1 – 10 of 16Rilwan Kayode Apalowo, Mohamad Aizat Abas, Muhamed Abdul Fatah Muhamed Mukhtar, Fakhrozi Che Ani and Mohamad Riduwan Ramli
This study aims to investigate the reliability issues of microvoid cracks in solder joint packages exposed to thermal cycling fatigue.
Abstract
Purpose
This study aims to investigate the reliability issues of microvoid cracks in solder joint packages exposed to thermal cycling fatigue.
Design/methodology/approach
The specimens are subjected to JEDEC preconditioning level 1 (85 °C/85%RH/168 h) with five times reflow at 270°C. This is followed by thermal cycling from 0°C to 100°C, per IPC-7351B standards. The specimens' cross-sections are inspected for crack growth and propagation under backscattered scanning electronic microscopy. The decoupled thermomechanical simulation technique is applied to investigate the thermal fatigue behavior. The impacts of crack length on the stress and fatigue behavior of the package are investigated.
Findings
Cracks are initiated from the ball grid array corner of the solder joint, propagating through the transverse section of the solder ball. The crack growth increases continuously up to 0.25-mm crack length, then slows down afterward. The J-integral and stress intensity factor (SIF) values at the crack tip decrease with increased crack length. Before 0.15-mm crack length, J-integral and SIF reduce slightly with crack length and are comparatively higher, resulting in a rapid increase in crack mouth opening displacement (CMOD). Beyond 0.25-mm crack length, the values significantly decline, that there is not much possibility of crack growth, resulting in a negligible change in CMOD value. This explains the crack growth arrest obtained after 0.25-mm crack length.
Practical implications
This work's contribution is expected to reduce the additional manufacturing cost and lead time incurred in investigating reliability issues in solder joints.
Originality/value
The work investigates crack propagation mechanisms of microvoid cracks in solder joints exposed to moisture and thermal fatigue, which is still limited in the literature. The parametric variation of the crack length on stress and fatigue characteristics of solder joints, which has never been conducted, is also studied.
Details
Keywords
Zhili Zhao, Mingqiang Zhang, Xi Meng, Zhenkun Li, Jiazhe Li, Luying Qiu and Zeyu Ren
The author proposed a friction plunge micro-welding (FPMW) method and applied it to column grid array packaging to realize the connection of copper columns without precision molds…
Abstract
Purpose
The author proposed a friction plunge micro-welding (FPMW) method and applied it to column grid array packaging to realize the connection of copper columns without precision molds assisted positioning. The purpose of this paper is to study the flow behavior of the solder undergoing frictional thermo-mechanical action during the FPMW and to determine the source of the solders in the micro-zones with different microstructure characteristics near the solder/Cu column friction interface.
Design/methodology/approach
Three kinds of Sn58Bi/SAC305 and SAC305/Pb90Sn composite solder samples were designed to study the flow behavior of the solder during FPMW using Bi and Pb as tracer elements.
Findings
The results show that most of the solders in the position occupied by the copper column was softened and plasticized during the welding process and was extruded to side of the copper column, flowing axially, circumferentially and radially along a trajectory similar to a conical spiral line. Under the drive of the tangential friction force and the radial hold-tight force, the extruded out visco-plastic solders fully mixed with the visco-plastic solders on the sides of the copper column, and bonded with the solders that deformed plastically on the periphery, so that a stir zone and a dynamic recrystallization zone finally evolved. The outside plastically deformed solders evolved into a thermo-mechanical affected zone.
Originality/value
The flow behavior of the solder during the FPMW was determined, as well as the source of the solders in micro-zones with different microstructure characteristics.
Details
Keywords
Zhenkun Li, Zhili Zhao, Jinliang Liu and Xin Ding
To solve the problems caused by using precise molds for copper column positioning in the current column grid array package, this paper aims to optimize the proposed friction…
Abstract
Purpose
To solve the problems caused by using precise molds for copper column positioning in the current column grid array package, this paper aims to optimize the proposed friction plunge micro-welding (FPMW) technology without mold assistance, to overcome the problems of low interfacial bonding strength, shrinkage cavities and flash defects caused by the low hold-tight force of solder on the copper column.
