This study aims to report the oxidation behaviors of the T91 ferritic/martensitic steel (T91 steel) and 304 austenitic stainless steel (304 steel) in supercritical water (SCW) at 600°C.

The microstructure, elemental distribution and phase structure of the oxidation layers derived from the corrosion of the T91 steel and 304 steel were analyzed by scanning electron microscopy, Oxford Instrument X-ray spectroscopy, electron scattered diffraction and transmission electron microscopy.

The oxidation layers on the T91 steel and 304 steel have duplex structure. The two steels all suffer internal oxidation, and the phase of the internal oxidation layers are indexed as Fe-Cr spinel, although their morphologies are different. The formation of a continuous Cr-rich layer is not detected because of the relatively low Cr content of the steels, which is attributed to the corrosion property.

The accelerated corrosion and corrosion mechanism of the T91 steel and 304 steel with low Cr occurring in SCW at 600°C was clarified.

This paper aims to review the effect of traditional shot peening (SP), laser shock peening (LSP) and water jet cavitation peening (WJP) on microstructure evolution and corrosion behavior of austenitic stainless steels 316L and 304.

The effect of SP, LSP and WJP on corrosion behavior of 316L and 304 were discussed in terms of surface peening–induced change in surface roughness, stress state and grain size.

Residual compressive stress and grain refinement were introduced after SP, LSP and WJP treatment in 316L and 304 stainless steels. Superior corrosion resistance can be obtained by WJP compared with SP and LSP.

The relationship between SP-, LSP- and WJP-induced change in microstructure and stress state and corrosion resistance was summarized.

The purpose of this study is to examine the effects of sensitization on the metallurgical characteristics of weld joints made up of austenitic stainless steel (AISI 316L) and ferritic stainless steel (AISI 430), using the gas tungsten arc welding (GTAW) process with ER316L filler wires.

A non-consumable tungsten electrode with a diameter of 1.6 mm was used during the GTAW procedure. The filler wire, ER316L, was selected based on the recommendation provided in literature. To explore the interconnections among the structure and properties of these weldments, the techniques including scanning electron microscopy and optical analysis have been used. In addition, the sensitization behaviour of the weldments was investigated using the double loop electrochemical potentio-kinetic reactivation (DLEPR) test.

Microstructural analyses revealed the occurrences of coarsened grains with equiaxed columnar grains and migrating grain boundaries in the weld zone. The results of the DLEPR test demonstrated that heat affected zone (HAZ) of AISI 430 was more susceptible to sensitization than HAZ of AISI 316L. Microstructure analysis also revealed the precipitation of large amounts of chromium carbide at the grain boundaries region of AISI 430 welded steel, causing more sensitization and, as a result, more failure or breaking at the side of AISI 430 weld in the dissimilar weldment of AISI 316L–AISI 430.

The present work has been carried out to determine the appropriate welding conditions for joining AISI 316L and AISI 430, as well as the metallurgical properties of the dissimilar weldment formed between AISI 316L and AISI 430. Owing to the difficulties in measuring the performance of these types of dissimilar joints given their unique mechanical and microstructural characteristics, research on the subject is limited.

This study presents a numerical modeling by the finite element method of galvanic corrosion between the bolt (cathode) and the end plate (anode). The bolt is made of three types of stainless steel: austenitic (SS304L, SS316L), martensitic (SS410, SS420) and duplex (32,101), and the end plate is made of carbon steel (S235JR).

Finite element modeling.

The results obtained show, on the one hand, that this corrosion rate increases as the conductivity increases, on the other hand, the stainless steels having the highest corrosion resistance causes a considerable loss of mass of the end plate and subsequently a decrease in the lifetime of the bolted joint.

The galvanic corrosion of beam to column bolted joint with end plate, used in steel structures, was studied in order to determine the corrosion rate of the end plate and subsequently to predict the total lifetime of the bolted joint.

Stainless-clad bimetallic steels (SCBS) are widely investigated in some extremely environmental applications areas, such as polar sailing area and tropical oil and gas platforms areas, because of their excellent anticorrosion performance and relatively lower production costs. However, the properties of SCBS, including the mechanical strength, weldability and the anticorrosion behavior, have a direct relation with the manufacturing process and can affect their practical applications. This paper aims to review the application and the properties requirements of SCBS in marine environments to promote the application of this new material in more fields.

