This study aims to develop a polymer cement-based waterproof coating with self-healing capability to efficiently and intelligently solve the building leakage caused by cracking of waterproof materials, along with excellent durability to prolong its service life.

Ion chelators are introduced into the composite system based on ethylene vinyl acetate copolymer emulsion and ordinary Portland cement to prepare self-healing polymer cement-based waterproof coating. Hydration, microstructure, wettability, mechanical properties, durability, self-healing performance and self-healing products of polymer cement-based waterproof coating with ion chelator are investigated systematically. Meanwhile, the chemical composition of self-healing products in the crack was examined.

The results showed that ion chelators could motivate the hydration of C₂S and C₃S, as well as the formation of hydration products (C-S-H gel) of the waterproof coating to improve its compactness. Compared with the control group, the waterproof coating with ion chelator had more excellent water resistance, alkali resistance, thermal and UV aging resistance. When the dosage of ion chelator was 2%, after 28 days of curing, cracks with a width of 0.29 mm in waterproof coating could fully heal and cracks with a width of 0.50 mm could achieve a self-healing efficiency of 72%. Furthermore, the results reveal that the self-healing product in the crack was calcite crystalline CaCO₃.

A novel ion chelator was introduced into the composite coating system to endow it with excellent self-healing ability to prolong its service life. It has huge application potential in the field of building waterproofing.

Invented in late 1890s, asbestos cement sheeting rose to prominence during the post-Second World War period as a building material for low-cost housing by state housing commissions and low-income families (“fibro homes”). The adverse health effects of asbestos fibres in the building industry and home renovation activities are well documented. Fibro homes of the 1950s and 1960s are increasingly coming under the gaze of heritage studies, which brings to the fore the question of how to deal with the asbestos cement sheeting most are clad with.

This paper provides the first systematic review to assess the literature (126 papers were identified in Google Scholar and scanned for content) on the conservation management of asbestos cement sheeting in heritage properties.

Overall, engagement with the conservation management of asbestos cement sheeting in heritage properties was low, with only two sources dealing with asbestos cement sheeting in any level of detail. The studies note that if asbestos cement sheeting is in good condition, it should be left alone. Numerous conservation and repair options do exist, in particular the application of (coloured) sealants that extend the life of asbestos cement sheets and asbestos cement roofing.

This paper represents the first systematic review to assess conservation management options for asbestos cement sheeting in heritage properties.

Cement can be replaced to reduce the energy consumption and the environmental impact of cement. Also, foamed concrete can be used structurally in residential buildings to reduce weight and improve thermal insulation. To achieve these two goals, this paper aims to investigate the effect of basalt powder as a partial replacement of either cement or sand.

This paper investigates the effect of basalt powder as a partial replacement of either cement or sand on the mechanical properties of foamed concrete used to cast slabs. First, mechanical properties of foamed concrete are tested with and without replacement of basalt. Then, six slabs of different thicknesses and mixes are investigated. The thicknesses considered are 150- and 200-mm slabs. The three mixes used to construct these slabs are foamed concrete with no basalt powder, foamed concrete with replacement of 20% of cement by basalt powder and foamed concrete with replacement of 20% of sand by basalt powder. The flexural behavior of these slabs is investigated.

All the slabs failed in the commonly intended flexural mode. The results show that the basalt powder acted as a strong filler material in the foamed concrete mix based on mechanical properties and flexural behavior. The proposed foamed concrete slabs can be used structurally in residential buildings.

A natural waste material that can be used to promote energy efficiency and reduce emission is basalt. In this paper, basalt powder is suggested to be used due to its chemical composition that is similar to cement. Also, basalt powder is low in cost as it is waste, while basalt aggregate is prepared, and it is only used as filler in paved roads. Accordingly, basalt is partially used instead of cement to reduce the emission of carbon dioxide that results from the cement manufacturing. Also, it is used as a partial alternative to sand which can be considered as a new stronger source as filling material used in the production of concrete.

The aim of this paper is to determine the thermal conductivity of a protective layer of alkali-activated cement and the possibility of performing fire protection with fireclay sand and Lightweight mortar. Unprotected steel structures have generally low fire resistance and require surface protection. The design of passive protection of a steel element must consider the service life of the structure and the possible need to replace the fire protection layer. Currently, conventional passive protection options include intumescent coatings, which are subject to frequent inspection and renewal, gypsum and cement-based fire coatings and gypsum and cement board fire protection.

Alkali-activated cements provide an alternative to traditional Portland clinker-based materials for specific areas. This paper presents the properties of hybrid cement, its manufacturability for conventional mortars and the development of passive fire protection. Fire experiments were conducted with mortar with alkali-activated and fireclay sand and lightweight mortar with alkali-activated cement and expanded perlite. Fire experiment FE modelling.

