This paper aims to present the fabrication of 6061 aluminum alloy (AA6061) using a promising laser additive manufacturing process, called the laser-foil-printing (LFP) process. The process window of AA6061 in LFP was established to optimize process parameters for the fabrication of high strength, dense and crack-free parts even though AA6061 is challenging for laser additive manufacturing processes due to hot-cracking issues.

The multilayers AA6061 parts were fabricated by LFP to characterize for cracks and porosity. Mechanical properties of the LFP-fabricated AA6061 parts were tested using Vicker’s microhardness and tensile testes. The electron backscattered diffraction (EBSD) technique was used to reveal the grain structure and preferred orientation of AA6061 parts.

The crack-free AA6061 parts with a high relative density of 99.8% were successfully fabricated using the optimal process parameters in LFP. The LFP-fabricated parts exhibited exceptional tensile strength and comparable ductility compared to AA6061 samples fabricated by conventional laser powder bed fusion (LPBF) processes. The EBSD result shows the formation of cracks was correlated with the cooling rate of the melt pool as cracks tended to develop within finer grain structures, which were formed in a shorter solidification time and higher cooling rate.

This study presents the pioneering achievement of fabricating crack-free AA6061 parts using LFP without the necessity of preheating the substrate or mixing nanoparticles into the melt pool during the laser melting. The study includes a comprehensive examination of both the mechanical properties and grain structures, with comparisons made to parts produced through the traditional LPBF method.

Additive manufacturing (AM) can achieve significant weight savings with only minor compromises in strength if high-performance wrought aluminum alloys are used as feedstock. Despite the advantages in strength that aluminum alloys (AA) 6061 offer, they cannot be manufactured via printing because of hot cracking and other solidification problems. The purpose of this study is to achieve high-quality printing of AA6061 with nanotreated wires.

Nanotreating was used to modify the AA6061 alloy composition by adding a small fraction of nanoparticles to enhance the alloy’s manufacturability and resultant properties. Wire arc additive manufacturing (WAAM) was used to print the nanotreated AA6061 wire feedstock. The microstructure of the printed AA6061 was characterized by X-ray crystallography, optical microscopy, scanning electron microscopy and energy dispersive spectroscopy mapping. The microhardness profile, tensile behavior and fracture surface were analyzed.

This work successfully used WAAM to print nanotreated AA 6061 components. The resulting AA6061 parts were crack-free, with exceptional grain morphology and superior mechanical properties. Owing to the excellent size control capabilities of nanoparticles, a homogeneous distribution of small grains was maintained in all deposited layers, even during repeated thermal cycles.

Previous studies have not successfully printed AA6061 using WAAM. Conventional WAAM products exhibit anisotropic mechanical properties. The nanotreated AA6061 was successfully printed to achieve homogeneous microhardness and isotropic tensile properties. The promising results of this study reflect the great potential of nanotech metallurgy as applied to the WAAM process.

The weld joint mechanical properties of friction stir welding (FSW) are majorly reliant on different input parameters of the FSW machine. The study and optmization of these parameters is uttermost requirement and aim of this study to increase the suitability of FSW in different manufacturing industries. Hence, the input parameters are optimized through different soft computing methods to increase the considered objective in this study.

In this research, ultimate tensile strength (UTS), yield strength (YS) and elongation (EL) of FSW prepared butt joints of AA6061 and AA5083 Aluminium alloys materials are investigated as per American Society for Testing and Materials (ASTM E8-M04) standard. The FSW joints were prepared by changing the three input process parameters. To develop experimental run order design matrix, rotatable central composite design strategy was used. Furthermore, genetic algorithm (GA) in combination (Hybrid) with response surface methodology (RSM), artificial neural network (ANN), i.e. RSM-GA, ANN-GA, is exercised to optimize the considered process parameters.

The maximum value of UTS, YS and EL of test specimens on universal testing machine was measured as 264 MPa, 204 MPa and 14.41%, respectively. The most optimized results (UTS = 269.544 MPa, YS = 211.121 MPa and EL = 17.127%) are obtained with ANN-GA for the considered objectives.

The optimization of input parameters to increase the output objective values using hybrid soft computing techniques is unique in this research paper. The outcomes of this study will help the FSW using manufacturing industries to choose the best optimized parameters set for FSW prepared butt joint with improved mechanical properties.

The purpose of this paper is to investigate the impact of ultrasonic vibration (UV) and tool pin profile on mechanical properties and microstructural behaviour of AA7075-T651 and AA6061-T6 joints was analysed.

The joints were fabricated using three different tool pin profiles such as cylindrical, square and triangle. For each tool pin profile, two different UV powers of 1.5 kW and 2 kW were used.

