The purpose of this paper is to study the corrosion of the coupling of two different types of stainless steel, austenitic and ferritic, used in the fabrication of water reservoirs in the solar energy industry.

Potentiodynamic polarization and gravimetric immersion tests were used to evaluate corrosion of the coupling of two different types of stainless steel, austenitic and ferritic.

The galvanic corrosion was not significant in the case of the coupling of AISI 304 and 444 steels. The difference of the open circuit potentials obtained for the AISI 304 and AISI 444 steels was 28 mV for the polished samples. The galvanic current density (i_g) was 55 nA/cm². The corrosion observed in the stainless steel couple was in the weld area.

The methodology used is adequate to evaluate generalized galvanic corrosion. The problem of the corrosion in the coupling of the stainless steels is a problem of localized corrosion and the observed 28 mV potential difference was lower than the dispersion of results usually obtained from readings of corrosion potentials in electrochemical cells.

The use of two different types of steel in contact with each other may lead to galvanic corrosion, and the welding of steel pieces may lead to several corrosion problems. Since the boiler may be used in different countries, subject to a great diversity of water quality, corrosion may be a significant problem.

Literature data of the AISI 444 steel corrosion behaviour are still scarce. The coupling of two different stainless steels (AISI 304 and 444) in the water reservoir manufacturing was a necessary requirement of the solar energy industry. The manufacturers of boilers must evaluate and quantify the corrosion processes, which occur in the equipment used in the solar energy industry. As the solar energy industry has matured in the last ten years, the corrosion of this equipment may be a significant problem in due course.

Friction welding is a solid state bonding process, where the joint between two metals has been established without melting the metal. The relative motion between the faying surfaces (surfaces to be joined) under the application of pressure promotes surface interaction, friction and heat generation which subsequently results in joint formation. Stainless steel is an iron based alloy, contains various combinations of other elements to give desired characteristics, and found a wider range of applications in the areas such as petro‐chemical, fertilizer, automotive, food processing, cryogenic, nuclear and beverage sectors. In order to exploit the complete advantages of stainless steels, suitable joining techniques are highly demanded. The Friction welding is an easily integrated welding method of stainless steel, which considered as non‐weldable through fusion welding. Grain coarsening, creep failure and failure at heat‐affected zone are the major limitations of fusion welding of similar stainless steels. Friction welding eliminates such pitfalls. In the present work an attempt is made to investigate experimentally, the mechanical and metallurgical properties of friction welded joints, namely, austenitic stainless steel (AISI 304) and ferritic stainless steel (AISI 430). Evaluation of the characteristics of welded similar stainless steel joints are carried out through tensile test, hardness measurement and metallurgical investigations.

The purpose of this paper is to investigate interface characterization of CO₂ laser welded AISI 304 austenitic stainless steel and AISI 1010 low carbon steel couple. Laser welding experiments were carried under argon and helium atmospheres at 2000, 2250 and 2500 W heat inputs and 200‐300 cm/min welding speeds.

The microstructures of the welded joints and the heat affected zones (HAZ) were examined by optical microscopy, SEM, EDS and X‐Ray analysis. The tensile strength of the welded joints was measured.

The result of this study indicated that the width of welding zone and HAZ became much thinner depending on the increased welding speed. On the other hand, this width widened depending on the increased heat input. Tensile strength values also confirmed this result. The best properties were observed at the specimens welded under helium atmosphere, at 2500 W heat input and at 200 cm/min welding speed.

There are many reports which deal with the shape and solidification structure of the fusion zone of laser beam welds in relation to different laser parameters. However, the effect of all influencing factors of laser welding has up to now not been extensively researched. Much work is required for understanding the combined effect of laser parameters on the shape and microstructure of the fusion zone. This paper, therefore, is concerned with laser power, welding speed, defocusing distance and type of shielding gas and their effects on the fusion zone shape and final solidification structure of some stainless steels.

The purpose of this paper is to investigate the influence of turning parameters such as cutting speed, feed rate and depth of cut on tool flank wear and machined surface quality of AISI 304 stainless steel during environment friendly turning under nanofluid minimum quantity lubrication (NMQL) conditions using PVD-coated carbide cutting inserts.

Turning experiments are conducted as per the central composite rotatable design under the response surface methodology. ANOVA and regression analysis are employed to examine significant cutting parameters and develop mathematical models for VB (tool flank wear) and R_a (surface roughness). Multi-response desirability optimization approach is used to investigate optimum turning parameters for simultaneously minimizing VB and R_a.