The temperatures of the protected steel and the formation of cracks in the protective layer were investigated. Based on the experiments, the thermal conductivities of the two protective layers were determined. Conclusions are presented on the applicability of alkaline-activated cement mortars and the possibilities of applicability for the protection of steel structures. The functionality of the passive fire layer was confirmed and the strengths of the mortar used were determined. The use of alkali-activated cements was shown to be a suitable option for sustainable passive fire protection of steel structures.

Eco-friendly fire protection based on hybrid alkali-activated cement of steel members.

The stabilization of earthen blocks improves their mechanical strength and avoids adobe construction erosion due to rainwater. However, the stabilization affects the thermal properties of the earthen blocks, and thus their capacity to provide adequate thermal comfort to occupants. This article examines the influence of cement and geopolymer binders on thermal comfort in compressed earthen buildings in hot and arid climates.

The test cell is on the building platform in Burkina Faso. The building is made of compressed earth blocks (CEB) consisting of laterite, water and binder. The thermal models of the building were implemented in EnergyPlus v9.0.1 software. Empirical validation is used to check whether the model used for the thermal dynamic simulation can reproduce with accuracy the thermal behavior in a real situation. The adaptive thermal comfort model of ASHRAE 55–2010 was used to assess thermal comfort in long-term hot and dry tropical conditions.

The results show that the CEB buildings remain hot despite the use of cement or geopolymer binder. Indeed, with both cement and geopolymer binders, on a daily basis, 19 h and 15 h are uncomfortable during, respectively, the hot and cold seasons. An increase of 1% in cement content raises the comfort hours by 9.2 h during the hot season and 11.7 h during the cold season. Hence, the comfort time varies linearly with the cement content in the building material. Moreover, there is no linear relationship between comfort time and geopolymer rate.

Complementary work should also assess the influence of stabilization on building humidity levels. In fact, earthen materials are very sensitive to outdoor humidity and indoor humidity affects thermal comfort even if it is not taken into account in the ASHRAE adaptive thermal comfort model.

The present study will certainly contribute to a better valorization of clay potential in countries with similar climatic conditions.

The use of geopolymer binder is a suitable ecological option to replace the cement binder. It is important to mention that nighttime comfort can be increased through passive strategies such as natural ventilation.

Most CEB material stabilization analyses including cement and geopolymer ones were mostly investigated at the laboratory scale and less at the building scale. Also, the influence of the binder rate on the thermal performance of buildings made of cement and geopolymer has not yet been assessed. This paper fills this gap of knowledge by assessing the impact of cement and geopolymer binder rates on the thermal comfort of CEB dwellings.

The purpose of this paper is to describe sustainability of hollow and solid blocks in sub-Saharan Africa.

Indicators of stakeholder value are proposed for measuring block sustainability based on comparisons of user building value price and carbon emissions. Block manufacturing processes in Tanzania and Uganda are described and assessed in this context.

The results from Uganda indicate that there are economic and environmental advantages in using hollow blocks as long as they are produced to statutory compliance levels. However, where blocks are not produced to standard requirements, the results indicate that it is better to use solid blocks. This surprising result seems to indicate that blocks prepared using low additions of cement might have sufficient functional quality for simple residential building applications even though they might not meet current standard strength requirements and have low cement productivity. These results also indicate that the improvement potential indicated previously cannot be realised when hollow blocks are used for simple construction needs.

Clear benchmarks for the best practical level of cement block sustainability seem to be missing. The first reasons is that the lowest acceptable compressive strength has not been defined since standard requirements might not be relevant in the studied context. The second one is that the lowest possible practically achievable cement content with acceptable cement productivity has not been established.

Understanding sustainability can be very difficult and substantial work needs to be done to introduce operational sustainability indicators.

The results contribute to the discussion of understanding, defining and measuring sustainability.

The purpose of this paper is to check the feasibility of using biomaterial such as of Phragmites-Australis (PA) in cement paste to achieve sustainable building materials.

In this study, cement pastes were prepared by adding locally produced PA fibers in four different volumes: 0%, 0.5%, 1% and 2% for a duration of 180 days. Bottles and prisms were subjected to chemical shrinkage (CS), drying shrinkage (DS), autogenous shrinkage (AS) and expansion tests. Besides, prism specimens were tested for flexural strength and compressive strength. Furthermore, a mathematical model was proposed to determine the variation length change as function of time.