On both the advancing and retreating sides of the weld, the thermo-mechanically affected zone has the lowest microhardness. In all joints, the tensile fracture locations match to the minimum hardness values. Field emission scanning electron microscope fractography of tensile tested specimens reveals heterogeneous modes of brittle, shear and ductile fracture. Three-point bending analysis was performed to determine the ductility and soundness of the weld joint. The acoustic softening effect of UV, as well as the static and dynamic ratio of tool pin profile, plays an important role in determining the material flow and mechanical behaviour of the joint.

Dissimilar aluminium joining fascinates many applications like aircraft, aerospace, automobiles, ship building and electronics, where fusion welding is a very intricate process because of the deviation in its physical and chemical properties.

From this study investigation, it is found that the square pin profiled tool with 2 kW UV power produces metallurgical defect-free and mechanically sound weld with maximum tensile strength, hardness and bending load of 297 MPa, 151HV and 3.82 kN, respectively.

The purpose of this paper is to compile a comprehensive status report on pipes/piping networks across different industrial sectors, along with specifications of materials and sizes, and showcase welding avenues. It further extends to highlight the promising friction stir welding as a single solid-state pipe welding procedure. This paper will enable all piping, welding and friction stir welding stakeholders to identify scope for their engagement in a single window.

The paper is a review paper, and it is mainly structured around sections on materials, sizes and standards for pipes in different sectors and the current welding practice for joining pipe and pipe connections; on the process and principle of friction stir welding (FSW) for pipes; identification of main welding process parameters for the FSW of pipes; effects of process parameters; and a well-carved-out concluding summary.

A well-carved-out concluding summary of extracts from thoroughly studied research is presented in a structured way in which the avenues for the engagement of FSW are identified.

The implications of the research are far-reaching. The FSW is currently expanding very fast in the welding of flat surfaces and has evolved into a vast number of variants because of its advantages and versatility. The application of FSW is coming up late but catching up fast, and as a late starter, the outcomes of such a review paper may support stake holders to expand the application of this process from pipe welding to pipe manufacturing, cladding and other high-end applications. Because the process is inherently inclined towards automation, its throughput rate is high and it does not need any consumables, the ultimate benefit can be passed on to the industry in terms of financial gains.

To the best of the authors’ knowledge, this is the only review exclusively for the friction stir welding of pipes with a well-organized piping specification detailed about industrial sectors. The current pipe welding practice in each sector has been presented, and the avenues for engaging FSW have been highlighted. The FSW pipe process parameters are characteristically distinguished from the conventional FSW, and the effects of the process parameters have been presented. The summary is concise yet comprehensive and organized in a structured manner.

The criteria importance through intercriteria correlation (CRITIC) and range of value (ROV) combined methods were used to determine a single index for all multiple responses.

This paper used cold metal transfer (CMT) and pulse metal-inert gas (MIG) welding processes to study the weld-on-bead geometry of AA2099-T86 alloy. This study used Taguchi's approach to find the optimal setting of the input welding parameters. The welding current, welding speed and contact-tip-to workpiece distance were the input welding parameters for finding the output responses, i.e. weld penetration, dilution and heat input. The L9 orthogonal array of Taguchi's approach was used to find out the optimal setting of the input parameters.

The optimal input welding parameters were determined with combined output responses. The predicted optimum welding input parameters were validated through confirmation tests. Analysis of variance showed that welding speed is the most influential factor in determining the weld bead geometry of the CMT and pulse MIG welding techniques.

The heat input and weld bead geometry are compared in both welding processes. The CMT welding samples show superior defect-free weld beads than pulse MIG welding due to lesser heat input and lesser dilution.

The conflicting results on the corrosion characteristics of aluminium matrix composites reinforced with agrarian waste have stimulated an investigation on the hardness and corrosion rate of sugar palm fibre ash (SPFA) reinforced LM26 Al/alloy composite by varying the SPFA from 0 to 10 wt% in an interval of 2 wt%. This paper aims to discuss the aforementioned issue.

The composites were produced via stir-casting and the hardness was determined using a Vickers hardness testing machine, corrosion rate was examined through the weight loss method by immersion in 0.5, 1.0 and 1.5 M hydrochloric acid (HCl) at temperatures of 303, 318, and 333 K for the maximum duration of 120 h. The morphological study was conducted using a scanning electron microscope (SEM) on the samples before and after immersion in HCl.

The incorporation of SPFA improved the hardness of the alloy from 58.22 to 93.62 VH after 10 wt% addition. The corrosion rate increases with increased content of SPFA, the concentration of HCl and temperature. The least corrosion rate of 0.0272 mpy was observed for the LM26 Al alloy in 0.5 M after 24 h while the highest corrosion rate of 0.8511 mpy was recorded for LM26 Al/10 wt% SPFA in 1.5 M HCl acid after 120 h. The SEM image of corroded samples revealed an increased number of pits with increased SPFA content.

