This paper aims to investigate the sintering and solid liquid interdiffusion bonding (SLID) techniques to attach AlGaN/GaN-on-Si chips to direct bond copper (DBC) substrate. The influence of metal layers deposited on the backside of AlGaN/GaN-on-Si dies on the assembly process is also investigated.

The authors assumed the value of the shear strength to be a basic parameter for evaluation of mechanical properties. Additionally, the surface condition after shearing was assessed by SEM photographs and the shear surface was studied by X-ray diffraction method. The SLID requires Sn-plated DBC substrate and can be carried out at temperature slightly higher than 250°C and pressure reduced to 4 MPa, while the sintering requires process temperature of 350°C and the pressure at least 7.5 MPa.

Ag-, Au-backside covered high electron mobility transistor (HEMT) chips can be assembled on Sn-plated DBC substrates by SLID technology. In case of sintering technology, Cu- or Ag-backside covered HEMT chips can be assembled on Ag- or Ni/Au-plated DBC substrates. The SLID process can be realized at lower temperature and decreased pressure than sintering process.

For SLID technology, the adhesion between Cu-backside covered HEMT die and DBC with Sn layer loses its operational properties after short-term ageing in air at temperature of 300°C.

In the SLID process, Sn-Cu and Sn-Ag intermetallic compounds and alloys are responsible for creation of the joint between Sn-plated DBC and micropowder Ag layer, while the sintered joint between the chip and Ag-based micropowder is formed in diffusion process.