Studies of luminescence property of long afterglow Eu2+, Dy3+ activated Sr2MgSi2O7 phosphor
Article publication date: 1 August 2004
Long afterglow Sr2MgSi2O7 (SMS) phosphor was prepared by Douby's methods at high temperature and reductive atmosphere. The excitation and emission spectra of this phosphor showed that both had broad bands and that the main emission peak at 469 nm was due to 4f‐5d transitions of Eu+2 and implied that the luminescence centres Eu+2 occupied the Sr+2 sites in the Sr2MgSi2O7 host. The phosphor doped only with Eu ions did not demonstrate the long afterglow phenomenon, but when co‐doped with Dy+3 ions in the SMS matrix, significant long afterglow was observed.
Mirhabibi, A.R., Moztarzadeh, F., Aghajani Bazazi, A., Solati, M., Maghsoudipour, A. and Sarrafi, M.H. (2004), "Studies of luminescence property of long afterglow Eu2+, Dy3+ activated Sr2MgSi2O7 phosphor", Pigment & Resin Technology, Vol. 33 No. 4, pp. 220-225. https://doi.org/10.1108/03699420410546908
Emerald Group Publishing Limited
Copyright © 2004, Emerald Group Publishing Limited