AB  - Purpose Cu/Cu diffusion bonding is characterised by high electrical and thermal conductivity, as well as the mechanical strength of the interconnects. But despite a number of advantages, Cu oxidises readily upon exposure to air. To break through the adsorbed oxide-layer high temperature and pressure, long bonding time and inert gas atmosphere are required during the bonding process. This paper aims to present the implementation of an organic self-assembled monolayer (SAM) as a temporary protective coating that inhibits Cu oxidation.Design/methodology/approach Information concerning elemental composition of the Cu surface has been yielded by X-ray photoelectron spectroscopy (XPS) and Fourier-transform infrared (FTIR) spectroscopy. Two types of substrates (electroplated and sputtered Cu) are prepared for thermocompression bonding in two different ways. In the first case, Cu is cleaned with dilute sulphuric acid to remove native copper oxide. In the second case, passivation with SAM followed the cleaning step with dilute sulphuric acid. Shear strength, fracture surface, microstructure of the received Cu/Cu interconnects are investigated after the bonding procedure.Findings The XPS method revealed that SAM can retard Cu from oxidation on air for at least 12 h. SAM passivation on the substrates with sputtered Cu appears to have better quality than on the electroplated ones. This derives from the results of the shear strength tests and scanning electron microscopy (SEM) imaging of Cu/Cu interconnects cross sections. SAM passivation improved the bonding quality of the interconnects with sputtered Cu in comparison to the cleaned samples without passivation.Originality/value The Cu/Cu bonding procedure was optimised by a novel preparation method using SAMs which enables storage and bonding of Si-dies with Cu microbumps at air conditions while remaining a good-quality interconnect. The passivation revealed to be advantageous for the smooth surfaces. SEM and shear strength tests showed improved bonding quality for the passivated bottom dies with sputtered Cu in comparison to the samples without SAM.
VL  - 30
IS  - 2
SN  - 0954-0911
DO  - 10.1108/SSMT-10-2017-0033
UR  - https://doi.org/10.1108/SSMT-10-2017-0033
AU  - Lykova Maria
AU  - Panchenko Iuliana
AU  - Künzelmann Ulrich
AU  - Reif Johanna
AU  - Geidel Marion
AU  - Wolf M. Jürgen
AU  - Lang Klaus-Dieter
PY  - 2018
Y1  - 2018/01/01
TI  - Characterisation of Cu/Cu bonding using self-assembled monolayer
T2  - Soldering & Surface Mount Technology
PB  - Emerald Publishing Limited
SP  - 106
EP  - 111
Y2  - 2024/04/25
ER  -