Design/methodology/approach
A pressurizing device installed under the drill chuck of the friction welding machine is designed, which is used to apply a static constraint to the solder ball obliquely downward to increase the hold-tight force of the peripheral solder on the copper column during welding and promote the friction metallurgical connection between them.
Findings
The results show that the application of static constraint during welding can increase the compactness of the solder near the friction interface and effectively inhibit occurrences of flash, shrinkage cavities and crystal defects such as vacancies. Therefore, compared with the unconstrained (UC) FPMW, the average strength of the statically constrained (SC) FPMW joints and aged SC-FPMW joints can be increased by 51.1% and 122.6%, and the problem of the excessive growth of the interfacial connection layer in the UC-FPMW joints during aging can be effectively avoided.
Originality/value
The application of static constraint effectively inhibits the occurrence of defects such as shrinkage cavities, vacancies and flash in FPMW joints, and the welding quality is significantly improved.
Details
Keywords
Calvin Ling, Muhammad Taufik Azahari, Mohamad Aizat Abas and Fei Chong Ng
This paper aims to study the relationship between the ball grid array (BGA) flip-chip underfilling process parameter and its void formation region.
Abstract
Purpose
This paper aims to study the relationship between the ball grid array (BGA) flip-chip underfilling process parameter and its void formation region.
Design/methodology/approach
A set of top-down scanning acoustic microscope images of BGA underfill is collected and void labelled. The labelled images are trained with a convolutional neural network model, and the performance is evaluated. The model is tested with new images, and the void area with its region is analysed with its dispensing parameter.
Findings
All findings were well-validated with reference to the past experimental results regarding dispensing parameters and their quantitative regional formation. As the BGA is non-uniform, 85% of the test samples have void(s) formed in the emptier region. Furthermore, the highest rating factor, valve dispensing pressure with a Gini index of 0.219 and U-type dispensing pattern set of parameters generally form a lower void percentage within the underfilling, although its consistency is difficult to maintain.
Practical implications
This study enabled manufacturers to forecast the void regional formation from its filling parameters and array pattern. The filling pressure, dispensing pattern and BGA relations could provide qualitative insights to understand the void formation region in a flip-chip, enabling the prompt to formulate countermeasures to optimise voiding in a specific area in the underfill.
Originality/value
The void regional formation in a flip-chip underfilling process can be explained quantitatively with indicative parameters such as valve pressure, dispensing pattern and BGA arrangement.
Details
Keywords
Rilwan Kayode Apalowo, Mohamad Aizat Abas, Fakhrozi Che Ani, Muhamed Abdul Fatah Muhamed Mukhtar and Mohamad Riduwan Ramli
This study aims to investigate the thermal fracture mechanism of moisture-preconditioned SAC305 ball grid array (BGA) solder joints subjected to multiple reflow and thermal…
Abstract
Purpose
This study aims to investigate the thermal fracture mechanism of moisture-preconditioned SAC305 ball grid array (BGA) solder joints subjected to multiple reflow and thermal cycling.
Design/methodology/approach
The BGA package samples are subjected to JEDEC Level 1 accelerated moisture treatment (85 °C/85%RH/168 h) with five times reflow at 270 °C. This is followed by multiple thermal cycling from 0 °C to 100 °C for 40 min per cycle, per IPC-7351B standards. For fracture investigation, the cross-sections of the samples are examined and analysed using the dye-and-pry technique and backscattered scanning electron microscopy. The packages' microstructures are characterized using an energy-dispersive X-ray spectroscopy approach. Also, the package assembly is investigated using the Darveaux numerical simulation method.
Findings
The study found that critical strain density is exhibited at the component pad/solder interface of the solder joint located at the most distant point from the axes of symmetry of the package assembly. The fracture mechanism is a crack fracture formed at the solder's exterior edges and grows across the joint's transverse section. It was established that Au content in the formed intermetallic compound greatly impacts fracture growth in the solder joint interface, with a composition above 5 Wt.% Au regarded as an unsafe level for reliability. The elongation of the crack is aided by the brittle nature of the Au-Sn interface through which the crack propagates. It is inferred that refining the solder matrix elemental compound can strengthen and improve the reliability of solder joints.
