Friction material in an automotive brake system plays an important role for effective and safe brake performance. A single material has never been sufficient to solve performance related issues. Current research aimed to examine properties of Boron mixed brake pads by comparing them with the commercial brake pads. Friction coefficient of Boron mixed brake pads and commercial brake pads were significantly different and increased with the increase in surface roughness. The abrupt reduction of friction coefficient is more significant in commercial brake pad samples than in Boron mixed brake pad formulations. Fade occurred in commercial brake pad sample at lower temperatures. Boron formulations are more stable than their commercial counterparts.

The purpose of this paper is to investigate use of colemanite (C) upon friction and wear performance of automotive brake lining. Brake lining production with the boron product colemanite addition and braking characterization investigated for development of non-asbestos organic (NAO) brake lining because of negative effects on human health and environmental hazard of asbestos containing linings. During the braking, brake lining is warmed up extremely due to friction, and the high temperature causes to decreasing of breaking performance. Colemanite has high melting temperature, and this makes this material valuable for brake lining.

This study investigated the effect of colemanite (C) upon friction and wear performance of automotive brake lining. Based on a simple experimental formulation, different amounts of boron product colemanite were used and then evaluated using a friction assessment and screening test. In these specimens, half of the samples (shown with H indices) were heat treated in 4 h at 180°C temperature. Friction coefficient, wear rate and scanning electron microscope for friction surfaces were used to assess the performance of these samples.

The results of test showed that colemanite can substantially improve properties of friction materials. The friction coefficient of friction materials modified with colemanite varies steadily with the change of temperature, and the wearing rate of friction materials is relatively low by using colemanite. Heat treatment-applied samples (CH) have provided a higher and stable friction coefficient. These results indicate that colemanite has ideal application effect in various friction materials.

This paper fulfils an identified information and offers practical help to the industrial firms working with brake lining and also to the academicians working on wear of materials. Parallel results have been presented between previously reported and present study, in view of brake characteristics and wear resistance. Use of the lower cost and productive organic sources of material are the main improvement of the present study.

The purpose of this paper is to investigate use of calabrian pine (pinus brutia) cone (CPC) dust along with borax (BX) to assess the effect of friction coefficient. Despite the number of research studies completed on the mechanism of friction in automotive brake lining materials, the phenomenon is still not fully understood. Complex mechano-chemical processes occurring on the friction interface of a composite friction material make it difficult to understand the correlation between the formulation of brake lining and the frictional performance.

In this study, the use of CPC dust along with BX has been investigated for assessing the effect on friction coefficient. CPC has resin in it. BX is a boron production which is widely used in boron glass production and in ceramic industry for increasing the heat- resistant and -forming abrasion resistant. Newly formulated brake lining material with five different ingredients has been tested under Friction Assessment and Screening Test. Friction coefficient, wear rate and scanning electron microscope for friction surface were examined to assess the performance of these samples.

Analysis of the experimental results shows that the brake lining material containing CPC and BX significantly improved the stability of the friction coefficient, fade and wear resistance.

Several investigations have been conducted to use different materials in brake pads. The brake pad standards have been provided in previous studies, as well as the aims for economical and sustainable production. In the present study, production of brake pads by CPC dust and BX has been executed. Parallel results have been presented between previously reported and present study, in view of brake characteristics and wear resistance. Use of the lower cost and productive organic sources of material are the main improvement of the present study.

Aluminium metal matrix composites are used in automotive and aerospace industries because of their high performance and weight reduction benefits. The current investigation aims to focus on the development of the stir cast aluminium-boron carbide composites with enhanced mechanical and tribological properties.