Optimal input turning parameters are observed as follows: cutting speed: 168.06 m/min., feed rate: 0.06 mm/rev. and depth of cut: 0.25 mm with predicted optimal output response factors: VB: 106.864 µm and R_a: 0.571 µm at the 0.753 desirability level. ANOVA test reveals depth of cut and cutting speed-feed rate interaction as statistically significant factors influencing tool flank wear, whereas cutting speed is a dominating factor affecting surface roughness. Confirmation tests show 5.70 and 3.71 percent error between predicted and experimental examined values of VB and R_a, respectively.

AISI 304 is a highly consumed grade of stainless steel in aerospace components, chemical equipment, nuclear industry, pressure vessels, food processing equipment, paper industry, etc. However, AISI 304 stainless steel is considered as a difficult-to-cut material because of its high strength, rapid work hardening and low heat conductivity. This leads to lesser tool life and poor surface finish. Consequently, the optimization of machining parameters is necessary to minimize tool wear and surface roughness. The results obtained in this research can be used as turning database for the above-mentioned industries for attaining a better machined surface quality and tool performance under environment friendly machining conditions.

Turning of AISI 304 stainless steel under NMQL conditions results in environment friendly machining process by maintaining a dry, healthy, clean and pollution free working area.

Machining of AISI 304 stainless steel under vegetable oil-based NMQL conditions has not been investigated previously.

The purpose of this paper is to present the results of a study on friction characteristics of plasma, salt‐bath and gas nitrided layers produced in AISI 304 type austenitic and AISI 420 type martensitic stainless steels.

Plasma nitriding processes were carried out with DC‐pulsed plasma in 80% N₂+20% H₂ atmosphere at 450°C and 520°C for 8 h at a pressure of 2 mbar. Salt‐bath nitriding was performed in a cyanide‐cyanate salt‐bath at 570°C for 1.5 h. Gas nitriding was also conducted in NH₃ and CO₂ atmosphere at 570°C for 13 h. Characterization of all nitrided samples has been carried out by means of microstructure, microhardness, surface roughness measurement and friction coefficient. The morphologies of the worn surfaces of the nitrided samples were also observed using a scanning electron microscope. Friction characteristics of the nitrided samples have been investigated using a ball‐on‐disc friction and wear tester with a WC‐Co ball as the counterface under dry sliding conditions.

The plasma nitrided and salt‐bath nitrided layers on the 420 steel surfaces were much thicker than on the 304 steel surfaces. However, there was no obvious and homogeneous nitrided layer on the gas nitrided samples' surface. The plasma and salt‐bath nitriding techniques significantly increased the surface hardness of the 304 and 420 samples. The highest surface hardness of the 304 nitrided samples was obtained by the plasma nitrided technique at 520°C. On the other hand, the highest surface hardness of the 420 nitrided layers was observed in the 450°C plasma nitrided layer. Experimental friction test results showed that the salt‐bath and 450°C plasma nitrided layers were more effective in reducing the friction coefficient of the 304 and 420 stainless steels, respectively.

The relatively poor hardness and hence wear resistance of austenitic and martensitic stainless steels needs to be improved. Friction characteristic is a key property of performance for various applications of austenitic and martensitic stainless steels. This work has reported a comparison of friction characteristics of austenitic 304 and martensitic 420 stainless steels, modified using plasma, salt‐bath and gas nitriding processes. The paper is of significances for improving friction characteristics, indirectly wear performances, of austenitic and martensitic stainless steels.

The paper aims to clarify the effect of boriding on the corrosion behavior and mechanical properties of AISI 304 austenitic stainless steel.

The commercially available steel was subjected to a boriding treatment with Ekabor III powders at temperatures of 1,223-1,273 K with boriding durations of 2-4 h. Microstructural characterization of the steel was carried out with optical microscopy, scanning electron microscopy and X-ray diffraction analyses. Static immersion corrosion tests were made using a 10 percent H₂SO₄ acid solution and salt spray tests were carried out in accord with the ASTM B-117 standard.

Grain boundary precipitation of carbides was observed in the transition zone beneath the boride layers. The corrosion resistance of the steel against the acid solution increased to about seven times its untreated value with the boriding treatment.

The boride coating improved the corrosion resistance of the AISI 304 stainless steel against acidic media, but suffered from spalling in the salt spray test. Future work will focus on improving the adhesion between the coating and the substrate by changing the parameters for the boriding process.

Pack boriding is a simple, environmentally friendly coating process and can be recommended for use in small and medium enterprises. The boride coatings deposited have potential in further improving the wear and corrosion resistance of stainless steels.

The outcome of the research is of great importance for the industry using wear- and corrosion-resistant coatings.