Practical implications
Inspection lead time and additional manufacturing expenses spent on investigating reliability issues in BGA solder joints can be reduced using the study's findings on understanding the solder joint fracture mechanism.
Originality/value
Limited studies exist on the thermal fracture mechanism of moisture-preconditioned BGA solder joints exposed to both multiple reflow and thermal cycling. This study applied both numerical and experimental techniques to examine the reliability issue.
Details
Keywords
Yang Liu, Xin Xu, Shiqing Lv, Xuewei Zhao, Yuxiong Xue, Shuye Zhang, Xingji Li and Chaoyang Xing
Due to the miniaturization of electronic devices, the increased current density through solder joints leads to the occurrence of electromigration failure, thereby reducing the…
Abstract
Purpose
Due to the miniaturization of electronic devices, the increased current density through solder joints leads to the occurrence of electromigration failure, thereby reducing the reliability of electronic devices. The purpose of this study is to propose a finite element-artificial neural network method for the prediction of temperature and current density of solder joints, and thus provide reference information for the reliability evaluation of solder joints.
Design/methodology/approach
The temperature distribution and current density distribution of the interconnect structure of electronic devices were investigated through finite element simulations. During the experimental process, the actual temperature of the solder joints was measured and was used to optimize the finite element model. A large amount of simulation data was obtained to analyze the neural network by varying the height of solder joints, the diameter of solder pads and the magnitude of current loads. The constructed neural network was trained, tested and optimized using this data.
Findings
Based on the finite element simulation results, the current is more concentrated in the corners of the solder joints, generating a significant amount of Joule heating, which leads to localized temperature rise. The constructed neural network is trained, tested and optimized using the simulation results. The ANN 1, used for predicting solder joint temperature, achieves a prediction accuracy of 96.9%, while the ANN 2, used for predicting solder joint current density, achieves a prediction accuracy of 93.4%.
Originality/value
The proposed method can effectively improve the estimation efficiency of temperature and current density in the packaging structure. This method prevails in the field of packaging, and other factors that affect the thermal, mechanical and electrical properties of the packaging structure can be introduced into the model.
Details
Keywords
Bingyi Li, Songtao Qu and Gong Zhang
This study aims to focus on the surface mount technology (SMT) mass production process of Sn-9Zn-2.5Bi-1.5In solder. It explores it with some components that will provide…
Abstract
Purpose
This study aims to focus on the surface mount technology (SMT) mass production process of Sn-9Zn-2.5Bi-1.5In solder. It explores it with some components that will provide theoretical support for the industrial SMT application of Sn-Zn solder.
Design/methodology/approach
This study evaluates the properties of solder pastes and selects a more appropriate reflow parameter by comparing the microstructure of solder joints with different reflow soldering profile parameters. The aim is to provide an economical and reliable process for SMT production in the industry.
Findings
Solder paste wettability and solder ball testing in a nitrogen environment with an oxygen content of 3,000 ppm meet the requirements of industrial production. The printing performance of the solder paste is good and can achieve a printing rate of 100–160 mm/s. When soldering with a traditional stepped reflow soldering profile, air bubbles are generated on the surface of the solder joint, and there are many voids and defects in the solder joint. A linear reflow soldering profile reduces the residence time below the melting point of the solder paste (approximately 110 s). This reduces the time the zinc is oxidized, reducing solder joint defects. The joint strength of tin-zinc joints soldered with the optimized reflow parameters is close to that of Sn-58Bi and SAC305, with high joint strength.
Originality/value
This study attempts to industrialize the application of Sn-Zn solder and solves the problem that Sn-Zn solder paste is prone to be oxidized in the application and obtains the SMT process parameters suitable for Sn-9Zn-2.5Bi-1.5In solder.
Details
Keywords
Rilwan Kayode Apalowo, Mohamad Aizat Abas, Zuraihana Bachok, Mohamad Fikri Mohd Sharif, Fakhrozi Che Ani, Mohamad Riduwan Ramli and Muhamed Abdul Fatah bin Muhamed Mukhtar
This study aims to investigate the possible defects and their root causes in a soft-termination multilayered ceramic capacitor (MLCC) when subjected to a thermal reflow process.
Abstract
Purpose
This study aims to investigate the possible defects and their root causes in a soft-termination multilayered ceramic capacitor (MLCC) when subjected to a thermal reflow process.
