The potential measurements in NaCl solutions of varying concentrations carried out separately on galvanised steel and aluminised steel, each coupled galvanically with mild steel, have shown continuous rise of potential with increase in the concentration of NaCl in both the cases. For the aluminised steel‐mild steel couple, the protective potential of −760 mV is reached close to the NaCl concentration of 2%, while the potential in the case of galvanised steel‐mild steel couple has always been above the protective potential, right from the beginning, within the concentration range of NaCl (upto 3%) studied. The current and potential measurements in 0.1% NaCl solution have shown that the resistance of the surface film on aluminised steel grows from 1.037 ×103 ohm to 5.500×103 ohm within the test duration ranging from 20 hours to 100 hours and that on the galvanised steel increases from 0.90×103 ohm to 2.307×103 ohm within the test span ranging from 30 hours to 100 hours. The low current found to have been associated with the aluminised steel‐mild steel couple is not sufficient to bring the potential at the required protective level for the protection, while about 4 times higher current measured in the galvanised‐mild steel couple helps it in attaining the protective potential.

This paper aims to evaluate the inhibitive potential of borage flowers’ aqueous extract (BFAE), Borago officinalis L., against the corrosion of mild steel in 1.0 M phosphoric acid.

Evaluation was carried out by chemical hydrogen evolution (HE), mass loss (ML) and electrochemical potentiodynamic polarization (PDP) measurements. SEM-EDX analysis also was used to confirm the existence of the adsorbed film.

It was found that the inhibition efficiency of BFAE increases with the increase in its concentration, but decreases with the increase in temperature. The potentiodynamic polarization curves indicated that BFAE acts as a mixed-type inhibitor with a predominantly anodic action. The adsorption of BFAE on mild steel surface was found to obey Langmuir and thermodynamic-kinetic adsorption isotherms by forming a thin film on the metal surface. SEM-EDX analysis confirms the corrosion inhibition ability of BFEA in 1.0 M H₃PO₄ by forming a thin film on mild steel surface. In this study, the inhibitive action of BFAE components is discussed on the basis of the physical adsorption mechanism. The same results were obtained for both the freshly prepared extract and the one that kept in a refrigerator for one year.

This paper indicates that BFAE can act as a good inhibitor for the corrosion of mild steel in 1.0 M H₃PO₄ even after one year of preparation.

The purpose of this study is to use polybenzoxazine (Pbz) functionalized ZrO₂ nanoparticles to synthesize polyurethane (PU)-PbZ/ZrO₂ nanocomposite. The results derived from the electrochemical impedance spectroscopy (EIS) and polarization studies indicated the superior anticorrosive activity of PU-Pbz/ZrO₂ nanocomposite coatings compared to those of plain PU coatings. The decreased corrosion current was detected on the scratch of the PU-Pbz/ZrO₂ nanocomposite-coated mild steel surface by scanning electrochemical microscopy (SECM) compared to other studied coatings. The superior anticorrosive and mechanical properties of the proposed nanocomposite coatings provide a new horizon in the development of high-performance anticorrosive coatings for various industries.

The Pbz functionalized ZrO₂ nanoparticles were characterized by Fourier-transform infrared spectroscopy (FT-IR), X-ray diffraction (XRD), scanning electron microscopy (SEM) with energy dispersive X-ray analysis (EDX) and thermogravimetric analysis (TGA) in terms of the structural, morphological and thermal properties of these coatings. A different formulation of coatings such as PU, PU-Pbz, PU-ZrO₂ and PU-Pbz/ZrO₂ were prepared and investigated for their corrosion protection performance on mild steel in natural seawater by electrochemical techniques. The surface morphological studies were done by SEM/EDX and XRD analysis.

The superior anticorrosive property of the proposed nanocomposite coatings provides a new horizon in the development of high-performance anticorrosive coatings for various industries. Addition of Pbz wrapped ZrO₂ nanoparticles into the PU coating resulted in the blockage of charge transfer at the metal/electrolyte interface, which reduced the dissolution of mild steel. It was revealed from the SEM/EDX analysis that the formation of the corrosion products at the metal/electrolyte interface behaved as the passive layer which reduced the dissolution of steel.

