Oxidation behavior of TiAl alloy for various times

Abstract

Purpose

The purpose of this paper is to investigate the oxidation behavior of Ti‐48Al‐8Cr‐2Ag (at.%) at 900°C and 1000°C for various different times.

Design/methodology/approach

Laboratory tests were performed to determine growth process of the oxide scale at 900°C and 1000°C for various different times with SEM/EDX, XRD and TEM.

Findings

Merely Al2O3 occurred on the Laves phase at the initial stage at 900°C, while a mixture of Al2O3+TiO2 formed at the initial stage at 1000°C. Oxidation rate of the alloy at 900°C after long‐term oxidation was higher than that at 1000°C because a dense Al2O3 scale formed on the surface at 1000°C.

Originality/value

The paper shows that the oxidation behavior of TiAl alloy at initial stage is the basis of the revealing mechanism of oxidation. It is necessary to further investigate the oxidation of Ti‐Al‐Cr‐Ag alloy in more detail to clearly understand its oxidation process and growth process of the oxide scale.

Citation