), X-ray diffraction (XRD) and energy dispersive spectroscopy (EDS). The EIS tests were performed in a corrosive solution of 3.5% NaCl.

The results showed that the coating of ceria sol modified by ZnO nanoparticles has higher corrosion resistance than the ceria sol coating and the bare sample. Also, the best efficiency is related to aluminum sample immersion after 1 h in NaCl corrosive solution for coating modified by ZnO nanoparticles.

In this research, the modification of ceria sol coating by ZnO nanoparticles had an effect on improving the corrosion behavior of aluminum alloy. It is also understood that modification of coatings is an effective parameter on corrosion resistance.

The purpose of this study is to examine the impact of MoS₂ on the microstructure and characteristics of micro-arc oxidized (MAO) ceramic coatings created on ZK60 magnesium alloy through the addition of varying concentrations of MoS₂ particles to the electrolyte, aiming to enhance the corrosion resistance of magnesium alloy.

The surface morphology, roughness and phase composition of the coatings were analyzed using scanning electron microscopy, a hand-held roughness tester and an X-ray diffractometer, respectively, and the corrosion resistance of the MAO coatings prepared by the addition of different contents of MoS₂ particles was tested and analyzed using an electrochemical workstation.

The results demonstrate that MoS₂/MgO composite coatings have been successfully prepared on the surface of magnesium alloys through micro-arc oxidation. Furthermore, the corrosion resistance of the ZK60 magnesium alloy prepared with the addition of 1.0 g/L MoS₂ was the best compared to the other samples.

MoS₂ particles were able to penetrate the coatings successfully during the micro-arc oxidation process, acting as a barrier in the micropores to prevent the corrosion medium from touching the surface, thus improving the corrosion resistance of the sample. The electrochemical workstation was used to study the corrosion resistance of the MoS₂/MAO coating on the ZK60 magnesium alloy.

The purpose of this paper was prepared a Ni-based superhydrophobic coating on the surface of copper to enhence its corrosion resistance. The superhydrophobic coating (SHPC) has proven to be an effective surface treatment in corrosion protection. In this paper, a Ni-based SHPC was prepared on the surface of copper (Cu) to enhance its corrosion resistance.

The coating was prepared through a two-step electrodeposition process. The first step involves the formation of a micro-nano structure Ni layer formed by an electrodeposition process. Subsequently, the polysiloxane layer was deposited on the Ni surface to create an SHPC. The morphology, composition, structure, wettability and corrosion resistance of the coating were characterized and discussed.

The results show that the water contact angle of the as-prepared coating reaches 155.5°±1.0°. The corrosion current density (i_corr = 3.90 × 10⁻⁹ A·cm⁻²) decreased by three orders of magnitude compared to the substrate, whereas |Z|_{f = 0.01 Hz} (2.40 × 10⁶ Ω·cm²) increased by three orders of magnitude. It indicated that the prepared coating has excellent superhydrophobicity and high corrosion resistance, which can provide better protection for the substrate.

The prepared coating provides long-lasting protection for Cu and other metals and offers valuable data for developing SHPCs.