In this paper, the manufacturing process, welding and corrosion-resistant properties of SCBS were introduced systematically by reviewing the related literatures, and some results of the authors’ research group were also introduced briefly.

Different preparation methods, such as rolling composite, casting rolling composite, explosive composite, laser cladding and plasma arc cladding, as well as the process parameters, including the vacuum degree, rolling temperature, rolling reduction ratio, volume ratios of liquid to solid, explosive ratio and the heat treatment, influenced a lot on the properties of the SCBS through changing the interface microstructures. Otherwise, the variations in rolling temperature, pass, reduction and the grain size of clad steel also brought the dissimilarities of the mechanical properties, microhardness, bonding strength and toughness. Another two new processes, clad teeming method and interlayer explosive welding, deserve more attention because of their excellent microstructure control ability. The superior corrosion resistance of SCBS can alleviate the corrosion problem in the marine environment and prolong the service life of the equipment, but the phenomenon of galvanic corrosion should be noted as much as possible. The high dilution rate, welding process specifications and heat treatment can weaken the intergranular corrosion resistance in the weld area.

This paper summarizes the application of SCBS in marine environments and provides an overview and reference for the research of stainless-clad bimetallic steel.

This paper aims to examine dissimilar joints for various applications in chemical, petrochemical, oil, gas, shipbuilding, defense, rail and nuclear industry.

This study examined the effects of cold metal transfer welding on stainless steel welds for 316L austenitic and 430 ferritic dissimilar welds with ER316L, ER309L and without (autogenous) fillers. The microstructural observation was done with an optical microscope. The mechanical test was done to reveal the strength, hardness and toughness of the joint. The electrochemical polarization tests were done to reveal intergranular and pitting corrosion in the dissimilar joints.

This microstructural study shows the presence of austenitic and ferritic phases with vermicular ferrite for ER309L filler weld, and for ER316L filler weld specimen shows predominately martensitic phase in the weld region, whereas the autogenous weld shows lathy ferrite mixed with martensitic phase. Mechanical test results indicated that filler welded specimen (ER316L and ER309L) has relatively higher strength and hardness than the autogenous weld, whereas ER316L filler weld exhibited the highest impact toughness than ER309L filler weld and lowest in autogenous weld. The electrochemical corrosion results displayed the highest degree of sensitization (DOS) in without filler welded specimen (45.62%) and lower in case of filler welded specimen ER309L (4.95%) and least in case of ER316L filler welded specimen (3.51%). The high DOS in non-filler welded specimen is correlated with the chromium carbide formation. The non-filler welded specimen shows the highest pitting corrosion attack as compared to the ER316L filler weld specimen and relatively better in ER309L filler welded specimen. The highest pitting corrosion resistance is related with the high chromium content in ER309L composition.

This experimental study is original and conducted with 316L and 430 stainless steel with ER316L, ER309 and without fillers, which will help the oil, shipbuilding and chemical industries.

Dissimilar joining of austenitic stainless steels and ferritic steels is a challenging task and has a wide range of applications due to its excellent mechanical and thermal characteristics. They are joined mostly by using conventional modes. In the current investigation, the study and optimization of hot wire TIG welding parameters was carried out.

These parameters will govern the desired characteristics of the joint. Solutions were found out through multi-response optimization by using response surface methodology and single response optimization using particle swarm optimization.

Optimized input welding parameters that were achieved are electrode current 180 amps, wire feed rate 1870 mm/min and hot wire current 98 amps and the optimized UTS is 665.45 MPa. The results from PSO were compared with RSM and the optimized input welding parameters for the electrode current, hot wire current and wire feed rate exhibited maximum ultimate tensile strength which were also confirmed from response and contour plots.

Sensitivity analysis was also performed to understand the effect of each individual parameters on the response. Microstructure features were evaluated for the joints and was found that the characteristics are within the desired criteria.

This paper aims to explore the influence of corrosion-deformation interactions (CDI) on the corrosion behavior and mechanisms of 316LN under applied tensile stresses.

