Determination of the performance of epoxy coatings containing feldspars filler

Abstract

Purpose

To study the effect of feldspars as inorganic filler on the mechanical and dielectric properties of epoxy coatings.

Design/methodology/approach

Coating systems used were of either filler‐free epoxy resin (as reference), or epoxy resin filled with feldspars powder at four different levels by weight. Mechanical properties of the coatings were evaluated via damping hardness and abrasion and impact resistance measurements. Electrochemical impedance spectroscopy measurements were used for the evaluation of the dielectric properties while visual observations of the test panels after salt‐spray test were also made.

Findings

The addition of 15 per cent w/w feldspars resulted in a formulation giving the most positive results, e.g. improvement of the coating's mechanical characteristics and dielectric behaviour similar to that of filler‐free epoxy coatings. Practically comparable to this behaviour was that possessed by coatings with 30 per cent w/w feldspars, while further increase of the feldspars content resulted either in a reduction in the extent of the enhancement of the mechanical behaviour or even in a worsening of both mechanical and dielectric characteristics.

Originality/value

Feldspars are the most abundant group of minerals in the earth's crust; it is an inorganic, environmentally friendly material, which exhibits high Mohs hardness. The effects of feldspars in improving the mechanical characteristics of organic coatings, while not causing any reduction in the anticorrosive performance of the polymeric matrix was found through the study.