This paper aims to target to print functionally gradient materials (FGM) devices made of immiscible polymers in multi-material fused deposition modelling (FDM) systems. The design is intended to improve adhesion of dissimilar thermoplastics without the need for chemical compatibilization so that filaments from many different sources can be used effectively. Therefore, there is a need to invent an alternative solution for printing multiple immiscible polymers in an FDM system with the desired adhesion.

In this study, the authors have developed a bi-extruder for FDM systems which can print two thermoplastics through a single nozzle with a static intermixer to enhance bonding between input materials. The system can also change the composition of extrudates continuously.

The uniqueness of this extruder is in its easy access to the internal channel so that a static intermixer can be inserted, enabling deposition of mechanically interlocked extrudates composed of two immiscible polymers. Without this intermixer, the bi-extruder extrudes with simple side-by-side co-extrusion having no mechanical interlocking. The bi-extruder was characterized by printing objects using pairs of materials including polylactic acid, acrylonitrile butadiene styrene and high impact polystyrene. Microscope images of the cross-sections of the extrudates confirm the ability of this bi-extruder to control the composition as desired. It was also found that the mechanically interlocked extrudates composed of two immiscible polymers substantially reduces adhesion failures within and between filaments.

In this study, the first-ever FDM extruder with a mechanical blending feature next to the nozzle has been designed and used to successfully print FGM objects with improved mechanical properties.

Additive manufacturing has disadvantages, such as the maximum part size being limited by the machine’s working volume. Therefore, if a part more considerable than the working volume is required, the part is produced in parts and joined together. Among the many methods of joining thermoplastic parts, adhesives and mechanical interlocking are considered. This study aims to characterize and optimize mechanically stressed adhesive joints combined with female and male mechanical interlocking on acrylonitrile butadiene styrene (ABS) specimens made with fused filament fabrication (FFF) so that the joint strength is as close as possible to the strength of the base material.

This study characterized the subject’s state of the art to justify the decisions regarding the experimental design planned in this research. Subsequently, this study designed, executed and analyzed the experiment using a statistical analysis of variance. The output variables were yield strength and tensile strength. The input variables were two different cyanoacrylate adhesives, two different types of mechanical interlock (truncated pyramid and cylindrical pin) and the dimensions of each type of mechanical interlock. This study used simple and factorial experiments to select the best adhesive and interlocking to be optimized using the response surface and the steep ascent method.

The two adhesives have no statistical difference, but they show different data dispersion. The design or yield stress was a determining factor for selecting the optimal specimen, with cylindrical geometry exhibiting higher resistance at initial failure. Geometry type is crucial due to the presence of stress concentrators. The cylindrical geometry with fewer stress concentrators demonstrated better tensile strength. Ultimately, the specimen with a mechanically reinforced joint featuring a cylindrical pin of radius 5.45 mm and height of 4.6 mm exhibited the maximum tensile and yield strength.

Previous research suggests that a research opportunity is the combination of bonding methods in FFF or fused deposition modeling, which is not a frequent topic, and this research to enrich that topic combines the adhesive with mechanically interlocked joints and studies it experimentally for FFF materials, to provide unpublished information of the performance of the adhesive joint with mechanical interlocking, to designers and manufacturers of this technology.

This paper aims to understand the effect of extrusion conditions on the degree of foaming of polylactic acid (PLA) during three-dimensional (3D) printing. It was also targeted to optimize the slicing parameters for 3D printing and to study how the properties of printed parts are influenced by the extrusion conditions.

This study used a commercially available PLA filament that undergoes chemical foaming. An extrusion 3D printer was used to produce individual extrudates and print samples that were characterized using an optical microscope, scanning electron microscope and custom in-house apparatuses.

The degree of foaming of the extrudates was found to strongly depend on the extrusion temperature and the material feed speed. Higher temperatures significantly increased the number of nucleation sites for the blowing agent as well as the growth rate of micropores. Also, as the material feed speed increased, the micropores were allowed to grow bigger which resulted in higher degrees of foaming. It was also found that, as the degree of foaming increased, the porous parts printed with optimized slicing parameters were lightweight and thermally less conductive.

This study fills the gap in literature where it examines the foaming behavior of individual extrudates as they are extruded. By doing so, this work distinguishes the effect of extrusion conditions from the effect of slicing parameters on the foaming behavior which enhances the understanding of extrusion of chemically foamed PLA.