AB  - Purpose– The purpose of this paper is to examine the effect of substrate temperature on friction coefficient and surface roughness of titanium nitride (TiN) coatings deposited on high‐speed steel (HSS) using commercially available cathodic arc evaporation physical vapour deposition system.Design/methodology/approach– The goal of this work is to determine the usefulness of TiN coatings in order to improve the friction coefficient and surface roughness of HSS verses substrate temperature, as vastly used in cutting tool industry and many others. A Pin‐on‐Disc test was carried out to study the coefficient of friction verses sliding distance. Surface roughness of deposited coatings was studied via surface roughness tester and atomic force microscope (AFM).Findings– Friction coefficient increased at higher temperature as compared to the coating deposited at lower substrate temperature. Surface roughness measured via both instruments showed similar trend in recorded data and, i.e. increased by increasing substrate temperature. AFM study showed that bearing ratio (per cent) decreased, whereas, fractal dimension increased with an increase in substrate temperature.Research limitations/implications– It is implied that choosing a substrate temperature above 450°C in the existing coating system could damage some machine parts.Practical implications– This scenario develops an approach to optimize the coating properties verses substrate temperature for specific application, such as cutting tools for automobiles and aircrafts.Originality/value– The coating deposited at lower temperature showed better friction coefficient and surface roughness than the coating deposited at higher temperature and vice versa.
VL  - 60
IS  - 3
SN  - 0036-8792
DO  - 10.1108/00368790810871048
UR  - https://doi.org/10.1108/00368790810871048
AU  - Ali Mubarak
AU  - Hamzah Esah
AU  - Radzi Toff Mohammad
PY  - 2008
Y1  - 2008/01/01
TI  - Friction coefficient and surface roughness of TiN‐coated HSS deposited using cathodic arc evaporation PVD technique
T2  - Industrial Lubrication and Tribology
PB  - Emerald Group Publishing Limited
SP  - 121
EP  - 130
Y2  - 2024/04/24
ER  -