The work is limited to SPFA up to 10 wt% as reinforcement in LM26 Al alloy, the use of HCl as corrosion medium, temperatures in the range of 303–333 K, and a weight loss method were used to evaluate the corrosion rate.

The corrosion rate was determined for LM26 Al/SPFA composites with various amounts of SPFA in 0.5, 1.0 and 1.5 M HCl at 303, 318 and 333 K and compared with the matrix alloy.

The purpose of this paper is to study the effect of vapor assembly sequence and assembly temperature on the corrosion protection of the complex silane films Al alloy. The performance and application range of silane films are enhanced.

The complex silane films were successfully prepared on the surface of aluminum alloy using via vapor phase assembly of 1,2,3-benzotriazole (BTA) and dodecyltrimethoxysilanes (DTMS). The protection of the assembly films against corrosion of Al alloy is investigated by the electrochemical measurements and the alkaline solution accelerated corrosion test. Thickness and hydrophobicity of the complex films are studied using ellipsometric spectroscopy and contact angle tests.

It shows that the anti-corrosion ability of the complex films is overall superior to that of the single-component assembled films. DTMS-BTA films have larger thickness and best anti-corrosion ability. The alkyl chains in DTMS have better compatibility with BTA molecules. The rigid BTA molecule can permeate into the long alkyl chain of DTMS as fillers and improve the barrier properties of the complex films.

In this paper, a green and efficient method of vapor phase assembly is proposed to rust prevention during manufacture of Al alloy workpiece.

This paper aims to determine the optimum parametric settings for yielding superior mechanical properties, namely, ultimate tensile strength (UTS), yield strength (YS) and percentage elongation (EL) of AZ91D/AgNPs/TiO₂ hybrid composite fabricated by friction stir processing.

An empirical model has been developed to govern crucial influencing parameters, namely, rotation speed (RS), tool transverse speed (TS), number of passes (NPS) and reinforcement fraction (RF) or weight percentage. Box Behnken design (BBD) with four input parameters and three levels of each parameter was used to design the experimental work, and analysis of variance (ANOVA) was used to check the acceptability of the developed model. Desirability function analysis (DFA) for a multiresponse optimization approach is integrated with response surface methodology (RSM). The individual desirability index (IDI) was calculated for each response, and a composite desirability index (CDI) was obtained. The optimal parametric settings were determined based on maximum CDI values. A confirmation test is also performed to compare the actual and predicted values of responses.

The relationship between input parameters and output responses (UTS, YS, and EL) was investigated using the Box-Behnken design (BBD). Silver nanoparticles (AgNPs) and nano-sized titanium dioxide (TiO₂) enhanced the ultimate tensile strength and yield strength. It was observed that the inclusion of AgNPs led to an increase in ductility, while the increase in the weight fraction of TiO₂ resulted in a decrease in ductility.

AZ91D/AgNPs/TiO₂ hybrid composite finds enormous applications in biomedical implants, aerospace, sports and aerospace industries, especially where lightweight materials with high strength are critical.

In terms of optimum value through desirability, the experimental trials yield the following results: maximum value of UTS (318.369 MPa), maximum value of YS (200.120 MPa) and EL (7.610) at 1,021 rpm of RS, 70 mm/min of TS, 4 NPS and level 3 of RF.

This paper aims to accomplish friction stir welding (FSW) of Al–Li alloy AA8090 to determine optimal settings of the process parameters for higher tensile strength and higher micro-hardness (MH) to achieve the objective of adequate butt-joint strength.

An empirical relation is implemented to govern the utmost influence parameters, i.e. tool rotation speed (TRS), tool transverse speed (TTS) and dwell time (DT). Taguchi grey relational analysis (GRA) was applied for multi-response optimization of response parameters. The grey relational grades (GRs) have been calculated for both the responses MH and ultimate tensile strength to get optimal parametric settings. The variance test has been performed to check the adequacy of the model.

The Taguchi L9 orthogonal array design was used in establishing the relation between input parameter and output parameter (tensile and MH). TTS and DT have been predicted to be the two most important parameters that influence the extreme quality features of joints by using friction stir welding. Scanning electron microscopy fractography shows the ductile failure of the welded joints.

The experimental trials provided the followings results, maximum ultimate tensile strength (UTS) of 219 MPa and MH 107.1 HV under 1,400 rpm of TRS, 40 mm/min of TTS and 8 s of DT founded the optimum value through GRA.