Corrosion of metals would be aggravated by CDI under applied stress. Notably, the presence of nitrogen in 316LN austenitic stainless steel (SS) would enhance the corrosion resistance compared to the nitrogen-absent 316L SS. To clarify the CDI behaviors, electrochemical corrosion experiments were performed on 316LN specimens under different applied stress levels. Complementary analyses, including three-dimensional morphological examinations by KH-7700 digital microscope and scanning electron microscopy coupled with energy dispersive spectroscopy, were conducted to investigate the macroscopic and microscopic corrosion morphology and to characterize the composition of corrosion products within pits. Furthermore, ion chromatography was used to analyze the solution composition variations after immersion corrosion tests of 316LN in a 6 wt.% FeCl₃ solution compared to original FeCl₃ solution. Electrochemical experiment results revealed the linear decrease in free corrosion potential with increasing applied stress. Electrochemical impedance spectroscopy results indicated that high tensile stress level damaged the integrity of passivation film, as evidenced by the remarkable reduction in electrochemical impedance. Ion chromatography analyses proved the concentrations increase of NO₃⁻ and NH₄⁺ ion concentrations in the corrosion media after corrosion tests.

The enhanced corrosion resistance of 316LN SS is attributable to the presence of nitrogen.

The scope of this study is confined to the influence of tensile stress on the electrochemical corrosion of 316LN at ambient temperatures; it does not encompass the potential effects of elevated temperatures or compressive stress.

The resistance to stress electrochemical corrosion in SS may be enhanced through nitrogen alloying.

This paper presents a systematic investigation into the stress electrochemical corrosion of 316LN, marking the inaugural study of its impact on corrosion behaviors and underlying mechanisms.

In this paper, the authors aim to study the effect of hydrogen on the pitting corrosion behavior of Incoloy 825, a commonly used material for heat exchanger tubes in hydrogenated heat exchangers.

The pitting initiation and propagation behaviors were investigated by electrochemical and chemical immersion experiments and observed and analyzed by scanning electron microscope and energy dispersive spectrometer methods.

The results show that hydrogen significantly affects the electrochemical behavior of Incoloy 825; the self-corrosion potential decreased from −197 mV before hydrogen charging to −263 mV, −270 mV and −657 mV after hydrogen charging, and the corrosion current density increased from 0.049 µA/cm² before hydrogen charging to 2.490 µA/cm², 2.560 µA/cm² and 2.780 µA/cm² after hydrogen charging. The pitting susceptibility of the material increases.

Hydrogen is enriched on the precipitate, and the pitting corrosion also initiates at that location. The synergistic effect of hydrogen and precipitate destroys the passive film on the metal surface and promotes pitting initiation.

The purpose of this paper is to compile a comprehensive status report on pipes/piping networks across different industrial sectors, along with specifications of materials and sizes, and showcase welding avenues. It further extends to highlight the promising friction stir welding as a single solid-state pipe welding procedure. This paper will enable all piping, welding and friction stir welding stakeholders to identify scope for their engagement in a single window.

The paper is a review paper, and it is mainly structured around sections on materials, sizes and standards for pipes in different sectors and the current welding practice for joining pipe and pipe connections; on the process and principle of friction stir welding (FSW) for pipes; identification of main welding process parameters for the FSW of pipes; effects of process parameters; and a well-carved-out concluding summary.

A well-carved-out concluding summary of extracts from thoroughly studied research is presented in a structured way in which the avenues for the engagement of FSW are identified.

The implications of the research are far-reaching. The FSW is currently expanding very fast in the welding of flat surfaces and has evolved into a vast number of variants because of its advantages and versatility. The application of FSW is coming up late but catching up fast, and as a late starter, the outcomes of such a review paper may support stake holders to expand the application of this process from pipe welding to pipe manufacturing, cladding and other high-end applications. Because the process is inherently inclined towards automation, its throughput rate is high and it does not need any consumables, the ultimate benefit can be passed on to the industry in terms of financial gains.

To the best of the authors’ knowledge, this is the only review exclusively for the friction stir welding of pipes with a well-organized piping specification detailed about industrial sectors. The current pipe welding practice in each sector has been presented, and the avenues for engaging FSW have been highlighted. The FSW pipe process parameters are characteristically distinguished from the conventional FSW, and the effects of the process parameters have been presented. The summary is concise yet comprehensive and organized in a structured manner.