Search results

The purpose of this paper is to study the Mode I fracture behavior of polycarbonate (PC) parts produced using fused deposition modeling (FDM). The focus of this study is on samples printed along the out-of-plane direction with different raster angles.

Tensile and Mode I fracture tests were conducted. Semi-circular bend specimens were used for the fracture tests, which were printed in four different raster patterns of (0/90), (15/−75) (30/−60) and (45/−45). Moreover, the finite element method (FEM) was used to determine the applicability of linear elastic fracture mechanics (LEFM) for the printed PC parts. The fracture toughness results, as well as the fracture path and the fracture surfaces, were studied to describe the fracture behavior of the samples.

Finite element results confirm that the use of LEFM is allowed for the tested PC samples. The fracture toughness results show that changing the direction of the printed rasters can have an effect of up to 50% on the fracture toughness of the printed parts, with the (+45/−45) and (0/90) orientations having the highest and lowest resistance to crack propagation, respectively. Moreover, except for the (0/90) orientation, the other samples have higher crack resistance compared to the bulk material. The fracture toughness of the tested PC depends more on the toughness of the printed sample, rather than its tensile strength.

The toughness and the energy absorption capability of the printed samples (with different raster patterns) were identified as the main properties affecting the fracture toughness of the AM PC parts. Because the fracture resistance of almost all the samples was higher than that of the base material, it is evident that by choosing the right raster patterns for 3D-printed parts, very high resistance to crack growth may be obtained. Also, using FEM and comparing the size of the plastic zones, it was concluded that, although the tensile curves show nonlinearity, LEFM is still applicable for the printed parts.

The purpose of this paper is to investigate the effect of layer orientation on the tensile, flexural and fracture behavior of additively manufactured (AM) polycarbonate (PC) produced using fused deposition modeling (FDM).

An experimental approach is undertaken and a total number of 48 tests are conducted. Two types of tensile specimens are used and their mechanical behavior and fracture surfaces are studied. Also, circular parts with different layer orientations are printed and two semi-circular bending (SCB) samples are extracted from each part. Finally, the results of samples with different build directions are compared to one another to better understand the mechanical behavior of additively manufactured PC.

The results demonstrate anisotropy in the tensile, flexural and fracture behavior of the additively manufactured PC parts with the latter being less anisotropic compared to the first two. It is also demonstrated that the anisotropy of the elastic modulus is small and can be neglected. Tensile strength ranges from 40 MPa to 53 MPa. At the end, mode I fracture toughness prediction curves are provided for different directions of the FDM samples. Fracture toughness ranges from 1.93 to 2.37 MPa.mm^1/2.

The SCB specimen, a very suitable geometry for characterizing anisotropic materials, was used to characterize FDM parts for the first time. Also, the fracture properties of the AM PC have not been studied by the researchers in the past. Therefore, fracture toughness prediction curves are presented for this anisotropic material. These curves can be very suitable for designing parts that are going to be produced by 3D printing. Moreover, the effect of the area to perimeter ratio on the tensile properties of the printed parts is investigated.