The purpose of this paper is to focus on diversification between electrical parameters determined on the basis of instantaneous impedance measurements within the activation and reactivation scan of dissolution of sensitized AISI 304 stainless steel during a proceeding intergranular corrosion process.

The investigations were carried out by means of dynamic electrochemical impedance spectroscopy (DEIS). DEIS measurements were conducted “on‐line” while the samples were polarized in agreement with a measurement procedure presented in the ASTM G108‐94 standard, in order to guarantee conditions equivalent with the DL‐EPR tests performed on AISI 304 stainless steel.

Performed researches revealed the advantages of the DEIS technique over standard double‐loop electrochemical potentiokinetic reactivation (DL‐EPR) tests in the field of intergranular corrosion investigations. Application of the DEIS technique made it possible to trace instantaneous changes in the examined system's impedance versus potential during the intergranular corrosion process. The form of recorded DEIS spectra and obtained distribution of measurement frequencies within the reactivation potential range were equivalent to those obtained for pure iron dissolution in sulfuric acid medium. As a result, instantaneous changes of electrical double layer capacitance and charge transfer resistance as a function of potential have been obtained in the range of activation and reactivation scans.

The paper provides information regarding diversification between the electrical double layer capacitance and the charge transfer resistance determined for sensitized AISI 304 stainless steel with respect to polarization conditions during the standard DL‐EPR test, which were obtained in order to evaluate the susceptibility to intergranular corrosion.

The purpose of the paper is to investigate photochemical machining characteristics of stainless steel (AISI 304-SS304) parts with a novel design are investigated experimentally from the aspect of process parameters. The effects of phototool pattern geometry, ultraviole (UV) exposure time and etching time on of AISI 304 were evaluated.

The designed semi-automated photochemical manufacturing (PCM) equipment consists of 4 units, which include UV exposure, etching, developing and surface cleaning units. Experimental procedure has been designed via Taguchi method. Results were evaluated via Analysis of Variance (ANOVA) method.

Etching time is the most effective factor in PCM quality of AISI 304 stainless steel. Surface roughness is sensitive to geometrical pattern of the phototool for PCM of AISI 304 UV exposure time is less influential on the PCM quality for stainless steel.

The designed PCM equipment prototype is not fully automated, which requires automation for part replacements into units. The effects of the temperature inside chemical processing units on process characteristics cannot be evaluated due to equipment limitations. The effects of surface cleaning time inside surface cleaning unit are not analyzed.

The utilized PCM equipment is semi-automated equipment, with which the process parameters such as etching time, surface cleaning time, UV exposure time and developing time can be controlled. Different from literature, the effects of phototool pattern geometries on the photochemical machining quality parameters are evaluated for the processing of AISI 304. The effects of processing parameters on dimensional accuracy, which is not common in the literature for AISI 304 stainless steel, are also evaluated.

The properties of the recently developed alloy SAF 2304 and of other duplex stainless steels are reviewed. When stress corrosion cracking is a potential problem, this group of alloys offers advantages as compared to the standard austenitic stainless steels AISI 304†316. This is even more true when the high yield strength and the physical properties of the duplex stainless steels can be utilized. When duplex stainless steels do not have sufficient corrosion resistance, Sanicro 28 is a suitable material selection.

The purpose of this study is to determine the effects of post-annealing and post-tempering processes on the microstructure, mechanical properties and corrosion resistance of the AISI 304 stainless steel gas metal arc weldment.

Gas metal arc welding of AISI 304 stainless steel was carried out at an optimized processing condition. Thereafter, post-annealing and post-tempering processes were performed on the weldment. The microstructure, mechanical and electrochemical corrosion properties of the post-weld heat treated samples, as compared with the as-welded, were investigated.

The as-welded joint was characterized with sub-granular grain structure, martensite formation and Cr-rich carbides precipitates. This made it harder than the post-annealed and post-tempered joints. Because of slower cooling in the furnace, the post-annealed joint contained Cr-rich carbides precipitates. However, the microstructure of the post-tempered joint is more refined and significantly devoid of the carbide precipitates. Post-tempering process improved the elongation (∼23%), tensile (∼10%) and impact (∼31%) strengths of the gas metal arc AISI 304 stainless steel weldment, while post-annealing process improved the elongation (∼20%) and impact strength (∼72%). Owing to the refined grain structure and significant elimination of the Cr-rich carbide precipitates at the joint, the post-tempered joint exhibited better corrosion resistance in 3.5 Wt.% NaCl solution than the post-annealed and the as-welded joints.

The appropriate post-weld heat treatment that enhances microstructural homogeneity and quality of the AISI 304 gas metal arc welded joint was determined.