Design/methodology/approach
Specimens of the capacitor assembly were subjected to JEDEC level 1 preconditioning (85 °C/85%RH/168 h) with 5× reflow at 270°C peak temperature. Then, they were inspected using a 2 µm scanning electron microscope to investigate the evidence of defects. The reliability test was also numerically simulated and analyzed using the extended finite element method implemented in ABAQUS.
Findings
Excellent agreements were observed between the SEM inspections and the simulation results. The findings showed evidence of discontinuities along the Cu and the Cu-epoxy layers and interfacial delamination crack at the Cu/Cu-epoxy interface. The possible root causes are thermal mismatch between the Cu and Cu-epoxy layers, moisture contamination and weak Cu/Cu-epoxy interface. The maximum crack length observed in the experimentally reflowed capacitor was measured as 75 µm, a 2.59% difference compared to the numerical prediction of 77.2 µm.
Practical implications
This work's contribution is expected to reduce the additional manufacturing cost and lead time in investigating reliability issues in MLCCs.
Originality/value
Despite the significant number of works on the reliability assessment of surface mount capacitors, work on crack growth in soft-termination MLCC is limited. Also, the combined experimental and numerical investigation of reflow-induced reliability issues in soft-termination MLCC is limited. These cited gaps are the novelties of this study.
Details
Keywords
Rizk Mostafa Shalaby and Mohamed Saad
The purpose of the present work is to study the impacts of rapid cooling and Tb rare-earth additions on the structural, thermal and mechanical behavior of Bi–0.5Ag lead-free…
Abstract
Purpose
The purpose of the present work is to study the impacts of rapid cooling and Tb rare-earth additions on the structural, thermal and mechanical behavior of Bi–0.5Ag lead-free solder for high-temperature applications.
Design/methodology/approach
Effect of rapid solidification processing on structural, thermal and mechanical properties of Bi-Ag lead-free solder reinforced Tb rare-earth element.
Findings
The obtained results indicated that the microstructure consists of rhombohedral Bi-rich phase and Ag99.5Bi0.5 intermetallic compound (IMC). The addition of Tb could effectively reduce the onset and melting point. The elastic modulus of Tb-containing solders was enhanced to about 90% at 0.5 Tb. The higher elastic modulus may be attributed to solid solution strengthening effect, solubility extension, microstructure refinement and precipitation hardening of uniform distribution Ag99.5Bi0.5 IMC particles which can reasonably modify the microstructure, as well as inhibit the segregation and hinder the motion of dislocations.
Originality/value
It is recommended that the lead-free Bi-0.5Ag-0.5Tb solder be a candidate instead of common solder alloy (Sn-37Pb) for high temperature and high performance applications.
Details
Keywords
Linqiang Liu, Feng Chen and Wangyun Li
The purpose of this paper is to investigate the effects of electric current stressing on damping properties of Sn5Sb solder.
Abstract
Purpose
The purpose of this paper is to investigate the effects of electric current stressing on damping properties of Sn5Sb solder.
Design/methodology/approach
Uniformly shaped Sn5Sb solders were prepared as samples. The length, width and thickness of the samples were 60.0, 5.0 and 0.5 mm, respectively. The damping properties of the samples were tested by dynamic mechanical analyzer with a cooling system to control the test temperature in the range of −100 to 100°C. Simultaneously, electric current was imposed to the tested samples using a direct current supply. After tests, the samples were characterized using scanning electron microscope, electron backscatter diffraction and transmission electron microscope, which was aimed to figure out the damping mechanism in terms of electric current stressing induced microstructure evolution.
Findings
It is confirmed experimentally that the increase in damping properties is due to Joule heating and athermal effects of current stressing, in which Joule heating should make a higher contribution. G–L theory can be used to explain the damping properties of strain amplitude under current stressing by quantitative description of geometrically necessary dislocation density. While the critical strain amplitude and high temperature activation energy decrease with increasing electric current.
Originality/value
These results provide a new method for vibration reliability evaluation of high-temperature lead-free solders in serving electronics. Notably, this method should be also inspiring for the mechanical performance evaluation and reliability assessment of conductive materials and structures serving under electric current stressing.
Details