The inclusion of polybenzoxazine functionalized ZrO₂ nanoparticles to the polyurethane coating reinforces the barrier and mechanical properties of PU-Pbz/ZrO₂ nanocomposite, which is due to the synergistic effect of ZrO₂ and Pbz.

The purpose of this paper is to investigate how to improve the corrosion inhibition behavior of molybdate‐based inhibitors for mild steel, using organic compounds containing a phenyl ring together with nitrite agent. As picrate contains a phenyl ring together with three substituent nitrite anions, it is used as an organic compound. In this study a new molybdate‐based inhibitor was introduced with the composition of 60 ppm molybdate/40 ppm nitrite/20 ppm picrate. Inhibition efficiency of molybdate alone and with nitrite and picrate on the uniform corrosion of mild steel in stimulated cooling water was assessed.

The inhibition efficiency of molybdate alone and with nitrite and picrate on the uniform corrosion of mild carbon steel in stimulated cooling water (SCW) was assessed by electrochemical techniques such as potentiodynamic polarization, electrochemical impedance (AC impedance) measurements and weight loss determinations at the room temperature. Studies of electron microscopy included scanning electron microscopy (SEM) photography and X‐Ray energy dispersive (EDS) microanalysis were used.

The results obtained from the polarization and AC impedance curves were in agreement with those from the corrosion weight loss results. The results indicated that the new inhibitor was as effective as molybdate alone, though at one quarter of the concentration range of molybdate, which is economically favorable.

The paper demonstrates improvement in corrosion inhibition of mild steel in SCW via a blend of molybdate, nitrite and picrate as a new anodic inhibitor.

The purpose of this study is to determine the effect of current density on the surface roughness and corrosion performance of electrodeposited Co–Ni–Fe-coated mild steel. Process variables are the key factor in controlling the electrodeposition process. It is important to study the processing parameter to optimize the mechanical and corrosion resistance performance of the coating substrate.

A low-cost electrodeposition method was used to the synthesize Co–Ni–Fe coating on the mild steel substrate. In the electrodeposition, electrochemistry concept was applied. The temperature of the process was controlled at 50 ± 5°C in an acidic environment. The influence of current density (11, 22 and 33 mA/cm²) and deposition time (15, 20 and 30 min) toward the surface roughness, hardness and corrosion rate was investigated.

The increases of time deposition and current density have improved the microhardness and corrosion resistance of Co–Ni–Fe-coated mild steel. The Co–Ni–Fe nanoparticles deposited at 30 min and current density of 33 mA/cm² experienced the smallest surface roughness value (Ra). The same sample also obtained the highest Vickers microhardness of 122.6 HV and the lowest corrosion rate. This may be due to the homogenous and complete protection coating performed on the mild steel.

The findings from the study are important for future application of Co–Ni–Fe on the mild steel parts such as fasteners, car body panels, metal chains, wire ropes, engine parts, bicycle rims, nails and screws and various outdoor uses. The improvement of corrosion resistance using optimum electrodeposition parameters is essential for these applications to prolong the life span of the parts.

A new process which pertains to fabrication of Co–Ni–Fe as a protective coating on mild steel was proposed. The Co–Ni–Fe coating can enhance the corrosion protection and thus prolong the lifespan of the mild steel parts.

The purpose of this study is to understand the inhibitor behavior of specific drug against mild steel corrosion and their adsorption mechanism on the surface.

Corrosion rates are influenced by the formation of inhibitor aggregates at the mild steel surface. Detail surface characterizations of mild steel have been studied before and after adsorption of drugs in 1N HCl solution. Scanning electron microscopy, atomic force microscopy and Fourier transform infrared spectroscopy were used to examine the effect of drug adsorption on steel surface.

Scanning electron microscopy analysis suggested that the metal had been protected from aggressive corrosion because of the addition of the inhibitors. Atomic force microscopy visualization confirmed the formation of protective layer on steel surface, resulting in the decrease in surface roughness with corrosion rates. The nature of metal surface has been analyzed by Fourier transform infrared spectroscopy.

The findings of this study will help us to understand the interaction of specific drugs with mild steel surface and their potential inhibition mechanism.

The purpose of this paper is to present the results of a two-year long study carried out in order to evaluate the corrosion performance of mild steel bare bars (BB) and epoxy-coated rebar (ECR) in concrete under a simulated harsh environment of chlorides.

