This paper aims to study the synergistic lubrication effects of Sn–Ag–Cu and MXene–Ti₃C₂ to improve the tribological properties of M50 bearing steel with microporous channels.

M50 matrix self-lubricating composites (MMSC) were designed and prepared by filling Sn–Ag–Cu and MXene–Ti₃C₂ in the microporous channels of M50 bearing steel. The tribology performance testing of as-prepared samples was executed with a multifunction tribometer. The optimum hole size and lubricant content, as well as self-lubricating mechanism of MMSC, were studied.

The tribological properties of MMSC are strongly dependent on the synergistic lubrication effect of MXene–Ti₃C₂ and Sn–Ag–Cu. When the hole size of microchannel is 1 mm and the content of MXene–Ti₃C₂ in mixed lubricant is 4 wt.%, MMSC shows the lowest friction coefficient and wear rate. The Sn–Ag–Cu and MXene–Ti₃C₂ are extruded from the microporous channels and spread to the friction interface, and a relatively complete lubricating film is formed at the friction interface. Meanwhile, the synergistic lubrication of Sn–Ag–Cu and MXene–Ti₃C₂ can improve the stability of the lubricating film, thus the excellent tribological property of MMSC is obtained.

The results help in deep understanding of the synergistic lubrication effects of Sn–Ag–Cu and MXene–Ti₃C₂ on the tribological properties of M50 bearing steel. This work also provides a useful reference for the tribological design of mechanical components by combining surface texture with solid lubrication.

The peer review history for this article is available at: https://publons.com/publon/10.1108/ILT-12-2023-0381/