The aluminium-boron carbide composites are produced by stir casting process. Aluminium alloy A356 is chosen as the matrix material and three sets of composites are produced with different weight fractions of boron carbide particles. Higher particle size (63 µm) of boron carbide is chosen as the reinforcement material. Aluminium-boron carbide composites are tested for mechanical and tribological properties. The effect of process parameters like load, speed and percentage of reinforcement on the wear rate are studied using the pin-on-disc method. The interaction of the process parameters with the wear rate is analysed by DesignExpert software using RSM methodology and desirability analysis. The coded levels for parameters for independent variables used in the experimental design are arranged according to the central composite design. The worn surface of the pin is examined using a scanning electron microscope. The phases and reaction products of the composites are identified by X-ray diffraction (XRD) analysis.

Aluminium-boron carbide composites reveal better mechanical properties compared to monolithic aluminium alloys. Mechanical properties improved with the addition of strontium-based master alloy Al10Sr. The ultimate tensile strength, hardness and compressive strength increase with an increase in the reinforcement content. The wettability of the boron carbide particles in the matrix improved with the addition of potassium flurotitanate to the melt. Uniform dispersion of particles into the alloy during melting is facilitated by the addition of magnesium. Wear resistance is optimal at 8 per cent of boron carbide with a load 20 N and sliding speed of 348 RPM. The wear rate is optimized by the numerical optimization method using desirability analysis. The amount of wear is less in Al-B₄C composites when compared to unreinforced aluminium alloy. The wear rate increases with an increase in load and decreases with the sliding speed. The wear resistance increases with an increase in the weight fraction of the boron carbide particles.

The produced Al-B₄C composites can retain properties at high temperature. It is used in nuclear and automotive products owing its high specific strength and stiffness. The main applications are neutron absorbers, armour plates, high-performance bicycles, brake pads, sand blasting nozzles and pump seals.

Al/B₄C composites have good potential in the development of wear-resistant products.

The purpose of this paper is to deal with the tribological study on the brake pads developed using various purity-based graphitized graphite.

This paper deals with developing copper-free brake pads by using graphite as a key lubricant produced using a graphitization process with purity percentages (85, 90 and 95%). The brake pads were developed using traditional manufacturing processes and evaluated for their physical, chemical, thermal and mechanical properties as per industrial standards. Fade and recovery characteristics were analyzed using a full-scale inertia brake dynamometer as per JASO-C-406. The scanning electron microscope was used to analyze the worn surfaces of the brake pads.

The testing findings reveal that the brake pads with 95% graphitized graphite showed better shear strength with good adhesion levels and lesser density, hardness, acetone extract value, loss on ignition and higher porosity. Effectiveness studies of brake pads with graphite (95% graphitized) showed better results at higher pressure speed conditions than others because of better plateau formation and adequate lubrication.

This paper discusses graphitized graphite of different purity influences brake pad's tribological performance by modifying tribo-films and reducing friction undulations.

This paper aims to investigate the effect of straight phenolic resin content on the fade behavior, frictions and wear characteristics of pre-determined brake pad composite matrix having specific amount of barite (BaSO₄), rock wool, Kevlar, graphite and magnetite.

Different amount of resin ranging between 16 and 20 wt. per cent were added by changing only the filler (barite) content of composite matrix. Subsequently, friction and wear behavior of the composite samples were analyzed using a special pin-on-disc type test system developed for brake pad sample. The worn surfaces were investigated by SEM and three-dimensional (3D) surface profilometer.

The average coefficient of friction (CoF) of composite samples and temperature of the disc surface showed a linear increase with decreasing the resin content. The sample having 20 wt. per cent resin showed the minimum wear rate with smooth worn surface. But the amount of fade is quite high in that sample. Decreasing resin content decreased the fade formation, and the composite with 16 per cent resin brought about the minimum fade formation. As the fade formation is unwanted in brake pad applications, the composite with 16 wt. per cent resin was proposed as the most appropriate one considering the performance parameters related to friction and wear.

This paper optimizes the resin content of composite brake pad materials to achieve the best combination of its tribo-performance and mechanical properties and provides valuable information for scientists and engineers working in that area.

This paper aims to discuss the influence of graphite with varying purity on the tribological performance of brake pads.