The blocks are subjected to Southern Exposure testing. The electrochemical impedance spectroscopy (EIS), linear polarization resistance (LPR) and Tafel plot are performed to measure the polarization resistance and corrosion current densities of these rebars. Knife-peel test was performed to assess the adhesion between epoxy and underlying steel after two years of exposure.

Mild steel BB showed a high corrosion current density of 1.24 µA/ cm² in Tafel plots and a very low polarization resistance of 4.5 kΩ cm² in LPR technique, whereas very high charge transfer resistance of 1672 and 1675 kΩ cm² is observed on ECR and ECR with controlled damage (ECRCD), through EIS technique, respectively. EIS is observed to be a suitable tool to detect the defects in epoxy coatings. After two years of immersion in 3.89 percent NaCl⁻ solution, the mild steel BB were severely corroded and a considerable weight loss was observed, whereas under heavy chloride attack, ECR showed no deterioration of epoxy coating and neither any corrosion of underlying steel. Results of this study show that the durability of reinforced concrete (RC) structures with respect to corrosion could be enhanced by using ECR, especially in harsh climatic conditions.

The corrosion performance of mild steel and ECR in concrete under a simulating splash zone environment is evaluated. EIS was used to evaluate the health of epoxy and corrosion state of underneath steel rebars. EIS was able to detect the defects in epoxy. The durability of RC structures could be enhanced in harsh climate regions by using ECR.

This study aims to investigate the inhibition effect of a newly synthesized1,2,3-triazole containing a carbohydrate and imidazole substituents, namely, 1-((1-((2,2,7,7-tetramethyltetrahydro-5H-bis([1,3]dioxolo)[4,5-b:4′,5′-d]pyran-5-yl)methyl)-1H-1,2,3-triazol-4-yl)methyl)-1H-benzo[d]imidazole (TTB) on the corrosion of mild steel in aerated 1 M H₂SO₄.

The authors have used weight loss measurement, potentiodynamic polarization, electrochemical impedance spectroscopy, FT-IR studies, scanning electron microscopy analysis and energy dispersive X-ray (EDX) spectroscopy techniques.

It is found that, in the working range of 298-328 K, the inhibition efficiency of TTB increases with increasing concentration to attain the highest value (92 per cent) at 2.5 × 10⁻³ M. Both chemisorption and physisorption of TTB take place on the mild steel, resulting in the formation of an inhibiting film. Computational methods point to the imidazole and phenyl ring as the main structural parts responsible of adsorption by electron-donating to the steel surface, while the triazol ring is responsible for the electron accepting. Such strong donating–accepting interactions lead to higher inhibition efficiency of TTB in the aqueous working system.

This work is original with the aim of finding new acid corrosion inhibitors.

Use of aluminium is coming into vogue in the canning industry. However, the very much higher cost of aluminium than tin plate inhibits the scope for substitution of tin plate by aluminium. It is therefore of interest to examine whether steel coated with aluminium by any of the known methods is suitable for manufacture of containers for canned products. Aluminium‐coated steel can be considered only if the coating has a more negative potential than the base metal. In a study of the behaviour of sprayed aluminium coatings on mild steel in sodium chloride solutions at different pHs, Ross has pointed out that sprayed aluminium (99.5%) is more negative than steel in neutral and alkaline solutions. In this paper, the potential relationships between steel, steel sprayed with aluminium, and aluminised steel in some organic acids commonly present in food stuffs are discussed.

This paper aims to investigate and assess a perspective of combining high-strength-steel endplate with mild-steel beam and column in endplate connections.

First, experimental tests on high strength steel endplate connections were conducted at fire temperature 550°C and at an ambient temperature for reference.

The moment-rotation characteristic, rotation capacity and failure mode of high-strength-steel endplate connections in fire and at an ambient temperature were obtained through tests and compared with those of mild-steel endplate connections. Further, the provisions of Eurocode 3 were validated with test results. Moreover, the numerical study was carried out via ABAQUS and verified against the experimental results.

It is found that a thinner high-strength-steel endplate can enhance the connection’s rotation capacity both at an ambient temperature and in fire (which guarantees the safety of an entire structure) and simultaneously achieve almost the same moment resistance with a mild steel endplate connection.