The experimental findings showed that the mechanical properties of cement paste were significantly improved by the addition of 1% PA fiber compared to other PA mixes. The effect of increasing the % of PA fibers reduces the CS, AS, DS and expansion of cement paste. For example, the addition of 2% PA fibers reduces the CS, expansion, AS and DS at 180 days by 36%, 20%, 13% and 10%, respectively compared to the control mix. The proposed nonlinear model fit to the experimental data is appropriate with R2 values above 0.92. There seems to be a strong positive linear correlation between CS and AS/DS with R2 above 0.95. However, there exists a negative linear correlation between CS and expansion.

The PA used in this study was obtained from one specific location. This can exhibit a limitation as soil type may affect PA properties. Also, one method was used to treat the PA fibers.

The utilization of PA fibers in paste may well reduce the formation of cracks and limit its propagation, thus using a biomaterial such as PA in cementitious systems can be an environmentally friendly option as it will make good use of the waste generated and enhance local employment, thereby contributing toward sustainable development.

To the authors best knowledge, there is hardly any research on the effect of PA on the volume stability of cement paste. Therefore, the research outputs are considered to be original.

This study aims to characterize the behavior of blended concrete, including metakaolin (MK) and quarry dust (QD), as supplementary cementing materials. The study focuses on evaluating the effects of these materials on the fresh and hardened properties of concrete.

MK, a pozzolanic material, and QD, a fine aggregate by-product, are potentially sustainable alternatives for enhancing concrete performance and reducing environmental impact. The addition of different percentages of MK enhances the pozzolanic reaction, resulting in improved strength development. Furthermore, the optimum dosage of MK, mixed with QD, and mechanical properties like compressive, flexural and split tensile strength of concrete were evaluated to investigate the synergetic effect of MK and quarry dust for M20-grade concrete.

The results reveal the influence of metakaolin and QD on the overall performance of blended concrete. Cost analysis showed that the optimum mix can reduce the 7%–8% overall cost of the materials for M20-grade concrete. Energy analysis showed that the optimum mix can reduce 7%–8% energy consumption.

The effective utilization is determined with the help of the analytical hierarchy process method to find an optimal solution among the selected criteria. According to the AHP analysis, the optimum content of MK and quarry dust is 12% and 16%, respectively, performing best among all other trial mixes.

The purpose of this study is to advance the application of pulverised cow bone ash (PCBA) as a partial replacement of cement in soil stabilisation for the production of bricks. The study investigated the impact of PCBA substitution on the characteristic strength of clay bricks under variant curing media.

Dried cow bones were pulverised, and an energy-dispersive X-ray fluorescence test was conducted on PCBA samples to determine the chemical constituents and ascertain the pozzolanic characteristics. Ordinary Portland cement (OPC) and PCBA were blended at 100%, 75%, 50%, 25% and 0% of cement substitution by mass to stabilise lateritic clay at 10% total binder content for the production of bricks. The binder-to-lateritic clay matrixes were used to produce clay bricks and cylinders for compressive and splitting tensile strength tests, respectively.

The study found that PCBA and OPC have similar chemical compositions. The strength of the clay bricks increased with curing age, and the thermal curing of clay bricks positively impacted the strength development. The study established that PCBA is a suitable substitute for cement, up to 25% for stabilisation in clay brick production.

Construction stakeholders can successfully use a PCBA-OPC binder blend of 1:3 to stabilise clay at 10% total binder content for the production of bricks. The stabilised clay bricks should be cured at an elevated temperature of approximately 90°C for 48 h to achieve satisfactory performance.

The PCBA-OPC binder blend provides adequate soil stabilisation for the production of clay bricks and curing the clay bricks at elevated temperature. This aspect of the biomass/OPC binder blend has not been explored for brick production, and this is important for the reduction of the environmental impacts of cement production and waste from abattoirs.

This study aims at designing consistent and durable concrete by making use of waste materials. An investigation has been carried out to evaluate the performance of conventional and optimal concrete (including 5% GP) at high temperatures for different exposure times.

An experimental work is carried out to compare the conventional and optimal concrete with respect to weight loss, mechanical strength characteristics (compressive, tensile and flexural) after exposed to 100, 200 and 300 °C with 1, 2 and 3 h duration of exposure followed by cooling in furnace for 24 h and then air cooling.

The workability of granite powder modified concrete decreases as percentage of replacement increases. Compressive, tensile and flexural strengths all increased at 100 °C when compared to strength characteristics at normal temperature, regardless of the exposure conditions, and there was no weight loss noticed. For 200 and 300 °C, the strengths were decreased compared to normal temperature and an elevated temperature of 100 °C, as weight loss of concrete specimens are observed to be decreased at these temperatures. So, the optimum elevated temperature can be concluded as 100 °C.

Incorporating pozzolanic binder (granite powder) as cement replacement subjecting to elevated temperatures in an electric furnace is the research gap in this area. Many of the works were carried out replacing GP for fine aggregate at normal temperatures and not at elevated temperatures.