Three distinct brake pads were created within the scope of this experiment by varying the graphite purity without affecting the other components. The brake pads were made using a traditional manufacturing procedure, and industry standards were used to test the chemical, physical and mechanical properties of the newly produced brake pad. A full-scale inertia brake dynamometer was used to determine the material’s tribological characteristics. The worn surfaces of the brake pads were examined using a scanning electron microscope.

The test results indicate that brake pads containing 99% pure graphite (artificial grade) displayed good physical, chemical and mechanical features, such as consistent friction and a reduced rate of wear because of the lower impurity level, which eliminates frictional undulations.

This paper discusses the influence of graphite purity on the tribological performance of brake pads by modifying tribofilms and reducing friction undulations.

This paper aims to deal with the effect of natural barytes purity levels on the tribological performance of brake pads.

In this study, brake pads were developed by varying three different natural barytes without varying other ingredients. The brake pads were developed as per the standard industrial practice. The physical, mechanical and thermal properties of the developed brake pads were tested as per the industrial standards. The tribological properties were analyzed using a full-scale inertia brake dynamometer. Worn surface analysis was done using scanning electron microscope coupled with elemental mapping.

The experimental results indicate that the brake pads filled with natural barytes 95% purity had good physical, chemical and mechanical properties with stable friction and less wear rate due to reduced impurity level preventing frictional undulations.

This paper explains the effect of the purity level of natural barytes in brake pads formulation to enhance the tribological performance by altering tribofilms and preventing friction undulations.

This paper aims to deal with the synergistic effect of steel slag-molybdenum disulfide particles on fade-recovery performances of non-asbestos organic friction material.

The brake friction materials were developed by using steel slag and molybdenum disulfide particles as individual and combination in the formulation. The brake friction materials were developed in the form of standard brake pads as per the industrial practice. The physical, mechanical and thermal properties of the developed brake pads were tested as per the industrial standards. The tribological properties were analyzed using the Chase test as per IS2742-Part-4. Worn surface analysis was done using a scanning electron microscope.

The experimental results indicate that the brake pads filled with a combination of steel slag and molybdenum disulfide showed stable friction and less wear rate due to the synergetic nature of abrasive and lubricant.

This paper explains the influence of steel slag and molybdenum disulfide particles as individual and combined in brake pads formulation to enhance the tribological performance by producing stabilized friction with undulations.

The peer review history for this article is available at: https://publons.com/publon/10.1108/ILT-06-2020-0216/

The purpose of this work is to optimize the monitoring of vibrations on dynamometric test rigs for railway brakes. This is a quite demanding application considering the continuous increase of performances of high-speed trains that involve higher testing specifications for brake pads and disks.

In this work, authors propose a mixed approach in which relatively simple finite element models are used to support the optimization of a diagnostic system that is used to monitor vibration levels and rotor-dynamical behavior of the machine. The model is calibrated with experimental data recorded on the same rig that must be identified and monitored. The whole process is optimized to not interfere with normal operations of the rig, using common inertial sensor and tools and are available as standard instrumentation for this kind of applications. So at the end all the calibration activities can be performed normally without interrupting the activities of the rig introducing additional costs due to system unavailability.

Proposed approach was able to identify in a very simple and fast way the vibrational behavior of the investigated rig, also giving precious information concerning the anisotropic behavior of supports and their damping. All these data are quite difficult to be found in technical literature because they are quite sensitive to assembly tolerances and to many other factors. Dynamometric test rigs are an important application widely diffused for both road and rail vehicles. Also proposed procedure can be easily extended and generalized to a wide value of machine with horizontal rotors.

Most of the studies in literature are referred to electrical motors or turbomachines operating with relatively slow transients and constant inertial properties. For investigated machines both these conditions are not verified, making the proposed application quite unusual and original with respect to current application. At the same time, there is a wide variety of special machines that are usually marginally covered by standard testing methodologies to which the proposed approach can be successfully extended.